CN101845275A - Environment-friendly wood wax oil and preparation method thereof - Google Patents
Environment-friendly wood wax oil and preparation method thereof Download PDFInfo
- Publication number
- CN101845275A CN101845275A CN201010179211A CN201010179211A CN101845275A CN 101845275 A CN101845275 A CN 101845275A CN 201010179211 A CN201010179211 A CN 201010179211A CN 201010179211 A CN201010179211 A CN 201010179211A CN 101845275 A CN101845275 A CN 101845275A
- Authority
- CN
- China
- Prior art keywords
- wood wax
- oil
- environment
- wax oil
- friendly wood
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides an environment-friendly wood wax oil and a preparation method thereof, which belong to the technical field of products of chemical industry. The environment-friendly wood wax oil is prepared by the following components in part by weight: 3 to 8 parts of alkane, 10 to 20 parts of wax, 30 to 40 parts of animal wax, 15 to 25 parts of plant resin and 5 to 15 parts of plant synthetic oil, wherein the general formula for the alkane is CnH2n+2 and n is more than or equal to 6 and less than or equal to 16. The preparation method is characterized by simple process flow, less steps, wide source for the raw material and low cost; and the prepared product has high uniformity, no toxicity and no pollution and has the functions of mildew resistance, damp proofing, moisture protection, moth proofing, surface maintenance, beautification and the like after use.
Description
Technical field
The present invention relates to a kind of woodwork coating and compound method thereof, particularly a kind of environment-friendly wood wax oil and compound method thereof belong to technical field of chemical products.
Background technology
Wood wax oil (oil based finish) is to be the wood lacquer of base-material with vegetables oil wax, is different from all kinds of traditional paints with filmogens such as synthetic resins.Traditional paint is " outside a timber ", and wood wax oil is " in timber " protection timber, that is: traditional paint forms one deck as " plasticlike " air-locked paint film at the timber outside surface, lack real timber feel, and paint film with the passing of time easily peels off cracking; Wood wax oil is then infiltrated in the timber, and the no paint film in surface so kept the feel of timber fully, makes texture more clear, more the log style.Its raw material is mainly with crude vegetal and vegetable wax and cooperate some other natural component to merge to form, wood wax oil can be infiltrated timber fully, therefore completely different in appearance with the traditional paint that has paint film to exist, the surface is open grain effect, different timber can bring different true senses of touch, and can locally repair and renovate and leave no trace, and it is also very simple to construct, only need embrocate one to twice, also can workmen's health not caused damage simultaneously.
Chinese patent application (publication number: C N101407068A) relate to wood wax oil for protecting lumber and preparation method thereof, form and comprise: vegetables oil, animal wax or vegetable wax, ferric oxide, rare earth catalyst, mineral dye, silicone oil and polyethers silicone oil dispersion agent and defoamer dimethyl silicone oil by the raw material of this wood wax oil.Though this wood wax oil for protecting lumber makes timber have certain drying, anticorrosion, insect protected, protection against the tide, mildew-resistant, termite-proof, anticracking, multiple over-all properties such as fire-retardant.But raw material rare earth catalyst, silicone oil and polyethers silicone oil dispersion agent and defoamer dimethyl-silicon wet goods expensive raw material price that this wood wax oil adopts, product cost is higher, is not suitable for the demand of the marketization.And compatibility is unreasonable between each raw material, and homogeneity is relatively poor after mixing, and uses to cause spraying inhomogeneous its over-all properties that influences on the timber.
Summary of the invention
The present invention is directed to the defective that prior art exists, good combination properties such as a kind of environmental-protecting performance and protection against the tide, mildew-resistant are provided, cost is lower, is fit to the environment-friendly wood wax oil of market-oriented demand.
Above-mentioned technical purpose of the present invention is implemented by the following technical programs: a kind of environment-friendly wood wax oil, and this wood wax oil comprises by the composition of following weight part formulated:
Alkane: 3-8 part; Paraffin: 10-20 part; Animal wax: 30-40 part
Propolis: 15-25 part; Plant is oil comprehensively: 5-15 part; Wherein said alkane general formula is CnH2n+2,6≤n≤16.
The present invention adopts the comprehensive oil of natural phant with animal wax, paraffin and propolis and cooperate normal heptane formulated, it does not contain toxic ingredients such as triphen, formaldehyde and heavy metal, do not have pungent smell, alternative paint is used for solid wood furniture, plank, three-ply wood and wooden skin etc.Wherein the vegetables oil porous in the wood wax oil enters timber inside, gives the timber deep layer and moistens maintenance; Animal wax, vegetable jelly and propolis can be combined closely with lumber fibre, strengthen surface hardness, and waterproof is antifouling, wear-resisting anti-wiping, and such compatible combination provides outstanding maintenance and decoration function to timber.
The wood wax oil that the present invention adopts is applied to solid wood furniture, plank, three-ply wood and wooden skin surface; not only play decoration function; also has good provide protection; the drying shrinkage that at first can reduce timber is wet to rise; prevent its buckling deformation, the vegetables oil porous in the wood wax oil that the present invention adopts enters timber inside.Because timber expands with heat and contract with cold because of the conversion meeting of seasonal climate.When weather is cold, the timber pore can shrink, when weather is hot, the timber pore can be expanded, and animal wax, paraffin and propolis have certain water repellency, its perviousness is better, enter in the pipe hole of timber, stopped up pore, when pore shrinks, animal wax, paraffin and propolis can be extruded a part, when pore is expanded, and the animal wax of extruding, paraffin and propolis can penetrate in the pore again again and go, fine adjustment so repeatedly is necessary to wood structure, can reduce the structural distortion that causes because of timber pore complete closed, and reduce the ability of its suction to a certain extent, reduce timber and change the distortion that causes because of external environment.Wood wax oil of the present invention in addition can increase the hardness of timber, makes it durable in use, improves its wear resistance, is coated with the erosion that wood wax oil of the present invention can also reduce the worm ant at wood surface, prevents that timber from corroding rotten because of the worm ant.
The dilution material composition that the present invention adopts is a kind of dilution raw material of full environment-friendly type, is only by carbon and two kinds of elementary composition organic compound alkane of hydrogen, and its formula of is CnH2n+2,6≤n≤16.Octane is arranged, normal hexane, normal heptane, n-decane, positive nonane etc., this class alkane is liquid at normal temperatures and pressures, effect is other main raw material of dilution wood wax oil.
In above-mentioned feature of environmental protection wood wax oil, this wood wax oil comprises by the composition of following preferred weight part formulated:
Alkane: 4-6 part; Paraffin: 12-18 part; Animal wax: 32-36 part
Propolis: 16-20 part; Plant is oil comprehensively: 8-12 part, wherein said alkane general formula is CnH2n+2,6≤n≤8.
This weight part is further optimization and the restriction to wood wax oil component of the present invention, adopt wood wax oil that the composition of this weight part is mixed with in mildew-resistant, protection against the tide, damp proof, mothproof, top layer maintenance, the effect better effects if such as beautify.
In above-mentioned feature of environmental protection wood wax oil, described animal wax is one or both in Insect Wax, the beeswax.As preferably, described animal wax is an Insect Wax.Insect Wax is river wax again, and it is big to have hardness, characteristics such as stable in properties.The effect of river wax in the preparation wood wax oil: be penetrated into timber inside and prevent the worm ant, can improve the hardness of wood again.
In above-mentioned feature of environmental protection wood wax oil, the comprehensive oil of described plant is grouped into by two or more one-tenth in Oleum Citri Reticulatae, Oleum Cocois, tung oil, the Chinese catalpa oil.As preferably, the comprehensive oil of described plant is made up of following component in percentage by weight:
Oleum Citri Reticulatae: 10%-20%; Oleum Cocois: 25%-35%; Viscotrol C 10-15%
Tung oil: 35%-45%; Chinese catalpa oil: 15%-25%.
The comprehensive oil of plant can automatically be penetrated into timber inside, protection expanding with heat and contract with cold of timber and modification.
In above-mentioned feature of environmental protection wood wax oil, described wood wax oil comprises that also weight part is the calcium naphthenate of 0-5 part.Calcium naphthenate plays solidification in the preparation wood wax oil.
In above-mentioned feature of environmental protection wood wax oil, described wood wax oil comprises that also weight part is the Viscotrol C of 0-20 part.
Another object of the present invention is to provide a kind of compound method of environment-friendly wood wax oil, and this method may further comprise the steps:
A, vegetable jelly and propolis by weight ratio add vegetable jelly in the container then, and being heated to temperature is 70～110 ℃, will stir fusing after the propolis input again, and wherein churning time is 8-15 minute;
B. animal wax, Viscotrol C and plant are comprehensively oily by weight ratio, it are joined in the vegetable jelly and propolis that melts among the step a then, fully stir 1-10 minute, and being cooled to temperature is 40～80 ℃;
C. calcium naphthenate and alkane by weight ratio join in the cooled material of step b then, and fully churning time 1-10 minute postcooling to room temperature promptly is mixed with environment-friendly wood wax oil.
In the compound method of above-mentioned environment-friendly wood wax oil, as preferably, Heating temperature is 80～100 ℃ among the step a, and churning time is 10-12 minute.
In the compound method of above-mentioned environment-friendly wood wax oil, as preferably, churning time is 3-5 minute among the step b, and cooling temperature is 50～60 ℃.
In the compound method of above-mentioned environment-friendly wood wax oil, as preferably, churning time is 3-5 minute among the step c.
In sum, the present invention compared with prior art has the following advantages:
1, wood wax oil raw material of the present invention wide material sources not only, cheap, cost is lower, is fit to large-scale market-oriented demand, and does not contain objectionable impurities in the component, has nontoxicly, pollution-free, meets the demand of every environmental protection, belongs to Green Product.
2, the compatibility rational Application has mildew-resistant, protection against the tide, damp proof, mothproof, top layer maintenance, effect such as beautifies between each component of wood wax oil of the present invention on woodworks such as solid wood furniture, plank, three-ply wood and wooden skin or bamboo product.
3, wood wax oil compound method of the present invention technical process is simple, and step is few, and preparation back product homogeneity is better, uses on woodwork or the bamboo product to spray evenly.
Embodiment
Below by specific embodiment, technical scheme of the present invention is described in further detail; But the present invention is not limited to these embodiment.
The weight part of table 1: embodiment 1～5 preparation wood wax oil
Wherein the alkane described in the embodiment 1 is that loopful is protected normal heptane, and animal wax is an Insect Wax, and propolis is a rosin, and the comprehensive oil of plant is made up of following component in percentage by weight: Oleum Citri Reticulatae: 10%; Oleum Cocois: 35%; Tung oil: 35%; Chinese catalpa oil: 20%.
Alkane described in the embodiment 2 is the normal hexane that loopful is protected, and animal wax is a beeswax, and propolis is the diene modified resin of dicyclo, and the comprehensive oil of plant is made up of following component in percentage by weight: Oleum Citri Reticulatae: 15%; Oleum Cocois: 30%; Tung oil: 40%; Chinese catalpa oil: 15%.
Alkane described in the embodiment 3 is the octane that loopful is protected, and animal wax is an Insect Wax, and propolis is a rosin, and the comprehensive oil of plant is made up of following component in percentage by weight: Oleum Citri Reticulatae: 20%; Oleum Cocois: 25%; Tung oil: 35%; Chinese catalpa oil: 20%.
Alkane described in the embodiment 4 is the positive nonane that loopful is protected, and animal wax is an Insect Wax, and propolis is the diene modified resin of dicyclo, and the comprehensive oil of plant is made up of following component in percentage by weight: Oleum Citri Reticulatae: 25%; Oleum Cocois: 30%; Tung oil: 45%.
Alkane described in the embodiment 5 is the isodecane that loopful is protected, and animal wax is an Insect Wax, and propolis is a rosin, and the comprehensive oil of plant is made up of following component in percentage by weight: Oleum Cocois: 25%; Tung oil: 50%; Chinese catalpa oil: 25%.
Embodiment 1
Take by weighing vegetable jelly and propolis by the 1 weight part proportioning of embodiment in the table 1, then vegetable jelly is added in the container, being heated to temperature is 90 ℃, will stir fusing after the propolis input again, and wherein churning time is 12 minutes;
Take by weighing comprehensively oil of animal wax, Viscotrol C and plant by the 1 weight part proportioning of embodiment in the table 1, it is joined in the vegetable jelly and propolis of above-mentioned fusing then, fully stirred 5 minutes, being cooled to temperature is 50 ℃;
Take by weighing calcium naphthenate and normal heptane by the 1 weight part proportioning of embodiment in the table 1, join then in the above-mentioned cooled material, fully 5 minutes postcooling to room temperatures of churning time promptly are mixed with environment-friendly wood wax oil.
Embodiment 2
Take by weighing vegetable jelly and propolis by the 2 weight part proportionings of embodiment in the table 1, then vegetable jelly is added in the container, being heated to temperature is 80 ℃, will stir fusing after the propolis input again, and wherein churning time is 12 minutes;
Take by weighing comprehensively oil of animal wax, Viscotrol C and plant by the 2 weight part proportionings of embodiment in the table 1, it is joined in the vegetable jelly and propolis of above-mentioned fusing then, fully stirred 3 minutes, being cooled to temperature is 60 ℃;
Take by weighing calcium naphthenate and normal hexane by the 2 weight part proportionings of embodiment in the table 1, join then in the above-mentioned cooled material, fully 3 minutes postcooling to room temperatures of churning time promptly are mixed with environment-friendly wood wax oil.
Embodiment 3
Take by weighing vegetable jelly and propolis by the 3 weight part proportionings of embodiment in the table 1, then vegetable jelly is added in the container, being heated to temperature is 100 ℃, will stir fusing after the propolis input again, and wherein churning time is 10 minutes;
Take by weighing comprehensively oil of animal wax, Viscotrol C and plant by the 3 weight part proportionings of embodiment in the table 1, it is joined in the vegetable jelly and propolis of above-mentioned fusing then, fully stirred 4 minutes, being cooled to temperature is 50 ℃;
Take by weighing calcium naphthenate and octane by the 3 weight part proportionings of embodiment in the table 1, join then in the above-mentioned cooled material, fully 4 minutes postcooling to room temperatures of churning time promptly are mixed with environment-friendly wood wax oil.
Embodiment 4
Take by weighing vegetable jelly and propolis by the 4 weight part proportionings of embodiment in the table 1, then vegetable jelly is added in the container, being heated to temperature is 70 ℃, will stir fusing after the propolis input again, and wherein churning time is 15 minutes;
Take by weighing comprehensively oil of animal wax, Viscotrol C and plant by the 4 weight part proportionings of embodiment in the table 1, it is joined in the vegetable jelly and propolis of above-mentioned fusing then, fully stirred 8 minutes, being cooled to temperature is 40 ℃;
Take by weighing positive nonane by the 4 weight part proportionings of embodiment in the table 1, join then in the above-mentioned cooled material, fully 3 minutes postcooling to room temperatures of churning time promptly are mixed with environment-friendly wood wax oil.
Embodiment 5
Take by weighing vegetable jelly and propolis by the 5 weight part proportionings of embodiment in the table 1, then vegetable jelly is added in the container, being heated to temperature is 110 ℃, will stir fusing after the propolis input again, and wherein churning time is 8 minutes;
Take by weighing comprehensively oil of animal wax and plant by the 5 weight part proportionings of embodiment in the table 1, it is joined in the vegetable jelly and propolis of above-mentioned fusing then, fully stirred 3 minutes, being cooled to temperature is 70 ℃;
Take by weighing calcium naphthenate and isodecane by the 1 weight part proportioning of embodiment in the table 1, join then in the above-mentioned cooled material, fully 8 minutes postcooling to room temperatures of churning time promptly are mixed with environment-friendly wood wax oil.
The detailed process that the wood wax oil of the present invention preparation is applied on the solid wood furniture is as follows: keep the moisture content of solid wood furniture to be no more than 20%, with the sand papering solid wood furniture till the smooth satisfaction of smooth surface.Sand paper will use from small to large successively, and the big more polishing effect of sand paper order number is fine and smooth more.The solid wood furniture surface is moist more, and the wood wax oil effect is good more, also more economizes wood wax oil simultaneously.Hole for nailing, knot eye are repaired to smooth with transparent or homochromy putty, made brushing preceding cleaning surfaces, drying, no grease and dust.
Get the wood wax oil of embodiment of the invention 1-5 preparation at random, be stirred well to during use evenly.With instruments such as cotton, scrub-brush, rollers coating is prolonged the brushing of solid wood furniture grain direction equably, after the drying, wipe with clean cotton if any uneven coating on the surface, makes and be coated with the solid wood furniture smooth surface slightly.The solid wood furniture external coating puts in place, does not stay the dead angle; Available scouring pad polishing behind 6 hours surface dryings is to reach the light effect.Keep the surperficial well-ventilated of brushing, surface drying 4-6 hour, did solid work 20-24 hour.
Above-mentioned solid wood furniture through the wood wax oil spary is placed campaigns such as warehouse 3 months through water logging 6 hours and with sample, this invention is verified and can plays mildew-resistant, protection against the tide, damp proof, mothproof, top layer maintenance and decoration function to solid wood furniture;
Specific embodiment described in the present invention only is that the present invention's spirit is illustrated.The technician of the technical field of the invention can make various modifications or replenishes or adopt similar mode to substitute described specific embodiment, but can't depart from spirit of the present invention or surmount the defined scope of appended claims.
Claims (10)
1. environment-friendly wood wax oil, this wood wax oil comprises by the composition of following weight part formulated:
Alkane: 3-8 part; Paraffin: 10-20 part; Animal wax: 30-40 part
Propolis: 15-25 part; Plant is oil comprehensively: 5-15 part; Wherein said alkane general formula is C
nH
2n+2, 6≤n≤16.
2. environment-friendly wood wax oil according to claim 1 is characterized in that: described wood wax oil comprises by the composition of following weight part formulated:
Alkane: 4-6 part; Paraffin: 12-18 part; Animal wax: 32-36 part
Propolis: 16-20 part; Plant is oil comprehensively: 8-12 part, wherein said alkane general formula is C
nH
2n+2, 6≤n≤8.
3. environment-friendly wood wax oil according to claim 1 and 2 is characterized in that: described animal wax is one or both in Insect Wax, the beeswax.
4. environment-friendly wood wax oil according to claim 1 and 2 is characterized in that: the comprehensive oil of described plant is grouped into by two or more one-tenth in Oleum Citri Reticulatae, Oleum Cocois, tung oil, the Chinese catalpa oil.
5. environment-friendly wood wax oil according to claim 1 and 2 is characterized in that: described wood wax oil comprises that also weight part is the calcium naphthenate of 0-5 part.
6. environment-friendly wood wax oil according to claim 1 and 2 is characterized in that: described wood wax oil comprises that also weight part is the Viscotrol C of 0-20 part.
7. the compound method of an environment-friendly wood wax oil, this method may further comprise the steps:
This method may further comprise the steps:
A, vegetable jelly and propolis by weight ratio add vegetable jelly in the container then, and being heated to temperature is 70～110 ℃, will stir fusing after the propolis input again, and wherein churning time is 8-15 minute;
B. animal wax, Viscotrol C and plant are comprehensively oily by weight ratio, it are joined in the vegetable jelly and propolis that melts among the step a then, fully stir 1-10 minute, and being cooled to temperature is 40～80 ℃;
C. calcium naphthenate and general formula are C by weight ratio
nH
2n+2, the alkane of 6≤n≤16 joins in the cooled material of step b then, and fully churning time 1-10 minute postcooling to room temperature promptly is mixed with environment-friendly wood wax oil.
8. the compound method of environment-friendly wood wax oil according to claim 7, it is characterized in that: Heating temperature is 80～100 ℃ among the step a, churning time is 10-12 minute.
9. the compound method of environment-friendly wood wax oil according to claim 8, it is characterized in that: churning time is 3-5 minute among the step b, cooling temperature is 50～60 ℃.
10. according to Claim 8 or the compound method of 9 or 10 described environment-friendly wood wax oils, it is characterized in that: churning time is 3-5 minute among the step c.