CN103740244A - Water-based high ultraviolet blocking paint - Google Patents

Water-based high ultraviolet blocking paint Download PDF

Info

Publication number
CN103740244A
CN103740244A CN201310602724.9A CN201310602724A CN103740244A CN 103740244 A CN103740244 A CN 103740244A CN 201310602724 A CN201310602724 A CN 201310602724A CN 103740244 A CN103740244 A CN 103740244A
Authority
CN
China
Prior art keywords
nano
paint
minute
water
raw material
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310602724.9A
Other languages
Chinese (zh)
Inventor
陈国术
马高峰
冯新生
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CHIZHOU YINGPAI TECHNOLOGY CO LTD
Original Assignee
CHIZHOU YINGPAI TECHNOLOGY CO LTD
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CHIZHOU YINGPAI TECHNOLOGY CO LTD filed Critical CHIZHOU YINGPAI TECHNOLOGY CO LTD
Priority to CN201310602724.9A priority Critical patent/CN103740244A/en
Publication of CN103740244A publication Critical patent/CN103740244A/en
Pending legal-status Critical Current

Abstract

The invention discloses an ultraviolet protective paint, which is formed by adopting nano-silica modified waterbased acrylic acid-polyurethane resin as a carrier, and adding the inorganic nano-ultraviolet absorber zinc oxide, titanium dioxide and an organic polymer ultraviolet absorber and a light stabilizer, as well as some film-forming additives, etc. With a very good paint protection effect, the paint can be widely applied to protection of exterior wall paint surfaces, protection of steel structure bridges and other large outdoor facilities, paint protection of park wooden chairs, statue carving crafts, and plastic products, etc., and can stop color change caused by ultraviolet radiation discoloration, aging and the like.

Description

The high ultraviolet-resistant coating of a kind of water-based
Technical field
The present invention relates generally to a kind of coating, relates in particular to the high ultraviolet-resistant coating of a kind of water-based.
Background technology
Coating is a kind of product that defencive function has again beautifying articles that has, and visible everywhere in the middle of people live, it is widely used in all respects such as building, steel product, woodenware, has become the indispensable product of society.
In the middle of a large amount of coating using and paint; different due to the quality of product and cost performance; also expose many problems; for example a lot of products use just there is not for a long time efflorescence, come off, the phenomenon of variable color (fading); its due defencive function is reduced greatly, lost the decoration function to object and article.Effect attractive in appearance and work-ing life are not long, have wasted greatly resource.
Its reason is exactly that people just think that coating, paint just can play the protection of object and increase gorgeous color for a long time, has ignored the Nature they are destroyed, and does not also understand coating and also needs protection with paint.
To the destruction of coating and paint, be mainly the cold and hot variation that derives from weather, the impact of dust storm, the infringement to it of environmental pollution and sunlight.If for the reason that causes coating with paint infringement, to its protection, just can make extend its work-ing life.
The annual production of domestic 2010 at present statistics building coatings is 5,000,000 tons of left and right, and the output of common paint, at-ten thousand tons, if can extend coating and the work-ing life of painting 10%, just means can reduce every year and produces 500,000 tons of building coatings, paint-ton.By 30,000 yuan/ton of calculating of middle-grade building coating, 1 year will reduce the use of 15,000,000,000 yuan of coating.This is a huge amount of money, if can reduce input, economize on resources, makes great efforts exactly to facilitate the concrete manifestation of conservation-minded society.Just can economize on resources with the energy, cut the waste and pollute, increase the economic benefit of user's use and the effect of social benefit.
Our company utilizes a kind of of high-tech approach research and production to have being applied to the existing coating such as building, steel-product, timber and plastics, painting the ultraviolet isolating paint that has defencive function.
Summary of the invention
The object of the invention is just to provide a kind of ultraviolet isolating paint that has defencive function.
The present invention is achieved by the following technical solutions:
The high ultraviolet-resistant coating of water-based, it is comprised of the raw material of following weight parts:
ZY628-75 Synolac 90-100, nano silicon 0.3-2, nano zine oxide 0.4-1, nano titanium oxide 0.1-1, Octabenzone 0.6-1,3-pyrroline 1-2, casein food grade 0.6-1, polyvinyl alcohol 3-5, zirconium silicate 0.1-0.3, tripoly phosphate sodium STPP 0.6-1, polydimethyl silane 2-3, auxiliary agent 4-6, deionized water 10-25;
Described auxiliary agent is comprised of the raw material of following weight parts:
Polyvinyl acetate emulsion 10-15, propolis 2-3, polyoxyethylene oleic acid ester 0.8-1, sodium silicoaluminate 1-2, polyoxypropyleneglycol 1-2, nano montmorillonite powder 4-5;
Above-mentioned propolis and polyoxypropyleneglycol Hybrid Heating are arrived to 60-80 ℃, after stirring, add nano montmorillonite powder, 100-200 rev/min of dispersed with stirring 4-6 minute, add polyoxyethylene oleic acid ester, 400-600 rev/min of dispersed with stirring 2-4 minute, adds each raw material of residue, at 80-100 ℃, is incubated 10-15 minute, fully ball milling, obtains described auxiliary agent.
A preparation method for the high ultraviolet-resistant coating of water-based, comprises the following steps:
Above-mentioned nano silicon, nano zine oxide, nano titanium oxide are mixed, through high speed dispersor, disperse 3-5 minute, obtain dispersion;
ZY628-75 Synolac is mixed to speed lapping 30-40 minute with above-mentioned dispersion;
Add each raw material of residue, fully mix, obtain the high ultraviolet-resistant coating of described water-based.
Advantage of the present invention is:
Coating of the present invention has good coating protection effect, can be widely used in the protection of Exterior Wall Paint Coatings, the protection of the large-scale outdoor facilities such as steel structure bridge, the lacquer painting protection of park wood chair, statue carving handicraft article, plastics etc.Stop it because of the variable color that uv irradiating causes, aging etc.
Embodiment
Embodiment 1
A water-based high ultraviolet-resistant coating, it by following weight parts (kilogram) raw material form:
ZY628-75 Synolac 100, nano silicon 0.3, nano zine oxide 0.4, nano titanium oxide 1, Octabenzone 0.6,3-pyrroline 2, casein food grade 0.6, polyvinyl alcohol 3, zirconium silicate 0.3, tripoly phosphate sodium STPP 0.6, polydimethyl silane 3, auxiliary agent 4, deionized water 25;
Described auxiliary agent is comprised of the raw material of following weight parts:
Polyvinyl acetate emulsion 15, propolis 3, polyoxyethylene oleic acid ester 0.8, sodium silicoaluminate 2, polyoxypropyleneglycol 2, nano montmorillonite powder 4;
By above-mentioned propolis and polyoxypropyleneglycol Hybrid Heating to 80 ℃, after stirring, add nano montmorillonite powder, 200 revs/min of dispersed with stirring 6 minutes, add polyoxyethylene oleic acid ester, 600 revs/min of dispersed with stirring 4 minutes, add each raw material of residue, at 100 ℃, are incubated 15 minutes, fully ball milling, obtains described auxiliary agent.
A preparation method for the high ultraviolet-resistant coating of water-based, comprises the following steps:
Above-mentioned nano silicon, nano zine oxide, nano titanium oxide are mixed, through high speed dispersor, disperse 5 minutes, obtain dispersion;
ZY628-75 Synolac is mixed to speed lapping 40 minutes with above-mentioned dispersion;
Add each raw material of residue, fully mix, obtain the high ultraviolet-resistant coating of described water-based.
Coating of the present invention needs protected face to clean in use, can suitably add pure water and be adjusted to spraying condition employing spraying application, also can adopt the forms of construction work such as roller coating, brushing.
Implementation result:
Tu is tested on PET film:
? Coat-thickness UV transmitance % VL transmitance % Surface hardness Fold resistance
Contrast PET film 0 85 89 --- ---
Sample 25μm 3 88 H ?
Sample contrast after 500h uv irradiation:
Two boards is left half of swabbing, and does not brush on the right.Top panel does not pass through irradiation, comes off duty as postradiation.

Claims (2)

1. the high ultraviolet-resistant coating of water-based, is characterized in that what it was comprised of the raw material of following weight parts:
ZY628-75 Synolac 90-100, nano silicon 0.3-2, nano zine oxide 0.4-1, nano titanium oxide 0.1-1, Octabenzone 0.6-1,3-pyrroline 1-2, casein food grade 0.6-1, polyvinyl alcohol 3-5, zirconium silicate 0.1-0.3, tripoly phosphate sodium STPP 0.6-1, polydimethyl silane 2-3, auxiliary agent 4-6, deionized water 10-25;
Described auxiliary agent is comprised of the raw material of following weight parts:
Polyvinyl acetate emulsion 10-15, propolis 2-3, polyoxyethylene oleic acid ester 0.8-1, sodium silicoaluminate 1-2, polyoxypropyleneglycol 1-2, nano montmorillonite powder 4-5;
Above-mentioned propolis and polyoxypropyleneglycol Hybrid Heating are arrived to 60-80 ℃, after stirring, add nano montmorillonite powder, 100-200 rev/min of dispersed with stirring 4-6 minute, add polyoxyethylene oleic acid ester, 400-600 rev/min of dispersed with stirring 2-4 minute, adds each raw material of residue, at 80-100 ℃, is incubated 10-15 minute, fully ball milling, obtains described auxiliary agent.
2. a preparation method for the high ultraviolet-resistant coating of water-based as claimed in claim 1, is characterized in that comprising the following steps:
Above-mentioned nano silicon, nano zine oxide, nano titanium oxide are mixed, through high speed dispersor, disperse 3-5 minute, obtain dispersion;
ZY628-75 Synolac is mixed to speed lapping 30-40 minute with above-mentioned dispersion;
Add each raw material of residue, fully mix, obtain the high ultraviolet-resistant coating of described water-based.
CN201310602724.9A 2013-11-22 2013-11-22 Water-based high ultraviolet blocking paint Pending CN103740244A (en)