CN103666133A - Stain-resistant waterborne coating - Google Patents
Stain-resistant waterborne coating Download PDFInfo
- Publication number
- CN103666133A CN103666133A CN201310612861.0A CN201310612861A CN103666133A CN 103666133 A CN103666133 A CN 103666133A CN 201310612861 A CN201310612861 A CN 201310612861A CN 103666133 A CN103666133 A CN 103666133A
- Authority
- CN
- China
- Prior art keywords
- parts
- minute
- coating
- stirring
- raw material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a stain-resistant waterborne coating which comprises raw materials in parts by weight as follows: 53-60 parts of a polytetrafluoroethylene emulsion, 1-2 parts of molybdenum disulfide, 0.1-0.3 part of cerium tetrafluoride, 1-2 parts of 2, 6- butylated hydroxytoluene, 0.4-1 part of 2-hydroxy-4-n-octoxy-benzophenone, 8-10 parts of silicon whisker, 0.8-2 parts of bisphenol A phosphite, 1-2 parts of alumina powder, 1-2 parts of alkyl phosphate diethanolamine salt, 1-2 parts of alkylolamide, 4-6 parts of maleic anhydride-acrylic copolymer, 5-10 parts of calcium silicate, 4-6 parts of an auxiliary and 10-25 parts of deionized water. The waterproof coating has good stain resistance, the adhesion on a substrate is high, the coating is stable, the drying speed is high, the coating is compact and uniform, the appearance is flat, the applicability is high, and the application range is wide.
Description
Technical field
The present invention relates generally to a kind of coating, relates in particular to a kind of stain resistant water-borne coatings.
Background technology
Coating is a kind of product that defencive function has again beautifying articles that has, and visible everywhere in the middle of people live, it is widely used in all respects such as building, steel product, woodenware, has become the indispensable product of society.
In the middle of a large amount of coating using and paint; different due to the quality of product and cost performance; also expose many problems; for example a lot of products use just there is not for a long time efflorescence, come off, the phenomenon of variable color (fading); its due defencive function is reduced greatly, lost the decoration function to object and article.Effect attractive in appearance and work-ing life are not long, have wasted greatly resource.
Its reason is exactly that people just think that coating, paint just can play the protection of object and increase gorgeous color for a long time, has ignored the Nature they are destroyed, and does not also understand coating and also needs protection with paint.
To the destruction of coating and paint, be mainly the cold and hot variation that derives from weather, the impact of dust storm, the infringement to it of environmental pollution and sunlight.If for the reason that causes coating with paint infringement, to its protection, just can make extend its work-ing life.
The annual production of domestic 2010 at present statistics building coatings is 5,000,000 tons of left and right, and the output of common paint, at-ten thousand tons, if can extend coating and the work-ing life of painting 10%, just means can reduce every year and produces 500,000 tons of building coatings, paint-ton.By 30,000 yuan/ton of calculating of middle-grade building coating, 1 year will reduce the use of 15,000,000,000 yuan of coating.This is a huge amount of money, if can reduce input, economize on resources, makes great efforts exactly to facilitate the concrete manifestation of conservation-minded society.Just can economize on resources with the energy, cut the waste and pollute, increase the economic benefit of user's use and the effect of social benefit.
Our company utilizes a kind of of high-tech approach research and production to have being applied to the existing coating such as building, steel-product, timber and plastics, painting the ultraviolet isolating paint that has defencive function.
Summary of the invention
The object of the invention is just to provide a kind of ultraviolet isolating paint that has defencive function.
The present invention is achieved by the following technical solutions:
A stain resistant water-borne coatings, it is comprised of the raw material of following weight parts:
Ptfe emulsion 53-60, molybdenumdisulphide 1-2, ceric fluoride 0.1-0.3,2,6-ditertbutylparacresol 1-2, Octabenzone 0.4-1, silicon whisker 8-10, phosphorous acid dihydroxyphenyl propane ester 0.8-2, aluminum oxide powder 1-2, alkyl phosphate diethanolamine salt 1-2, alkylol amide 1-2, copolymer of maleic anhydride and acrylic acid 4-6, Calucium Silicate powder 5-10, auxiliary agent 4-6, deionized water 10-25;
Described auxiliary agent is comprised of the raw material of following weight parts:
Polyvinyl acetate emulsion 10-15, propolis 2-3, polyoxyethylene oleic acid ester 0.8-1, sodium silicoaluminate 1-2, polyoxypropyleneglycol 1-2, nano montmorillonite powder 4-5;
Above-mentioned propolis and polyoxypropyleneglycol Hybrid Heating are arrived to 60-80 ℃, after stirring, add nano montmorillonite powder, 100-200 rev/min of dispersed with stirring 4-6 minute, add polyoxyethylene oleic acid ester, 400-600 rev/min of dispersed with stirring 2-4 minute, adds each raw material of residue, at 80-100 ℃, is incubated 10-15 minute, fully ball milling, obtains described auxiliary agent.
A preparation method for stain resistant water-borne coatings, comprises the following steps:
Above-mentioned copolymer of maleic anhydride and acrylic acid, Calucium Silicate powder, silicon whisker are mixed, pre-heat agitated 4-6 minute at 80-100 ℃, add phosphorous acid dihydroxyphenyl propane ester, aluminum oxide powder, 1800-2500 rev/min of dispersed with stirring 15-25 minute, add each raw material of residue, fully mix, obtain described stain resistant water-borne coatings.
Advantage of the present invention is:
Waterproof paint of the present invention has good contamination resistance, strong to the cohesiveness of base material, and coating is stable, and rate of drying is fast, and coating is evenly fine and close, flat appearance, and suitability is strong, applied widely.
Embodiment
Embodiment 1
A stain resistant water-borne coatings, it by following weight parts (kilogram) raw material form:
Ptfe emulsion 60, molybdenumdisulphide 2, ceric fluoride 0.3,2,6-ditertbutylparacresol 2, Octabenzone 0.4, silicon whisker 10, phosphorous acid dihydroxyphenyl propane ester 2, aluminum oxide powder 1, alkyl phosphate diethanolamine salt 2, alkylol amide 1, copolymer of maleic anhydride and acrylic acid 4, Calucium Silicate powder 10, auxiliary agent 6, deionized water 25;
Described auxiliary agent is comprised of the raw material of following weight parts:
Polyvinyl acetate emulsion 15, propolis 2, polyoxyethylene oleic acid ester 0.8, sodium silicoaluminate 1, polyoxypropyleneglycol 1, nano montmorillonite powder 5;
By above-mentioned propolis and polyoxypropyleneglycol Hybrid Heating to 80 ℃, after stirring, add nano montmorillonite powder, 200 revs/min of dispersed with stirring 6 minutes, add polyoxyethylene oleic acid ester, 600 revs/min of dispersed with stirring 2 minutes, add each raw material of residue, at 100 ℃, are incubated 15 minutes, fully ball milling, obtains described auxiliary agent.
A preparation method for stain resistant water-borne coatings, comprises the following steps:
Above-mentioned copolymer of maleic anhydride and acrylic acid, Calucium Silicate powder, silicon whisker are mixed, and at 100 ℃, pre-heat agitated is 4 minutes, adds phosphorous acid dihydroxyphenyl propane ester, aluminum oxide powder, 2500 revs/min of dispersed with stirring 25 minutes, add each raw material of residue, fully mix, obtain described stain resistant water-borne coatings.
Performance test:
Abrasion resistance test: pass through for 10000 times, paint film is without breakage;
Artificial ageing resistance test: 2000 hours non-foaming, do not peel off, flawless.
Claims (2)
1. a stain resistant water-borne coatings, is characterized in that what it was comprised of the raw material of following weight parts:
Ptfe emulsion 53-60, molybdenumdisulphide 1-2, ceric fluoride 0.1-0.3,2,6-ditertbutylparacresol 1-2, Octabenzone 0.4-1, silicon whisker 8-10, phosphorous acid dihydroxyphenyl propane ester 0.8-2, aluminum oxide powder 1-2, alkyl phosphate diethanolamine salt 1-2, alkylol amide 1-2, copolymer of maleic anhydride and acrylic acid 4-6, Calucium Silicate powder 5-10, auxiliary agent 4-6, deionized water 10-25;
Described auxiliary agent is comprised of the raw material of following weight parts:
Polyvinyl acetate emulsion 10-15, propolis 2-3, polyoxyethylene oleic acid ester 0.8-1, sodium silicoaluminate 1-2, polyoxypropyleneglycol 1-2, nano montmorillonite powder 4-5;
Above-mentioned propolis and polyoxypropyleneglycol Hybrid Heating are arrived to 60-80 ℃, after stirring, add nano montmorillonite powder, 100-200 rev/min of dispersed with stirring 4-6 minute, add polyoxyethylene oleic acid ester, 400-600 rev/min of dispersed with stirring 2-4 minute, adds each raw material of residue, at 80-100 ℃, is incubated 10-15 minute, fully ball milling, obtains described auxiliary agent.
2. a preparation method for stain resistant water-borne coatings as claimed in claim 1, is characterized in that comprising the following steps:
Above-mentioned copolymer of maleic anhydride and acrylic acid, Calucium Silicate powder, silicon whisker are mixed, pre-heat agitated 4-6 minute at 80-100 ℃, add phosphorous acid dihydroxyphenyl propane ester, aluminum oxide powder, 1800-2500 rev/min of dispersed with stirring 15-25 minute, add each raw material of residue, fully mix, obtain described stain resistant water-borne coatings.