CN110256945A - A kind of open air high-weatherability wood wax oil and preparation method thereof - Google Patents
A kind of open air high-weatherability wood wax oil and preparation method thereof Download PDFInfo
- Publication number
- CN110256945A CN110256945A CN201910688324.1A CN201910688324A CN110256945A CN 110256945 A CN110256945 A CN 110256945A CN 201910688324 A CN201910688324 A CN 201910688324A CN 110256945 A CN110256945 A CN 110256945A
- Authority
- CN
- China
- Prior art keywords
- oil
- mixture
- weatherability
- wood wax
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to wood wax oil technical fields, more particularly to a kind of outdoor high-weatherability wood wax oil and preparation method thereof, the raw material which includes has soybean oil modified long oil alkyd resin, boiled wood oil, palm wax, drier, UV absorbers, antioxidant, diluent.Due to being using soybean oil modified long oil alkyd resin and boiled wood oil as main component; using palm wax as assistance ingredient; pass through the synergistic effect of soybean oil modified long oil alkyd resin, boiled wood oil and palm wax; so that the open air high-weatherability wood wax oil is not easy depainting; it is long to the protection period of timber-work, and outdoor weathe resistance is good.In addition, the weatherability of the wood wax oil can be further increased due to being added with UV absorbers and antioxidant.The preparation method of the open air high-weatherability wood wax oil has method simple, and production cost is low, and can be suitable for the characteristics of being mass produced.
Description
Technical field
The present invention relates to wood wax oil technical fields, and in particular to a kind of open air high-weatherability wood wax oil and preparation method thereof.
Background technique
Wood wax oil is a kind of wiping agent of extracted form natural plant, suitable for the surface treatment of nature material, absorbent material,
The surface for being mainly used for all kinds of timber (including cork and hardwood) oils, waxes, polishes and repairs, it can also be used to terra cotta,
The surface treatment such as crude pottery ceramic tile, composite board, OSB plate.Its main material is divided into linseed oil, castor oil, soya-bean oil, babassu
Wax, candelila wax etc..Wood wax oil has the natural faint scent of plant, and it is saturating can to promote its water proof on the basis of conserving woodwork
The function of gas gives full play to its natural characteristic, and can deepen the texture of timber, maintains its gentle texture, additionally it is possible to realize wood
The sectional repair of product and renovation.Compared with general coating, wood wax oil it is easy to operate, coating weight is few, and workload is small, repairing at
This is low.
Because being the product that pure plant extracts, wood wax oil is without phenol, formaldehyde, polycyclic aromatic hydrocarbon, heavy metal etc. to people
Body harmful chemical component is a kind of surface wipes agent of natural environmental-protective, is used in European and American developed countries and area very extensive.
The wood wax oil of the prior art contains mostly on a small quantity to human body and the harmful substance of environment, although environmentally friendly price
But not cheap, some wood paint not only japanning complex procedures, but also shorter to the protection period of timber-work, easily depainting, cannot be right
Timber carries out digital preservation.In addition, weatherability, durability be not good enough when haze tallow oil product in the prior art is for outdoor.
Summary of the invention
It, should it is an object of the present invention in view of the deficiencies of the prior art, providing a kind of outdoor high-weatherability wood wax oil
Outdoor high-weatherability wood wax oil is not easy depainting, long to the protection period of timber-work, and outdoor weathe resistance is good.
The second object of the present invention is to provide a kind of system of outdoor high-weatherability wood wax oil in view of the deficiencies of the prior art
Preparation Method.
One of to achieve the goals above, the present invention adopts the following technical scheme:
A kind of outdoor high-weatherability wood wax oil is provided, it includes the raw material of following parts by weight:
Preferably, a kind of outdoor high-weatherability wood wax oil, it includes the raw material of following parts by weight:
More preferably, a kind of outdoor high-weatherability wood wax oil, it includes the raw material of following parts by weight:
The drier is the composition of one or both of isooctyl acid cerium or zirconium iso-octoate.
The antioxidant is diacetylmonoxime.
The diluent is one of turpentine oil, ethyl alcohol or naphtha or any two or more composition.
To achieve the goals above two, the present invention adopts the following technical scheme:
A kind of preparation method of outdoor high-weatherability wood wax oil is provided, it the following steps are included:
Step 1: the first mixture of preparation: soybean oil modified long oil alkyd resin and the palm fibre of formula ratio being added in a reservoir
Then palmitic acid wax heats certain time under certain temperature, and stirs evenly, obtain the first mixture；
Step 2: the second mixture of preparation: the boiled wood oil of formula ratio being added into the first mixture that step 1 obtains, so
Certain time is stirred with certain revolving speed afterwards, obtains the second mixture；
Step 3: preparation third mixture: the drier, ultraviolet of formula ratio is added in the second mixture obtained toward step 2
Light absorber and antioxidant obtain third mixture after mixing evenly；
Step 4, dilution: the diluent of formula ratio is added in the third mixture obtained toward step 3, after mixing evenly, i.e.,
The outdoor high-weatherability wood wax oil is made.
In above-mentioned technical proposal, in the step 1, the soybean oil modified long oil tree of formula ratio is added in a reservoir
Then rouge and palm wax heat 10min~20min at 70 DEG C~80 DEG C, and stir evenly, obtain the first mixture.
In above-mentioned technical proposal, in the step 2,3min~7min is then stirred with the revolving speed of 450rpm~550rpm,
Obtain the second mixture.
Compared with prior art, beneficial effect is the present invention:
(1) a kind of outdoor high-weatherability wood wax oil provided by the invention, including raw material have soybean oil modified long oil
Resin, boiled wood oil, palm wax, drier, UV absorbers, antioxidant, diluent.Due to being with soybean oil modified long oil
Alkyd resin and boiled wood oil are as main component, using palm wax as assisting ingredient, by soybean oil modified long oil alkyd resin,
The synergistic effect of boiled wood oil and palm wax, so that the open air high-weatherability wood wax oil is not easy depainting, to the protection period of timber-work
It is long, and outdoor weathe resistance is good.In addition, the haze tallow can be further increased due to being added with UV absorbers and antioxidant
The weatherability of oil.
(2) preparation method of a kind of outdoor high-weatherability wood wax oil provided by the invention, has method simple, production cost
It is low, and the characteristics of being mass produced can be suitable for.
Specific embodiment
In order to which the technical problems, technical solutions and beneficial effects solved by the present invention is more clearly understood, below in conjunction with
Embodiment, the present invention will be described in further detail.It should be appreciated that specific embodiment described herein is only to explain this
Invention, is not intended to limit the present invention.
Embodiment 1.
A kind of open air high-weatherability wood wax oil, it includes the raw material of following parts by weight:
In the present embodiment, drier is isooctyl acid cerium.
Wherein, antioxidant is diacetylmonoxime.
In the present embodiment, diluent is turpentine oil.
A kind of preparation method of above-mentioned outdoor high-weatherability wood wax oil, it the following steps are included:
Step 1: the first mixture of preparation: soybean oil modified long oil alkyd resin and the palm fibre of formula ratio being added in a reservoir
Then palmitic acid wax heats 15min at 75 DEG C, and stirs evenly, obtain the first mixture；
Step 2: the second mixture of preparation: the boiled wood oil of formula ratio being added into the first mixture that step 1 obtains, so
5min is stirred with the revolving speed of 500rpm afterwards, obtains the second mixture；
Step 3: preparation third mixture: the drier, ultraviolet of formula ratio is added in the second mixture obtained toward step 2
Light absorber and antioxidant obtain third mixture after mixing evenly；
Step 4, dilution: the diluent of formula ratio is added in the third mixture obtained toward step 3, after mixing evenly, i.e.,
The outdoor high-weatherability wood wax oil is made.
Embodiment 2.
A kind of open air high-weatherability wood wax oil, it includes the raw material of following parts by weight:
In the present embodiment, drier is zirconium iso-octoate.
Wherein, antioxidant is diacetylmonoxime.
In the present embodiment, diluent is ethyl alcohol.
A kind of preparation method of above-mentioned outdoor high-weatherability wood wax oil, it the following steps are included:
Step 1: the first mixture of preparation: soybean oil modified long oil alkyd resin and the palm fibre of formula ratio being added in a reservoir
Then palmitic acid wax heats 20min at 70 DEG C, and stirs evenly, obtain the first mixture；
Step 2: the second mixture of preparation: the boiled wood oil of formula ratio being added into the first mixture that step 1 obtains, so
7min is stirred with the revolving speed of 450rpm afterwards, obtains the second mixture；
Step 3: preparation third mixture: the drier, ultraviolet of formula ratio is added in the second mixture obtained toward step 2
Light absorber and antioxidant obtain third mixture after mixing evenly；
Step 4, dilution: the diluent of formula ratio is added in the third mixture obtained toward step 3, after mixing evenly, i.e.,
The outdoor high-weatherability wood wax oil is made.
Embodiment 3.
A kind of open air high-weatherability wood wax oil, it includes the raw material of following parts by weight:
In the present embodiment, drier is the composition of isooctyl acid cerium and zirconium iso-octoate.
Wherein, antioxidant is diacetylmonoxime.
In the present embodiment, diluent is naphtha.
A kind of preparation method of above-mentioned outdoor high-weatherability wood wax oil, it the following steps are included:
Step 1: the first mixture of preparation: soybean oil modified long oil alkyd resin and the palm fibre of formula ratio being added in a reservoir
Then palmitic acid wax heats 10min at 80 DEG C, and stirs evenly, obtain the first mixture；
Step 2: the second mixture of preparation: the boiled wood oil of formula ratio being added into the first mixture that step 1 obtains, so
3min is stirred with the revolving speed of 550rpm afterwards, obtains the second mixture；
Step 3: preparation third mixture: the drier, ultraviolet of formula ratio is added in the second mixture obtained toward step 2
Light absorber and antioxidant obtain third mixture after mixing evenly；
Step 4, dilution: the diluent of formula ratio is added in the third mixture obtained toward step 3, after mixing evenly, i.e.,
The outdoor high-weatherability wood wax oil is made.
Embodiment 4.
A kind of open air high-weatherability wood wax oil, it includes the raw material of following parts by weight:
In the present embodiment, drier is isooctyl acid cerium.
Wherein, antioxidant is diacetylmonoxime.
In the present embodiment, diluent is the composition of turpentine oil and naphtha.
A kind of preparation method of above-mentioned outdoor high-weatherability wood wax oil, it the following steps are included:
Step 1: the first mixture of preparation: soybean oil modified long oil alkyd resin and the palm fibre of formula ratio being added in a reservoir
Then palmitic acid wax heats 18min at 72 DEG C, and stirs evenly, obtain the first mixture；
Step 2: the second mixture of preparation: the boiled wood oil of formula ratio being added into the first mixture that step 1 obtains, so
6min is stirred with the revolving speed of 480rpm afterwards, obtains the second mixture；
Step 3: preparation third mixture: the drier, ultraviolet of formula ratio is added in the second mixture obtained toward step 2
Light absorber and antioxidant obtain third mixture after mixing evenly；
Step 4, dilution: the diluent of formula ratio is added in the third mixture obtained toward step 3, after mixing evenly, i.e.,
The outdoor high-weatherability wood wax oil is made.
Embodiment 5.
A kind of open air high-weatherability wood wax oil, it includes the raw material of following parts by weight:
In the present embodiment, drier is zirconium iso-octoate.
Wherein, antioxidant is diacetylmonoxime.
In the present embodiment, diluent is the composition of turpentine oil, ethyl alcohol and naphtha.
A kind of preparation method of above-mentioned outdoor high-weatherability wood wax oil, it the following steps are included:
Step 1: the first mixture of preparation: soybean oil modified long oil alkyd resin and the palm fibre of formula ratio being added in a reservoir
Then palmitic acid wax heats 12min at 78 DEG C, and stirs evenly, obtain the first mixture；
Step 2: the second mixture of preparation: the boiled wood oil of formula ratio being added into the first mixture that step 1 obtains, so
4min is stirred with the revolving speed of 520rpm afterwards, obtains the second mixture；
Step 3: preparation third mixture: the drier, ultraviolet of formula ratio is added in the second mixture obtained toward step 2
Light absorber and antioxidant obtain third mixture after mixing evenly；
Step 4, dilution: the diluent of formula ratio is added in the third mixture obtained toward step 3, after mixing evenly, i.e.,
The outdoor high-weatherability wood wax oil is made.
Finally it should be noted that the above embodiments are merely illustrative of the technical solutions of the present invention, rather than the present invention is protected
The limitation of range is protected, although explaining in detail referring to preferred embodiment to the present invention, those skilled in the art are answered
Work as understanding, it can be with modification or equivalent replacement of the technical solution of the present invention are made, without departing from the reality of technical solution of the present invention
Matter and range.
Claims (9)
1. a kind of open air high-weatherability wood wax oil, it is characterised in that: it includes the raw material of following parts by weight:
2. a kind of outdoor high-weatherability wood wax oil according to claim 1, it is characterised in that: it includes following parts by weight
Raw material:
3. a kind of outdoor high-weatherability wood wax oil according to claim 1, it is characterised in that: it includes following parts by weight
Raw material:
4. a kind of outdoor high-weatherability wood wax oil according to claim 1, it is characterised in that: the drier is isooctyl acid
The composition of one or both of cerium or zirconium iso-octoate.
5. a kind of outdoor high-weatherability wood wax oil according to claim 1, it is characterised in that: the antioxidant is butanone
Oxime.
6. a kind of outdoor high-weatherability wood wax oil according to claim 1, it is characterised in that: the diluent is turpentine
One of oil, ethyl alcohol or naphtha or any two or more composition.
7. a kind of preparation method of open air high-weatherability wood wax oil described in claim 1 to 6 any one, it is characterised in that:
It the following steps are included:
Step 1: the first mixture of preparation: the soybean oil modified long oil alkyd resin and palm wax of formula ratio are added in a reservoir,
Then certain time is heated under certain temperature, and is stirred evenly, and the first mixture is obtained；
Step 2: preparation the second mixture: into the first mixture that step 1 obtains addition formula ratio boiled wood oil, then with
Certain revolving speed stirs certain time, obtains the second mixture；
Step 3: preparation third mixture: the drier of formula ratio is added in the second mixture obtained toward step 2, ultraviolet light is inhaled
It receives agent and antioxidant obtains third mixture after mixing evenly；
Step 4, dilution: the diluent that formula ratio is added in the third mixture obtained toward step 3 obtains after mixing evenly
The open air high-weatherability wood wax oil.
8. a kind of preparation method of outdoor high-weatherability wood wax oil according to claim 7, it is characterised in that: the step
In one, the soybean oil modified long oil alkyd resin and palm wax of formula ratio are added in a reservoir, then adds at 70 DEG C~80 DEG C
Hot 10min~20min, and stir evenly, obtain the first mixture.
9. a kind of preparation method of outdoor high-weatherability wood wax oil according to claim 7, it is characterised in that: the step
In two, 3min~7min is then stirred with the revolving speed of 450rpm~550rpm, obtains the second mixture.