CN108273712A - A kind of coating construction process - Google Patents
A kind of coating construction process Download PDFInfo
- Publication number
- CN108273712A CN108273712A CN201810053179.5A CN201810053179A CN108273712A CN 108273712 A CN108273712 A CN 108273712A CN 201810053179 A CN201810053179 A CN 201810053179A CN 108273712 A CN108273712 A CN 108273712A
- Authority
- CN
- China
- Prior art keywords
- coating
- plank
- plate surface
- construction process
- priming
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of coating construction process, specific preparation process is as follows：Step 1：Selection：Select good plank, coating and suitable diluent；Step 2：Preliminary treatment：The plate surface wiped clean that needs are sprayed；Step 3：Coating dilutes：According to actual use situation, suitable diluent is poured into coating, and be sufficiently stirred；Step 4：Priming：Plate surface of the coating after dilution after preliminary treatment is first uniformly brushed one layer；Step 5：Spraying：Plank after priming is placed into drying under room temperature, the coating after dilution is uniformly then painted on primed surface again.The present invention is avoided using priming paint is dried in primed surface sprayed coating, due to priming paint humidity, to make outer layer coating surface the different crackle of depth size occur, to affect beauty, and the coating quality that this construction method is sprayed is good, easy to operate.
Description
Technical field
The present invention relates to application techniques field, more particularly to a kind of coating construction process.
Background technology
Application is an important link in modern product manufacture, and antirust, anticorrosive coating quality are that product is comprehensive
One of importance of quality, product appearance quality not only reflect product protection, decoration performance, but also are also to constitute product valence
An important factor for value, but there is also some disadvantages for existing coating process, such as practical painting effect is poor, and coating layer is easy to fall off
Deng seriously affecting application service life.Therefore, it is necessary to solve the above problems to invent a kind of coating construction process.
Invention content
The purpose of the present invention is to provide a kind of coating construction process, to solve the problems mentioned in the above background technology.
To achieve the above object, the present invention provides the following technical solutions：A kind of coating construction process, specific preparation process is such as
Under：
Step 1：Selection：Select good plank, coating and suitable diluent；
Step 2：Preliminary treatment：The plate surface wiped clean that needs are sprayed；
Step 3：Coating dilutes：According to actual use situation, suitable diluent is poured into coating, and fully stir
It mixes；
Step 4：Priming：Plate surface of the coating after dilution after preliminary treatment is first uniformly brushed one layer；
Step 5：Spraying：Plank after priming is placed into drying under room temperature, then again uniformly applies the coating after dilution
It brushes in primed surface；
Step 6：Dry polishing：Plank after spraying is put under room temperature and is dried, to coating table after coating drying
It polishes in face.
Preferably, also contain anticoagulant in step 1.
Preferably, the plank excessively high to moisture content is also needed in step 2, processing is dried, to containing excessive tiny wood
Eye plate surface carry out brush bottom obtain it is precious.
Preferably, described to choose the high-quality plank that moisture content is 10%-30%.
Preferably, drying time is set as 10min-20min in step 5, and temperature setting is 20 DEG C -35 DEG C, dry environment
For dustfree environment.
Preferably, temperature is set as 20 DEG C -35 DEG C in step 6, and selected abrasor is that waterproof abrasive paper is gently polished.
The technique effect and advantage of the present invention：
1, using anticoagulant, avoiding coating can not use in a short time, and generate solidification, to cause resource
Waste；
2, it obtains precious by being wiped, being dried and brush bottom to choosing high-quality plate surface, it is recessed to avoid coating surface appearance
White haze shape is presented in sunken needle point pore, surface blistering and film, to be impacted to the quality of spraying；
3, it is dried, is avoided in primed surface sprayed coating using to priming paint, it is outer to make due to priming paint humidity
There is the different crackle of depth size in layer coating surface, to affect beauty, and the painting that this construction method is sprayed
Expect it is high-quality, it is easy to operate.
Description of the drawings
Fig. 1 is step structural schematic diagram of the present invention.
Specific implementation mode
Following will be combined with the drawings in the embodiments of the present invention, and technical solution in the embodiment of the present invention carries out clear, complete
Site preparation describes, it is clear that described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.It is based on
Embodiment in the present invention, it is obtained by those of ordinary skill in the art without making creative efforts every other
Embodiment shall fall within the protection scope of the present invention.
Embodiment 1：A kind of coating construction process, specific preparation process are as follows：
Step 1：Selection：It is high-quality plank, coating and the suitable diluent of 10%-20% to select moisture content；
Step 2：Preliminary treatment：The plate surface wiped clean that needs are sprayed, and to containing the excessive tiny wooden eye
Plate surface carry out brush bottom obtain it is precious；
Step 3：Coating dilutes：According to actual use situation, suitable diluent is poured into coating, and fully stir
It mixes；
Step 4：Priming：Plate surface of the coating after dilution after preliminary treatment is first uniformly brushed one layer；
Step 5：Spraying：Plank after priming is placed to drying 10 minutes under the dustfree environment of 20 DEG C of -35 DEG C of temperature,
Then the coating after dilution is uniformly painted on primed surface again；
Step 6：Dry polishing：Plank after spraying is put into temperature to be dried for 20 DEG C -35 DEG C, waits for that coating is dried
It is gently polished coating surface with waterproof abrasive paper afterwards.
Embodiment 2：A kind of coating construction process, specific preparation process are as follows：
Step 1：Selection：It is high-quality plank, coating and the suitable diluent of 10%-20% to select moisture content；
Step 2：Preliminary treatment：The plate surface wiped clean that needs are sprayed, and to containing the excessive tiny wooden eye
Plate surface carry out brush bottom obtain it is precious；
Step 3：Coating dilutes：According to actual use situation, suitable diluent is poured into coating, and fully stir
It mixes；
Step 4：Priming：Plate surface of the coating after dilution after preliminary treatment is first uniformly brushed one layer；
Step 5：Spraying：Plank after priming is placed to drying 15 minutes under the dustfree environment of 20 DEG C of -35 DEG C of temperature,
Then the coating after dilution is uniformly painted on primed surface again；
Step 6：Dry polishing：Plank after spraying is put into temperature to be dried for 25 DEG C -35 DEG C, waits for that coating is dried
It is gently polished coating surface with waterproof abrasive paper afterwards.
Embodiment 3：A kind of coating construction process, specific preparation process are as follows：
Step 1：Selection：It is high-quality plank, coating and the suitable diluent of 10%-20% to select moisture content；
Step 2：Preliminary treatment：The plate surface wiped clean that needs are sprayed, and to containing the excessive tiny wooden eye
Plate surface carry out brush bottom obtain it is precious；
Step 3：Coating dilutes：According to actual use situation, suitable diluent is poured into coating, and fully stir
It mixes；
Step 4：Priming：Plate surface of the coating after dilution after preliminary treatment is first uniformly brushed one layer；
Step 5：Spraying：Plank after priming is placed to drying 20 minutes under the dustfree environment of 20 DEG C of -35 DEG C of temperature,
Then the coating after dilution is uniformly painted on primed surface again；
Step 6：Dry polishing：Plank after spraying is put into temperature to be dried for 20 DEG C -35 DEG C, waits for that coating is dried
It is gently polished coating surface with waterproof abrasive paper afterwards.
Embodiment 4：A kind of coating construction process, specific preparation process are as follows：
Step 1：Selection：It is high-quality plank, coating and the suitable diluent of 20%-30% to select moisture content；
Step 2：Preliminary treatment：The plate surface wiped clean that needs are sprayed, and to containing the excessive tiny wooden eye
Plate surface carry out brush bottom obtain it is precious；
Step 3：Coating dilutes：According to actual use situation, suitable diluent is poured into coating, and fully stir
It mixes；
Step 4：Priming：Plate surface of the coating after dilution after preliminary treatment is first uniformly brushed one layer；
Step 5：Spraying：Plank after priming is placed to drying 10 minutes under the dustfree environment of 20 DEG C of -35 DEG C of temperature,
Then the coating after dilution is uniformly painted on primed surface again；
Step 6：Dry polishing：Plank after spraying is put into temperature to be dried for 20 DEG C -35 DEG C, waits for that coating is dried
It is gently polished coating surface with waterproof abrasive paper afterwards.
Embodiment 5：A kind of coating construction process, specific preparation process are as follows：
Step 1：Selection：It is high-quality plank, coating and the suitable diluent of 20%-30% to select moisture content；
Step 2：Preliminary treatment：The plate surface wiped clean that needs are sprayed, and to containing the excessive tiny wooden eye
Plate surface carry out brush bottom obtain it is precious；
Step 3：Coating dilutes：According to actual use situation, suitable diluent is poured into coating, and fully stir
It mixes；
Step 4：Priming：Plate surface of the coating after dilution after preliminary treatment is first uniformly brushed one layer；
Step 5：Spraying：Plank after priming is placed to drying 15 minutes under the dustfree environment of 20 DEG C of -35 DEG C of temperature,
Then the coating after dilution is uniformly painted on primed surface again；
Step 6：Dry polishing：Plank after spraying is put into temperature to be dried for 20 DEG C -35 DEG C, waits for that coating is dried
It is gently polished coating surface with waterproof abrasive paper afterwards.
Embodiment 6：A kind of coating construction process, specific preparation process are as follows：
Step 1：Selection：It is high-quality plank, coating and the suitable diluent of 20%-30% to select moisture content；
Step 2：Preliminary treatment：The plate surface wiped clean that needs are sprayed, and to containing the excessive tiny wooden eye
Plate surface carry out brush bottom obtain it is precious；
Step 3：Coating dilutes：According to actual use situation, suitable diluent is poured into coating, and fully stir
It mixes；
Step 4：Priming：Plate surface of the coating after dilution after preliminary treatment is first uniformly brushed one layer；
Step 5：Spraying：Plank after priming is placed to drying 20 minutes under the dustfree environment of 20 DEG C of -35 DEG C of temperature,
Then the coating after dilution is uniformly painted on primed surface again；
Step 6：Dry polishing：Plank after spraying is put into temperature to be dried for 20 DEG C -35 DEG C, waits for that coating is dried
It is gently polished coating surface with waterproof abrasive paper afterwards.
Embodiment 7：A kind of coating construction process, specific preparation process are as follows：
Step 1：Selection：It is the high-quality plank of 10%-20%, coating, suitable diluent and suitable to select moisture content
Anticoagulant；
Step 2：Preliminary treatment：The plate surface wiped clean that needs are sprayed, and to containing the excessive tiny wooden eye
Plate surface carry out brush bottom obtain it is precious；
Step 3：Coating dilutes：According to actual use situation, suitable diluent and anticoagulant are poured into coating,
And it is sufficiently stirred；
Step 4：Priming：Plate surface of the coating after dilution after preliminary treatment is first uniformly brushed one layer；
Step 5：Spraying：Plank after priming is placed to drying 10 minutes under the dustfree environment of 20 DEG C of -35 DEG C of temperature,
Then the coating after dilution is uniformly painted on primed surface again；
Step 6：Dry polishing：Plank after spraying is put into temperature to be dried for 20 DEG C -35 DEG C, waits for that coating is dried
It is gently polished coating surface with waterproof abrasive paper afterwards.
Embodiment 8：A kind of coating construction process, specific preparation process are as follows：
Step 1：Selection：It is the high-quality plank of 10%-20%, coating, suitable diluent and suitable to select moisture content
Anticoagulant；
Step 2：Preliminary treatment：The plate surface wiped clean that needs are sprayed, and to containing the excessive tiny wooden eye
Plate surface carry out brush bottom obtain it is precious；
Step 3：Coating dilutes：According to actual use situation, suitable diluent and anticoagulant are poured into coating,
And it is sufficiently stirred；
Step 4：Priming：Plate surface of the coating after dilution after preliminary treatment is first uniformly brushed one layer；
Step 5：Spraying：Plank after priming is placed to drying 15 minutes under the dustfree environment of 20 DEG C of -35 DEG C of temperature,
Then the coating after dilution is uniformly painted on primed surface again；
Step 6：Dry polishing：Plank after spraying is put into temperature to be dried for 25 DEG C -35 DEG C, waits for that coating is dried
It is gently polished coating surface with waterproof abrasive paper afterwards.
Embodiment 9：A kind of coating construction process, specific preparation process are as follows：
Step 1：Selection：It is the high-quality plank of 10%-20%, coating, suitable diluent and suitable to select moisture content
Anticoagulant；
Step 2：Preliminary treatment：The plate surface wiped clean that needs are sprayed, and to containing the excessive tiny wooden eye
Plate surface carry out brush bottom obtain it is precious；
Step 3：Coating dilutes：According to actual use situation, suitable diluent and anticoagulant are poured into coating,
And it is sufficiently stirred；
Step 4：Priming：Plate surface of the coating after dilution after preliminary treatment is first uniformly brushed one layer；
Step 5：Spraying：Plank after priming is placed to drying 20 minutes under the dustfree environment of 20 DEG C of -35 DEG C of temperature,
Then the coating after dilution is uniformly painted on primed surface again；
Step 6：Dry polishing：Plank after spraying is put into temperature to be dried for 20 DEG C -35 DEG C, waits for that coating is dried
It is gently polished coating surface with waterproof abrasive paper afterwards.
Embodiment 10：A kind of coating construction process, specific preparation process are as follows：
Step 1：Selection：It is the high-quality plank of 20%-30%, coating, suitable diluent and suitable to select moisture content
Anticoagulant；
Step 2：Preliminary treatment：The plate surface wiped clean that needs are sprayed, and to containing the excessive tiny wooden eye
Plate surface carry out brush bottom obtain it is precious；
Step 3：Coating dilutes：According to actual use situation, suitable diluent and anticoagulant are poured into coating,
And it is sufficiently stirred；
Step 4：Priming：Plate surface of the coating after dilution after preliminary treatment is first uniformly brushed one layer；
Step 5：Spraying：Plank after priming is placed to drying 10 minutes under the dustfree environment of 20 DEG C of -35 DEG C of temperature,
Then the coating after dilution is uniformly painted on primed surface again；
Step 6：Dry polishing：Plank after spraying is put into temperature to be dried for 20 DEG C -35 DEG C, waits for that coating is dried
It is gently polished coating surface with waterproof abrasive paper afterwards.
Embodiment 11：A kind of coating construction process, specific preparation process are as follows：
Step 1：Selection：It is the high-quality plank of 20%-30%, coating, suitable diluent and suitable to select moisture content
Anticoagulant；
Step 2：Preliminary treatment：The plate surface wiped clean that needs are sprayed, and to containing the excessive tiny wooden eye
Plate surface carry out brush bottom obtain it is precious；
Step 3：Coating dilutes：According to actual use situation, suitable diluent and anticoagulant are poured into coating,
And it is sufficiently stirred；
Step 4：Priming：Plate surface of the coating after dilution after preliminary treatment is first uniformly brushed one layer；
Step 5：Spraying：Plank after priming is placed to drying 15 minutes under the dustfree environment of 20 DEG C of -35 DEG C of temperature,
Then the coating after dilution is uniformly painted on primed surface again；
Step 6：Dry polishing：Plank after spraying is put into temperature to be dried for 20 DEG C -35 DEG C, waits for that coating is dried
It is gently polished coating surface with waterproof abrasive paper afterwards.
Embodiment 12：A kind of coating construction process, specific preparation process are as follows：
Step 1：Selection：It is the high-quality plank of 20%-30%, coating, suitable diluent and suitable to select moisture content
Anticoagulant；
Step 2：Preliminary treatment：The plate surface wiped clean that needs are sprayed, and to containing the excessive tiny wooden eye
Plate surface carry out brush bottom obtain it is precious；
Step 3：Coating dilutes：According to actual use situation, suitable diluent and anticoagulant are poured into coating,
And it is sufficiently stirred；
Step 4：Priming：Plate surface of the coating after dilution after preliminary treatment is first uniformly brushed one layer；
Step 5：Spraying：Plank after priming is placed to drying 20 minutes under the dustfree environment of 20 DEG C of -35 DEG C of temperature,
Then the coating after dilution is uniformly painted on primed surface again；
Step 6：Dry polishing：Plank after spraying is put into temperature to be dried for 20 DEG C -35 DEG C, waits for that coating is dried
It is gently polished coating surface with waterproof abrasive paper afterwards.
By the comparison of embodiment 1-12 as can be seen that the high-quality plank that moisture content is 10%-20% is chosen, in coating
Suitable anticoagulant and priming paint are added under the dustfree environment of 20 DEG C of -35 DEG C of temperature at dry 20 minutes, construct made from
Effect is most ideal.
Finally it should be noted that：The foregoing is only a preferred embodiment of the present invention, is not intended to restrict the invention,
Although the present invention is described in detail referring to the foregoing embodiments, for those skilled in the art, still may be used
With technical scheme described in the above embodiments is modified or equivalent replacement of some of the technical features,
All within the spirits and principles of the present invention, any modification, equivalent replacement, improvement and so on should be included in the present invention's
Within protection domain.
Claims (6)
1. a kind of coating construction process, which is characterized in that specific preparation process is as follows：
Step 1：Selection：Select good plank, coating and suitable diluent；
Step 2：Preliminary treatment：The plate surface wiped clean that needs are sprayed；
Step 3：Coating dilutes：According to actual use situation, suitable diluent is poured into coating, and be sufficiently stirred；
Step 4：Priming：Plate surface of the coating after dilution after preliminary treatment is first uniformly brushed one layer；
Step 5：Spraying：Plank after priming is placed into drying under room temperature, is then again uniformly painted on the coating after dilution
Primed surface；
Step 6：Dry polishing：Plank after spraying is put under room temperature and is dried, after coating drying after to coating surface into
Row polishing.
2. a kind of coating construction process according to claim 1, it is characterised in that：Also contain anticoagulant in step 1.
3. a kind of coating construction process according to claim 1, it is characterised in that：It is also needed in step 2 to moisture content mistake
Processing is dried in high plank, to the plate surface containing the excessive tiny wooden eye brush bottom obtain it is precious.
4. a kind of coating construction process according to claim 3, it is characterised in that：The selection moisture content is 10%-
30% high-quality plank.
5. a kind of coating construction process according to claim 1, it is characterised in that：Drying time is set as in step 5
10min-20min, temperature setting are 20 DEG C -35 DEG C, and dry environment is dustfree environment.
6. a kind of coating construction process according to claim 1, it is characterised in that：In step 6 temperature be set as 20 DEG C-
35 DEG C, selected abrasor is that waterproof abrasive paper is gently polished.