CN105040259A - Complex deodorization cloth - Google Patents
Complex deodorization cloth Download PDFInfo
- Publication number
- CN105040259A CN105040259A CN201510331696.0A CN201510331696A CN105040259A CN 105040259 A CN105040259 A CN 105040259A CN 201510331696 A CN201510331696 A CN 201510331696A CN 105040259 A CN105040259 A CN 105040259A
- Authority
- CN
- China
- Prior art keywords
- cloth
- fiber
- special health
- yarn
- composite deodurizing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a complex deodorization cloth. The complex deodorization cloth comprises a raw material composition of blended staple fiber yarn and filament yarn and anti-slip finished complex deodorization cloth; the staple fiber yarn is formed by blending acrylic fibers, dacron, chinlon and special health-care fibers; the filament yarn consists of dacron and polypropylene fiber wrap yarn; the special health-care fibers are made of bamboo fibers, outlast fibers and carbon nanofibers. The complex deodorization cloth disclosed by the invention has a simple production process and is low in cost; the produced cloth has a good thermoregulation effect; the thermoregulation range of the complex deodorization cloth is 21 DEG C to 26 DEG C; the thermoregulation function of the complex deodorization cloth reaches more than 2000mJ/g; moreover, the fabric style is good; meanwhile, the complex deodorization cloth has an excellent sterilization effect, is capable of preventing bacterial infection and killing bacteria, has very powerful sterilization ability and moisture adsorption ability, and is very soft.
Description
Technical field
The present invention relates to field of textiles, particularly a kind of composite deodurizing cloth.
Background technology
Along with the raising of people's living standard, people progressively change pursuit that is functional to it, comfortableness into from simple warmth retention property for the requirement of woollen blanket, wherein temperature adjustment, wrinkle resistant, fire-retardant, refuse the coming out one after another of functional textile such as oil, waterproof, moisture-inhibiting and promoted the development of after-finishing of textile products technology greatly.
Along with spinning, weave, the lifting of the continuous advancement of Final finishing industrial technology and people's living standard, wear washability and get more and more, people pay attention to comfortableness and the ergonomics performance of socks gradually, in order to adapt to consumer demand, adopt new raw material can produce various Fresh fats material in conjunction with new spinning technology, improved by the hindlimb unload that matches again, increase, improving product wear function, making product cater to market development demand, is also the development trend of new product from now on.
China Patent Publication No. CN101407962A, publication date on April 15th, 2009, name is called Outlast air-conditioning fiber polar fleece and production technology thereof, this application case discloses a kind of Outlast air-conditioning fiber polar fleece and production technology is using Outlast air-conditioning fiber as wire gauze, using polyester filament as loop yarn, weave and process, wherein the content of Outlast air-conditioning fiber is 35-65%.A production technology for Outlast air-conditioning fiber polar fleece, step comprise weave, stamp, dry, roll fluffing and pre-setting, plucking, sizing, carding, cropping after plucking, shake grain and shake grain after shape.Its weak point is, fabric feeling and comfort level poor.
Summary of the invention
The object of the invention is to, in order to solve the temperature adjustment of prior art energy but fabric feeling and comfort level is poor or fabric feeling and comfort level good but can not temperature adjustment defect and provide a kind of can temperature adjustment and the good a kind of composite deodurizing cloth of comfort level.
To achieve these goals, the present invention is by the following technical solutions:
A kind of composite deodurizing cloth, this composite deodurizing cloth comprises blend spun yarn and filament raw material combines and the composite deodurizing cloth of anti-skidding Final finishing; Described staple fibre yarn is formed by acrylic fibers, terylene, polyamide fibre and special health fiber blend, and described long filament is made up of terylene, polypropylene fibre wrap yarn, and described special health fiber is made up of bamboo fibre, outlast fiber and carbon nano-fiber.
As preferably, the ratio of acrylic fibers, terylene, polyamide fibre and special health fiber is 1:2:3:1.
As preferably, described special health fiber is prepared by following methods: by the bamboo fibre of 20-25 weight portion, add after 15-20 weight portion outlast fiber mixes with the carbon nano-fiber of 25-30 weight portion and be mixed with mixed solution in the silver ion mixed liquor of dissolved in purified water, wherein in silver ion mixed liquor, the content of silver ion is that 1-1000 microgram often rises, bamboo fibre, outlast fiber and carbon nano-fiber are completely infused in ultrasonic vibration 45-60min after silver ion mixed liquor, add ethanol or acetone or isopropyl alcohol after centrifuge dripping to carry out wash-out and dehydrate, solvent is taken out through heated-air drying after drying, thus obtain bamboo fibre, what outlast fiber mixed with carbon nano-fiber carries silver-colored fiber.
Owing to containing a certain amount of microcapsules in Outlast fiber, temperature-sensitive phase-change material in microcapsules realizes heat absorption and release by solid-state with the mutual conversion of liquid state, the cloth adopting the blended yarn of Outlast fiber and varicosity acrylic fibers to make can need to carry out absorbing, storing and release heat according to human body on the one hand, makes human body remain on comfortable temperature range; Fluffy, plentiful, beautiful in colour, the soft feature of cloth itself is retained on the other hand.
As preferably, composite deodurizing cloth comprises preparation method and comprises the following steps:
A) weave: special health fiber is woven on double-needle bed raschel warp knitting machine the grey cloth of 3 interlayers every tissue, sley bar L1 and L6 of double-needle bed raschel warp knitting machine adopts the staple fibre yarn braiding inlaid thread of 100D/50F-150D/75F, sley bar L2 and L5 adopts the polyester filament braiding chaining of 100D/50F-150D/75F, sley bar L3 mono-wears 200D-300D special health fiber every a sky and weaves through flat on two-needle bar, sley bar L4 is vacant, after having woven, the grey cloth woven is tested;
B) stamp: qualified grey cloth is examined to step a) base and carries out stamp process, stamp speed 11-13m/min, printing rollers pressure 3-5Kg, printing paste used contains 1227 levelling agents of mass fraction 0.6-0.8%o.w.f and the former paste of mass fraction 40%, surplus is water, and the pH value of printing paste is 4-5;
C) vapour steaming colour fixing: by the cloth after step b) stamp, puts vapour steaming colour fixing in vapor can into, steam temperature 100-110 DEG C, time 10-30min;
D) wash: the cloth after step c) vapour steaming colour fixing is carried out washing process, washing speed of a motor vehicle 12-14m/min, water lotion used contains 209 detergents and the 2-5ml/L softener of 5-10ml/L;
E) shape: to the cloth stentering forming after step d) washing, stentering forming temperature 110-130 DEG C, cloth speed 5-7m/min, after stentering forming, the fabric width of cloth is 1.35-1.45m;
F) bristle: bristle process is carried out, the speed 2-3m/min of hairbrush to the cloth after step e) sizing;
G) post processing: to the cloth after step f) bristle carry out scald cut, hot light, smooth, warehouse-in.
5. the preparation method of a kind of composite deodurizing cloth according to right 4, is characterized in that, in described step f) the direction of bristle be first along cant backward against cant to along hair.
As preferably, scald in step g) cut, the number of times of hot light is 5-7 time.
The invention has the beneficial effects as follows:
1. the cloth adopting the blended yarn of Outlast fiber and varicosity acrylic fibers to make can need to carry out absorbing, storing and release heat according to human body, makes human body remain on comfortable temperature range;
2. production technology of the present invention is simple, with low cost, and the thermoregulation effect of the temperature adjustment cloth produced is good, and its thermoregulation range is 21 ~ 26 DEG C, and temperature adjustment function reaches more than 2000mJ/g, and Fabric Style is good.
Detailed description of the invention
Below in conjunction with specific embodiment, the present invention is further explained:
This composite deodurizing cloth comprises blend spun yarn and filament raw material combines and the composite deodurizing cloth of anti-skidding Final finishing; Described staple fibre yarn is formed by acrylic fibers, terylene, polyamide fibre and special health fiber blend, and described long filament is made up of terylene, polypropylene fibre wrap yarn, and described special health fiber is made up of bamboo fibre, outlast fiber and carbon nano-fiber.The ratio of acrylic fibers, terylene, polyamide fibre and special health fiber is 1:2:3:1.
Embodiment one
A kind of composite deodurizing cloth, composite deodurizing cloth comprises preparation method and comprises the following steps:
A) weave: special health fiber is woven on double-needle bed raschel warp knitting machine the grey cloth of 3 interlayers every tissue, sley bar L1 and L6 of double-needle bed raschel warp knitting machine adopts the staple fibre yarn braiding inlaid thread of 100D/50F-150D/75F, sley bar L2 and L5 adopts the polyester filament braiding chaining of 100D/50F-150D/75F, sley bar L3 mono-wears 200D-300D special health fiber every a sky and weaves through flat on two-needle bar, sley bar L4 is vacant, after having woven, the grey cloth woven is tested;
B) stamp: qualified grey cloth is examined to step a) base and carries out stamp process, stamp speed 11-13m/min, printing rollers pressure 3-5Kg, printing paste used contains 1227 levelling agents of mass fraction 0.6-0.8%o.w.f and the former paste of mass fraction 40%, surplus is water, and the pH value of printing paste is 4-5;
C) vapour steaming colour fixing: by the cloth after step b) stamp, puts vapour steaming colour fixing in vapor can into, steam temperature 100-110 DEG C, time 10-30min;
D) wash: the cloth after step c) vapour steaming colour fixing is carried out washing process, washing speed of a motor vehicle 12-14m/min, water lotion used contains 209 detergents and the 2-5ml/L softener of 5-10ml/L;
E) shape: to the cloth stentering forming after step d) washing, stentering forming temperature 110-130 DEG C, cloth speed 5-7m/min, after stentering forming, the fabric width of cloth is 1.35-1.45m;
F) bristle: bristle process is carried out, the speed 2-3m/min of hairbrush to the cloth after step e) sizing;
G) post processing: to the cloth after step f) bristle carry out scald cut, hot light, smooth, warehouse-in.Scald cut, the number of times of hot light is 5-7 time.
Wherein, described special health fiber is prepared by following methods: by the bamboo fibre of 20 weight portions, add after 15 weight portion outlast fibers mix with the carbon nano-fiber of 25 weight portions and be mixed with mixed solution in the silver ion mixed liquor of dissolved in purified water, wherein in silver ion mixed liquor, the content of silver ion is that 1 microgram often rises, bamboo fibre, outlast fiber and carbon nano-fiber are completely infused in ultrasonic vibration 45min after silver ion mixed liquor, add ethanol after centrifuge dripping to carry out wash-out and dehydrate, solvent is taken out through heated-air drying after drying, thus obtain bamboo fibre, what outlast fiber mixed with carbon nano-fiber carries silver-colored fiber.
Embodiment two
A kind of composite deodurizing cloth, composite deodurizing cloth comprises preparation method and comprises the following steps:
A) weave: special health fiber is woven on double-needle bed raschel warp knitting machine the grey cloth of 3 interlayers every tissue, sley bar L1 and L6 of double-needle bed raschel warp knitting machine adopts the staple fibre yarn braiding inlaid thread of 100D/50F-150D/75F, sley bar L2 and L5 adopts the polyester filament braiding chaining of 100D/50F-150D/75F, sley bar L3 mono-wears 200D-300D special health fiber every a sky and weaves through flat on two-needle bar, sley bar L4 is vacant, after having woven, the grey cloth woven is tested;
B) stamp: qualified grey cloth is examined to step a) base and carries out stamp process, stamp speed 11-13m/min, printing rollers pressure 3-5Kg, printing paste used contains 1227 levelling agents of mass fraction 0.6-0.8%o.w.f and the former paste of mass fraction 40%, surplus is water, and the pH value of printing paste is 4-5;
C) vapour steaming colour fixing: by the cloth after step b) stamp, puts vapour steaming colour fixing in vapor can into, steam temperature 100-110 DEG C, time 10-30min;
D) wash: the cloth after step c) vapour steaming colour fixing is carried out washing process, washing speed of a motor vehicle 12-14m/min, water lotion used contains 209 detergents and the 2-5ml/L softener of 5-10ml/L;
E) shape: to the cloth stentering forming after step d) washing, stentering forming temperature 110-130 DEG C, cloth speed 5-7m/min, after stentering forming, the fabric width of cloth is 1.35-1.45m;
F) bristle: bristle process is carried out, the speed 2-3m/min of hairbrush to the cloth after step e) sizing;
G) post processing: to the cloth after step f) bristle carry out scald cut, hot light, smooth, warehouse-in.Scald cut, the number of times of hot light is 5-7 time.
Wherein, described special health fiber is prepared by following methods: by the bamboo fibre of 22 weight portions, add after 18 weight portion outlast fibers mix with the carbon nano-fiber of 28 weight portions and be mixed with mixed solution in the silver ion mixed liquor of dissolved in purified water, wherein in silver ion mixed liquor, the content of silver ion is that 200 micrograms often rise, bamboo fibre, outlast fiber and carbon nano-fiber are completely infused in ultrasonic vibration 50min after silver ion mixed liquor, add acetone after centrifuge dripping to carry out wash-out and dehydrate, solvent is taken out through heated-air drying after drying, thus obtain bamboo fibre, what outlast fiber mixed with carbon nano-fiber carries silver-colored fiber.
Embodiment three
A kind of composite deodurizing cloth, composite deodurizing cloth comprises preparation method and comprises the following steps:
A) weave: special health fiber is woven on double-needle bed raschel warp knitting machine the grey cloth of 3 interlayers every tissue, sley bar L1 and L6 of double-needle bed raschel warp knitting machine adopts the staple fibre yarn braiding inlaid thread of 100D/50F-150D/75F, sley bar L2 and L5 adopts the polyester filament braiding chaining of 100D/50F-150D/75F, sley bar L3 mono-wears 200D-300D special health fiber every a sky and weaves through flat on two-needle bar, sley bar L4 is vacant, after having woven, the grey cloth woven is tested;
B) stamp: qualified grey cloth is examined to step a) base and carries out stamp process, stamp speed 11-13m/min, printing rollers pressure 3-5Kg, printing paste used contains 1227 levelling agents of mass fraction 0.6-0.8%o.w.f and the former paste of mass fraction 40%, surplus is water, and the pH value of printing paste is 4-5;
C) vapour steaming colour fixing: by the cloth after step b) stamp, puts vapour steaming colour fixing in vapor can into, steam temperature 100-110 DEG C, time 10-30min;
D) wash: the cloth after step c) vapour steaming colour fixing is carried out washing process, washing speed of a motor vehicle 12-14m/min, water lotion used contains 209 detergents and the 2-5ml/L softener of 5-10ml/L;
E) shape: to the cloth stentering forming after step d) washing, stentering forming temperature 110-130 DEG C, cloth speed 5-7m/min, after stentering forming, the fabric width of cloth is 1.35-1.45m;
F) bristle: bristle process is carried out, the speed 2-3m/min of hairbrush to the cloth after step e) sizing;
G) post processing: to the cloth after step f) bristle carry out scald cut, hot light, smooth, warehouse-in.Scald cut, the number of times of hot light is 5-7 time.
Wherein, described special health fiber is prepared by following methods: by the bamboo fibre of 25 weight portions, add after 20 weight portion outlast fibers mix with the carbon nano-fiber of 30 weight portions and be mixed with mixed solution in the silver ion mixed liquor of dissolved in purified water, wherein in silver ion mixed liquor, the content of silver ion is that 1000 micrograms often rise, bamboo fibre, outlast fiber and carbon nano-fiber are completely infused in ultrasonic vibration 60min after silver ion mixed liquor, add isopropyl alcohol after centrifuge dripping to carry out wash-out and dehydrate, solvent is taken out through heated-air drying after drying, thus obtain bamboo fibre, what outlast fiber mixed with carbon nano-fiber carries silver-colored fiber.
Claims (6)
1. a composite deodurizing cloth, is characterized in that, this composite deodurizing cloth comprises blend spun yarn and filament raw material combines and the composite deodurizing cloth of anti-skidding Final finishing; Described staple fibre yarn is formed by acrylic fibers, terylene, polyamide fibre and special health fiber blend, and described long filament is made up of terylene, polypropylene fibre wrap yarn, and described special health fiber is made up of bamboo fibre, outlast fiber and carbon nano-fiber.
2. a kind of composite deodurizing cloth according to claim 1, is characterized in that, the ratio of acrylic fibers, terylene, polyamide fibre and special health fiber is 1:2:3:1.
3. a kind of composite deodurizing cloth according to claim 1 and 2, it is characterized in that, described special health fiber is prepared by following methods: by the bamboo fibre of 20-25 weight portion, add after 15-20 weight portion outlast fiber mixes with the carbon nano-fiber of 25-30 weight portion and be mixed with mixed solution in the silver ion mixed liquor of dissolved in purified water, wherein in silver ion mixed liquor, the content of silver ion is that 1-1000 microgram often rises, bamboo fibre, chitin fiber and carbon nano-fiber are completely infused in ultrasonic vibration 45-60min after silver ion mixed liquor, add ethanol or acetone or isopropyl alcohol after centrifuge dripping to carry out wash-out and dehydrate, solvent is taken out through heated-air drying after drying, thus obtain bamboo fibre, what outlast fiber mixed with carbon nano-fiber carries silver-colored fiber.
4. a kind of composite deodurizing cloth according to claim 1, is characterized in that, composite deodurizing cloth comprises preparation method and comprises the following steps:
A) weave: special health fiber is woven on double-needle bed raschel warp knitting machine the grey cloth of 3 interlayers every tissue, sley bar L1 and L6 of double-needle bed raschel warp knitting machine adopts the staple fibre yarn braiding inlaid thread of 100D/50F-150D/75F, sley bar L2 and L5 adopts the polyester filament braiding chaining of 100D/50F-150D/75F, sley bar L3 mono-wears 200D-300D special health fiber every a sky and weaves through flat on two-needle bar, sley bar L4 is vacant, after having woven, the grey cloth woven is tested;
B) stamp: qualified grey cloth is examined to step a) base and carries out stamp process, stamp speed 11-13m/min, printing rollers pressure 3-5Kg, printing paste used contains 1227 levelling agents of mass fraction 0.6-0.8%o.w.f and the former paste of mass fraction 40%, surplus is water, and the pH value of printing paste is 4-5;
C) vapour steaming colour fixing: by the cloth after step b) stamp, puts vapour steaming colour fixing in vapor can into, steam temperature 100-110 DEG C, time 10-30min;
D) wash: the cloth after step c) vapour steaming colour fixing is carried out washing process, washing speed of a motor vehicle 12-14m/min, water lotion used contains 209 detergents and the 2-5ml/L softener of 5-10ml/L;
E) shape: to the cloth stentering forming after step d) washing, stentering forming temperature 110-130 DEG C, cloth speed 5-7m/min, after stentering forming, the fabric width of cloth is 1.35-1.45m;
F) bristle: bristle process is carried out, the speed 2-3m/min of hairbrush to the cloth after step e) sizing;
G) post processing: to the cloth after step f) bristle carry out scald cut, hot light, smooth, warehouse-in.
5. a kind of composite deodurizing cloth according to right 4, is characterized in that, in described step f) the direction of bristle be first along cant backward against cant to along hair.
6. a kind of composite deodurizing cloth according to claim 4, is characterized in that, scald in step g) cut, the number of times of hot light is 5-7 time.