CN104987844A - 一种耐高温双层pet纤维复合胶带的后加工工艺 - Google Patents
一种耐高温双层pet纤维复合胶带的后加工工艺 Download PDFInfo
- Publication number
- CN104987844A CN104987844A CN201510380255.XA CN201510380255A CN104987844A CN 104987844 A CN104987844 A CN 104987844A CN 201510380255 A CN201510380255 A CN 201510380255A CN 104987844 A CN104987844 A CN 104987844A
- Authority
- CN
- China
- Prior art keywords
- adhesive tape
- temperature
- processing technology
- compound adhesive
- layer pet
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开一种耐高温双层PET纤维复合胶带的后加工工艺，所述耐高温双层PET纤维复合胶带的后加工工艺包括如下步骤：（1）烘焙；（2）蒸化；（3）皂洗水洗；（4）成品定型整理；（5）成品检验。本耐高温双层PET纤维复合胶带的后加工工艺具有减少废水排放、质量稳定，达到了经济与环境效益最大化等优点。
Description
技术领域
本发明涉及一种耐高温双层PET纤维复合胶带的后加工工艺。
背景技术
复合胶带由于其吸湿透气能力强、回弹性良好、不起静电、耐老化能力优异，因而以复合胶带加工而成的醋酸布胶带具有耐高温、抗老化、柔软服帖、耐酸碱、抗霉等特性，其绝缘性能优于一般玻璃纤维布和玻璃布，因而广泛地应用于电视机、变压器、空调、电脑等制造领域。醋酸布胶带是在复合胶带上粘结有一层亚克力胶形成，在未使用前，亚克力胶层上一般粘贴有离型纸，在使用时将离型纸揭去即可粘贴在待粘贴处。一些应用领域中需要采用截面为不规则形状的异形醋酸布胶带，以用于按生产工序依次粘贴于多个部件上，通常为 2 个部件上，这需要在醋酸布胶带上设置两个不同的粘贴区域。在对该类型的醋酸布胶带进行裁切时，需要对离型纸进行裁半断处理，这样用户在使用时可依序去掉半断的离型纸进行粘贴。现有技术中，获取该种醋酸布胶带时一般均是直接开此形状的模具，然后在离型纸面进行单件冲切，生产效率低，冲切的过程中半断的离型纸容易掉落而粘贴在冲头上，造成后续冲切的不便。此外，对于小规格的产品而言，冲切后在产线上拿取不便，严重地影响产线的生产效率，且单件的产品混合在包装袋中来回晃动摩擦，容易产生毛丝、翘角等不良现象，成品浪费率高。
发明内容
本发明的目的在于提供一种耐高温双层PET纤维复合胶带的后加工工艺，具有减少废水排放、质量稳定，达到了经济与环境效益最大化等优点。
本发明的技术方案是：一种耐高温双层PET纤维复合胶带的后加工工艺，所述一种耐高温双层PET纤维复合胶带的后加工工艺包括如下步骤：
（1）烘焙:先对胶带原材料经一定的温度干热处理，时间为3-5分钟；
（2）乳化：把烘焙后的胶带原材料置于乳化槽进行乳化，所述乳化的温度为102-104℃，时间为8-10分钟；
（3）皂洗水洗：然后把乳化后的胶带原材料通过使用皂洗剂，清除生产过程中产生的浮色、浆料，经多次清水洗涤之后放入脱水机进行高速脱水，脱水后开幅；
（4）成品定型整理：通过反应锅对开幅后的胶带原材料进行高温烘焙，得到固定的尺寸和良好的手感；
（5）成品检验：最后对定型的胶带按要求进行检验。
在本发明一个较佳实施例中，步骤（1）中，所述一定的温度为140-160℃。
在本发明一个较佳实施例中，步骤（4）中，所述反应锅的温度为150-160℃。
在本发明一个较佳实施例中，所述皂洗水洗的步骤为先冷水洗，所述冷水的温度为室温，然后用温度60-80℃的温水洗，接着加入净洗剂在预定的温度下皂洗，最后柔软剂处理。
在本发明一个较佳实施例中，所述预定的温度为80-85℃。
本发明所述为一种耐高温双层PET纤维复合胶带的后加工工艺，具有减少废水排放、质量稳定，达到了经济与环境效益最大化等优点。
附图说明
附图1为本发明耐高温双层PET纤维复合胶带的后加工工艺一较佳实施例的加工工艺框图。
具体实施方式
下面结合附图对本发明的较佳实施例进行详细阐述，以使本发明的优点和特征能更易于被本领域技术人员理解，从而对本发明的保护范围做出更为清楚明确的界定。
本发明所述为一种耐高温双层PET纤维复合胶带的后加工工艺，参见图1。所述一种耐高温双层PET纤维复合胶带的后加工工艺包括如下步骤：
（1）烘焙:先对胶带原材料经一定的温度干热处理，时间为3-5分钟；
（2）乳化：把烘焙后的胶带原材料置于乳化槽进行乳化，所述乳化的温度为102-104℃，时间为8-10分钟；
（3）皂洗水洗：然后把乳化后的胶带原材料通过使用皂洗剂，清除生产过程中产生的浮色、浆料，经多次清水洗涤之后放入脱水机进行高速脱水，脱水后开幅；
（4）成品定型整理：通过反应锅对开幅后的胶带原材料进行高温烘焙，得到固定的尺寸和良好的手感；
（5）成品检验：最后对定型的胶带按要求进行检验。
进一步说明，步骤（1）中，所述一定的温度为140-160℃。
进一步说明，所述反应锅的温度为150-160℃。
进一步说明，所述皂洗水洗的步骤为先冷水洗，所述冷水的温度为室温，然后用温度60-80℃的温水洗，接着加入净洗剂在预定的温度下皂洗，最后柔软剂处理。
进一步说明，所述预定的温度为80-85℃。
在一实施例中，本发明所述为一种耐高温双层PET纤维复合胶带的后加工工艺，烘焙:使生产中胶带上使用的颜料经一定的温度干热处理，温度为140-160℃，时间为3-5分钟，以使固着涂料的树脂固化、或使胶带上的整理剂起化学反应的染整加工工艺，生产后直接烘干；把胶带原材料置于蒸汽中进行乳化，使颜色固化在胶带纤维组织中，所述加热介质为蒸汽，温度为102-104℃，时间为8-10分钟；使用皂洗剂清除生产过程中产生的浮色、浆料，使手感柔软，色泽鲜艳，保证牢度。先冷水洗（室温），然后温水洗（60-80℃），接着皂洗（净洗剂），在温水洗（80-85℃），最后柔软剂处理，经多次清水洗涤之后放入脱水机进行高速脱水，脱水后开幅；通过反应锅进行高温烘焙、拉幅柔软，得到固定的尺寸和良好的手感，形成产品，加热介质为导热油，加热到所需温度为150-160℃；用物理方法减少浸水后的收缩以降低缩水，将缩好的胶带按要求进行检验。本发明一种耐高温双层PET纤维复合胶带的后加工工艺，具有减少废水排放、质量稳定，达到了经济与环境效益最大化等优点。
本发明的具体实施方式，但本发明的保护范围并不局限于此，任何熟悉本领域的技术人员在本发明所揭露的技术范围内，可不经过创造性劳动想到的变化或替换，都应涵盖在本发明的保护范围之内。因此，本发明的保护范围应该以权利要求书所限定的保护范围为准。
Claims (5)
1.一种耐高温双层PET纤维复合胶带的后加工工艺，其特征在于：所述一种耐高温双层PET纤维复合胶带的后加工工艺包括如下步骤：
（1）烘焙:先对胶带原材料经一定的温度干热处理，时间为3-5分钟；
（2）乳化：把烘焙后的胶带原材料置于乳化槽进行乳化，所述乳化的温度为102-104℃，时间为8-10分钟；
（3）皂洗水洗：然后把乳化后的胶带原材料通过使用皂洗剂，清除生产过程中产生的浮色、浆料，经多次清水洗涤之后放入脱水机进行高速脱水，脱水后开幅；
（4）成品定型整理：通过反应锅对开幅后的胶带原材料进行高温烘焙，得到固定的尺寸和良好的手感；
（5）成品检验：最后对定型的胶带按要求进行检验。
2.根据权利要求1所述的一种耐高温双层PET纤维复合胶带的后加工工艺，其特征在于：步骤（1）中，所述一定的温度为140-160℃。
3.根据权利要求1所述的一种耐高温双层PET纤维复合胶带的后加工工艺，其特征在于：步骤（4）中，所述反应锅的温度为150-160℃。
4.根据权利要求1所述的一种耐高温双层PET纤维复合胶带的后加工工艺，其特征在于：所述皂洗水洗的步骤为先冷水洗，所述冷水的温度为室温，然后用温度60-80℃的温水洗，接着加入净洗剂在预定的温度下皂洗，最后柔软剂处理。
5.根据权利要求4所述的一种耐高温双层PET纤维复合胶带的后加工工艺，其特征在于：所述预定的温度为80-85℃。