CN104942906A - 一种环保型高性能桉木胶合板的加工方法 - Google Patents
一种环保型高性能桉木胶合板的加工方法 Download PDFInfo
- Publication number
- CN104942906A CN104942906A CN201510321983.3A CN201510321983A CN104942906A CN 104942906 A CN104942906 A CN 104942906A CN 201510321983 A CN201510321983 A CN 201510321983A CN 104942906 A CN104942906 A CN 104942906A
- Authority
- CN
- China
- Prior art keywords
- veneer
- eucalyptus
- glued board
- plywood
- central layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种环保型高性能桉木胶合板的加工方法,包括:⑴对桉木进行预处理;⑵将预处理得到的桉木作为单板,采用复合表板结构,制备表板和芯板;单板的厚度为1.8~2.2mm,单板干燥采用辊筒干燥机,芯板含水率在6-7%,表板含水率在6~9%;⑶使用由含茶多酚的茶叶水、聚乙二醇、硫脲和尿素溶液制得的胶粘剂,通过胶合板组坯、涂胶和热压工艺,将芯板和表板粘合,制得所需胶合板。本发明的技术方案,可以克服现有技术中材料成本高、使用寿命短和安全环保性差等缺陷,以实现材料成本低、使用寿命长和安全环保性好的优点。
Description
技术领域
本发明涉及木板加工技术领域,具体地,涉及一种环保型高性能桉木胶合板的加工方法。
背景技术
胶合板也称夹板,俗称细芯板。是由三层或多层一毫米厚的单板或薄板胶贴热压制而成。胶合板有变形小、幅面大、施工方便、不翘曲、横纹抗拉力学性能好等优点,故广泛用于家具制造、室内装修、住宅建筑以及造船、车箱制造、各种军工、轻工产品以及包装等工业部门之用。
近年来,伴随房地产、家具、建筑工程、物流包装等上下游行业的快速发展,市场对胶合板板的需求量日益高涨,木材加工产业也获得了快速发展,胶合板的市场需求一直不断增大,其生产技术、产品质量也有较大提升。
胶合板的生产,热压是关键程序,目前多数生产胶合板的厂家,在热压工序中都使用甲醛或脲树脂,会释放游离的甲醛气体,存在严重的甲醛污染。而且由于生产工艺水平的问题,生产的胶合板在耐磨、耐腐蚀、静曲强度、胶合强度、抗冲击度等方面技术指标的不够高,不能更好的满足市场需要。
在实现本发明的过程中,发明人发现现有技术中至少存在材料成本高、使用寿命短和安全环保性差等缺陷。
发明内容
本发明的目的在于,针对上述问题,提出一种环保型高性能桉木胶合板的加工方法,以实现材料成本低、使用寿命长和安全环保性好的优点。
为实现上述目的,本发明采用的技术方案是:一种环保型高性能桉木胶合板的加工方法,包括:
⑴对桉木进行预处理;该预处理的操作具体包括:
①通过包括打皮、磨光、找中心,去虫眼的处理后,进行旋切;
②单板处理,利用木材改性、阻燃剂,直接将桉木原木进行改性、阻燃剂处理后,进行磨光和一次干燥处理;
⑵将预处理得到的桉木作为单板,采用复合表板结构,制备表板和芯板;单板的厚度为1.8~2.2mm,单板干燥采用辊筒干燥机,芯板含水率在6-7%,表板含水率在6~9%;
⑶使用由含茶多酚的茶叶水、聚乙二醇、硫脲和尿素溶液制得的胶粘剂,通过胶合板组坯、涂胶和热压工艺,将芯板和表板粘合,制得所需胶合板。
本发明各实施例的环保型高性能桉木胶合板的加工方法,由于包括:⑴对桉木进行预处理;⑵将预处理得到的桉木作为单板,采用复合表板结构,制备表板和芯板;单板的厚度为1.8~2.2mm,单板干燥采用辊筒干燥机,芯板含水率在6-7%,表板含水率在6~9%;⑶使用由含茶多酚的茶叶水、聚乙二醇、硫脲和尿素溶液制得的胶粘剂,通过胶合板组坯、涂胶和热压工艺,将芯板和表板粘合,制得所需胶合板;从而可以克服现有技术中材料成本高、使用寿命短和安全环保性差的缺陷,以实现材料成本低、使用寿命长和安全环保性好的优点。
本发明的其它特征和优点将在随后的说明书中阐述,并且,部分地从说明书中变得显而易见,或者通过实施本发明而了解。
下面通过实施例,对本发明的技术方案做进一步的详细描述。
具体实施方式
以下对本发明的优选实施例进行说明,应当理解,此处所描述的优选实施例仅用于说明和解释本发明,并不用于限定本发明。
本发明的技术方案,利用桉木开发低甲醛环保型高强度桉木胶合板,通过对桉木进行改性处理,对胶水配方的改进控制甲醛污染,使用特殊的结构设计生产工艺本保证胶合板的强度,耐磨等物理指标,并对铺板机等主要生产设备进行改进,在达到胶合板环保低甲醛高强度的同时,以提高生产效率,节约木材用量。
根据本发明实施例,提供了一种环保型高性能桉木胶合板的加工方法,包括:
㈠桉木预处理,该预处理的操作具体包括:
①通过包括打皮、磨光、找中心,去虫眼的处理后,进行旋切;
②单板处理,利用木材改性、阻燃剂,直接将桉木原木进行改性、阻燃剂处理后,进行磨光和一次干燥处理;
㈡桉木胶合板产品方案设计
⑴原料选择和设计:以桉木为主要原料,既充分利用了桉木各种优良的性能,也使产品的质量和综合性能更优良。
⑵产品组坯结构:采用复合表板结构设计。这种结构可减少热压压力和木材压缩率,产品的强重比较高,同时解决了高压力、高压缩率产品湿回弹性大和变形大的问题。
⑶单板加工参数设计:在制造胶合板的单板时,若采用薄单板,有利于提高胶合板的力学性能,但也增加了胶合板的单板层数,增加了耗胶量和合板热压工艺的难度。而应用厚单板,特别是桉木短中板的厚度大于2.0mm时,板子的力学性能很难提高,这主要是由于桉木单板较厚时,易从单板串闻剪断、分层。
本发明技术方案中,单板厚度控制在1.8~2.2mm之间,单板干燥采用辊筒干燥机,可提高单板平整度,降低耗胶量;芯板含水率在6-7%,表板含水率在8%~l0%,能保证达到最佳力学性能指标。
㈢胶粘剂改良
胶粘剂作为胶合板必须使用的材料之一,在生产和使用中会产生游离甲醛,造成环境污染。要控制甲醛释放,达到环保目的,必须对其配方改良并添加合适的添加剂。采用茶叶水(含茶多酚)、聚乙二醇、硫脲、尿素溶液等经一系列工艺改良胶水,生产的胶合板甲醛释放量≤0.5mg/100g,大大高于国家标准,达到国际E0标准。
㈣生产工艺的设计和生产线的改进,主要是铺板设备的改进
⑴胶合板组坯、涂胶和热压工艺
生产中采用的胶水,要有利于提高其固化速度,缩短热压时间。组坯时还要注意单板松紧面的问题,以使结构胶合板的组织结构对称,减少产品翘曲变形。
针对现在胶合板热压工序中使用甲醛或脲树脂,存在严重的甲醛污染;而且由于生产工艺落后,胶合板在耐磨、耐腐蚀、静曲强度、胶合强度、抗冲击度等方面质量技术指标低下等问题。本发明的技术方案,使用特殊工艺和配方改良的胶合剂,改进铺板生产设备,解决了相关问题污染问题和原材料浪费问题,大大提高了生产效率,节约成本25%以上。
最后应说明的是:以上所述仅为本发明的优选实施例而已,并不用于限制本发明,尽管参照前述实施例对本发明进行了详细的说明,对于本领域的技术人员来说,其依然可以对前述各实施例所记载的技术方案进行修改,或者对其中部分技术特征进行等同替换。凡在本发明的精神和原则之内,所作的任何修改、等同替换、改进等,均应包含在本发明的保护范围之内。
Claims (1)
1.一种环保型高性能桉木胶合板的加工方法,其特征在于,包括:
⑴对桉木进行预处理;该预处理的操作具体包括:
①通过包括打皮、磨光、找中心,去虫眼的处理后,进行旋切;
②单板处理,利用木材改性、阻燃剂,直接将桉木原木进行改性、阻燃剂处理后,进行磨光和一次干燥处理;
⑵将预处理得到的桉木作为单板,采用复合表板结构,制备表板和芯板;单板的厚度为1.8~2.2mm,单板干燥采用辊筒干燥机,芯板含水率在6-7%,表板含水率在6~9%;
⑶使用由含茶多酚的茶叶水、聚乙二醇、硫脲和尿素溶液制得的胶粘剂,通过胶合板组坯、涂胶和热压工艺,将芯板和表板粘合,制得所需胶合板。