CN104928683A - 一种钛钯管的抗氧化处理工艺 - Google Patents
一种钛钯管的抗氧化处理工艺 Download PDFInfo
- Publication number
- CN104928683A CN104928683A CN201510270343.4A CN201510270343A CN104928683A CN 104928683 A CN104928683 A CN 104928683A CN 201510270343 A CN201510270343 A CN 201510270343A CN 104928683 A CN104928683 A CN 104928683A
- Authority
- CN
- China
- Prior art keywords
- palladium tube
- titanium palladium
- antioxidant
- titanium
- antioxidation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种钛钯管的抗氧化处理工艺，主要包括以下步骤：脱脂、一次清洗、抗氧化处理、二次清洗、吹干烘干，所述一次清洗采用丙酮清洗，所述抗氧化处理为将钛钯管放入抗氧化溶液中浸泡，所述抗氧化溶液由70%的纯水和30%的抗氧化剂混合而成，所述抗氧化剂包括以下重量配比的原料：生育酚25%~40%；丁基羟基茴香醚24%~30%；二丁基羟基甲苯12%~20%；柠檬酸钠18%～25%；所述抗氧化溶液的温度为40-50度，浸泡时间为40-50s，通过上述方式，本发明能够使得钛钯管具备有较强的抗氧化性能，便于保存、运输，提高使用寿命，减小成本损耗。
Description
技术领域
本发明涉及一种处理工艺，特别涉及一种钛钯管的抗氧化处理工艺。
背景技术
随着科学技术的不断提高，钛钯合金使用的也越来越广泛，同时由于在制氢领域中由于纯钯价格较为昂贵，因此在目前已经慢慢开始利用钛钯合金代替纯钯来制氢，但是现有技术中的钛钯合金在储存的过程中，易被氧化，从而会在合金表面生成一层氧化膜，不仅降低使用寿命，增加成本的消耗，而且会影响钛钯合金在制备高纯度氢的效率。
发明内容
本发明主要解决的技术问题是提供一种钛钯管的抗氧化处理工艺。
为解决上述技术问题，本发明采用的一个技术方案是：提供一种钛钯管的抗氧化处理工艺，包括如下步骤：
（1）、脱脂：将钛钯管放入脱脂液内浸泡，随后用脱脂棉擦拭干净；
（2）、一次清洗：采用丙酮对上述脱脂后的钛钯管进行清洗处理，彻底清除钛钯管表面的杂质；
（3）、抗氧化处理：将钛钯管放入抗氧化溶液中浸泡，所述抗氧化溶液由70%的纯水和30%的抗氧化剂混合而成，所述抗氧化剂包括以下重量配比的原料：生育酚25%~40%；丁基羟基茴香醚24%~30%；二丁基羟基甲苯12%~20%；柠檬酸钠18%～25%；所述抗氧化溶液的温度为40-50度，浸泡时间为40-50s；
（4）、二次清洗：将上述抗氧化处理后的钛钯管放入水温为50-60度的清水中浸泡2-3min；
（5）、吹干烘干：采用温度小于50度的风将钛钯管吹干，然后将钛钯管放入烘箱中进行烘烤处理。
在本发明一个较佳实施例中，所述步骤（1）中的脱脂液为浓度25%的NaOH水溶液。
在本发明一个较佳实施例中，所述步骤（5）中的烘烤处理的烘烤温度为85～95度。
在本发明一个较佳实施例中，所述步骤（5）中烘烤处理的烘烤时间为8-10min。
本发明的有益效果是：本发明能够使得钛钯管具备有较强的抗氧化性能，能够在保存、运输的过程中不被氧化，提高使用寿命，减小成本损耗，并且能保证在制备高纯度氢的过程中较好。
具体实施方式
下面对本发明的较佳实施例进行详细阐述，以使本发明的优点和特征能更易于被本领域技术人员理解，从而对本发明的保护范围做出更为清楚明确的界定。
实施例1：
一种钛钯管的抗氧化处理工艺，包括如下步骤：
（1）、脱脂：将钛钯管放入脱脂液内浸泡，随后用脱脂棉擦拭干净；
（2）、一次清洗：采用丙酮对上述脱脂后的钛钯管进行清洗处理，彻底清除钛钯管表面的杂质；
（3）、抗氧化处理：将钛钯管放入抗氧化溶液中浸泡，所述抗氧化溶液由70%的纯水和30%的抗氧化剂混合而成，所述抗氧化剂包括以下重量配比的原料：生育酚30%；丁基羟基茴香醚25%；二丁基羟基甲苯20%；柠檬酸钠25%；所述抗氧化溶液的温度为40度，浸泡时间为50s；
（4）、二次清洗：将上述抗氧化处理后的钛钯管放入水温为50度的清水中浸泡3min；
（5）、吹干烘干：采用温度小于50度的风将钛钯管吹干，然后将钛钯管放入烘箱中进行烘烤处理，烘烤温度为85度，烘烤时间为10min。
经测试，经上述处理后的钛钯管相比于普通的钛钯管，其抗氧化性能提升75%。
实施例2：
一种钛钯管的抗氧化处理工艺，包括如下步骤：
（1）、脱脂：将钛钯管放入脱脂液内浸泡，随后用脱脂棉擦拭干净；
（2）、一次清洗：采用丙酮对上述脱脂后的钛钯管进行清洗处理，彻底清除钛钯管表面的杂质；
（3）、抗氧化处理：将钛钯管放入抗氧化溶液中浸泡，所述抗氧化溶液由70%的纯水和30%的抗氧化剂混合而成，所述抗氧化剂包括以下重量配比的原料：生育酚40%；丁基羟基茴香醚30%；二丁基羟基甲苯12%；柠檬酸钠18%；所述抗氧化溶液的温度为50度，浸泡时间为40s；
（4）、二次清洗：将上述抗氧化处理后的钛钯管放入水温为60度的清水中浸泡2min；
（5）、吹干烘干：采用温度小于50度的风将钛钯管吹干，然后将钛钯管放入烘箱中进行烘烤处理，烘烤温度为95度，烘烤时间为8min。
经测试，经上述处理后的钛钯管相比于普通的钛钯管，其抗氧化性能提升72%。
实施例3：
一种钛钯管的抗氧化处理工艺，包括如下步骤：
（1）、脱脂：将钛钯管放入脱脂液内浸泡，随后用脱脂棉擦拭干净；
（2）、一次清洗：采用丙酮对上述脱脂后的钛钯管进行清洗处理，彻底清除钛钯管表面的杂质；
（3）、抗氧化处理：将钛钯管放入抗氧化溶液中浸泡，所述抗氧化溶液由70%的纯水和30%的抗氧化剂混合而成，所述抗氧化剂包括以下重量配比的原料：生育酚35%；丁基羟基茴香醚27%；二丁基羟基甲苯16%；柠檬酸钠18%～22%；所述抗氧化溶液的温度为45度，浸泡时间为45s；
（4）、二次清洗：将上述抗氧化处理后的钛钯管放入水温为55度的清水中浸泡2.5min；
（5）、吹干烘干：采用温度小于50度的风将钛钯管吹干，然后将钛钯管放入烘箱中进行烘烤处理，烘烤温度为90度，烘烤时间为9min。
经测试，经上述处理后的钛钯管相比于普通的钛钯管，其抗氧化性能提升80%。
区别于现有技术，本发明能够使得钛钯管具备有较强的抗氧化性能，能够在保存、运输的过程中不被氧化，提高使用寿命，减小成本损耗，并且能保证在制备高纯度氢的过程中较好。
以上所述仅为本发明的实施例，并非因此限制本发明的专利范围，凡是利用本发明说明书内容所作的等效结构或等效流程变换，或直接或间接运用在其他相关的技术领域，均同理包括在本发明的专利保护范围内。
Claims (4)
1.一种钛钯管的抗氧化处理工艺，其特征在于，包括如下步骤：
（1）、脱脂：将钛钯管放入脱脂液内浸泡，随后用脱脂棉擦拭干净；
（2）、一次清洗：采用丙酮对上述脱脂后的钛钯管进行清洗处理，彻底清除钛钯管表面的杂质；
（3）、抗氧化处理：将钛钯管放入抗氧化溶液中浸泡，所述抗氧化溶液由70%的纯水和30%的抗氧化剂混合而成，所述抗氧化剂包括以下重量配比的原料：生育酚25%~40%；丁基羟基茴香醚24%~30%；二丁基羟基甲苯12%~20%；柠檬酸钠18%～25%；所述抗氧化溶液的温度为40-50度，浸泡时间为40-50s；
（4）、二次清洗：将上述抗氧化处理后的钛钯管放入水温为50-60度的清水中浸泡2-3min；
（5）、吹干烘干：采用温度小于50度的风将钛钯管吹干，然后将钛钯管放入烘箱中进行烘烤处理。
2.根据权利要求1所述的钛钯管的抗氧化处理工艺，其特征在于，所述步骤（1）中的脱脂液为浓度25%的NaOH水溶液。
3.根据权利要求1所述的钛钯管的抗氧化处理工艺，其特征在于，所述步骤（5）中烘烤处理的烘烤温度为85～95度。
4.根据权利要求1所述的钛钯管的抗氧化处理工艺，其特征在于，所述步骤（5）中烘烤处理的烘烤时间为8-10min。