CN104912936A - 舵销轴承的防腐处理方法 - Google Patents

舵销轴承的防腐处理方法 Download PDF

Info

Publication number
CN104912936A
CN104912936A CN201510245069.5A CN201510245069A CN104912936A CN 104912936 A CN104912936 A CN 104912936A CN 201510245069 A CN201510245069 A CN 201510245069A CN 104912936 A CN104912936 A CN 104912936A
Authority
CN
China
Prior art keywords
coating
carried out
anticorrosion
pin bearing
film thickness
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510245069.5A
Other languages
English (en)
Inventor
范明昌
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
GUANGXI WUZHOU YUNLONG PORT & SHIP MACHINERY MANUFACTURING Co Ltd
Original Assignee
GUANGXI WUZHOU YUNLONG PORT & SHIP MACHINERY MANUFACTURING Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by GUANGXI WUZHOU YUNLONG PORT & SHIP MACHINERY MANUFACTURING Co Ltd filed Critical GUANGXI WUZHOU YUNLONG PORT & SHIP MACHINERY MANUFACTURING Co Ltd
Priority to CN201510245069.5A priority Critical patent/CN104912936A/zh
Publication of CN104912936A publication Critical patent/CN104912936A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种舵销轴承的防腐处理方法，涉及船用配套设备制造技术领域，该方法用有机溶剂对舵销轴承进行除油处理，然后进行高压冲洗和干燥；进行喷砂处理，使舵销轴承的表面清洁度达到Sa3级，表面粗糙度达到10-30um；在30分钟内，浸涂钛纳米高分子合金涂料，闪干25-30分钟后，入炉烘干20-30分钟，烘干温度为250-280℃；烘干后，喷涂一道环氧防腐纳米涂料，在室温下晾干12-24小时，涂层干膜厚度为80-120um；随后再喷涂两道硅氧烷改性丙烯酸聚氨酯涂料，两道喷涂间隔小于1小时，每道涂层干膜厚度为60-80um，喷涂完毕后在室温下干燥5-7天。本发明解决了现有舵销轴承防腐性能差的问题。

Description

舵销轴承的防腐处理方法
技术领域
本发明涉及船用配套设备制造技术领域，尤其是一种舵销轴承的防腐处理方法。
背景技术
船舵是用来控制船舶航行方向的操作机构，一般设置于船舶尾部，它主要由舵叶、舵杆、舵销、舵销轴承等组成。舵销轴承长期浸泡在海水中，使用环境十分恶劣，其不仅会受到海水的强烈腐蚀，还会受到海洋微生物的腐蚀，腐蚀的舵销轴承会影响船舶舵系的转向精度。现有的舵销轴承的防腐蚀性能差，需要经常修理，增加了维修成本。
发明内容
本发明的目的是提供一种舵销轴承的防腐处理方法，它能够解决现有舵销轴承防腐性能差的问题。
为了解决上述问题，本发明采用的技术方案是：一种舵销轴承的防腐处理方法包括以下步骤：
A、用有机溶剂对舵销轴承进行除油处理，然后进行高压冲洗和干燥；
B、进行喷砂处理，使舵销轴承的表面清洁度达到Sa3级，表面粗糙度达到10-30um；
C、在步骤B完成后的30分钟内，浸涂钛纳米高分子合金涂料，闪干25-30分钟后，入炉烘干，烘干温度为250-280℃，时间为20-30分钟；
D、烘干后，喷涂一道环氧防腐纳米涂料，在室温下晾干12-24小时，涂层干膜厚度为80-120um；
E、随后再喷涂两道硅氧烷改性丙烯酸聚氨酯涂料，两道喷涂间隔小于1小时，每道涂层干膜厚度为60-80um，喷涂完毕后在室温下干燥5-7天。
上述舵销轴承的防腐处理方法的技术方案中，更具体的技术方案还可以是：步骤C的涂层干膜厚度大于100um。
进一步的，步骤C的浸涂粘度为20-25s。
由于采用了上述技术方案，本发明与现有技术相比具有如下有益效果：喷砂处理利于后续的浸涂，浸涂的钛纳米高分子合金涂层在附着力、抗冲击、涂层硬度、耐磨蚀、耐高温、耐高压等物理性能和耐化学腐蚀性方面表现优良；多涂层有利于提高防腐层的附着力、密实度、稳定性、耐候性、耐酸碱性等，防腐能力高，使用寿命可达50年以上。
具体实施方式
下面结合实施例对本发明作进一步的详述：
实施例1
本实施例的舵销轴承的防腐处理方法包括以下步骤：
A、用有机溶剂对舵销轴承进行除油处理，然后进行高压冲洗和干燥；
B、进行喷砂处理，使舵销轴承的表面清洁度达到Sa3级，表面粗糙度达到10um；
C、在步骤B完成后的15分钟，浸涂钛纳米高分子合金涂料，浸涂粘度为（涂-4杯）20s，闪干25分钟后，入炉烘干，烘干温度为250℃，时间为30分钟，涂层干膜厚度为105um；
D、烘干后，喷涂一道环氧防腐纳米涂料，在室温下晾干12小时，涂层干膜厚度为80um；
E、随后再喷涂两道硅氧烷改性丙烯酸聚氨酯涂料，两道喷涂间隔0.5小时，每道涂层干膜厚度为60um，喷涂完毕后在室温下干燥5天。
实施例2
本实施例的舵销轴承的防腐处理方法包括以下步骤：
A、用有机溶剂对舵销轴承进行除油处理，然后进行高压冲洗和干燥；
B、进行喷砂处理，使舵销轴承的表面清洁度达到Sa3级，表面粗糙度达到25um；
C、在步骤B完成后的20分钟，浸涂钛纳米高分子合金涂料，浸涂粘度为（涂-4杯）23s，闪干30分钟后，入炉烘干，烘干温度为280℃，时间为25分钟，涂层干膜厚度为120um；
D、烘干后，喷涂一道环氧防腐纳米涂料，在室温下晾干24小时，涂层干膜厚度为110um；
E、随后再喷涂两道硅氧烷改性丙烯酸聚氨酯涂料，两道喷涂间隔45分钟，每道涂层干膜厚度为80um，喷涂完毕后在室温下干燥7天。
实施例3
本实施例的舵销轴承的防腐处理方法包括以下步骤：
A、用有机溶剂对舵销轴承进行除油处理，然后进行高压冲洗和干燥；
B、进行喷砂处理，使舵销轴承的表面清洁度达到Sa3级，表面粗糙度达到30um；
C、在步骤B完成后的30分钟，浸涂钛纳米高分子合金涂料，浸涂粘度为（涂-4杯）25s，闪干25分钟后，入炉烘干，烘干温度为270℃，时间为20分钟，涂层干膜厚度为125um；
D、烘干后，喷涂一道环氧防腐纳米涂料，在室温下晾干18小时，涂层干膜厚度为120um；
E、随后再喷涂两道硅氧烷改性丙烯酸聚氨酯涂料，两道喷涂间隔55分钟，每道涂层干膜厚度为70um，喷涂完毕后在室温下干燥6天。

Claims (3)

1.一种舵销轴承的防腐处理方法,其特征在于包括以下步骤：
A、用有机溶剂对舵销轴承进行除油处理，然后进行高压冲洗和干燥；
B、进行喷砂处理，使舵销轴承的表面清洁度达到Sa3级，表面粗糙度达到10-30um；
C、在步骤B完成后的30分钟内，浸涂钛纳米高分子合金涂料，闪干25-30分钟后，入炉烘干，烘干温度为250-280℃，时间为20-30分钟；
D、烘干后，喷涂一道环氧防腐纳米涂料，在室温下晾干12-24小时，涂层干膜厚度为80-120um；
E、随后再喷涂两道硅氧烷改性丙烯酸聚氨酯涂料，两道喷涂间隔小于1小时，每道涂层干膜厚度为60-80um，喷涂完毕后在室温下干燥5-7天。
2.根据权利要求1所述的舵销轴承的防腐处理方法, 其特征在于:步骤C的涂层干膜厚度大于100um。
3.根据权利要求1所述的舵销轴承的防腐处理方法, 其特征在于:步骤C的浸涂粘度为20-25s。
CN201510245069.5A 2015-05-14 2015-05-14 舵销轴承的防腐处理方法 Pending CN104912936A (zh)