CN104877427A - Diatom ooze coating and preparation method thereof - Google Patents
Diatom ooze coating and preparation method thereof Download PDFInfo
- Publication number
- CN104877427A CN104877427A CN201510285577.6A CN201510285577A CN104877427A CN 104877427 A CN104877427 A CN 104877427A CN 201510285577 A CN201510285577 A CN 201510285577A CN 104877427 A CN104877427 A CN 104877427A
- Authority
- CN
- China
- Prior art keywords
- parts
- xylogen
- diatom ooze
- ooze coating
- lignin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a diatom ooze coating which is made of raw materials comprising, by weight, 15-25 parts of water, 0.6-2.6 parts of lignin or lignin derivatives, 10-15 parts of tourmalines, 0.1-0.3 part of silver oxide, 10-15 parts of titanium dioxide, 3-6 parts of precipitated barium sulphate, 5-15 parts of kaoline, 5-10 parts of sea-foam stone powder, 30-45 parts of nano diatomite, 0.5-1.5 parts of palladium, 5-10 parts of nanometer titania, 0.4-0.6 part of leveling agents, 1.5-4 parts of thickening agents, 0.6-1.2 parts of mildew preventives, 1-5 parts of active carbon nanoparticles, 0.5-3 parts of net-flavor emulsions, 8-15 parts of dispersible adhesive powder and 0-3 parts of pigment. The diatom ooze coating is excellent in breathability and moisture absorption, gas ion negatively charged can be released, human body synthesis and vitamin storage can be promoted, and human immune ability is improved; functions of sterilization, mold prevention, deodorization, air purification and fire prevention are achieved; the preparation method is simple, easy to operate and convenient for large-scale production.
Description
Technical field
The present invention relates to paint field, be specifically related to a kind of diatom ooze coating and preparation method thereof.
Background technology
Coating is a kind of material, and this material can be coated in article surface by different construction technologies, forms adhere well, has some strength, continuous print solid film.The film common name film of such formation, also known as paint film or coating, it is made up of filmogen, film forming subsidiary material matter and auxiliary film forming matter three kinds of base substances.Existing coating, adopt potassium silicate solution as filmogen, potassium silicate provides excellent bond properties, but due to the existence of alkalimetal ion, makes coating adhesion inadequate, simultaneously due to the existence of alkalimetal ion, make the water tolerance of coating on the low side; Present coating also exists can not reduce formaldehyde in air content, mildew-resistant, antibacterial, diatom ooze coating cohesive force is poor, the problem of easy dry linting.
Summary of the invention
The object of the invention is to propose a kind of diatom ooze coating and preparation method thereof.
Object of the present invention can be achieved through the following technical solutions:
A kind of diatom ooze coating, is made up of the raw material of following weight part:
A kind of diatom ooze coating, is characterized in that, be made up of the raw material of following weight part:
15 ~ 25 parts, water, xylogen or lignin derivative 0.6 ~ 2.6 part, 10 ~ 15 parts, tourmalinite, silver suboxide 0.1 ~ 0.3 part, titanium dioxide 10 ~ 15 parts, process white 3 ~ 6, kaolin 5 ~ 15, sepiolite powder 5 ~ 10, nano diatomite 30 ~ 45 parts, palladium 0.5 ~ 1.5 part, nano titanium oxide 5 ~ 10 parts, flow agent 0.4 ~ 0.6 part, thickening material 1.5 ~ 4 parts, mould inhibitor 0.6 ~ 1.2 part, active carbon nanoparticles 1 ~ 5 part, clean taste emulsion 0.5 ~ 3 part, re-dispersible glue powder 8 ~ 15 parts, pigment 0 ~ 3 part.
Preferably, described a kind of diatom ooze coating, is made up of the raw material of following weight part: 20 parts, water, xylogen or lignin derivative 1.2 parts, 13 parts, tourmalinite, silver suboxide 0.2 part, titanium dioxide 13 parts, process white 4.5 parts, kaolin 10 parts, sepiolite powder 8 parts, nano diatomite 37 parts, palladium 1 part, nano titanium oxide 6 parts, flow agent 0.5 part, thickening material 2.5 parts, mould inhibitor 0.9 part, active carbon nanoparticles 3 parts, clean taste emulsion 1.5 parts, re-dispersible glue powder 11 parts, pigment 2 parts.
Preferably, described re-dispersible glue powder is any one or the multiple combination in the multipolymer of ethene-vinyl acetate, vinyl acetate between to for plastic-tertiary monocarboxylic acid ethylene copolymer, acrylic copolymer.
Preferably, described tourmalinite, nano titanium oxide and palladium are Powdered.
Preferably, described a kind of diatom ooze coating, described xylogen is the one in ligninsulfonate, hydrochloric acid xylogen, Milled wood lignin, alkali lignin, enzymolysis xylogen, steam explosion xylogen and ethanol xylogen; Described lignin derivative is the one in sulfonation modifying xylogen, epoxide modified xylogen, amination modifying xylogen, methylolation modified lignin resin, graft modification xylogen.
Preferably, described a kind of diatom ooze coating, its preparation method comprises the following steps:
(1) xylogen or lignin derivative are dissolved in the NaOH solution of 1.5%, cross and filter insoluble impurities, obtain filtrate, filtrate pH to 3 is regulated to make xylogen coagulation sedimentation, filter, obtain xylogen or the lignin derivative of purifying, airflow drying is to weight, then grinding sieves, and chooses xylogen or lignin derivative that granularity is 80 ~ 100 object purifying;
(2) weigh each component by formula ratio, water, Mierocrystalline cellulose have been added in stirred vessel, stir 5min with the stirring velocity of 450r/min;
(3) tourmalinite, titanium dioxide, process white, kaolin, sepiolite powder, nano diatomite, nano titanium oxide are added in stirred vessel, stir 30min with the stirring velocity of 1200r/min;
(4) silver suboxide and palladium are added in stirred vessel, stir 10min with the stirring velocity of 800r/min;
(5) flow agent, thickening material, mould inhibitor, clean taste emulsion, re-dispersible glue powder are added in stirred vessel, stir 10min with the stirring velocity of 500r/min;
(6) in stirred vessel, add pigment, stir, obtain product.
Compared with prior art, the invention has the advantages that: the present invention take Pd/TiO2 as catalyzer, at pollutents such as catalyze oxidation of formaldehyde under no light condition, the object purified air can be realized, therefore there is application prospect widely.
The present invention is added with diatomite, therefore there is excellent ventilation property, water absorbability, diatomite has the structure of special porous, add active carbon nanoparticles simultaneously, possesses extremely strong physisorption, can the pollutent such as formaldehyde in absorbed air, more accelerate the conversion rate of the pollutents such as formaldehyde, its cohesiveness can be improved again.The present invention can discharge electronegative gaseous ion, human body can be facilitated to synthesize and vitamin storage, be conducive to blood Oxygen deliver simultaneously, have promotion human metabolism, improve human immunological competence, regulate the effect of human body function balance; , the re-dispersible glue powder added can improve liquidity, improve workability.Improve force of cohesion, extend the open hour and strengthen water-retentivity coating of the present invention and also there is sterilization, mildew-resistant, deodorizing, purify air and fire-proof function; Preparation method of the present invention is simple, easy to operate, is convenient to realize scale operation.
Embodiment
Embodiment 1
A kind of diatom ooze coating, it is made up of the following component according to weight part:
15 parts, water, xylogen or lignin derivative 0.6 part, 10 parts, tourmalinite, silver suboxide 0.1 part, titanium dioxide 10 parts, process white 3 parts, kaolin 5 parts, sepiolite powder 5 parts, nano diatomite 30 parts, palladium 0.5 part, nano titanium oxide 5 parts, flow agent 0.4 part, thickening material 1.5 parts, mould inhibitor 0.6 part, active carbon nanoparticles 1 part, clean taste emulsion 0.5 part, re-dispersible glue powder 8 parts, pigment 1 part.
Described xylogen is the one in ligninsulfonate, hydrochloric acid xylogen, Milled wood lignin, alkali lignin, enzymolysis xylogen, steam explosion xylogen and ethanol xylogen; Described lignin derivative is the one in sulfonation modifying xylogen, epoxide modified xylogen, amination modifying xylogen, methylolation modified lignin resin, graft modification xylogen.
Described tourmalinite, nano titanium oxide and palladium are Powdered, and described Mierocrystalline cellulose is one or more the mixing in lignocellulose, hydroxypropylcellulose, carboxymethyl cellulose, Polyanionic Cellulose, sodium polyacrylate ethyl cellulose, methylcellulose gum and calcium mercaptoacetate polyoxyethylene glycol Vltra tears.
Described re-dispersible glue powder is any one or multiple combination in the multipolymer of ethene-vinyl acetate, vinyl acetate between to for plastic-tertiary monocarboxylic acid ethylene copolymer, acrylic copolymer.
Tourmalinite is with the addition of in the present invention, tourmalinite can produce negative ion, micro-electric current and far infrared rays, under the multiple excitation of tourmalinite, Pd/TiO2 can realize a kind of brand-new catalysis energy under no light condition, thus reach the target of the pollutents such as catalyze oxidation of formaldehyde, therefore there is application prospect widely.
Described a kind of diatom ooze coating, its preparation method in turn includes the following steps:
(1) xylogen or lignin derivative are dissolved in the NaOH solution of 1.5%, cross and filter insoluble impurities, obtain filtrate, filtrate pH to 3 is regulated to make xylogen coagulation sedimentation, filter, obtain xylogen or the lignin derivative of purifying, airflow drying is to weight, then grinding sieves, and chooses xylogen or lignin derivative that granularity is 80 ~ 100 object purifying;
(2) weigh each component by formula ratio, water, Mierocrystalline cellulose have been added in stirred vessel, stir 5min with the stirring velocity of 450r/min;
(3) tourmalinite, titanium dioxide, process white, kaolin, sepiolite powder, nano diatomite, nano titanium oxide are added in stirred vessel, stir 30min with the stirring velocity of 1200r/min;
(4) silver suboxide and palladium are added in stirred vessel, stir 10min with the stirring velocity of 800r/min;
(5) by flow agent, thickening material, mould inhibitor, clean taste breast re-dispersible glue powder, add in stirred vessel, stir 10min with the stirring velocity of 500r/min;
(6) in stirred vessel, add pigment, stir, obtain product.
Embodiment 2
The difference of the present embodiment and embodiment 1 is only,
20 parts, water, xylogen or lignin derivative 1.2 parts, 13 parts, tourmalinite, silver suboxide 0.2 part, titanium dioxide 13 parts, process white 4.5 parts, kaolin 10 parts, sepiolite powder 8 parts, nano diatomite 37 parts, palladium 1 part, nano titanium oxide 6 parts, flow agent 0.5 part, thickening material 2.5 parts, mould inhibitor 0.9 part, active carbon nanoparticles 3 parts, clean taste emulsion 1.5 parts, re-dispersible glue powder 11 parts, pigment 2 parts.
Embodiment 3
The difference of the present embodiment and embodiment 1 is only,
25 parts, water, xylogen or lignin derivative 2.6 parts, 15 parts, tourmalinite, silver suboxide 0.3 part, titanium dioxide 15 parts, process white 6, kaolin 15, sepiolite powder 10, nano diatomite 45 parts, palladium 1.5 parts, nano titanium oxide 10 parts, flow agent 0.6 part, thickening material 4 parts, mould inhibitor 1.2 parts, active carbon nanoparticles 5 parts, clean taste emulsion 2 parts, re-dispersible glue powder 13 parts, pigment 2.5 parts.
The above; be only the present invention's preferably embodiment; but protection scope of the present invention is not limited thereto; anyly be familiar with those skilled in the art in the technical scope that the present invention discloses; be equal to according to technical scheme of the present invention and inventive concept thereof and replace or change, all should be encompassed within protection scope of the present invention.
Claims (6)
1. a diatom ooze coating, is characterized in that, is made up of the raw material of following weight part:
15 ~ 25 parts, water, xylogen or lignin derivative 0.6 ~ 2.6 part, 10 ~ 15 parts, tourmalinite, silver suboxide 0.1 ~ 0.3 part, titanium dioxide 10 ~ 15 parts, process white 3 ~ 6, kaolin 5 ~ 15, sepiolite powder 5 ~ 10, nano diatomite 30 ~ 45 parts, palladium 0.5 ~ 1.5 part, nano titanium oxide 5 ~ 10 parts, flow agent 0.4 ~ 0.6 part, thickening material 1.5 ~ 4 parts, mould inhibitor 0.6 ~ 1.2 part, active carbon nanoparticles 1 ~ 5 part, clean taste emulsion 0.5 ~ 3 part, re-dispersible glue powder 8 ~ 15 parts, pigment 0 ~ 3 part.
2. a kind of diatom ooze coating according to claim 1, it is characterized in that, be made up of the raw material of following weight part: 20 parts, water, xylogen or lignin derivative 1.2 parts, 13 parts, tourmalinite, silver suboxide 0.2 part, titanium dioxide 13 parts, process white 4.5 parts, kaolin 10 parts, sepiolite powder 8 parts, nano diatomite 37 parts, palladium 1 part, nano titanium oxide 6 parts, flow agent 0.5 part, thickening material 2.5 parts, mould inhibitor 0.9 part, active carbon nanoparticles 3 parts, clean taste emulsion 1.5 parts, re-dispersible glue powder 11 parts, pigment 2 parts.
3. a kind of diatom ooze coating according to claim 1, is characterized in that, described re-dispersible glue powder is any one or multiple combination in the multipolymer of ethene-vinyl acetate, vinyl acetate between to for plastic-tertiary monocarboxylic acid ethylene copolymer, acrylic copolymer.
4. a kind of diatom ooze coating according to claim 1, is characterized in that, described tourmalinite, nano titanium oxide and palladium are Powdered.
5. a kind of diatom ooze coating according to claim 1, is characterized in that, described xylogen is the one in ligninsulfonate, hydrochloric acid xylogen, Milled wood lignin, alkali lignin, enzymolysis xylogen, steam explosion xylogen and ethanol xylogen; Described lignin derivative is the one in sulfonation modifying xylogen, epoxide modified xylogen, amination modifying xylogen, methylolation modified lignin resin, graft modification xylogen.
6. a kind of diatom ooze coating according to any one of claim 1-5, it is characterized in that, its preparation method comprises the following steps:
(1) xylogen or lignin derivative are dissolved in the NaOH solution of 1.5%, cross and filter insoluble impurities, obtain filtrate, filtrate pH to 3 is regulated to make xylogen coagulation sedimentation, filter, obtain xylogen or the lignin derivative of purifying, airflow drying is to weight, then grinding sieves, and chooses xylogen or lignin derivative that granularity is 80 ~ 100 object purifying;
(2) weigh each component by formula ratio, water, Mierocrystalline cellulose have been added in stirred vessel, stir 5min with the stirring velocity of 450r/min;
(3) tourmalinite, titanium dioxide, process white, kaolin, sepiolite powder, nano diatomite, nano titanium oxide are added in stirred vessel, stir 30min with the stirring velocity of 1200r/min;
(4) silver suboxide and palladium are added in stirred vessel, stir 10min with the stirring velocity of 800r/min;
(5) flow agent, thickening material, mould inhibitor, clean taste emulsion, re-dispersible glue powder are added in stirred vessel, stir 10min with the stirring velocity of 500r/min;
(6) in stirred vessel, add pigment, stir, obtain product.