CN106147446A - A kind of water negative ion functional paint and preparation method thereof - Google Patents
A kind of water negative ion functional paint and preparation method thereof Download PDFInfo
- Publication number
- CN106147446A CN106147446A CN201610524673.6A CN201610524673A CN106147446A CN 106147446 A CN106147446 A CN 106147446A CN 201610524673 A CN201610524673 A CN 201610524673A CN 106147446 A CN106147446 A CN 106147446A
- Authority
- CN
- China
- Prior art keywords
- parts
- weight
- negative ion
- agent
- functional paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to functional coating technical field, be specifically related to a kind of water negative ion functional paint and preparation method thereof.It is an object of the invention to provide and a kind of have only to simple process water negative ion functional paint being just obtained in that persistently efficiently anion releasing and preparation method thereof.One water negative ion functional paint of the present invention, including the raw material of following parts by weight: deionized water 15 25 parts, wetting dispersing agent 0.5 1 parts, mineral oil defoaming agent 0.2 0.5 parts, propylene glycol 12 parts, acrylic compounds levelling agent 0.1 0.2 parts, 10 20 parts of rutile titanium white lead, anion powder 10 18 parts, inserts 20 30 parts, clean taste acrylic emulsion 25 35 parts, Kazon preservative 0.1 0.5 parts, alcohol ester 12 coalescents 12 parts, multifunctional assistant 0.1 0.2 parts, alkali swelling association thickener 0.5 0.8 parts.The present invention has that technique is simple and environmentally-friendly and the advantage such as length in service life.
Description
Technical field
The invention belongs to functional coating technical field, be specifically related to a kind of water negative ion functional paint and preparation side thereof
Method.
Technical background
It is said that in general, people needs about 13,000,000,000 anion every day, and our room, office, the ring such as public place of entertainment
Border, can only provide about 1-20 hundred million.Huge contrast between this supply and demand, tends to cause pneumonia, the breathing disease of tracheitis
Sick.Central heating and the air conditioning system of air-cooling system, anion is often purged.Synthetic fibers, carpet are easily inhaled with positive charge
Receive anion.Reinforcing bar, fibre board all absorb anion.Anion is referred to as " air vitamin ", and it is as the vitamin one of food
Sample, has highly important impact to the vital movement of human body and other biological.In medical circle, anion is identified it is to have to kill
Go out pathogenic bacteria and purify air effective means.Medical research shows, in air, electronegative microgranule makes oxygen content in blood increase, and has
It is beneficial to the conveying of blood oxygen, absorbs and utilize, there is promotion human metabolism, improve human body immunity, strengthen human body flesh energy, adjust
The effect of joint human body function balance.According to textual criticism, anion is to 7 systems of human body, and nearly more than 30 kinds of diseases have suppression, alleviate and auxiliary
Help therapeutical effect, especially the health-care effect of human body is become apparent from.
Summary of the invention
It is an object of the invention to provide a kind of simple process that has only to and be just obtained in that the water of persistently efficiently anion releasing
Property anion function coating and preparation method thereof.
The technical scheme that the present invention takes for achieving the above object is:
A kind of water negative ion functional paint, including the raw material of following parts by weight:
Deionized water 15-25 part, wetting dispersing agent 0.5-1 part, mineral oil defoaming agent 0.2-0.5 part, propylene glycol 1-2
Part, acrylic compounds levelling agent 0.1-0.2 part, rutile titanium white lead 10-20 part, anion powder 10-18 part, inserts 20-30 part,
Clean taste acrylic emulsion 25-35 part, Kazon preservative 0.1-0.5 part, alcohol ester 12 coalescents 1-2 part, multifunctional assistant
0.1-0.2 part, alkali swelling association thickener 0.5-0.8 part.
Further, inserts of the present invention is calcined kaolin and the mixture of Pulvis Talci arbitrary proportion or forges
Burn the mixture of Kaolin and Pulvis Talci arbitrary proportion and the one in heavy calcium carbonate, wollastonite in powder or lithopone or
The mixture of two or more arbitrary proportions.
The preparation method of water negative ion functional paint of the present invention, comprises the following steps:
S1: take the deionized water of described parts by weight, wetting dispersing agent, mineral oil defoaming agent, propylene glycol, acrylic compounds
Levelling agent, after 2000-3000 rev/min of lower high-speed stirred to uniform state, rotating speed is down to less than 800 revs/min；
S2: add the rutile titanium white lead of described parts by weight, anion powder, inserts, at 2000-3000 rev/min
Lower dispersion 30-40 minute, makes uniform sizing material；
S3: add alcohol ester 12 coalescents of described parts by weight, Kazon preservative, clean taste under at the uniform velocity stirring
Acrylic emulsion is to stirring；
S4: the multifunctional assistant adding described parts by weight stirs, is subsequently adding the alkali swelling of described parts by weight
Association thickener regulation viscosity, to 100-110KU, prepares finished product coating.
The method have the advantages that
The manufacturing process of water negative ion functional paint prepared by the present invention is simple, and coating can be released in film forming procedure rapidly
Amplification quantity anion, then may proceed to after film forming tie with the service life of a value sustained release anion direct fluctuated to film
Bundle.This coating can the effective irritative gas such as the benzene of release, formaldehyde, ketone, ammonia in the used decorative materials of decontamination chamber interior decoration, with
And stink that in daily life, rubbish rots, the harmful abnormal flavour such as smoke；The living environment of the mankind can be effectively improved, carry
The immunity of high human body.
Detailed description of the invention
Embodiment 1
A kind of water negative ion functional paint, including the raw material of following parts by weight:
Deionized water 15 parts, wetting agent (PE-100) 0.2 part, dispersant (5040) 0.6 parts, mineral oil defoaming agent
(NXZ) 0.2 part, propylene glycol 1 part, acrylic compounds levelling agent (621N) 0.1 part, 10 parts of rutile titanium white lead, anion powder 10 parts,
Calcined kaolin (1250 mesh) 3 parts, Pulvis Talci (1000 mesh) 3 parts, heavy calcium carbonate (1000 mesh) 4 parts, wollastonite in powder (1000
Mesh) 4 parts, clean taste acrylic emulsion 25 parts, 0.1 part of card conifer preservative (K14), alcohol ester 12 coalescents 1 part, multifunctional assistant
Agent (AMP-95) 0.1 part, 0.5 part of alkali swelling association thickener (L-344).
The preparation method of the present embodiment water negative ion functional paint, comprises the following steps:
S1: take the deionized water of described parts by weight, wetting dispersing agent, mineral oil defoaming agent, propylene glycol, acrylic compounds
Levelling agent, after 1000 revs/min of lower high-speed stirred to uniform state, rotating speed is down to 600 revs/min；
S2: add the rutile titanium white lead of described parts by weight, anion powder, calcined kaolin, Pulvis Talci, heavy carbonic acid
Calcium powder and wollastonite in powder, disperse 40 minutes under 2000 revs/min, make uniform sizing material；
S3: add alcohol ester 12 coalescents of described parts by weight, Kazon preservative, clean taste under at the uniform velocity stirring
Acrylic emulsion is to stirring；
S4: the multifunctional assistant AMP-95 adding described parts by weight stirs, and is subsequently adding described parts by weight
Alkali swelling association thickener regulation viscosity, to 100-110KU, prepares finished product coating.
The NXZ defoamer that mineral oil defoaming agent is break Thailand of Nantong City Chemical Manufacture that the present embodiment uses；Acrylic compounds
Levelling agent is Nuo Pu section 621N levelling agent；Alkali swelling association thickener is Nuo Pu section L-344 thickening agent.
Record from metope 5 centimeters after the water negative ion coating application being made up of above-mentioned raw materials proportioning and technique after testing
Every cubic centimetre of anion concentration reaches 4000.
Embodiment 2
A kind of water negative ion functional paint, including the raw material of following parts by weight:
Deionized water 20 parts, wetting agent (PE-100) 0.2 part, dispersant (5040) 0.6 parts, mineral oil defoaming agent
(NXZ) 0.4 part, propylene glycol 1.5 parts, acrylic compounds levelling agent (621N) 0.15 part, 15 parts of rutile titanium white lead, anion powder 14
Part, calcined kaolin (1250 mesh) 5 parts, Pulvis Talci (1000 mesh) 5 parts, clean taste acrylic emulsion 30 parts, Kazon preservative (K14)
0.3 part, alcohol ester 12 coalescents 1.5 parts, multifunctional assistant (AMP-95) 0.15 part, alkali swelling association thickener (L-
344) 0.6 part.
The preparation method of the present embodiment water negative ion functional paint, comprises the following steps:
S1: take the deionized water of described parts by weight, wetting dispersing agent, mineral oil defoaming agent, propylene glycol, acrylic compounds
Levelling agent, after 1000 revs/min of lower high-speed stirred to uniform state, rotating speed is down to 600 revs/min；
S2: add the rutile titanium white lead of described parts by weight, anion powder, calcined kaolin, Pulvis Talci, 2000
Disperse 40 minutes under rev/min, make uniform sizing material；
S3: add alcohol ester 12 coalescents of described parts by weight, card conifer preservative, clean under at the uniform velocity stirring
Taste acrylic emulsion is to stirring；
S4: the multifunctional assistant AMP-95 adding described parts by weight stirs, and is subsequently adding described parts by weight
Alkali swelling association thickener regulation viscosity, to 100-110KU, prepares finished product coating.
The NXZ defoamer that mineral oil defoaming agent is break Thailand of Nantong City Chemical Manufacture that the present embodiment uses；Acrylic compounds
Levelling agent is Nuo Pu section 621N levelling agent；Alkali swelling association thickener is Nuo Pu section L-344 thickening agent.
Record from metope 5 centimeters after the water negative ion coating application being made up of above-mentioned raw materials proportioning and technique after testing
Every cubic centimetre of anion concentration reaches 6000.
Embodiment 3
A kind of water negative ion functional paint, including the raw material of following parts by weight:
Deionized water 25 parts, wetting agent (PE-100) 0.2 part, dispersant (5040) 0.7 parts, mineral oil defoaming agent 0.5
Part, propylene glycol 2 parts, acrylic compounds levelling agent 0.2 part, 20 parts of rutile titanium white lead, anion powder 18 parts, calcined kaolin
(1000 mesh) 5 parts, Pulvis Talci (1000 mesh) 5 parts, 10 parts of lithopone (1000 mesh), clean taste acrylic emulsion 35 parts, Kazon anticorrosion
Agent (K14) 0.5 part, alcohol ester 12 coalescents 2 parts, multifunctional assistant (AMP-95) 0.2 part, alkali swelling association thickener
(L-344) 0.8 part.
The preparation method of the present embodiment water negative ion functional paint, comprises the following steps:
S1: take the deionized water of described parts by weight, wetting dispersing agent, mineral oil defoaming agent, propylene glycol, acrylic compounds
Levelling agent, after 1000 revs/min of lower high-speed stirred to uniform state, rotating speed is down to 600 revs/min；
S2: add the rutile titanium white lead of described parts by weight, anion powder, calcined kaolin, Pulvis Talci, lithopone,
Disperse 50 minutes under 2000 revs/min, make uniform sizing material；
S3: add alcohol ester 12 coalescents of described parts by weight, Kazon preservative, clean taste under at the uniform velocity stirring
Acrylic emulsion is to stirring；
S4: the multifunctional assistant AMP-95 adding described parts by weight stirs, and is subsequently adding described parts by weight
Alkali swelling association thickener regulation viscosity, to 100-110KU, prepares finished product coating.
The NXZ defoamer that mineral oil defoaming agent is break Thailand of Nantong City Chemical Manufacture that the present embodiment uses；Acrylic compounds
Levelling agent is Nuo Pu section 621N levelling agent；Alkali swelling association thickener is Nuo Pu section L-344 thickening agent.
Record from metope 5 centimeters after the water negative ion coating application being made up of above-mentioned raw materials proportioning and technique after testing
Every cubic centimetre of anion concentration reaches 8000.
Claims (3)
1. a water negative ion functional paint, it is characterised in that include the raw material of following parts by weight:
Deionized water 15-25 part, wetting dispersing agent 0.5-1 part, mineral oil defoaming agent 0.2-0.5 part, propylene glycol 1-2 part, third
Olefin(e) acid class levelling agent 0.1-0.2 part, rutile titanium white lead 10-20 part, anion powder 10-18 part, inserts 20-30 part, clean taste
Acrylic emulsion 25-35 part, card conifer preservative 0.1-0.5 part, alcohol ester 12 coalescents 1-2 part, multifunctional assistant 0.1-
0.2 part, alkali swelling association thickener 0.5-0.8 part.
2. water negative ion functional paint as claimed in claim 1, it is characterised in that described inserts is calcined kaolin
With the mixture of the mixture of Pulvis Talci arbitrary proportion or calcined kaolin and Pulvis Talci arbitrary proportion and heavy calcium carbonate,
The mixture of the one or more kinds of arbitrary proportions in wollastonite in powder or lithopone.
3. the preparation method of the water negative ion functional paint described in claim 1 or 2, it is characterised in that comprise the following steps:
S1: take the deionized water of described parts by weight, wetting dispersing agent, mineral oil defoaming agent, propylene glycol, acrylic compounds levelling
Agent, after 2000-3000 rev/min of lower high-speed stirred to uniform state, rotating speed is down to less than 800 revs/min；
S2: add the rutile titanium white lead of described parts by weight, anion powder, inserts, at 2000-3000 rev/min lower point
Dissipate 30-40 minute, make uniform sizing material；
S3: add alcohol ester 12 coalescents of described parts by weight, card conifer preservative, clean taste third under at the uniform velocity stirring
Olefin(e) acid emulsion is to stirring；
S4: the multifunctional assistant adding described parts by weight stirs, the alkali swelling being subsequently adding described parts by weight associates
Type thickening agent regulation viscosity, to 100-110KU, prepares finished product coating.