CN101381543A - Nano negative ion wall paint - Google Patents
Nano negative ion wall paint Download PDFInfo
- Publication number
- CN101381543A CN101381543A CNA2008102184019A CN200810218401A CN101381543A CN 101381543 A CN101381543 A CN 101381543A CN A2008102184019 A CNA2008102184019 A CN A2008102184019A CN 200810218401 A CN200810218401 A CN 200810218401A CN 101381543 A CN101381543 A CN 101381543A
- Authority
- CN
- China
- Prior art keywords
- percent
- negative ion
- wall paint
- nano
- nano negative
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a nano negative-ion metope lacquer, which consists of the following materials in weight percentage: 10 to 16 percent of clean tap water, 0.6 to 1.2 percent of amine polycarboxylate, 0.1 to 0.2 percent of surface active agent, 0.1 to 0.2 percent of pH conditioning agent, 0.3 to 0.7 percent of foam killer, 2.5 to 4.5 percent of glycol, 1.5 to 3.0 percent of alcohol ester-12, 15 to 25 percent of titanium pigment, 6 to 12 percent of calcined kaolin, 6 to 12 percent of coarse whiting, 2 to 5 percent of aluminum silicate, 30 to 45 percent of styrene-acrylate emulsion, 2 to 5 percent of nano negative ions, 0.6 to 1.2 percent of polyurethane thickener, 0.2 to 0.6 percent of mildew preventive, and 0.1 to 0.2 percent of preservative. The nano negative-ion metope lacquer integrates decorative property and functions of releasing negative ions constantly, purifying air, covering tiny cracks, having good resistance to water and alkali of film coating, resisting mildew and aquatic grasses, having resistance to soiling and so on.
Description
Technical field
The present invention relates to a kind of interior wall wall paint, particularly a kind of lasting release negative ion, purify air, cover hair line, paint film is water-fast, the anti-algae of alkaline-resisting good, mildew-resistant, pollution resistance etc. are functional and the environmental protection wall surface paint of ornamental perfect unity.
Background technology
People yearn for the air and the environment of nature, in the house fitting-up life, formaldehyde limit the quantity of exceed standard, Air quality decline, metope crackle, grow dim, mildew, leak, problem such as anti-soil perplexs people's life staying idle at home for a long time, and these all can solve by the brushing wall paint.Present many wall paintes all can not solve or can not address these problems fully, air quality problems particularly, trace it to its cause, mainly be that present employed wall paint can not purify air or effect is bad, water-alkali resistance is not strong, what have does not have elasticity, and pollution resistance is poor, and the anti-algae function of mildew-resistant is poor, VOC content height, not enough safety and environmental protection.
Summary of the invention
In order to overcome the deficiencies in the prior art, the invention provides a kind of lasting release negative ion, purify air, cover hair line, paint film is water-fast, alkaline-resisting good, the anti-algae of mildew-resistant, pollution resistance etc. are functional and the environmental protection wall surface paint of ornamental perfect unity.
The technical solution adopted for the present invention to solve the technical problems is:
A kind of nano negative ion wall paint, it is characterized in that this wall paint is made up of following materials in weight percentage: clean tap water 10-16%, poly carboxylic acid amine salt 0.6-1.2%, tensio-active agent 0.1-0.2%, PH conditioning agent 0.1-0.2%, defoamer 0.3-0.7%, ethylene glycol is 2.5-4.5%, 12 alcohol esters are 1.5-3.0%, titanium dioxide is 15-25%, and calcined kaolin is 6-12%, and coarse whiting is 6-12%, pure aluminium silicate is 2-5%, benzene emulsion is 30-45%, and the nano-negative ion element is 2-5%, and the Polyurethane thickening material is 0.6-1.2%, mould inhibitor is 0.2-0.6%, and sanitas is 0.1-0.2%.
Functional material that can the release air negative ion mainly contains tourmalinite (tourmaline), opal, marine bottom sediment, aethiops vegetabilis 4 big classes.Wherein, tourmalinite is the silicates mineral crystal of a kind of naturally occurring trigonal system, column crystallization, can charged lastingly (having electric energy), and with uranium (having radiant), magnet (having magnetic energy) and be called the world's three macro-energy ores.The crystalline structure of tourmalinite has determined it to have along two natural positive-negative polarities of crystallization end of C axle.This inherent permanent electrode is the basis that produces negative ion.The nano-negative ion element that the present invention adopts is a kind of multifunction negative ion element of the rock company in sky, and model is ASC-01, can discharge negative ion lastingly, purifies air, and absorbs formaldehyde.
The CF-10 that the tensio-active agent that the present invention adopts is produced for DOW company, main component is a nonyl phenol.
The mould inhibitor that the present invention adopts is the AF2130 of first wound company, and main component is the mixture of amido formic acid-1-chloro-benzimidazolyl-2 radicals-methyl acid and N-(3,4 dichlorophenyl)-N.N-dimethyl urea.
The sanitas that the present invention adopts is the GT2060 of first wound company, and main component is an isothiazolinone.
The benzene emulsion that the present invention adopts is the vinylbenzene and the CALCIUM ACRYLATE synthetic emulsion of BASF AG, and model is 296DS.
The defoamer that the present invention adopts is the organosilicon and the mineral oil mixture of Ming Jia company, and model is 7120.
The Polyurethane thickening material that the present invention adopts is the NLS300 of BASF AG.
The pH value conditioning agent can adopt according to the soda acid situation of batching as alkaline matter or acidic substance such as calcium hydroxides, and the pH value conditioning agent that the present invention adopts is that the model of DOW company is the material of AMP-95.
The present invention's technology routinely can produce, and as feeding intake in order, casts a kind of material again after every kind of material stirs, and stirs while feeding intake, and the back of waiting to be uniformly dispersed is detected viscosity and can be finished.
The invention has the beneficial effects as follows: the present invention adopts that perviousness is strong, water-tolerant, flexible and have an alkali-resisting particulate footpath benzene emulsion film forming matter of deciding, adopt the plain lasting negative ion that discharges of multifunction negative ion, purify air, adopt the nano level superfine pure aluminium silicate to improve weathering resistance and sticking power, adopt poly carboxylic acid amine salt and Polyurethane thickening material to improve water tolerance and stability, adopt the high-quality Rutile type Titanium Dioxide, make metope beautiful lastingly.
The present invention is further described below in conjunction with embodiment.
Embodiment
Embodiment 1
At first prepare burden, take by weighing clean tap water 14kg, dispersion agent 1kg, tensio-active agent 0.1kg, PH conditioning agent 0.1kg, defoamer 0.3kg, ethylene glycol is 2.5kg, 12 alcohol esters are 1.8kg, titanium dioxide is 18kg, calcined kaolin is 8kg, coarse whiting is 8kg, and pure aluminium silicate is 2kg, and benzene emulsion is 38kg, the nano-negative ion element is 2kg, the Polyurethane thickening material is 0.8kg, and mould inhibitor is 0.2kg, and sanitas is 0.2kg, making lacquer craftwork routinely feeds intake in proper order, cast a kind of material after every kind of material stirs again, stir while feeding intake, viscosity is detected in the back of waiting to be uniformly dispersed can make nano negative ion wall paint of the present invention.
Embodiment 2
At first batching takes by weighing clean tap water 15kg, dispersion agent 0.8kg, tensio-active agent 0.15kg, PH conditioning agent 0.1kg, defoamer 0.4kg, ethylene glycol is 3kg, 12 alcohol esters are 2kg, titanium dioxide is 20kg, and calcined kaolin is 10kg, and coarse whiting is 6kg, pure aluminium silicate is 2kg, benzene emulsion is 35kg, and the nano-negative ion element is 3kg, and the Polyurethane thickening material is 0.7kg, mould inhibitor is 0.3kg, sanitas is 0.2kg, makes lacquer craftwork routinely and feeds intake in proper order, casts a kind of material again after every kind of material stirs, stir while feeding intake, viscosity is detected in the back of waiting to be uniformly dispersed can make nano negative ion wall paint of the present invention.
Embodiment 3
At first batching takes by weighing clean tap water 16kg, dispersion agent 0.6kg, tensio-active agent 0.1kg, PH conditioning agent 0.1kg, defoamer 0.3kg, ethylene glycol is 2.5kg, 12 alcohol esters are 2.2kg, titanium dioxide is 22kg, and calcined kaolin is 8kg, and coarse whiting is 10kg, pure aluminium silicate is 4kg, benzene emulsion is 40kg, and the nano-negative ion element is 4kg, and the Polyurethane thickening material is 0.9kg, mould inhibitor is 0.5kg, sanitas is 0.2kg, makes lacquer craftwork routinely and feeds intake in proper order, casts a kind of material again after every kind of material stirs, stir while feeding intake, viscosity is detected in the back of waiting to be uniformly dispersed can make nano negative ion wall paint of the present invention.
The raw material that the present invention adopts is easy to get, and is convenient to construction, can effectively purify air, water-fast, alkaline-resisting good, to cover hair line, the anti-algae of mildew-resistant, pollution resistance strong, fast in colour beautiful.
Claims (6)
1. nano negative ion wall paint, it is characterized in that this wall paint is made up of following materials in weight percentage: clean tap water 10-16%, poly carboxylic acid amine salt 0.6-1.2%, tensio-active agent 0.1-0.2%, PH conditioning agent 0.1-0.2%, defoamer 0.3-0.7%, ethylene glycol is 2.5-4.5%, 12 alcohol esters are 1.5-3.0%, titanium dioxide is 15-25%, and calcined kaolin is 6-12%, and coarse whiting is 6-12%, pure aluminium silicate is 2-5%, benzene emulsion is 30-45%, and the nano-negative ion element is 2-5%, and the Polyurethane thickening material is 0.6-1.2%, mould inhibitor is 0.2-0.6%, and sanitas is 0.1-0.2%.
2. a kind of nano negative ion wall paint according to claim 1 is characterized in that sanitas is an isothiazolinone.
3. a kind of nano negative ion wall paint according to claim 1 is characterized in that benzene emulsion is vinylbenzene and CALCIUM ACRYLATE synthetic emulsion.
4. a kind of nano negative ion wall paint according to claim 1 is characterized in that defoamer is organosilicon and mineral oil mixture.
5. a kind of nano negative ion wall paint according to claim 1 is characterized in that tensio-active agent is a nonyl phenol.
6. a kind of nano negative ion wall paint according to claim 1 is characterized in that mould inhibitor is the mixture of amido formic acid-1-chloro-benzimidazolyl-2 radicals-methyl acid and N-(3,4 dichlorophenyl)-N.N-dimethyl urea.