CN101760096B - Waterborne lotus leaf paint - Google Patents
Waterborne lotus leaf paint Download PDFInfo
- Publication number
- CN101760096B CN101760096B CN2009101938583A CN200910193858A CN101760096B CN 101760096 B CN101760096 B CN 101760096B CN 2009101938583 A CN2009101938583 A CN 2009101938583A CN 200910193858 A CN200910193858 A CN 200910193858A CN 101760096 B CN101760096 B CN 101760096B
- Authority
- CN
- China
- Prior art keywords
- percent
- lotus leaf
- paint
- waterborne
- good
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a waterborne lotus leaf paint, which contains the following materials by weight percent: 10-30 percent of clean tap water, 0.5-1.3 percent of polycarboxylic acid ammonium salt, 0.05-0.4 percent of surfactant, 0.1-0.3 percent of PH regulator, 0.4-0.8 percent of defoamer, 1.5-4 percent of ethylene glycol, 1.0-5.0 percent of film forming assistant, 10-30 percent of titanium white, 5-15 percent of talcum powder, 3-10 percent of organosilicon, 25-55 percent of emulsion, 0.1-0.8 percent of thickener, 0.1-1.0 percent of mildew preventive and 0.1-0.5 percent of preservative. The invention overcomes the defects in the prior art and has the advantages of simple construction, good recoatability, good water-fast alkali resistance, good mildew and algae prevention capacity, strong adhesive force, good weather resistance and strong hydrophobicity.
Description
Technical field
The present invention relates to a kind of wall paint, particularly a kind of waterborne lotus leaf paint.
Background technology
In wall construction, the paint film wetting ability is strong, pollution resistance is bad, wall crazing, grow dim, problem such as efflorescence, peeling, mildew, recoatability difference perplex people's life staying idle at home for a long time and the city attractive in appearance, and these all can solve through the brushing wall paint.Wall paint is a kind of colloidal solution.It is spread upon body surface, and through physics, chemical transformation after a while, continuous film is realized its defencive function, decoration functions and other special functions with the tough and tensile of coated article surface secure bond in generation.Present many face wall lacquers all can not solve or can not address these problems fully; Trace it to its cause; Mainly be that present employed wall paint pollution resistance, water-alkali resistance property stability to aging are bad, the anti-algae function of mildew-resistant is poor, and coating surface tension force is high, wetting ability is strong, not enough safety and environmental protection.
Summary of the invention
The objective of the invention is in order to overcome weak point of the prior art, the waterborne lotus leaf paint of a kind of simple, good, water-fast alkali resistant of recoatability of constructing, the anti-algae of mildew-resistant, strong adhesion, good weatherability, strong-hydrophobicity is provided.
In order to achieve the above object, the present invention adopts following scheme:
A kind of waterborne lotus leaf paint, form by following materials in weight percentage:
Clean tap water 10-30%, poly carboxylic acid amine salt 0.5-1.3%, tensio-active agent 0.05-0.4%, PH regulator 0.1-0.3%; Skimmer 0.4-0.8%, terepthaloyl moietie is 1.5-4%, film coalescence aid is 1.0-5.0%; White titanium pigment is 10-30%, and talcum powder is 5-15%, and organosilicon is 3-10%; Emulsion is 25-55%, and thickening material is 0.1-0.8%, and mould inhibitor is 0.1-0.5% for the 0.1-1.0% sanitas.
Aforesaid a kind of waterborne lotus leaf paint, wherein said antiseptic content are 0.1-0.2%;
Aforesaid a kind of waterborne lotus leaf paint, wherein said sanitas are that the model that French first wound company produces is the RH-893 of GT2060;
Aforesaid a kind of waterborne lotus leaf paint, wherein said mould inhibitor are that French first wound company produces, and model is AF2130;
Aforesaid a kind of waterborne lotus leaf paint, wherein said film coalescence aid are that U.S. DOW company produces, and model is the tripropylene glycol butyl ether of TPnB;
Aforesaid a kind of waterborne lotus leaf paint, wherein said organosilicon are that Japan is clear and company's production, and model is 8861 pure organosilicon polymer;
Aforesaid a kind of waterborne lotus leaf paint, wherein said emulsion are BASF chemical company product, and model is the benzene emulsion of 296DS;
Aforesaid a kind of waterborne lotus leaf paint, wherein said skimmer is produced for Ming Jia company, and model is 7120 organosilicon and mineral oil mixture product;
Aforesaid a kind of waterborne lotus leaf paint, wherein said white titanium pigment is produced for Mei Lilian company, and model is 595 Rutile type Titanium Dioxide;
Aforesaid a kind of waterborne lotus leaf paint, the equal polyamine salt of wherein said poly carboxylic acid are that Britain BLACKBOWN company produces, and model is 165 product;
Aforesaid a kind of waterborne lotus leaf paint, wherein said tensio-active agent is produced for U.S.'s gas companies, and model is the T 46155 ether product of DC-01;
Aforesaid a kind of waterborne lotus leaf paint, wherein said thickening material are that BASF AG produces, and model is the Polyurethane thickening material of NLS300.
The present invention can produce by common process, as feeding intake in order, casts a kind of material again after every kind of material stirs, and stirs while feeding intake, and the back of waiting to be uniformly dispersed is detected viscosity and can be accomplished.
In sum, beneficial effect of the present invention:
One, lotus leaf lacquer of the present invention adopts resilient particulate footpath benzene emulsion to do film forming matter, improves paint film compactness, water-fast alkali-resistivity, stability to aging;
Two, adopt pure organosilicon polymer to improve paint film hydrophobicity, compactness, sticking power, construction recoatability in the lotus leaf lacquer of the present invention;
Three, adopt the equal polyamine salt of poly carboxylic acid to improve product dispersion stabilization and water tolerance in the lotus leaf lacquer of the present invention;
Four, adopt Polyurethane thickening material NLS300 to improve product stability, application property and water tolerance in the lotus leaf lacquer of the present invention;
Five, adopt the high-quality Rutile type Titanium Dioxide in the lotus leaf lacquer of the present invention, improve film stability to aging, reflected sunlight, make metope beautiful lastingly.
Embodiment
Below in conjunction with embodiment the present invention is done and to further describe:
Embodiment 1
Be equipped with 100kg lotus leaf lacquer of the present invention, its preparation of raw material by following weight content forms:
Clean tap water 17.25kg, poly carboxylic acid amine salt 0.5kg, Soxylat A 25-7 0.1kg, PH regulator 0.2kg; The mixture 0.35kg of organosilicon and MO, terepthaloyl moietie is 3kg, and the tripropylene glycol butyl ether is 3.5kg, and pure organosilicon polymer is 5kg; Rutile type Titanium Dioxide is 21kg, and talcum powder is 5kg, and benzene emulsion is 43kg; The Polyurethane thickening material is 0.35kg, and mould inhibitor is 0.6kg, and RH-893 is 0.15kg.
Feed intake in proper order by routine system lacquer craftwork, cast a kind of material again after every kind of material stirs, stir while feeding intake, viscosity is detected in the back of waiting to be uniformly dispersed can be worth waterborne lotus leaf paint of the present invention.
Embodiment 2
Be equipped with 100kg lotus leaf lacquer of the present invention, its preparation of raw material by following weight content forms:
Clean tap water 16.4kg, poly carboxylic acid amine salt 0.8kg, Soxylat A 25-7 0.15kg, PH regulator 0.1kg; The mixture 0.4kg of organosilicon and MO, terepthaloyl moietie is 3.5kg, the tripropylene glycol butyl ether is 4.0kg; Pure organosilicon polymer is 19kg for the 6kg Rutile type Titanium Dioxide, and talcum powder is 4kg, and benzene emulsion is 45kg; The Polyurethane thickening material is 0.15kg, and mould inhibitor is 0.3kg, and RH-893 is 0.2kg.
Feed intake in proper order by routine system lacquer craftwork, cast a kind of material again after every kind of material stirs, stir while feeding intake, viscosity is detected in the back of waiting to be uniformly dispersed can be worth waterborne lotus leaf paint of the present invention.
Embodiment 3
Be equipped with 100kg lotus leaf lacquer of the present invention, its preparation of raw material by following weight content forms:
Clean tap water 17.65kg, poly carboxylic acid amine salt 0.6kg, Soxylat A 25-7 0.2kg, PH regulator 0.1kg; The mixture 0.7kg of organosilicon and MO, terepthaloyl moietie is 2.5kg, and the tripropylene glycol butyl ether is 4.3kg, and pure organosilicon polymer is 8kg; Rutile type Titanium Dioxide is 18kg, and talcum powder is 7.5kg, and benzene emulsion is 40kg; The Polyurethane thickening material is 0.25kg, and mould inhibitor is 0.5kg, and RH-893 is 0.2kg.
Feed intake in proper order by routine system lacquer craftwork, cast a kind of material again after every kind of material stirs, stir while feeding intake, viscosity is detected in the back of waiting to be uniformly dispersed can be worth waterborne lotus leaf paint of the present invention.
Embodiment 4
Be equipped with 100kg lotus leaf lacquer of the present invention, its preparation of raw material by following weight content forms:
Clean tap water 10kg, poly carboxylic acid amine salt 0.5kg, Soxylat A 25-7 0.05kg, PH regulator 0.1kg; The mixture 0.4kg of organosilicon and MO, terepthaloyl moietie is 1.5kg, and the tripropylene glycol butyl ether is 1.0kg, and pure organosilicon polymer is 3kg; Rutile type Titanium Dioxide is 30kg, and talcum powder is 5kg, and benzene emulsion is 48.15kg; The Polyurethane thickening material is 0.1kg, and mould inhibitor is 0.1kg, and RH-893 is 0.1kg.
Feed intake in proper order by routine system lacquer craftwork, cast a kind of material again after every kind of material stirs, stir while feeding intake, viscosity is detected in the back of waiting to be uniformly dispersed can be worth waterborne lotus leaf paint of the present invention.
Embodiment 5
Be equipped with 100kg lotus leaf lacquer of the present invention, its preparation of raw material by following weight content forms:
Clean tap water 30kg, poly carboxylic acid amine salt 1.3kg, Soxylat A 25-7 0.4kg, PH regulator 0.3kg; The mixture 0.8kg of organosilicon and MO, terepthaloyl moietie is 4kg, and the tripropylene glycol butyl ether is 5.0kg, and pure organosilicon polymer is 10kg; Rutile type Titanium Dioxide is 10kg, and talcum powder is 10.9kg, and benzene emulsion is 25kg; The Polyurethane thickening material is 0.8kg, and mould inhibitor is 1kg, and RH-893 is 0.5kg.
Feed intake in proper order by routine system lacquer craftwork, cast a kind of material again after every kind of material stirs, stir while feeding intake, viscosity is detected in the back of waiting to be uniformly dispersed can be worth waterborne lotus leaf paint of the present invention.
Embodiment 6
Be equipped with 100kg lotus leaf lacquer of the present invention, its preparation of raw material by following weight content forms:
Clean tap water 20kg, poly carboxylic acid amine salt 1.0kg, Soxylat A 25-7 0.2kg, PH regulator 0.2kg; The mixture 0.6kg of organosilicon and MO, terepthaloyl moietie is 3kg, and the tripropylene glycol butyl ether is 3.0kg, and pure organosilicon polymer is 20kg; Rutile type Titanium Dioxide is 10kg, and talcum powder is 8kg, and benzene emulsion is 33kg; The Polyurethane thickening material is 0.5kg, and mould inhibitor is 0.3kg, and RH-893 is 0.2kg.
Feed intake in proper order by routine system lacquer craftwork, cast a kind of material again after every kind of material stirs, stir while feeding intake, viscosity is detected in the back of waiting to be uniformly dispersed can be worth waterborne lotus leaf paint of the present invention.
The raw material that the present invention adopts is easy to get, be a kind of simple, good, water-fast alkali resistant of recoatability of constructing, the anti-algae of mildew-resistant, strong adhesion, good weatherability, anti-ink, superpower hydrophobicity and recoatability perfect adaptation and have a lotus leaf effect environmental protection wall surface paint.
Claims (1)
1. a waterborne lotus leaf paint is characterized in that being made up of following materials in weight percentage: clean tap water 17.25%, poly carboxylic acid amine salt 0.5%; Soxylat A 25-7 0.1%, PH regulator 0.2%, the mixture 0.35% of organosilicon and MO; Terepthaloyl moietie is 3%, and the tripropylene glycol butyl ether is 3.5%, and pure organosilicon polymer is 5%; Rutile type Titanium Dioxide is 21%, and talcum powder is 5%, and benzene emulsion is 43%; The Polyurethane thickening material is 0.35%, and mould inhibitor is 0.6%, and RH-893 is 0.15%.