CN106947354A - Aqueous acrylic modified two component epoxy paint for priming paint and top lacquer and preparation method thereof - Google Patents
Aqueous acrylic modified two component epoxy paint for priming paint and top lacquer and preparation method thereof Download PDFInfo
- Publication number
- CN106947354A CN106947354A CN201710139202.8A CN201710139202A CN106947354A CN 106947354 A CN106947354 A CN 106947354A CN 201710139202 A CN201710139202 A CN 201710139202A CN 106947354 A CN106947354 A CN 106947354A
- Authority
- CN
- China
- Prior art keywords
- component
- acrylic modified
- paint
- aqueous acrylic
- top lacquer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses aqueous acrylic modified two component epoxy paint for priming paint and top lacquer and preparation method thereof, a kind of aqueous acrylic modified two component epoxy paint for priming paint and top lacquer of the present invention, the aqueous acrylic modified two component epoxy paint for priming paint and top lacquer is counted by weight to be made up of component A and B component：The component A is made up of following component：Aqueous acrylic modified epoxy resin dispersion, environmentally friendly solvent, wetting agent, dispersant, ultra-violet absorber, thickener, anti-flash rusting agent, titanium dioxide, rust resisting pigment, barium sulfate, aerosil, carbon black, deionized water；B component is aqueous fatty amines curing agent；The parts by weight of the component A and B component are 100：20~30.Preparation technology of the present invention is simple, and the VOC content that product is made is low, and pollution environment is few, and anti-corrosive properties and weatherability have both.
Description
Technical field
The present invention relates to metal protection field, more particularly to aqueous acrylic modified two component epoxy paint for priming paint and top lacquer and its
Preparation method.
Background technology
As people are to environment and the pay attention to day by day of health, water paint is increasingly widely applied, tradition
The pollution that the volatile organic content (VOC) that solvent based coating is discharged in the production and use process is produced, turns into row at present
City primary pollution source after automobile, water paint can reduce VOC as one of substitute of traditional solvent-borne coating
Discharge, the generation of waste, reduce contact of the workman to poisonous releaser.It is reported that, during " 13 ", the whole nation will be strengthened to waving
The control of hair property organic compound (VOC) total amount, collaboration emission reduction is carried out to nitrogen oxides and VOC.
Water-base epoxy paint has preferable antiseptic property, and adhesive force is good, and salt spray resistance is outstanding, is widely used in metal and prevents
In rotten priming paint, but have the disadvantage that ultraviolet resistance is poor, be not readily used for outdoor finish paint, acrylic paint is by stronger dicoration, weatherability, but
Have the disadvantage that antiseptic property is poor, so conventional do finish paint, now universal collocation is that priming paint is made of epoxy, and acrylic acid does finish paint, both
With anti-corrosive properties, good weatherability can be accomplished again, but there was only the system of single coating to some, both coating can not all expire
Sufficient performance requirement, so the single coating coating of a aqueous acrylic modified two component epoxy bottom surface unification is developed, with very
Important realistic meaning.
At present, a kind of few aqueous acrylic modified two component epoxy paint for priming paint and top lacquer of pollution environment and its preparation side are lacked
Method.
The content of the invention
To solve the above problems, it is an object of the invention to provide be to overcome the shortcoming of prior art dirty there is provided one kind
Contaminate few aqueous acrylic modified two component epoxy paint for priming paint and top lacquer of environment and preparation method thereof.
To realize above-mentioned technical purpose, the technical solution adopted by the present invention is as follows：A kind of water soluble acrylic acid of the present invention changes
Property two component epoxy paint for priming paint and top lacquer, the aqueous acrylic modified two component epoxy paint for priming paint and top lacquer is counted by A by weight
Component and B component composition：
The component A is made up of following component：
Base-material：
Aqueous acrylic modified 45~55 parts of epoxy resin dispersion,
Auxiliary agent：
Color stuffing：
B component is aqueous fatty amines curing agent；
The parts by weight of the component A and B component are 100：20~30.
Further, base-material：
Aqueous acrylic modified 50 parts of epoxy resin dispersion,
Auxiliary agent：
Color stuffing：
The parts by weight of the component A and B component are 100：20.
Above-mentioned raw materials prepare aqueous acrylic modified two component epoxy paint for priming paint and top lacquer, salt fog resistance more than 480 hours,
Resistance to artificial accelerated aging (Q~SUN) 500 hours, hardness H, adhesion 1 grade.
Further, described environmentally friendly solvent is that higher boiling environmentally friendly solvent is dipropylene；Described wetting agent
For the high Twin 4100 of enlightening；Described dispersant is the BYK194 of Bi Ke chemistry.
Further, described anti-flash rusting agent is U.S. RAYBO 60；Described ultra-violet absorber is that Taiwan is forever photochemical
AQ1.
Further, described thickener is that polyurethanes association thickener Asia is happy along RM-12W；Described titanium dioxide
For Du Pont titanium dioxide Ti-Pure R706；Described rust resisting pigment is the APW-2 in Guangxi.
The preparation method of aqueous acrylic modified two component epoxy paint for priming paint and top lacquer of the present invention, including following step
Suddenly：
(1) each component is accurately weighed by described raw material proportioning, the aqueous acrylic modified epoxy resin, environmental protection is molten
Agent, wetting agent, dispersant are added sequentially to get the raw materials ready in pot, are started with 500~800r/min speed and stirred；
(2) after stirring, the color stuffing is added in pot of getting the raw materials ready, at a high speed scattered 20~30min, forms uniform paint
Slurry；
(3) the uniform mill base is ground, component A is made；
(4) component A and B component made from step (3) are mixed, and used in 6 hours in proportion when in use
It is complete, aqueous acrylic modified two component epoxy paint for priming paint and top lacquer is made.
Further, in step (2), the color stuffing is by titanium dioxide, rust resisting pigment, carbon black, barium sulfate and gas phase two
Silica is constituted.
Further, in step (3), the mill base is ground to fineness less than or equal to 30 microns.
Beneficial effect：Preparation technology of the present invention is simple, and the VOC content that product is made is low, and pollution environment is few, anti-corrosive properties and resistance to
Time property has both.
Compared with prior art, the invention has the advantages that：
(1) present invention is incorporated into acrylic ester monomer in epoxy resin using acrylic acid and the crosslinking technology of epoxy,
Have both anti-corrosive properties and weatherability, suitable for single coating bottom surface unification corrosion resistant coating, unification excellent combination property in bottom surface solves single apply
The problem of layer sealing wax can not take into account anti-corrosive properties and weatherability.
(2) present invention is helped to catch ultraviolet, is extended coating using efficient novel aqueous special ultra-violet absorber
Service life；Using environment-friendly antirust pigment, antiseptic property is high, safety non-toxic.Salt fog resistance and ageing properties are substantially better than similar
Product.VOC content is extremely low, ＜ 50g/L, while capable of purifying air.
Embodiment
To make the object, technical solutions and advantages of the present invention clearer, embodiments of the present invention will be made below into
One step it is described in detail.
Embodiment 1
A kind of aqueous acrylic modified two component epoxy paint for priming paint and top lacquer of the present invention, the aqueous acrylic modified pair of group
Part epoxy paint for priming paint and top lacquer is counted by weight to be made up of component A and B component：
The component A is made up of following component：
Base-material：
Aqueous acrylic modified 52 parts of epoxy resin dispersion,
Auxiliary agent：
Color stuffing：
B component is aqueous fatty amines curing agent；The parts by weight of the component A and B component are 100：30.
30 parts of aqueous fatty amines curing agent；Aqueous acrylic modified two component epoxy bottom surface unification prepared by above-mentioned raw materials
Paint, salt fog resistance was more than 480 hours, resistance to artificial accelerated aging (Q~SUN) 500 hours, hardness H, adhesion 1 grade.
Described environmentally friendly solvent is that higher boiling environmentally friendly solvent is dipropylene；Described wetting agent is the high Twin of enlightening
4100；Described dispersant is BYK194.
Described anti-flash rusting agent is U.S. RAYBO 60；Described ultra-violet absorber is Taiwan photochemical AQ1 forever.
Described thickener is that polyurethanes association thickener Asia is happy along RM~12W；Described pigment be Du Pont Ti~
Pure R~706；Described rust resisting pigment is APW~2 in Guangxi.
The preparation method of aqueous acrylic modified two component epoxy paint for priming paint and top lacquer of the present invention, including following step
Suddenly：
(1) each component is accurately weighed by described raw material proportioning, the aqueous acrylic modified epoxy resin, environmental protection is molten
Agent, wetting agent, dispersant are added sequentially to get the raw materials ready in pot, are started with 700r/min speed and stirred；
(2) after stirring, the color stuffing is added in pot of getting the raw materials ready, scattered 25min, forms uniform mill base at a high speed；Institute
Color stuffing is stated to be made up of titanium dioxide, rust resisting pigment, carbon black, barium sulfate and aerosil；
(3) the uniform mill base is ground, component A is made；The mill base is ground to fineness less than or equal to 30 microns.
(4) component A and B component made from step (3) are mixed, and used in 6 hours in proportion when in use
It is complete, aqueous acrylic modified two component epoxy paint for priming paint and top lacquer is made.
Embodiment 2
The difference of embodiment 2 and embodiment 1 is：Raw material ratio slightly has difference, is all up performance requirement.
Claims (8)
1. a kind of aqueous acrylic modified two component epoxy paint for priming paint and top lacquer, it is characterised in that：It is described aqueous acrylic modified double
Component epoxy paint for priming paint and top lacquer is counted by weight to be made up of component A and B component：
The component A is made up of following component：
Base-material：
Aqueous acrylic modified 45~55 parts of epoxy resin dispersion,
Auxiliary agent：
Color stuffing：
B component is aqueous fatty amines curing agent；
The parts by weight of the component A and B component are 100：20~30.
2. aqueous acrylic modified two component epoxy paint for priming paint and top lacquer according to claim 1, it is characterised in that：
Base-material：
Aqueous acrylic modified 50 parts of epoxy resin dispersion,
Auxiliary agent：
Color stuffing：
The parts by weight of the component A and B component are 100：20.
3. the preparation method of aqueous acrylic modified two component epoxy paint for priming paint and top lacquer according to claim 1, its feature
It is：Described environmentally friendly solvent is that higher boiling environmentally friendly solvent is dipropylene；Described wetting agent is the high Twin4100 of enlightening；
Described dispersant is the BYK194 of Bi Ke chemistry.
4. aqueous acrylic modified two component epoxy paint for priming paint and top lacquer according to claim 1, it is characterised in that：Described
Anti- flash rusting agent is U.S. RAYBO 60；Described ultra-violet absorber is Taiwan photochemical AQ1 forever.
5. aqueous acrylic modified two component epoxy paint for priming paint and top lacquer according to claim 1, it is characterised in that：Described
Thickener is that polyurethanes association thickener Asia is happy along RM-12W；Described titanium dioxide is Du Pont titanium dioxide Ti-Pure
R706；Described rust resisting pigment is the APW-2 in Guangxi.
6. the preparation method of the aqueous acrylic modified two component epoxy paint for priming paint and top lacquer described in any one of claim 1 to 5, its
It is characterised by comprising the following steps：
(1) raw material proportioning as described in claim 1 accurately weighs each component, by the aqueous acrylic modified epoxy resin,
Environmentally friendly solvent, wetting agent, dispersant are added sequentially to get the raw materials ready in pot, are started with 500~800r/min speed and stirred；
(2) after stirring, the color stuffing is added in pot of getting the raw materials ready, scattered 20~30min, forms uniform mill base at a high speed；
(3) the uniform mill base is ground, component A is made；
(4) component A and B component made from step (3) are mixed in proportion when in use, and were finished in 6 hours, made
Obtain aqueous acrylic modified two component epoxy paint for priming paint and top lacquer.
7. the preparation method of aqueous acrylic modified two component epoxy paint for priming paint and top lacquer according to claim 6, its feature
It is：In step (2), the color stuffing is made up of titanium dioxide, rust resisting pigment, carbon black, barium sulfate and aerosil.
8. the preparation method of aqueous acrylic modified two component epoxy paint for priming paint and top lacquer according to claim 6, its feature
It is：In step (3), the mill base is ground to fineness less than or equal to 30 microns.