CN107244878A - High scrubbing resistance diatom ooze and preparation method thereof - Google Patents
High scrubbing resistance diatom ooze and preparation method thereof Download PDFInfo
- Publication number
- CN107244878A CN107244878A CN201710369841.3A CN201710369841A CN107244878A CN 107244878 A CN107244878 A CN 107244878A CN 201710369841 A CN201710369841 A CN 201710369841A CN 107244878 A CN107244878 A CN 107244878A
- Authority
- CN
- China
- Prior art keywords
- parts
- diatom ooze
- scrubbing resistance
- high scrubbing
- diatomite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to high scrubbing resistance diatom ooze and preparation method thereof, the high scrubbing resistance diatom ooze includes the raw material of following parts by weight：Wash 0.3 part~0.8 part of 10 parts~20 parts of diatomite, 10 parts~15 parts of calcined diatomite, 2 parts~5 parts of sepiolite, 10 parts~15 parts of nanometer calcium, 20 parts~30 parts of silica flour, 2 parts~3 parts of re-dispersible glue powder, 1.5 parts~3 parts of photocatalyst, 0.1 part~0.2 part of cellulose, 0.1 part~0.15 part of dispersant, 0.1 part~0.2 part of defoamer and mould inhibitor.The high scrubbing resistance diatom ooze of the present invention, utilizes the local behavior principle of water so that film synthesizes a kind of water insoluble CaSiO3, painting face had not only been there is environment-friendly function and with water-fast specific function, its preparation method is simply, easy construction, environmental protection, scrub performance be strong, technological effect is good.
Description
Technical field
The present invention relates to a kind of high scrubbing resistance diatom ooze and preparation method thereof.
Background technology
Diatom ooze is a kind of superior dry powder paint for inner walls of environmental-protecting performance, with humidity absorption and release regulation room temperature, decomposing formaldehyde,
Purify the function of air.But the problem of general diatom ooze also has many troubling, such as：Insufficient strength, easily break, difficulty is repaiied
Benefit, poor water resistance, painting face can not be cleaned after making dirty, service life is not ideal enough.
The content of the invention
It is an object of the present invention to propose a kind of high scrubbing resistance diatom ooze.
The high scrubbing resistance diatom ooze of the present invention, includes the raw material of following parts by weight：Wash 10 parts~20 parts of diatomite, forge
Burn 10 parts~15 parts of diatomite, it is 2 parts~5 parts of sepiolite, 10 parts~15 parts of nanometer calcium, 20 parts~30 parts of silica flour, redispersible
2 parts~3 parts of rubber powder, 1.5 parts~3 parts of photocatalyst, 0.1 part~0.2 part of cellulose, 0.1 part~0.15 part of dispersant, defoamer
0.1 part~0.2 part and 0.3 part~0.8 part of mould inhibitor.
The high scrubbing resistance diatom ooze of the present invention, utilizes the local behavior principle of water so that film synthesis is a kind of water insoluble
CaSiO3, painting face had not only been there is environment-friendly function and with water-fast specific function, its preparation method simply, it is easy construction, green
Colour circle is protected, scrub performance is strong, technological effect is good.
In addition, high scrubbing resistance diatom ooze according to the above embodiment of the present invention, can also have technology additional as follows special
Levy：
As the preferred embodiment of the present invention, described high scrubbing resistance diatom ooze includes the raw material of following parts by weight：
Wash 10 parts of diatomite, 15 parts of calcined diatomite, 2 parts of sepiolite, 15 parts of nanometer calcium, 20 parts of silica flour, re-dispersible glue powder 3
Part, 1.5 parts of photocatalyst, 0.2 part of cellulose, 0.1 part of dispersant, 0.2 part of defoamer and 0.3 part of mould inhibitor.
As the preferred embodiment of the present invention, described high scrubbing resistance diatom ooze includes the raw material of following parts by weight：
Wash 20 parts of diatomite, 10 parts of calcined diatomite, 5 parts of sepiolite, 10 parts of nanometer calcium, 30 parts of silica flour, re-dispersible glue powder 2
Part, 3 parts of photocatalyst, 0.1 part of cellulose, 0.15 part of dispersant, 0.1 part of defoamer and 0.8 part of mould inhibitor.
As the preferred embodiment of the present invention, described high scrubbing resistance diatom ooze includes the raw material of following parts by weight：
Wash 15 parts of diatomite, 12 parts of calcined diatomite, 3 parts of sepiolite, 12 parts of nanometer calcium, 25 parts of silica flour, re-dispersible glue powder 2
Part, 2 parts of photocatalyst, 0.1 part of cellulose, 0.15 part of dispersant, 0.1 part of defoamer and 0.5 part of mould inhibitor.
Further, the dispersant at least includes sodium tripolyphosphate, calgon, sodium pyrophosphate, triethyl group hexyl
Phosphoric acid, lauryl sodium sulfate, methyl anyl alcohol, cellulose derivative, polyacrylamide, guar gum and fatty acid polyethylene glycol ester
In one kind.
Further, the defoamer at least includes silicone emulsion, polyoxyethylene, polyoxypropylene, pentaerythrite ether, polyoxy
One kind in propyl alcohol amidogen ether, polypropylene glycerol aether and dimethyl silicone polymer.
Further, the mould inhibitor is Kathon.
It is another object of the present invention to the preparation method for proposing described high scrubbing resistance diatom ooze.
The preparation method of described high scrubbing resistance diatom ooze, comprises the following steps：The raw material is added into dry powder blender
Middle stirring 20min~30min, obtains high scrubbing resistance diatom ooze.
Further, when being stirred operation, the rotating speed of the dry powder blender is 300r/min~3000r/min.
The additional aspect and advantage of the present invention will be set forth in part in the description, and will partly become from the following description
Obtain substantially, or recognized by the practice of the present invention.
Embodiment
Embodiments of the invention are described below in detail, the embodiment is exemplary, it is intended to for explaining the present invention, and
It is not considered as limiting the invention.
Diatomaceous specific source in the embodiment of the present invention is as follows：
Diatom ooze is calcined purchased from the first clear and coherent receipts limited investment responsible company in Beijing, model：TL-301#；
Diatomite is washed purchased from Bei Feng diatomite Co., Ltd, model near a river：W-8023.
Embodiment 1
Embodiment 1 proposes a kind of high scrubbing resistance diatom ooze, includes the raw material of following parts by weight：Wash diatomite 10
Part, 15 parts of calcined diatomite, 2 parts of sepiolite, 15 parts of nanometer calcium, 20 parts of silica flour, 3 parts of re-dispersible glue powder, photocatalyst 1.5
Part, 0.2 part of cellulose, 0.1 part of sodium tripolyphosphate, 0.2 part of polypropylene glycerol aether and Kathon
0.3 part.
The preparation method of the high scrubbing resistance diatom ooze of embodiment 1, comprises the following steps：The raw material is added into dry powder blend
20min is stirred in machine, high scrubbing resistance diatom ooze is obtained；Wherein, the rotating speed of the dry powder blender is 3000r/min.
Embodiment 2
Embodiment 2 proposes a kind of high scrubbing resistance diatom ooze, includes the raw material of following parts by weight：Wash diatomite 20
Part, 10 parts of calcined diatomite, 5 parts of sepiolite, 10 parts of nanometer calcium, 30 parts of silica flour, 2 parts of re-dispersible glue powder, 3 parts of photocatalyst,
0.1 part of cellulose, 0.15 part of calgon, 0.1 part of polyoxy propyl alcohol amidogen ether and Kathon 0.8
Part.
The preparation method of the high scrubbing resistance diatom ooze of embodiment 2, comprises the following steps：The raw material is added into dry powder blend
30min is stirred in machine, high scrubbing resistance diatom ooze is obtained；Wherein, the rotating speed of the dry powder blender is 300r/min.
Embodiment 3
Embodiment 3 proposes a kind of high scrubbing resistance diatom ooze, includes the raw material of following parts by weight：Wash diatomite 15
Part, 12 parts of calcined diatomite, 3 parts of sepiolite, 12 parts of nanometer calcium, 25 parts of silica flour, 2 parts of re-dispersible glue powder, 2 parts of photocatalyst,
0.5 part of 0.1 part of cellulose, 0.15 part of sodium pyrophosphate, 0.1 part of pentaerythrite ether and Kathon.
The preparation method of the high scrubbing resistance diatom ooze of embodiment 3, comprises the following steps：The raw material is added into dry powder blend
25min is stirred in machine, high scrubbing resistance diatom ooze is obtained；Wherein, the rotating speed of the dry powder blender is 2000r/min.
Embodiment 4
Embodiment 4 proposes a kind of high scrubbing resistance diatom ooze, includes the raw material of following parts by weight：Wash diatomite 10
Part, 15 parts of calcined diatomite, 2 parts of sepiolite, 15 parts of nanometer calcium, 20 parts of silica flour, 3 parts of re-dispersible glue powder, photocatalyst 1.5
Part, 0.2 part of cellulose, 0.1 part of triethyl group hexyl phosphoric acid, 0.2 part of polyoxypropylene and Kathon 0.3
Part.
The preparation method of the high scrubbing resistance diatom ooze of embodiment 4, comprises the following steps：The raw material is added into dry powder blend
24min is stirred in machine, high scrubbing resistance diatom ooze is obtained；Wherein, the rotating speed of the dry powder blender is 2700r/min.
Embodiment 5
Embodiment 5 proposes a kind of high scrubbing resistance diatom ooze, includes the raw material of following parts by weight：Wash diatomite 20
Part, 10 parts of calcined diatomite, 5 parts of sepiolite, 10 parts of nanometer calcium, 30 parts of silica flour, 2 parts of re-dispersible glue powder, 3 parts of photocatalyst,
0.1 part of cellulose, 0.15 part of lauryl sodium sulfate, 0.1 part of polyoxyethylene and Kathon 0.8
Part.
The preparation method of the high scrubbing resistance diatom ooze of embodiment 5, comprises the following steps：The raw material is added into dry powder blend
33min is stirred in machine, high scrubbing resistance diatom ooze is obtained；Wherein, the rotating speed of the dry powder blender is 1500r/min.
Embodiment 6
Embodiment 6 proposes a kind of high scrubbing resistance diatom ooze, includes the raw material of following parts by weight：Wash diatomite 15
Part, 12 parts of calcined diatomite, 3 parts of sepiolite, 12 parts of nanometer calcium, 25 parts of silica flour, 2 parts of re-dispersible glue powder, 2 parts of photocatalyst,
0.5 part of 0.1 part of cellulose, 0.15 part of methyl anyl alcohol, 0.1 part of silicone emulsion and Kathon.
The preparation method of the high scrubbing resistance diatom ooze of embodiment 6, comprises the following steps：The raw material is added into dry powder blend
27min is stirred in machine, high scrubbing resistance diatom ooze is obtained；Wherein, the rotating speed of the dry powder blender is 2500r/min.
The high scrubbing resistance diatom ooze of the present invention, utilizes the local behavior principle of water so that film synthesis is a kind of water insoluble
CaSiO3, painting face had not only been there is environment-friendly function and with water-fast specific function, its preparation method simply, it is easy construction, green
Colour circle is protected, scrub performance is strong, technological effect is good.
In the description of this specification, reference term " one embodiment ", " some embodiments ", " example ", " specifically show
The description of example " or " some examples " etc. means to combine specific features, structure, material or the spy that the embodiment or example are described
Point is contained at least one embodiment of the present invention or example.In this manual, to the schematic representation of above-mentioned term not
Identical embodiment or example must be directed to.Moreover, specific features, structure, material or the feature of description can be with office
Combined in an appropriate manner in one or more embodiments or example.In addition, in the case of not conflicting, the skill of this area
Art personnel can be tied the not be the same as Example or the feature of example and non-be the same as Example or example described in this specification
Close and combine.
Although embodiments of the invention have been shown and described above, it is to be understood that above-described embodiment is example
Property, it is impossible to limitation of the present invention is interpreted as, one of ordinary skill in the art within the scope of the invention can be to above-mentioned
Embodiment is changed, changed, replacing and modification.
Claims (9)
1. a kind of high scrubbing resistance diatom ooze, it is characterised in that include the raw material of following parts by weight：Wash diatomite 10 parts~20
Part, 10 parts~15 parts of calcined diatomite, 2 parts~5 parts of sepiolite, 10 parts~15 parts of nanometer calcium, 20 parts~30 parts of silica flour, can be again
Scattered 2 parts~3 parts of rubber powder, 1.5 parts~3 parts of photocatalyst, 0.1 part~0.2 part of cellulose, 0.1 part~0.15 part of dispersant, froth breaking
0.3 part~0.8 part of 0.1 part~0.2 part of agent and mould inhibitor.
2. high scrubbing resistance diatom ooze according to claim 1, it is characterised in that include the raw material of following parts by weight：Water
Wash 10 parts of diatomite, 15 parts of calcined diatomite, 2 parts of sepiolite, 15 parts of nanometer calcium, 20 parts of silica flour, 3 parts of re-dispersible glue powder,
0.3 part of 1.5 parts of photocatalyst, 0.2 part of cellulose, 0.1 part of dispersant, 0.2 part of defoamer and mould inhibitor.
3. high scrubbing resistance diatom ooze according to claim 1, it is characterised in that include the raw material of following parts by weight：Water
Wash 20 parts of diatomite, 10 parts of calcined diatomite, 5 parts of sepiolite, 10 parts of nanometer calcium, 30 parts of silica flour, 2 parts of re-dispersible glue powder,
0.8 part of 3 parts of photocatalyst, 0.1 part of cellulose, 0.15 part of dispersant, 0.1 part of defoamer and mould inhibitor.
4. high scrubbing resistance diatom ooze according to claim 1, it is characterised in that include the raw material of following parts by weight：Water
Wash 15 parts of diatomite, 12 parts of calcined diatomite, 3 parts of sepiolite, 12 parts of nanometer calcium, 25 parts of silica flour, 2 parts of re-dispersible glue powder,
0.5 part of 2 parts of photocatalyst, 0.1 part of cellulose, 0.15 part of dispersant, 0.1 part of defoamer and mould inhibitor.
5. the high scrubbing resistance diatom ooze according to claim any one of 1-4, it is characterised in that the dispersant at least includes
Sodium tripolyphosphate, calgon, sodium pyrophosphate, triethyl group hexyl phosphoric acid, lauryl sodium sulfate, methyl anyl alcohol, cellulose
One kind in derivative, polyacrylamide, guar gum and fatty acid polyethylene glycol ester.
6. the high scrubbing resistance diatom ooze according to claim any one of 1-4, it is characterised in that the defoamer at least includes
Silicone emulsion, polyoxyethylene, polyoxypropylene, pentaerythrite ether, polyoxy propyl alcohol amidogen ether, polypropylene glycerol aether and poly dimethyl silicon
One kind in oxygen alkane.
7. the high scrubbing resistance diatom ooze according to claim any one of 1-4, it is characterised in that the mould inhibitor is that 2- is just pungent
Base -4- isothiazoline -3- ketone.
8. the preparation method of the high scrubbing resistance diatom ooze described in claim any one of 1-7, it is characterised in that including following step
Suddenly：The raw material is added 20min~30min is stirred in dry powder blender, obtain high scrubbing resistance diatom ooze.
9. the preparation method of high scrubbing resistance diatom ooze according to claim 8, it is characterised in that be stirred operation
When, the rotating speed of the dry powder blender is 300r/min~3000r/min.