CN105174810A - Scrub-resistant diatom ooze paint - Google Patents
Scrub-resistant diatom ooze paint Download PDFInfo
- Publication number
- CN105174810A CN105174810A CN201510693666.4A CN201510693666A CN105174810A CN 105174810 A CN105174810 A CN 105174810A CN 201510693666 A CN201510693666 A CN 201510693666A CN 105174810 A CN105174810 A CN 105174810A
- Authority
- CN
- China
- Prior art keywords
- calcium carbonate
- parts
- diatomite
- diatom ooze
- silicon
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a scrub-resistant diatom ooze paint which comprises the following components in parts by mass: 50-80 parts of diatomite, 30-60 parts of silicon styrene emulsion, 15-25 parts of elastic emulsion, 25-30 parts of mildew preventive, 10-20 parts of calcium carbonate, 20-25 parts of bactericide, 5-10 parts of defoaming agent, 8-10 parts of wetting agent and 5-16 composite carbon silicon. The original composite carbon silicon technique is utilized to ensure that a tough protective layer can be formed on the paint film surface. The scrub-resistant diatom ooze paint has the new function of keeping brightness after the wall surface is repeatedly scrubbed, can keep the wall surface air-permeable without mildewing, and is capable of effectively removing bacteria, absorbing harmful gas and purifying air.
Description
Technical field
The present invention relates to a kind of technical field of paint preparation, specifically, the present invention relates to a kind of scrubbing resistance diatom ooze coating.
Background technology
Interior wall coating is exactly the emulsion paint generally fitted up.Namely emulsion paint is emulsion coating, according to the difference of base material, is divided into polyvinyl acetate emulsion and the large class of ACRYLIC EMULSION two.Emulsion paint is thinner with diatomite, be a kind of easy construction, safety, resistance to diatomite wash, good permeability coating, it can mix different color and lusters according to different scheme of colo(u)r.Kind: water-based inner wall paint, oiliness interior wall paint, dry powder type interior wall paint, belongs to diatom soil nature coating, and primarily of water, emulsion, pigment, filler, additive five kinds of compositions are formed.And popularizing along with personalized theory, and the formation of novel harmonious society, design a kind of washable interior wall coating and be very important.
Summary of the invention
For above shortcomings in prior art, technical problem to be solved by this invention is to provide the good scrubbing resistance diatom ooze coating of a kind of maintenance effect.
The technical solution adopted for the present invention to solve the technical problems is: provide a kind of scrubbing resistance diatom ooze coating, comprise diatomite, silicon benzene emulsion, elastic emulsion, mould inhibitor, calcium carbonate, sterilant, defoamer, wetting agent, composite carbon silicon, the mass fraction of each component is: diatomite 50-80, silicon benzene emulsion 30-60, elastic emulsion 15-25, mould inhibitor 25-30, calcium carbonate 10-20, sterilant 20-25, defoamer 5-10, wetting agent 8-10, composite carbon silicon 5-16.
As preferably, the mass fraction of each component of described scrubbing resistance diatom ooze coating is: diatomite 80, silicon benzene emulsion 50, elastic emulsion 20, mould inhibitor 25, calcium carbonate 18, sterilant 25, defoamer 7, wetting agent 8, composite carbon silicon 16.
As preferably, the granularity of described calcium carbonate is 1220-1500 order, further preferred 1335 orders.
As preferably, the iron oxide content in described diatomite is 1 ~ 1.5%, and alumina content is 3 ~ 6%.
Concrete preparation process:
1., silicon benzene emulsion, elastic emulsion and diatomite are mixed obtain mixture A;
2., then calcium carbonate and deionization diatomite mix and blend are prepared the calcium carbonate tripolite solution that mass concentration is 10%;
3., then in reactor, add defoamer, wetting agent, composite carbon silicon and mould inhibitor successively and stir 30min at 50 DEG C of temperature, obtain mixture B;
4., then mixture A and calcium carbonate tripolite solution are joined in mixture B, mix, stir 55min, obtain mixture C;
5., finally sterilant is joined in mixture C, at 60 DEG C, insulation reaction 0.5h; Stop heating, be cooled to room temperature and get final product.
The present invention creates composite carbon silicon technology; guarantee that coating surface can form tough and tensile protective layer, this invention possesses scouring metope repeatedly and still keeps beautiful as while new function, and metope can also be kept ventilative not mouldy; effectively degerming, absorption obnoxious flavour, purifies air.
Embodiment
A kind of scrubbing resistance diatom ooze coating provided by the invention, comprise diatomite, silicon benzene emulsion, elastic emulsion, mould inhibitor, calcium carbonate, sterilant, defoamer, wetting agent, composite carbon silicon, the mass fraction of each component is: diatomite 50-80, silicon benzene emulsion 30-60, elastic emulsion 15-25, mould inhibitor 25-30, calcium carbonate 10-20, sterilant 20-25, defoamer 5-10, wetting agent 8-10, composite carbon silicon 5-16.
As preferably, the mass fraction of each component of described scrubbing resistance diatom ooze coating is: diatomite 80, silicon benzene emulsion 50, elastic emulsion 20, mould inhibitor 25, calcium carbonate 18, sterilant 25, defoamer 7, wetting agent 8, composite carbon silicon 16.
As preferably, the granularity of described calcium carbonate is 1220-1500 order, further preferred 1335 orders.
As preferably, the iron oxide content in described diatomite is 1 ~ 1.5%, and alumina content is 3 ~ 6%.
Concrete preparation process:
1., silicon benzene emulsion, elastic emulsion and diatomite are mixed obtain mixture A;
2., then calcium carbonate and deionization diatomite mix and blend are prepared the calcium carbonate tripolite solution that mass concentration is 10%;
3., then in reactor, add defoamer, wetting agent, composite carbon silicon and mould inhibitor successively and stir 30min at 50 DEG C of temperature, obtain mixture B;
4., then mixture A and calcium carbonate tripolite solution are joined in mixture B, mix, stir 55min, obtain mixture C;
5., finally sterilant is joined in mixture C, at 60 DEG C, insulation reaction 0.5h; Stop heating, be cooled to room temperature and get final product.
Claims (5)
1. a scrubbing resistance diatom ooze coating, it is characterized in that: comprise diatomite, silicon benzene emulsion, elastic emulsion, mould inhibitor, calcium carbonate, sterilant, defoamer, wetting agent, composite carbon silicon, the mass fraction of each component is: diatomite 50-80, silicon benzene emulsion 30-60, elastic emulsion 15-25, mould inhibitor 25-30, calcium carbonate 10-20, sterilant 20-25, defoamer 5-10, wetting agent 8-10, composite carbon silicon 5-16.
2. scrubbing resistance diatom ooze coating according to claim 1, is characterized in that: the mass fraction of each component of described scrubbing resistance diatom ooze coating is: diatomite 80, silicon benzene emulsion 50, elastic emulsion 20, mould inhibitor 25, calcium carbonate 18, sterilant 25, defoamer 7, wetting agent 8, composite carbon silicon 16.
3. scrubbing resistance diatom ooze coating according to claim 2, is characterized in that: the granularity of described calcium carbonate is 1220-1500 order, further preferred 1335 orders.
4. scrubbing resistance diatom ooze coating according to claim 1, is characterized in that: the iron oxide content in described diatomite is 1 ~ 1.5%, and alumina content is 3 ~ 6%.
5. concrete preparation process:
1., silicon benzene emulsion, elastic emulsion and deionization diatomite are mixed obtain mixture A;
2., then calcium carbonate and diatomite mix and blend are prepared the calcium carbonate tripolite solution that mass concentration is 10%;
3., then in reactor, add defoamer, wetting agent, composite carbon silicon and mould inhibitor successively and stir 30min at 50 DEG C of temperature, obtain mixture B;
4., then mixture A and calcium carbonate tripolite solution are joined in mixture B, mix, stir 55min, obtain mixture C;
5., finally sterilant is joined in mixture C, at 60 DEG C, insulation reaction 0.5h; Stop heating, be cooled to room temperature and get final product.