CN104790062A - 一种丝素蛋白与聚对苯二甲酸丁二醇酯的共混纤维及其制备方法 - Google Patents

一种丝素蛋白与聚对苯二甲酸丁二醇酯的共混纤维及其制备方法 Download PDF

Info

Publication number
CN104790062A
CN104790062A CN201510197952.1A CN201510197952A CN104790062A CN 104790062 A CN104790062 A CN 104790062A CN 201510197952 A CN201510197952 A CN 201510197952A CN 104790062 A CN104790062 A CN 104790062A
Authority
CN
China
Prior art keywords
polybutylene terephthalate
pbt
fibroin albumen
blended fiber
fiber
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510197952.1A
Other languages
English (en)
Inventor
吴惠英
周燕
刘尚楠
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Suzhou Institute of Trade and Commerce
Original Assignee
Suzhou Institute of Trade and Commerce
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Suzhou Institute of Trade and Commerce filed Critical Suzhou Institute of Trade and Commerce
Priority to CN201510197952.1A priority Critical patent/CN104790062A/zh
Publication of CN104790062A publication Critical patent/CN104790062A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种丝素蛋白与聚对苯二甲酸丁二醇酯的共混纤维，所述丝素蛋白与聚对苯二甲酸丁二醇酯的共混纤维包括按质量份数混合的以下组分：1.0％～5.0％的丝素蛋白纳米粉体和95.0％～99.0％的聚对苯二甲酸丁二醇酯。本发明还公开了丝素蛋白与聚对苯二甲酸丁二醇酯的共混纤维的制备方法。本发明制备的丝素蛋白与聚对苯二甲酸丁二醇酯的共混纤维中引入丝素蛋白，芯吸高度随时间变化明显变大，吸湿性较强，采用本发明提供的丝素蛋白与聚对苯二甲酸丁二醇酯的共混纤维制备的衣物吸湿排汗功能强，穿着较舒适；丝素蛋白富含18种氨基酸，对人体友好，有利于人体健康。

Description

一种丝素蛋白与聚对苯二甲酸丁二醇酯的共混纤维及其制备方法
技术领域
本发明涉及一种丝素蛋白与聚对苯二甲酸丁二醇酯的共混纤维及其制备方法
背景技术
PBT纤维是聚对苯二甲酸丁二酯纤维(Polybutyleneterephthalatefibre)的简称，由高纯度对苯二甲酸(TPA)或对苯二甲酸二甲酯(DMT)与1，4－丁二醇酯化后缩聚的线性聚合物，经熔体纺丝制得的纤维，属于聚酯纤维的一种。生产中常采用对苯二甲酸二甲酯与1，4－丁二醇通过酯交换，并在较高的温度和真空度下，以有机钛或锡化合物和钛酸四丁酯为催化剂进行缩聚反应，再经熔融纺丝而制得PBT纤维。PBT纤维是工程塑料的骄子。1979年日本帝人公司首先推出了PBT纤维制品。随着差别化纤维的发展，PBT作为纤维的使用价值逐步被人们认识。
由PBT制成的纤维具有聚酯纤维共有的一些性质，但由于在PBT大分子基本链节上的柔性部分较长，因而使PBT纤维的熔点和玻璃化温度较普通聚酯纤维为低，导致纤维大分子链的柔性和弹性有所提高。PBT纤维具有良好的耐久性、尺寸稳定性和较好的弹性。PBT纤维及其制品的手感柔软，耐磨性和纤维卷曲性好，拉伸弹性和压缩弹性极好，其弹性回复率优于涤纶。PBT纤维具有良好的染色性能，可用普通分散染料进行常压沸染，而无需载体。染得纤维色泽鲜艳，色牢度及耐氯性优良。具有优良的耐化学药品性、耐光性和耐热性但是PBT纤维吸湿性较差，采用这种纤维制备的衣物吸湿排汗功能差，穿着不舒适。
发明内容
为了增强吸湿性，提高穿着舒适性，本发明提供一种丝素蛋白与聚对苯二甲酸丁二醇酯的共混纤维。
为了解决上述技术问题，本发明的技术方案是：一种丝素蛋白与聚对苯二甲酸丁二醇酯的共混纤维，所述丝素蛋白与聚对苯二甲酸丁二醇酯的共混纤维的原料包括按质量份数混合的以下组分：1.0％～5.0％的丝素蛋白纳米粉体和95.0％～99.0％的聚对苯二甲酸丁二醇酯。
作为优选，所述丝素蛋白与聚对苯二甲酸丁二醇酯的共混纤维的原料还包括占丝素蛋白纳米粉体和聚对苯二甲酸丁二醇酯总质量的0.1％～0.8％的纳米银。
与现有技术相比，本发明制备的丝素蛋白与聚对苯二甲酸丁二醇酯的共混纤维中引入丝素蛋白，芯吸高度随时间变化明显变大，吸湿性较强，采用本发明提供的丝素蛋白与聚对苯二甲酸丁二醇酯的共混纤维制备的衣物吸湿排汗功能强，穿着较舒适；丝素蛋白富含18种氨基酸，对人体友好，有利于人体健康。
为了解决上述技术问题，本发明还公开了一种上述丝素蛋白与聚对苯二甲酸丁二醇酯的共混纤维的制备方法，将1.0％～5.0％的丝素蛋白纳米粉体和95.0％～99.0％聚对苯二甲酸丁二醇酯共混之后采用纺丝机进行纺丝。
作为优选，将1.0％～5.0％的丝素蛋白纳米粉体和95.0％～99.0％聚对苯二甲酸丁二醇酯共混之后，加入占丝素蛋白纳米粉体和聚对苯二甲酸丁二醇酯总质量的0.1％～0.8％的纳米银再次共混之后采用纺丝机进行纺丝。
作为优选，纺丝温度不高于280℃。
作为优选，纺丝方式是熔融纺丝。
作为优选，所述纺丝机是熔融纺丝机。
与现有技术相比，采用本发明公开的丝素蛋白与聚对苯二甲酸丁二醇酯的共混纤维的制备方法，制备的丝素蛋白与聚对苯二甲酸丁二醇酯的共混纤维中引入丝素蛋白芯吸高度随时间变化明显变大，吸湿性较强，采用本发明提供的丝素蛋白与聚对苯二甲酸丁二醇酯的共混纤维制备的衣物吸湿排汗功能强，穿着较舒适；丝素蛋白富含18种氨基酸，对人体友好，有利于人体健康。
附图说明
图1a是本发明一具体实施例的丝素蛋白与聚对苯二甲酸丁二醇酯的共混纤维红外光谱图；
图1b是图1a中A处的局部放大图；
图2是本发明一具体实施例的丝素蛋白与聚对苯二甲酸丁二醇酯的共混纤维以及现有技术中的聚对苯二甲酸丁二醇酯纤维芯吸高度随时间的变化图。
具体实施方式
为使本发明的上述目的、特征和优点能够更加明显易懂，下面结合附图对本发明的具体实施方式做详细的说明。
实施例1
一种丝素蛋白与聚对苯二甲酸丁二醇酯的共混纤维(SF-PBT)，包括2克的丝素蛋白(SF)纳米粉体和98.0克聚对苯二甲酸丁二醇酯，0.4克纳米银。
上述丝素蛋白与聚对苯二甲酸丁二醇酯的共混纤维的制备方法，将2克的丝素蛋白纳米粉体和98.0克聚对苯二甲酸丁二醇酯，0.4克纳米银共混之后采用熔融纺丝机进行纺丝，纺丝温度280℃，纺丝方式是熔融纺丝。
所纺丝素蛋白与聚对苯二甲酸丁二醇酯的共混纤维的共混长丝规格为：POY规格：267dtex/36f，DTY规格：150D/36f。
将得到的丝素蛋白与聚对苯二甲酸丁二醇酯的共混纤维进行以下测试：红外光谱测试、氨基酸含量测试、吸湿性测试，抗菌性测试。
1、红外光谱测试，测试结果见图1a和图1b；
请参考图1，在SF-PBT的红外光谱曲线测试结果中，出现1648cm-1，1636cm-1，1528cm-1，1318cm-1，1290cm-1，即丝素蛋白的特征吸收峰，说明在共混纤维中存在丝素蛋白(SF)成份，成功的制备了得丝素蛋白与聚对苯二甲酸丁二醇酯的共混纤维。
2、氨基酸含量测试，测试结果见表1；
表1：SF-PBT共混纤维中四种氨基酸含量测试结果。
本发明中引入丝素蛋白，制备的丝素蛋白与聚对苯二甲酸丁二醇酯的共混纤维含有大量氨基酸，对人体友好，有利于身体健康。
3、吸湿性测试：测试现有技术中的聚对苯二甲酸丁二醇酯纤维以及本发明制备的丝素蛋白与聚对苯二甲酸丁二醇酯的共混纤维的芯吸高度随时间的变化；测试结果见图2。
测试方法：FZ/T 01071《纺织品毛细效应试验方法》，
测试仪器：LFY-215型毛细效应测定仪。
请参考图2，现有技术中的聚对苯二甲酸丁二醇酯纤维的芯吸高度随时间变化较小，吸湿性较差；而本发明中引入丝素蛋白，制备的丝素蛋白与聚对苯二甲酸丁二醇酯的共混纤维的芯吸高度随时间变化明显变大，吸湿性较强，采用本发明提供的丝素蛋白与聚对苯二甲酸丁二醇酯的共混纤维制备的衣物吸湿排汗功能强，穿着较舒适。
4、抗菌性测试
抗菌功能测试方法(抗菌率):GB 20944.3-2008-T纺织品抑菌功能的评价第3部分：振荡法。
本发明提供的丝素蛋白与聚对苯二甲酸丁二醇酯的共混纤维对金黄色葡萄球菌和大肠杆菌的抗菌率可达98％。
实施例2
一种丝素蛋白与聚对苯二甲酸丁二醇酯的共混纤维，包括1克的丝素蛋白纳米粉体和99克聚对苯二甲酸丁二醇酯，0.8克纳米银。
实施例3
一种丝素蛋白与聚对苯二甲酸丁二醇酯的共混纤维，包括5克的丝素蛋白纳米粉体和95.0克聚对苯二甲酸丁二醇酯，0.1克纳米银。
本领域的技术人员可以对发明进行各种改动和变型而不脱离本发明的精神和范围。这样，倘若本发明的这些修改和变型属于本发明权利要求及其等同技术的范围之内，则本发明也意图包括这些改动和变型在内。

Claims (7)

1.一种丝素蛋白与聚对苯二甲酸丁二醇酯的共混纤维，其特征在于，所述丝素蛋白与聚对苯二甲酸丁二醇酯的共混纤维的原料包括按质量份数混合的以下组分：1.0％～5.0％的丝素蛋白纳米粉体和95.0％～99.0％的聚对苯二甲酸丁二醇酯。
2.如权利要求1所述的一种丝素蛋白与聚对苯二甲酸丁二醇酯的共混纤维，其特征在于，所述丝素蛋白与聚对苯二甲酸丁二醇酯的共混纤维的原料还包括占丝素蛋白纳米粉体和聚对苯二甲酸丁二醇酯总质量的0.1％～0.8％的纳米银。
3.一种如权利要求1所述的丝素蛋白与聚对苯二甲酸丁二醇酯的共混纤维的制备方法，其特征在于，将1.0％～5.0％的丝素蛋白纳米粉体和95.0％～99.0％聚对苯二甲酸丁二醇酯共混之后采用纺丝机进行纺丝。
4.如权利要求3所述的丝素蛋白与聚对苯二甲酸丁二醇酯的共混纤维的制备方法，其特征在于，将1.0％～5.0％的丝素蛋白纳米粉体和95.0％～99.0％聚对苯二甲酸丁二醇酯共混之后，加入占丝素蛋白纳米粉体和聚对苯二甲酸丁二醇酯总质量的0.1％～0.8％的纳米银再次共混之后采用纺丝机进行纺丝。
5.如权利要求3或4所述的丝素蛋白与聚对苯二甲酸丁二醇酯的共混纤维的制备方法，其特征在于，纺丝温度不高于280℃。
6.如权利要求3或4所述的丝素蛋白与聚对苯二甲酸丁二醇酯的共混纤维的制备方法，其特征在于，纺丝方式是熔融纺丝。
7.如权利要求3或4所述的丝素蛋白与聚对苯二甲酸丁二醇酯的共混纤维的制备方法，其特征在于，所述纺丝机是熔融纺丝机。
CN201510197952.1A 2015-04-24 2015-04-24 一种丝素蛋白与聚对苯二甲酸丁二醇酯的共混纤维及其制备方法 Pending CN104790062A (zh)