CN104762001A - 一种水性光固化uv涂料 - Google Patents

一种水性光固化uv涂料 Download PDF

Info

Publication number
CN104762001A
CN104762001A CN201510132355.0A CN201510132355A CN104762001A CN 104762001 A CN104762001 A CN 104762001A CN 201510132355 A CN201510132355 A CN 201510132355A CN 104762001 A CN104762001 A CN 104762001A
Authority
CN
China
Prior art keywords
epocryl
oligomeric
curing
coating
water
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510132355.0A
Other languages
English (en)
Inventor
牛无畏
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201510132355.0A priority Critical patent/CN104762001A/zh
Publication of CN104762001A publication Critical patent/CN104762001A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种水性光固化UV涂料，该水性光固化UV涂料含有改性低聚环氧丙烯酸酯树脂，所述的改性低聚环氧丙烯酸酯树脂为多元酸酐与低聚环氧丙烯酸酯树脂制备而成。该水性光固化UV涂料保持了优异的粘合力、化学稳定性、耐热性、耐化学品性及紫外光快速固化等优点，能广泛应用于金属、玻璃、塑料等涂层。

Description

一种水性光固化UV涂料
技术领域
本发明属于涂料领域，特别涉及一种水性光固化UV涂料。
背景技术
光固化涂料又称光敏涂料，它是利用UV引发具有化学活性的液态材料快速聚合交联，瞬间固化成膜。其组成主要由光敏树脂、光敏剂（光引发剂）和稀释剂组成，同时加入一些添加剂，如热稳定剂，制备色漆时加入颜料和填料。光敏树脂一般是带有不饱和键的低聚物树脂，对于传统的油性光固化涂料，由于低聚物树脂粘度大，涂装时，特别是喷涂工艺，要加入大量活性稀释剂，有时在使用过程中需要加入有机溶剂，使用时不安全，也污染环境。为了克服这些弊病，一种新颖的光固化涂料:水性光固化涂料应运而生。水性光固化涂料继承和发展了传统的油性光固化涂料技术和水性涂料、油墨技术的优点：不使用活性稀释剂，没有VOC不会产生刺激气味，喷涂安全不污染环境；同时可获得硬度和韧性都很好的涂层。因此水性光固化涂料已成为光固化技术研究和开发的一个非常活跃的领域，并且获得了很大的实际应用。环氧丙烯酸酯具有优异的粘合力、化学稳定性、耐热性、耐化学品性及紫外光快速固化等优点，使其成为UV光固化涂料中应用最多的感光性树脂之一，但作为传统的油性光固化树脂在光固化过程中需要使用大量活性稀释剂，而活性稀释剂对人体伤害比较大。
发明内容
为了保持环氧丙烯酸树脂优异的粘合力、化学稳定性、耐热性、耐化学品性及紫外光快速固化等优点，同时又能克服其在使用时，大量活性稀释剂的使用的缺点，本发明提供一种水性的含有低聚环氧丙烯酸酯树脂的UV光固化涂料，具体技术方案如下：
一种水性光固化UV涂料，含有改性低聚环氧丙烯酸酯树脂，其中，所述的改性低聚环氧丙烯酸酯树脂为二酸酐与低聚环氧丙烯酸酯树脂制备而成。
根据上述所述的水性光固化UV涂料，其中，所述的低聚环氧丙烯酸酯树脂为低聚双酚A型环氧丙烯酸酯树脂。
根据上述所述的水性光固化UV涂料，其特征在于所述的二酸酐为含有不饱和键的二酸酐。
根据上述所述的水性光固化UV涂料，其中，所述的含有不饱和键的二酸酐为马来酸酐。
根据权利上述所述的水性光固化UV涂料，其中，所述的改性低聚环氧丙烯酸酯树脂中羧基被有机胺中和以胺盐形式存在。
本发明提供了一种水性的含有低聚环氧丙烯酸酯树脂的UV光固化涂料，即保持了优异的粘合力、化学稳定性、耐热性、耐化学品性及紫外光快速固化等优点，又不需要使用有毒的活性稀释剂，能广泛应用于金属、玻璃、塑料等涂层。
具体实施方式
根据本发明，本发明的水性光固化UV涂料是一种含有改性低聚环氧丙烯酸酯树脂。其中的改性低聚环氧丙烯酸酯树脂通过利用二酸酐与低聚环氧丙烯酸酯树脂中的环氧进行反应而使低聚环氧丙烯酸酯树脂上带有丙烯酸基团，从而提高低聚环氧丙烯酸酯树脂的水溶性。为了进一步提高低聚环氧丙烯酸酯树脂的水溶性，进一步优选为利用有机胺对本发明的二酸酐改性的低聚环氧丙烯酸酯树脂进行中和改性为离子型的低聚环氧丙烯酸酯树脂，对于所述的有机胺没有限制，例如可以是伯胺、仲胺、或叔胺，但优选为叔胺，例如三乙胺。考虑到改性后交联固化强度，二酸酐优选为含有不饱和键的二酸酐，进一步优选为常用的马来酸酐。本发明的低聚环氧丙烯酸酯树脂，聚合度为10-100，优选为20-50；考虑到涂层的强度，本发明的低聚环氧丙烯酸酯树脂优选为低聚双酚A型环氧丙烯酸酯树脂。
本发明中光固化剂可以为任意常用的光固化剂，如果多元酸酐改性低聚环氧丙烯酸酯树脂以100重量份计算，光固化剂为5-10份。同时，本发明的水性光固化UV涂料中一般还会加入各种光固化涂料的常用助剂，例如流平剂、消泡剂、分散剂、或附着力促进剂等，还可以根据要求添加各种填料或颜料等。
以下结合具体实施例对本发明的技术方案做进行进一步举例说明。
实施例
改性低聚双酚A型环氧丙烯酸酯树脂的制备
往干净干燥好的三口瓶中加入低聚双酚A型环氧丙烯酸酯树脂。连接好搅拌器、冷凝管、温度计，边搅拌边升温到90℃，加入催化剂三乙胺和0.05%的对羟基苯甲醚，再加入马来酸酐反应2小时，然后停止加热降温到室温。然后用滴液漏斗慢慢加入三乙胺行中和，搅拌1小时。
将上述100g改性低聚双酚A型环氧丙烯酸酯树脂,5g光固化剂，1g流平剂，1g消泡剂，2g分散剂加入搅拌器高速搅拌10分钟。

Claims (5)

1.一种水性光固化UV涂料，含有改性低聚环氧丙烯酸酯树脂，其特征在于所述的改性低聚环氧丙烯酸酯树脂为多元酸酐与低聚环氧丙烯酸酯树脂制备而成。
2.根据权利要求1所述的水性光固化UV涂料，其特征在于所述的低聚环氧丙烯酸酯树脂为低聚双酚A型环氧丙烯酸酯树脂。
3.根据权利要求1所述的水性光固化UV涂料，其特征在于所述的二酸酐为含有不饱和键的二酸酐。
4.根据权利要求3所述的水性光固化UV涂料，其特征在于所述的含有不饱和键的二酸酐为马来酸酐。
5.根据权利要求1所述的水性光固化UV涂料，其特征在于所述的改性低聚环氧丙烯酸酯树脂中羧基被有机胺中和以胺盐形式存在。
CN201510132355.0A 2015-03-25 2015-03-25 一种水性光固化uv涂料 Pending CN104762001A (zh)