CN104668161A - 气弹簧自泳漆涂装工艺 - Google Patents
气弹簧自泳漆涂装工艺 Download PDFInfo
- Publication number
- CN104668161A CN104668161A CN201510121913.3A CN201510121913A CN104668161A CN 104668161 A CN104668161 A CN 104668161A CN 201510121913 A CN201510121913 A CN 201510121913A CN 104668161 A CN104668161 A CN 104668161A
- Authority
- CN
- China
- Prior art keywords
- workpiece
- time
- minutes
- described workpiece
- carry out
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种气弹簧自泳漆涂装工艺，它按以下步骤进行：将工件放在喷淋槽内用60～70摄氏度的脱脂液进行预脱脂；将经过预脱脂的所述工件浸入60～70摄氏度的脱脂液内进行酸洗除锈；在常温下将除锈后的所述工件用碱水进行喷淋清洗；在常温下将经过碱水清洗的所述工件用纯水清洗；将经过纯水清洗的所述工件置入装有水溶性涂料的涂装槽中放置；待所述工件表面形成漆膜后浸入清水中；然后将工件取出，放入漂洗槽中进行漂洗；将经过处理后的所述工件放入烘房中进行烘烤。它可以解决传统的喷漆气味比较难闻，抗腐蚀能力不够，污染环境的问题。
Description
技术领域
本发明涉及一种气弹簧自泳漆涂装工艺。
背景技术
目前，大多数厂家对气弹簧涂装依旧采用较传统的喷漆，行业内的人都知道，喷漆的优势是成本低，并且操作起来也比较简单，一般一个厂有一两个大师傅就可以生产了，但是喷漆工艺的不足之处在于：气味比较难闻，并且抗腐蚀能力也不够突出，而且对于环保这一块也是让各个厂家比较头疼的事情。
发明内容
本发明的目的是提供一种气弹簧自泳漆涂装工艺，它可以解决传统的喷漆气味比较难闻，抗腐蚀能力不够，污染环境的问题。
为了解决上述问题，本发明采用的技术方案是：这种气弹簧自泳漆涂装工艺，按以下步骤进行：
1）、将工件放在喷淋槽内用60～70摄氏度的脱脂液进行预脱脂，时间为3分钟；
2）、将经过预脱脂的所述工件浸入60～70摄氏度的脱脂液内进行酸洗除锈，时间为3分钟；
3）、在常温下将除锈后的所述工件用碱水进行喷淋清洗，时间为1分钟；
4）、在常温下将经过碱水清洗的所述工件用纯水清洗，时间为1分钟；
5）、将经过纯水清洗的所述工件置入装有20～22摄氏度水溶性涂料的涂装槽中放置1～3分钟；
6）、待所述工件表面形成漆膜后浸入清水中，放置20～30分钟；
7）、然后将工件取出，放入漂洗槽中进行漂洗；
8}、将经过处理后的所述工件放入烘房中进行烘烤，烘房温度为80～95摄氏度，烘烤时间为50～60分钟。
由于采用了上述技术方案，本发明与现有技术相比，具有的有益效果是：由于自泳漆不用有机溶剂，所以污染少而有利于环保，而且自泳漆的涂装设备简单，能耗少，易操作，涂装成本低且防锈能力强。
采用自泳漆涂装出的产品盐雾时间可达300小时左右；以水为分散剂，不含有机溶剂，重金属，无挥发性有机物；涂装无死角，只要工件能接触到的地方均能做到良好的漆膜。
具体实施方式
下面结合实施例对本发明作进一步详述：
实施例1：
这种气弹簧自泳漆涂装工艺，按以下步骤进行：
1）、将工件放在喷淋槽内用60摄氏度的脱脂液进行预脱脂，时间为3分钟；
2）、将经过预脱脂的所述工件浸入60摄氏度的脱脂液内进行酸洗除锈，时间为3分钟；
3）、在常温下将除锈后的所述工件用碱水进行喷淋清洗，时间为1分钟；
4）、在常温下将经过碱水清洗的所述工件用纯水清洗，时间为1分钟；
5）、将经过纯水清洗的所述工件置入装有20摄氏度水溶性涂料的涂装槽中放置3分钟；
6）、待所述工件表面形成漆膜后浸入清水中，放置20分钟；
7）、然后将工件取出，放入漂洗槽中进行漂洗；
8}、将经过处理后的所述工件放入烘房中进行烘烤，烘房温度为80摄氏度，烘烤时间为60分钟。
实施例2：
这种气弹簧自泳漆涂装工艺，按以下步骤进行：
1）、将工件放在喷淋槽内用65摄氏度的脱脂液进行预脱脂，时间为3分钟；
2）、将经过预脱脂的所述工件浸入65摄氏度的脱脂液内进行酸洗除锈，时间为3分钟；
3）、在常温下将除锈后的所述工件用碱水进行喷淋清洗，时间为1分钟；
4）、在常温下将经过碱水清洗的所述工件用纯水清洗，时间为1分钟；
5）、将经过纯水清洗的所述工件置入装有21摄氏度水溶性涂料的涂装槽中放置2分钟；
6）、待所述工件表面形成漆膜后浸入清水中，放置25分钟；
7）、然后将工件取出，放入漂洗槽中进行漂洗；
8}、将经过处理后的所述工件放入烘房中进行烘烤，烘房温度为90摄氏度，烘烤时间为55分钟。
实施例3：
这种气弹簧自泳漆涂装工艺，按以下步骤进行：
1）、将工件放在喷淋槽内用70摄氏度的脱脂液进行预脱脂，时间为3分钟；
2）、将经过预脱脂的所述工件浸入70摄氏度的脱脂液内进行酸洗除锈，时间为3分钟；
3）、在常温下将除锈后的所述工件用碱水进行喷淋清洗，时间为1分钟；
4）、在常温下将经过碱水清洗的所述工件用纯水清洗，时间为1分钟；
5）、将经过纯水清洗的所述工件置入装有22摄氏度水溶性涂料的涂装槽中放置1～3分钟；
6）、待所述工件表面形成漆膜后浸入清水中，放置30分钟；
7）、然后将工件取出，放入漂洗槽中进行漂洗；
8}、将经过处理后的所述工件放入烘房中进行烘烤，烘房温度为95摄氏度，烘烤时间为50分钟。
Claims (1)
1.一种气弹簧自泳漆涂装工艺，其特征在于：按以下步骤进行：
1）、将工件放在喷淋槽内用60～70摄氏度的脱脂液进行预脱脂，时间为3分钟；
2）、将经过预脱脂的所述工件浸入60～70摄氏度的脱脂液内进行酸洗除锈，时间为3分钟；
3）、在常温下将除锈后的所述工件用碱水进行喷淋清洗，时间为1分钟；
4）、在常温下将经过碱水清洗的所述工件用纯水清洗，时间为1分钟；
5）、将经过纯水清洗的所述工件置入装有20～22摄氏度水溶性涂料的涂装槽中放置1～3分钟；
6）、待所述工件表面形成漆膜后浸入清水中，放置20～30分钟；
7）、然后将工件取出，放入漂洗槽中进行漂洗；
8}、将经过处理后的所述工件放入烘房中进行烘烤，烘房温度为80～95摄氏度，烘烤时间为50～60分钟。