CN104649690A - 硅莫砖的制备方法 - Google Patents

硅莫砖的制备方法 Download PDF

Info

Publication number
CN104649690A
CN104649690A CN201410000865.8A CN201410000865A CN104649690A CN 104649690 A CN104649690 A CN 104649690A CN 201410000865 A CN201410000865 A CN 201410000865A CN 104649690 A CN104649690 A CN 104649690A
Authority
CN
China
Prior art keywords
silicon
brick
mullite brick
preparation
adobe
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410000865.8A
Other languages
English (en)
Inventor
叶树泉
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Cenxi City Newly-Built Ball Pottery Co Ltd
Original Assignee
Cenxi City Newly-Built Ball Pottery Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Cenxi City Newly-Built Ball Pottery Co Ltd filed Critical Cenxi City Newly-Built Ball Pottery Co Ltd
Priority to CN201410000865.8A priority Critical patent/CN104649690A/zh
Publication of CN104649690A publication Critical patent/CN104649690A/zh
Pending legal-status Critical Current

Abstract

本发明公开一种硅莫砖的制备方法，包括按一定比例将铝矾土、金属硅粉、纸浆废液；按比例将上述原料搅拌混合均匀，得到浆料；将得到的所述浆料放入模具中振动成型，静置3h，脱模，得到砖坯，再静置养护2天；将所述砖坯先在400℃下干燥2h，再通过真空吸附器将所述砖坯放到垫板上，将放置在所述垫板上的所述砖坯连同所述垫板一起送入辊道窑炉内以1200℃的温度进行烧制，烧制1h，得到本硅莫砖。本发明制备工艺简单，其原料之—纸浆废液价格廉价，降低了硅莫砖的生产成本，而且制得的硅莫砖耐磨性好、抗压强度大于108Mpa以及耐火度大于1800℃。

Description

硅莫砖的制备方法
技术领域
本发明涉及耐火材料技术领域，尤其是一种硅莫砖的制备方法。
背景技术
硅莫砖是一种耐火材料，以莫来石（3Al2O3·2SiO2）和碳化硅（SiC）为主要矿物组成的烧成砖。随着研究的深入和产业化的迅速发展，现已有多家耐火材料厂生产各种牌子的硅莫砖，但其产品耐磨性、抗压强度以及耐高温性还有待提高。
发明内容
本发明要解决的技术问题是提供一种耐磨性好、抗压强度高以及耐高温的硅莫砖的制备方法。
为解决上述技术问题，本发明采用的技术方案是：
一种硅莫砖的制备方法，其特征在于采用由以下重量份数的原料生产：铝矾土82份、金属硅粉20份以及纸浆废液14份；
其生产方法包括以下步骤：
A、按比例将上述原料搅拌混合均匀，得到浆料；
B、将得到的所述浆料放入模具中振动成型，静置3h，脱模，得到砖坯，再静置养护2天；
C、将所述砖坯先在400℃下干燥2h，再通过真空吸附器将所述砖坯放到垫板上，将放置在所述垫板上的所述砖坯连同所述垫板一起送入辊道窑炉内以1200℃的温度进行烧制，烧制1h，得到本硅莫砖。
由于采用了上述技术方案，本发明与现有技术相比，具有的有益效果是：
本发明制备工艺简单，其原料之———纸浆废液价格廉价，降低了本硅莫砖的生产成本，而且其制得的硅莫砖耐磨性好、抗压强度大于108Mpa以及耐火度大于1800℃。
具体实施方式
硅莫砖的制备原料是：铝矾土82吨、金属硅粉20吨、纸浆废液14吨；
其生产方法包括以下步骤：
A、将82吨铝矾土、20吨金属硅粉以及14吨纸浆废液搅拌混合均匀，得到浆料；
B、将得到的所述浆料放入模具中振动成型，静置3h，脱模，得到砖坯，再静置养护2天；
C、将所述砖坯先在400℃下干燥2h，再通过真空吸附器将所述砖坯放到垫板上，将放置在所述垫板上的所述砖坯连同所述垫板一起送入辊道窑炉内以1200℃的温度进行烧制，烧制1h，得到本硅莫砖。 

Claims (1)

1.一种硅莫砖的制备方法，其特征在于采用由以下重量份数的原料生产：铝矾土82份、金属硅粉20份以及纸浆废液14份；
其生产方法包括以下步骤：
A、按比例将上述原料搅拌混合均匀，得到浆料；
B、将得到的所述浆料放入模具中振动成型，静置3h，脱模，得到砖坯，再静置养护2天；
C、将所述砖坯先在400℃下干燥2h，再通过真空吸附器将所述砖坯放到垫板上，将放置在所述垫板上的所述砖坯连同所述垫板一起送入辊道窑炉内以1200℃的温度进行烧制，烧制1h，得到本硅莫砖。
CN201410000865.8A 2014-01-02 2014-01-02 硅莫砖的制备方法 Pending CN104649690A (zh)