CN104628304A - 一种金属阀门表面防腐抗氧化用纳米陶瓷复合涂料 - Google Patents
一种金属阀门表面防腐抗氧化用纳米陶瓷复合涂料 Download PDFInfo
- Publication number
- CN104628304A CN104628304A CN201510028273.1A CN201510028273A CN104628304A CN 104628304 A CN104628304 A CN 104628304A CN 201510028273 A CN201510028273 A CN 201510028273A CN 104628304 A CN104628304 A CN 104628304A
- Authority
- CN
- China
- Prior art keywords
- percent
- metal valve
- composite coating
- coupling agent
- coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种金属阀门表面防腐抗氧化用纳米陶瓷复合涂料,涉及阀门制造技术领域,由如下质量分数的原料制成:纳米陶瓷粉45-50%、聚四氟乙烯树脂10-15%、聚氨酯树脂10-15%、十二碳醇酯5-8%、碳酸钙3-4.5%、钛白粉3-5%、有机膨润土2-3%、气相二氧化硅1-2%、偶联剂1-1.5%、石蜡0.5-1%、异噻唑啉酮0.2-0.5%、氟碳有机硅改性流平剂0.5-1%、改性磷酸锌2-3%、大豆磷脂0.5-1%、乙酸乙酯5-8%、正丁醇5-8%。本发明制得的涂料能够在金属阀门表面形成一层致密而坚硬的涂层,并且该涂层具有较强的耐腐性和抗氧化作用,从而能有效延长金属阀门的使用寿命,并且扩大了金属阀门的使用范围。
Description
技术领域:
本发明涉及阀门制造技术领域,具体涉及一种金属阀门表面防腐抗氧化用纳米陶瓷复合涂料。
背景技术:
阀门是流体输送系统中的控制部件,具有截止、调节、导流、防止逆流、稳压、分流或溢流泄压等功能。因此,喷涂在阀门表面的涂料必须具有耐水、耐冲击、耐热、隔热等性能,尤其是喷涂在金属阀门表面的涂料需要具备较强的防腐和抗氧化性能。但是,目前市场是专用于金属阀门的涂料很少,并且其防腐、抗氧化效果较差。
发明内容:
本发明所要解决的技术问题在于提供一种原料易得、生产方法简单的金属阀门表面防腐抗氧化用纳米陶瓷复合涂料。
本发明所要解决的技术问题采用以下的技术方案来实现:
一种金属阀门表面防腐抗氧化用纳米陶瓷复合涂料,由如下质量分数的原料制成:
纳米陶瓷粉45-50%、聚四氟乙烯树脂10-15%、聚氨酯树脂10-15%、十二碳醇酯5-8%、碳酸钙3-4.5%、钛白粉3-5%、有机膨润土2-3%、气相二氧化硅1-2%、偶联剂1-1.5%、石蜡0.5-1%、异噻唑啉酮0.2-0.5%、氟碳有机硅改性流平剂0.5-1%、改性磷酸锌2-3%、大豆磷脂0.5-1%、乙酸乙酯5-8%、正丁醇5-8%。
所述纳米陶瓷粉的粒径为80-100纳米。
所述偶联剂选自硅烷偶联剂或钛酸酯偶联剂。
一种金属阀门表面防腐抗氧化用纳米陶瓷复合涂料的制备方法,包括下列步骤:
(1)向拉缸中加入钛白粉、乙酸乙酯和正丁醇,混合物高速搅拌20-25min后再用砂磨机砂磨至细度小于10um,即得钛白浆;
(2)先向反应釜中加入碳酸钙、有机膨润土、气相二氧化硅、石蜡、改性磷酸锌和钛白浆,搅拌10-15min后再加入聚四氟乙烯树脂和聚氨酯树脂,然后升温至80-90℃保温20-25min,随后自然冷却降温,当温度降至35-40℃后过滤得混合溶液;
(3)向高速搅拌机中加入步骤(2)制备的混合溶液,再加入纳米陶瓷粉、十二碳醇酯、偶联剂、异噻唑啉酮、氟碳有机硅改性流平剂和大豆磷脂,于800-1000r/min下搅拌15-20min,最后出料、装桶即得目标涂料。
本发明的有益效果是:本发明以纳米陶瓷粉为主要原料,并添加各种助剂制得复合涂料,该涂料能够在金属阀门表面形成一层致密而坚硬的涂层,并且该涂层具有较强的耐腐性和抗氧化作用,从而能有效延长金属阀门的使用寿命,并且扩大了金属阀门的使用范围。
具体实施方式:
为了使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解,下面结合具体实施例,进一步阐述本发明。
一种金属阀门表面防腐抗氧化用纳米陶瓷复合涂料,由如下质量分数的原料制成:
纳米陶瓷粉47%、聚四氟乙烯树脂11%、聚氨酯树脂10%、十二碳醇酯5.5%、碳酸钙3.5%、钛白粉3%、有机膨润土2%、气相二氧化硅1.5%、偶联剂1.5%、石蜡1%、异噻唑啉酮0.5%、氟碳有机硅改性流平剂1%、改性磷酸锌2%、大豆磷脂0.5%、乙酸乙酯5%、正丁醇5%。
所述纳米陶瓷粉的粒径为80-100纳米。
所述偶联剂选自硅烷偶联剂或钛酸酯偶联剂。
根据上述配方进行金属阀门表面防腐抗氧化用纳米陶瓷复合涂料的制备,具体操作步骤如下:
(1)向拉缸中加入钛白粉、乙酸乙酯和正丁醇,混合物高速搅拌20min后再用砂磨机砂磨至细度小于10um,即得钛白浆;
(2)先向反应釜中加入碳酸钙、有机膨润土、气相二氧化硅、石蜡、改性磷酸锌和钛白浆,搅拌10min后再加入聚四氟乙烯树脂和聚氨酯树脂,然后升温至85℃保温25min,随后自然冷却降温,当温度降至35-40℃后过滤得混合溶液;
(3)向高速搅拌机中加入步骤(2)制备的混合溶液,再加入纳米陶瓷粉、十二碳醇酯、偶联剂、异噻唑啉酮、氟碳有机硅改性流平剂和大豆磷脂,于800r/min下搅拌20min,最后出料、装桶即得目标涂料。
以上显示和描述了本发明的基本原理和主要特征和本发明的优点。本行业的技术人员应该了解,本发明不受上述实施例的限制,上述实施例和说明书中描述的只是说明本发明的原理,在不脱离本发明精神和范围的前提下,本发明还会有各种变化和改进,这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。
Claims (4)
1.一种金属阀门表面防腐抗氧化用纳米陶瓷复合涂料,其特征在于,由如下质量分数的原料制成:
纳米陶瓷粉45-50%、聚四氟乙烯树脂10-15%、聚氨酯树脂10-15%、十二碳醇酯5-8%、碳酸钙3-4.5%、钛白粉3-5%、有机膨润土2-3%、气相二氧化硅1-2%、偶联剂1-1.5%、石蜡0.5-1%、异噻唑啉酮0.2-0.5%、氟碳有机硅改性流平剂0.5-1%、改性磷酸锌2-3%、大豆磷脂0.5-1%、乙酸乙酯5-8%、正丁醇5-8%。
2.根据权利要求1所述的一种金属阀门表面防腐抗氧化用纳米陶瓷复合涂料,其特征在于:所述纳米陶瓷粉的粒径为80-100纳米。
3.根据权利要求1所述的一种金属阀门表面防腐抗氧化用纳米陶瓷复合涂料,其特征在于:所述偶联剂选自硅烷偶联剂或钛酸酯偶联剂。
4.一种金属阀门表面防腐抗氧化用纳米陶瓷复合涂料的制备方法,其特征在于,包括下列步骤:
(1)向拉缸中加入钛白粉、乙酸乙酯和正丁醇,混合物高速搅拌20-25min后再用砂磨机砂磨至细度小于10um,即得钛白浆;
(2)先向反应釜中加入碳酸钙、有机膨润土、气相二氧化硅、石蜡、改性磷酸锌和钛白浆,搅拌10-15min后再加入聚四氟乙烯树脂和聚氨酯树脂,然后升温至80-90℃保温20-25min,随后自然冷却降温,当温度降至35-40℃后过滤得混合溶液;
(3)向高速搅拌机中加入步骤(2)制备的混合溶液,再加入纳米陶瓷粉、十二碳醇酯、偶联剂、异噻唑啉酮、氟碳有机硅改性流平剂和大豆磷脂,于800-1000r/min下搅拌15-20min,最后出料、装桶即得目标涂料。