CN104592939A - 一种阀门密封面研磨用白刚玉-纳米陶瓷复合膏 - Google Patents
一种阀门密封面研磨用白刚玉-纳米陶瓷复合膏 Download PDFInfo
- Publication number
- CN104592939A CN104592939A CN201510028221.4A CN201510028221A CN104592939A CN 104592939 A CN104592939 A CN 104592939A CN 201510028221 A CN201510028221 A CN 201510028221A CN 104592939 A CN104592939 A CN 104592939A
- Authority
- CN
- China
- Prior art keywords
- nano
- fused alumina
- white fused
- grinding
- nano ceramic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种阀门密封面研磨用白刚玉-纳米陶瓷复合膏,涉及阀门制造技术领域,由如下质量分数的原料制成:白刚玉40-45%、纳米陶瓷粉20-25%、氧化铬5-10%、凡士林5-8%、松节油5-8%、硅藻土3-5%、碳酸钙2-3%、聚乙二醇2-3%、气相二氧化硅1.5-2%、油酸1-2%、松香1-2%、长石粉0.5-1%、水8-12%。本发明以白刚玉和纳米陶瓷粉为主要磨料,并加入适量辅助磨料和分散剂,制得的研磨膏稠度适中,能够在阀门密封面形成氧化膜,从而加速研磨过程,提高研磨效果,并且能够对研具产生一定的保护作用。
Description
技术领域:
本发明涉及阀门制造技术领域,具体涉及一种阀门密封面研磨用白刚玉-纳米陶瓷复合膏。
背景技术:
阀门是流体输送系统中的控制部件,具有截止、调节、导流、防止逆流、稳压、分流或溢流泄压等功能。阀门对其闸板、阀瓣等部件密封面光洁度的要求较高,在使用过程中密封面容易发生锈蚀,易附着油污等污染物,使得密封面的密封性降低,并且会缩短阀门的使用寿命。
研磨在阀门制造过程中是其密封面常用的一种光整加工方法,可以使阀门密封面获得很高的尺寸精度、几何形状及表面粗糙度,提高密封面的密封性能,从而延长阀门的使用寿命。目前,阀门密封面的研磨多采用机械研磨方式,为了增强研磨效果在研磨过程中需要使用研磨液或研磨膏。而大多数研磨液和研磨膏虽然能够增强研磨效果,但在使用时容易损坏研磨机械;另外由于研磨液属于液态形式,容易造成使用浪费,从而增加生产成本。
发明内容:
本发明所要解决的技术问题在于提供一种原料易得、制备方法简单的阀门密封面研磨用白刚玉-纳米陶瓷复合膏。
本发明所要解决的技术问题采用以下的技术方案来实现:
一种阀门密封面研磨用白刚玉-纳米陶瓷复合膏,由如下质量分数的原料制成:
白刚玉40-45%、纳米陶瓷粉20-25%、氧化铬5-10%、凡士林5-8%、松节油5-8%、硅藻土3-5%、碳酸钙2-3%、聚乙二醇2-3%、气相二氧化硅1.5-2%、油酸1-2%、松香1-2%、长石粉0.5-1%、水8-12%。
所述阀门密封面研磨用白刚玉-纳米陶瓷复合膏由如下质量分数的原料制成:白刚玉40%、纳米陶瓷粉20%、氧化铬7%、凡士林6%、松节油5%、硅藻土4%、碳酸钙2%、聚乙二醇2%、气相二氧化硅1.5%、油酸1%、松香1%、长石粉0.5%、水10%。
所述纳米陶瓷粉的粒径为80-100纳米。
一种阀门密封面研磨用白刚玉-纳米陶瓷复合膏的制备方法,主要包括下列步骤:
(1)先向高速混合机中加入凡士林、松节油、松香和聚乙二醇,升温至110-120℃后再加入白刚玉、纳米陶瓷粉和氧化铬,混合15-20min,然后自然冷却降温,当温度降至40-45℃时加入硅藻土、碳酸钙、气相二氧化硅和长石粉,继续混合10-15min,得混合物I;
(2)先将步骤(1)制备的混合物I加入到砂磨机中,再加入油酸和水,砂磨至细度小于10um后得混合物II;
(3)将步骤(2)制备的混合物II加入到冷冻干燥机中,冷冻至含水量为5%左右,最后出料、装桶得目标研磨膏。
本发明的有益效果是:本发明以白刚玉和纳米陶瓷粉为主要磨料,并加入适量辅助磨料和分散剂,制得的研磨膏稠度适中,能够在阀门密封面形成氧化膜,从而加速研磨过程,提高研磨效果,并且能够对研具产生一定的保护作用。
具体实施方式:
为了使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解,下面结合具体实施例,进一步阐述本发明。
一种阀门密封面研磨用白刚玉-纳米陶瓷复合膏,由如下质量分数的原料制成:
白刚玉40%、纳米陶瓷粉20%、氧化铬7%、凡士林6%、松节油5%、硅藻土4%、碳酸钙2%、聚乙二醇2%、气相二氧化硅1.5%、油酸1%、松香1%、长石粉0.5%、水10%。
其中,纳米陶瓷粉的粒径为80-100纳米。
一种阀门密封面研磨用白刚玉-纳米陶瓷复合膏的制备方法,主要包括下列步骤:
(1)先向高速混合机中加入凡士林、松节油、松香和聚乙二醇,升温至110-120℃后再加入白刚玉、纳米陶瓷粉和氧化铬,混合15-20min,然后自然冷却降温,当温度降至40-45℃时加入硅藻土、碳酸钙、气相二氧化硅和长石粉,继续混合10-15min,得混合物I;
(2)先将步骤(1)制备的混合物I加入到砂磨机中,再加入油酸和水,砂磨至细度小于10um后得混合物II;
(3)将步骤(2)制备的混合物II加入到冷冻干燥机中,冷冻至含水量为5%左右,最后出料、装桶得目标研磨膏。
本发明以白刚玉和纳米陶瓷粉为主要磨料,并加入适量辅助磨料和分散剂,制得的研磨膏稠度适中,能够在阀门密封面形成氧化膜,从而加速研磨过程,提高研磨效果,并且能够对研具产生一定的保护作用。
以上显示和描述了本发明的基本原理和主要特征和本发明的优点。本行业的技术人员应该了解,本发明不受上述实施例的限制,上述实施例和说明书中描述的只是说明本发明的原理,在不脱离本发明精神和范围的前提下,本发明还会有各种变化和改进,这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。
Claims (4)
1.一种阀门密封面研磨用白刚玉-纳米陶瓷复合膏,其特征在于,由如下质量分数的原料制成:
白刚玉40-45%、纳米陶瓷粉20-25%、氧化铬5-10%、凡士林5-8%、松节油5-8%、硅藻土3-5%、碳酸钙2-3%、聚乙二醇2-3%、气相二氧化硅1.5-2%、油酸1-2%、松香1-2%、长石粉0.5-1%、水8-12%。
2.根据权利要求1所述的一种阀门密封面研磨用白刚玉-纳米陶瓷复合膏,其特征在于,所述阀门密封面研磨用白刚玉-纳米陶瓷复合膏由如下质量分数的原料制成:白刚玉40%、纳米陶瓷粉20%、氧化铬7%、凡士林6%、松节油5%、硅藻土4%、碳酸钙2%、聚乙二醇2%、气相二氧化硅1.5%、油酸1%、松香1%、长石粉0.5%、水10%。
3.根据权利要求1或2所述的一种阀门密封面研磨用白刚玉-纳米陶瓷复合膏,其特征在于:所述纳米陶瓷粉的粒径为80-100纳米。
4.一种阀门密封面研磨用白刚玉-纳米陶瓷复合膏的制备方法,其特征在于,主要包括下列步骤:
(1)先向高速混合机中加入凡士林、松节油、松香和聚乙二醇,升温至110-120℃后再加入白刚玉、纳米陶瓷粉和氧化铬,混合15-20min,然后自然冷却降温,当温度降至40-45℃时加入硅藻土、碳酸钙、气相二氧化硅和长石粉,继续混合10-15min,得混合物I;
(2)先将步骤(1)制备的混合物I加入到砂磨机中,再加入油酸和水,砂磨至细度小于10um后得混合物II;
(3)将步骤(2)制备的混合物II加入到冷冻干燥机中,冷冻至含水量为5%左右,最后出料、装桶得目标研磨膏。