CN104529538A - Celeste blue glaze and preparation method thereof - Google Patents
Celeste blue glaze and preparation method thereof Download PDFInfo
- Publication number
- CN104529538A CN104529538A CN201410698792.4A CN201410698792A CN104529538A CN 104529538 A CN104529538 A CN 104529538A CN 201410698792 A CN201410698792 A CN 201410698792A CN 104529538 A CN104529538 A CN 104529538A
- Authority
- CN
- China
- Prior art keywords
- parts
- glaze
- oxide
- celeste
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a celeste blue glaze. The celeste blue glaze comprises, by weight, 2-3 parts of dolomite, 0.4-0.7 parts of tanzanite, 0.6-0.9 parts of asbolite, 0.3-0.5 parts of chalcedony, 1-2 parts of talcum, 89-93 parts of feldspar glaze, wherein the asbolite comprises, by weight, 21-26 parts of quartz, 2.3-2.7 parts of copper oxide, 1.5-1.9 parts of barium carbonate, 28-32 parts of manganese oxide, 1.6-2.1 parts of magnesium oxide, 30-35 parts of alumina, 3.2-3.4 parts of sodium carbonate, 4.5-6.8 parts of iron oxide and 6.5-9.2 parts of cobaltosic oxide. The celeste blue glaze obtained in the invention has bright and smooth glaze color, greatly maintains ancient celeste blue glaze, and can be massively applied in daily use porcelain products.
Description
Technical field
The present invention relates to ceramic glaze technical field, more specifically, relate to a kind of celeste glaze and preparation method thereof.
Background technology
Celeste glaze is the treasure in Han nationality's tradition technology in producing porcelain, and porcelain glaze color name, has another name called that The sky clears after the rain, and be the blue color glaze of a kind of deep and remote light meaningful high temperature, the green grass or young crops that Ancient Times in China Tao Shu is described is as sky, bright as mirror, just the describing of this glaze colours feature.The name of celeste glaze comes from five generation Later Zhou Dynasty, one of the Five Dynasties's bavin generation ancestor comments: " The sky clears after the rain cloud tear, color is done in the future so ".Be color porcelain will being burnt till the blue sky after rain according to the requirement of Zhou Shizong, thus celeste glaze is originally the glaze colours of wood kiln.But up to the present, wood kiln kiln site is not yet found.Current numerous expert studies intensively the formula attempting reduction celeste glaze, but skill is still immature.
Summary of the invention
The object of this invention is to provide a kind of celeste glaze and preparation method thereof.
The object of the invention is achieved by the following technical programs:
A kind of celeste glaze is provided, be made up of each component of following weight fraction: rhombspar 2 ~ 3 parts, smooth Sang Shi 0.4 ~ 0.7 part, 0.6 ~ 0.9 part, the bright material of pearl, chalcedony 0.3 ~ 0.5 part, 1 ~ 2 part, talcum, feldspar glaze 89 ~ 93 parts, wherein, the bright material of described pearl is made up of each component of following weight fraction: 21 ~ 26 parts, quartz, cupric oxide 2.3 ~ 2.7 parts, barium carbonate 1.5 ~ 1.9 parts, manganese oxide 28 ~ 32 parts, 1.6 ~ 2.1 parts, magnesium oxide, 30 ~ 35 parts, aluminum oxide, 3.2 ~ 3.4 parts, sodium carbonate, ferric oxide 4.5 ~ 6.8 parts, tricobalt tetroxide 6.5 ~ 9.2 parts.
Preferably, described celeste glaze is made up of each component of following weight fraction: rhombspar 2.5 parts, smooth Sang Shi 0.5 part, 0.8 part, the bright material of pearl, chalcedony 0.35 part, 1.8 parts, talcum, feldspar glaze 92 parts, wherein, the bright material of described pearl is made up of each component of following weight fraction: 23 parts, quartz, cupric oxide 2.6 parts, barium carbonate 1.7 parts, manganese oxide 30 parts, 1.7 parts, magnesium oxide, 32 parts, aluminum oxide, 3.3 parts, sodium carbonate, ferric oxide 5 parts, tricobalt tetroxide 7 parts.
Present invention also offers the preparation method of described celeste glaze, comprise the following steps:
The preparation of the bright material of S1 pearl: by formula weighing, wet-milling l20h, 1000 ~ 1100 DEG C of scope calcinings, then porphyrize, wet-milling 80h, dries stand-by;
The preparation of S2 celeste glaze: weighing according to quantity, grinding 30min, obtains celeste glaze.
Compared with prior art, the present invention has following beneficial effect:
The invention provides a kind of celeste glaze, its glaze colours jade-like stone profit, greatly reduces the celeste glaze in ancient times, can large-scale application in household china product.
Embodiment
Below in conjunction with specific embodiment, the present invention is further illustrated.
Embodiment 1
Present embodiment discloses a kind of celeste glaze, be made up of each component of following weight fraction: rhombspar 2.5 parts, smooth Sang Shi 0.5 part, 0.8 part, the bright material of pearl, chalcedony 0.35 part, 1.8 parts, talcum, feldspar glaze 92 parts, wherein, the bright material of described pearl is made up of each component of following weight fraction: 23 parts, quartz, cupric oxide 2.6 parts, barium carbonate 1.7 parts, manganese oxide 30 parts, 1.7 parts, magnesium oxide, 32 parts, aluminum oxide, 3.3 parts, sodium carbonate, ferric oxide 5 parts, tricobalt tetroxide 7 parts.
Embodiment 2
Present embodiment discloses a kind of celeste glaze, be made up of each component of following weight fraction: rhombspar 2 parts, smooth Sang Shi 0.4 part, 0.6 part, the bright material of pearl, chalcedony 0.3 part, 1 part, talcum, feldspar glaze 89 parts, wherein, the bright material of described pearl is made up of each component of following weight fraction: 21 parts, quartz, cupric oxide 2.3 parts, barium carbonate 1.5 parts, manganese oxide 28 parts, 1.6 parts, magnesium oxide, 30 parts, aluminum oxide, 3.2 parts, sodium carbonate, ferric oxide 4.5 parts, tricobalt tetroxide 6.5 parts.
Embodiment 3
Present embodiment discloses a kind of celeste glaze, be made up of each component of following weight fraction: rhombspar 2.8 parts, smooth Sang Shi 0.6 part, 0.8 part, the bright material of pearl, chalcedony 0.4 part, 1.8 parts, talcum, feldspar glaze 90 parts, wherein, the bright material of described pearl is made up of each component of following weight fraction: 26 parts, quartz, cupric oxide 2.6 parts, barium carbonate 1.7 parts, manganese oxide 29 parts, 1.7 parts, magnesium oxide, 32 parts, aluminum oxide, 3.4 parts, sodium carbonate, ferric oxide 4.7 parts, tricobalt tetroxide 7.2 parts.
Embodiment 4
Present embodiment discloses a kind of celeste glaze, be made up of each component of following weight fraction: rhombspar 3 parts, smooth Sang Shi 0.7 part, 0.9 part, the bright material of pearl, chalcedony 0.5 part, 2 parts, talcum, feldspar glaze 93 parts, wherein, the bright material of described pearl is made up of each component of following weight fraction: 24 parts, quartz, cupric oxide 2.7 parts, barium carbonate 1.9 parts, manganese oxide 32 parts, 2.1 parts, magnesium oxide, 35 parts, aluminum oxide, 3.1 parts, sodium carbonate, ferric oxide 6.8 parts, tricobalt tetroxide 9.2 parts.
Embodiment 5
The components by weight percent of Example 1 ~ 4 any embodiment prepares celeste glaze, and preparation process is as follows:
The preparation of the bright material of S1 pearl: by formula weighing, wet-milling l20h, in 1000 scope calcinings, then porphyrize, wet-milling 80h, dries stand-by;
The preparation of S2 celeste glaze: weighing according to quantity, grinding 30min, obtains celeste glaze.
Embodiment 6
The components by weight percent of Example 1 ~ 4 any embodiment prepares celeste glaze, and preparation process is as follows:
The preparation of the bright material of S1 pearl: by formula weighing, wet-milling l20h, 1100 DEG C of scope calcinings, then porphyrize, wet-milling 80h, dries stand-by;
The preparation of S2 celeste glaze: weighing according to quantity, grinding 30min, obtains celeste glaze.
Embodiment 7
The components by weight percent of Example 1 ~ 4 any embodiment prepares celeste glaze, and preparation process is as follows:
The preparation of the bright material of S1 pearl: by formula weighing, wet-milling l20h, 1080 DEG C of scope calcinings, then porphyrize, wet-milling 80h, dries stand-by;
The preparation of S2 celeste glaze: weighing according to quantity, grinding 30min, obtains celeste glaze.
Claims (3)
1. a celeste glaze, it is characterized in that, be made up of each component of following weight fraction: rhombspar 2 ~ 3 parts, smooth Sang Shi 0.4 ~ 0.7 part, 0.6 ~ 0.9 part, the bright material of pearl, chalcedony 0.3 ~ 0.5 part, 1 ~ 2 part, talcum, feldspar glaze 89 ~ 93 parts, wherein, the bright material of described pearl is made up of each component of following weight fraction: 21 ~ 26 parts, quartz, cupric oxide 2.3 ~ 2.7 parts, barium carbonate 1.5 ~ 1.9 parts, manganese oxide 28 ~ 32 parts, 1.6 ~ 2.1 parts, magnesium oxide, 30 ~ 35 parts, aluminum oxide, 3.2 ~ 3.4 parts, sodium carbonate, ferric oxide 4.5 ~ 6.8 parts, tricobalt tetroxide 6.5 ~ 9.2 parts.
2. celeste glaze according to claim 1, is characterized in that, is made up of each component of following weight fraction: rhombspar 2.5 parts, smooth Sang Shi 0.5 part, 0.8 part, the bright material of pearl, chalcedony 0.35 part, 1.8 parts, talcum, feldspar glaze 92 parts, wherein, the bright material of described pearl is made up of each component of following weight fraction: 23 parts, quartz, cupric oxide 2.6 parts, barium carbonate 1.7 parts, manganese oxide 30 parts, 1.7 parts, magnesium oxide, 32 parts, aluminum oxide, 3.3 parts, sodium carbonate, ferric oxide 5 parts, tricobalt tetroxide 7 parts.
3. the preparation method of celeste glaze according to claim 1, is characterized in that, comprise the following steps:
The preparation of the bright material of S1 pearl: by formula weighing, wet-milling l20h, 1000 ~ 1100 DEG C of scope calcinings, then porphyrize, wet-milling 80h, dries stand-by;
The preparation of S2 celeste glaze: weighing according to quantity, grinding 30min, obtains celeste glaze.