CN103332965A - Golden yellow crystallized dry-granular glaze and using method thereof - Google Patents
Golden yellow crystallized dry-granular glaze and using method thereof Download PDFInfo
- Publication number
- CN103332965A CN103332965A CN2013102729685A CN201310272968A CN103332965A CN 103332965 A CN103332965 A CN 103332965A CN 2013102729685 A CN2013102729685 A CN 2013102729685A CN 201310272968 A CN201310272968 A CN 201310272968A CN 103332965 A CN103332965 A CN 103332965A
- Authority
- CN
- China
- Prior art keywords
- glaze
- golden yellow
- crystallization
- dry granular
- evenly
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention provides golden yellow crystallized dry-granular glaze and a using method thereof. The using method comprises the following steps of: (1) weighing the following compositions in percentage by weight: 15%-22% of feldspar, 20%-40% of quartz, 6%-15% of calcium carbonate, 6%-15% of barium carbonate, 22%-50% of zinc oxide, 0.7%-2.2% of CuO, and 0.7%-2.2% of Fe2O3, evenly mixing and grinding, and sieving to obtain crystallized glaze; (2) weighing the following compositions in percentage by weight: 20%-78% of activated silicon and 22%-80% of zinc oxide, evenly dry-mixing, then calcinating at 1100 DEG C for 5-10 hours, and conducting water quenching to obtain a seed crystal; (3) evenly mixing and grinding the crystallized glaze in the step (1) and the seed crystal in the step (2) to obtain golden yellow crystallized dry-granular glaze, preparing the crystallized glaze and water as well as ball milling into slurry according to proportion in use, and evenly applying to the surface of a blank; drying and burning at 1200 DEG C-1350 DEG C for 5-7 hours. The glaze is brightly golden yellow, even and complete in crystal flowers, and the glaze is very attractive, and strong in adaptability.
Description
Technical field
The present invention relates to construction sanitary ceramic decoration technique field, especially relate to a kind of golden yellow crystallization dry granular glaze and using method thereof.
Background technology
Along with ceramic enters huge numbers of families, ceramic glaze is that pottery is made indispensable secondary raw material, and performance and the quality of ceramic had very important influence.Existing ceramic glaze is can rough classification as follows according to classification and purposes according to ceramic glaze: 1, lead glaze and leadless glaze; 2, raw glaze and fritted glaze; 3, once-firing or twice firing glaze; 4, ceramic tile, tableware, snitaryware and electroceramics glaze; 5, soak glaze, glaze spraying, water glaze by what enameling method was divided; 6, high melting glaze and low temperature glaze; 7, high expansion glaze and low bulk glaze; 8, firing atmosphere oxydizing flame, neutral flame and reducing flame; 9, coloured glaze and colourless glaze; 10, transparent and opaque glaze; 11, bright glaze, matt glaze, semi-mat glaze or figure glaze etc.; 12, function glaze is as fluorescence glaze, metal-lustrous glaze, crystalline glaze etc.Wherein the crystalline glaze ceramic tile is because its beautiful appearance exquisiteness extensively is subjected to liking of human consumer.Produce abundant, the beautiful in colour crystalline glaze of kind, become the target that China pottery producer is pursued.
Summary of the invention
The objective of the invention is to solve the problems of the prior art, and a kind of golden yellow crystallization dry granular glaze and using method thereof that is colour-stable, can satisfies the ceramic industry production requirement is provided.
The technical solution adopted in the present invention is such: a kind of golden yellow crystallization dry granular glaze may further comprise the steps:
(1), by weight percentage with 15%~22% feldspar, 20%~40% quartz, 6%~15% calcium carbonate, 6%~15% barium carbonate, 22%~50% zinc oxide, 0.7%~2.2%
With 0.7%~2.2%
, take by weighing that mixed grinding evenly behind each material, sieving obtains the crystallization glaze;
(2), by weight percentage with 20%~78% activated silica and 22%~80% zinc oxide, take by weighing mix dry mixing evenly behind each material after, after 5~10 hours, after shrend, obtain crystal seed through 1100 ℃ of calcinings again;
(3), the crystal seed that makes of crystallization glaze that step (1) is made and step (2), both mixed grindings evenly can make golden yellow crystallization dry granular glaze.
Preferably, the fineness of described crystallization glaze is less than 2% through the 10000-hole sieve excess.
A kind of using method of golden yellow crystallization dry granular glaze, (1), the golden yellow crystallization dry granular glaze that will make and water, ball milling, 1:(0.9~1 in proportion): (0.6~0.8) is through ball milling slurrying; (2), with the gained slurry, employing soaks glaze, be coated with glaze or glaze spraying mode to the base substrate glazing, and glazing thickness is 1~1.5mm, behind the body drying after the glazing, under 1200 ℃~1350 ℃, fired 5~7 hours, slowly obtain the golden yellow brilliant base substrate of spending face after the cooling with stove.
By adopting the aforementioned techniques scheme, the invention has the beneficial effects as follows: this crystalline glaze presents gorgeous golden yellow, and crystalline substance is spent evenly complete, and glaze integral body is intact, and is very attractive in appearance, and can be applicable to the glaze decoration of multiple base substrate, and adaptability is strong.During use, with this crystallization glaze and water, ball milling, 1:(0.9~1 in proportion): (0.6~0.8) makes slip, evenly imposes on billet surface; Wherein ball milling is the diameter of the ball of zirconium white or aluminum oxide material, the fineness of the corresponding meeting of the diameter value of different ball milling ectocrine abrasive lapping.Drying was fired 5~7 hours under 1200 ℃~1350 ℃, fired the base substrate that can obtain golden yellow brilliant flower face respectively; Method technology is simple, and cost is low, is fit to the batch process demand.
Embodiment
Describe the present invention particularly with embodiment below, scope of the present invention is not subjected to the restriction of embodiment.
Embodiment 1
(1), by weight percentage with 21% feldspar, 30% quartz, 8% calcium carbonate, 12% barium carbonate, 29% zinc oxide, 1.5%
With 2.5%
, taking by weighing that mixed grinding is evenly behind each material, sieving obtains the crystallization glaze, the fineness of crystallization glaze is less than 2% through the 10000-hole sieve excess;
(2), by weight percentage with 50% activated silica and 50% zinc oxide, take by weighing mix dry mixing evenly behind each material after, after 5~10 hours, after shrend, obtain crystal seed through 1100 ℃ of calcinings again;
(3), the crystal seed that makes of crystallization glaze that step (1) is made and step (2), both mixed grindings evenly can make golden yellow crystallization dry granular glaze.
A kind of using method of golden yellow crystallization dry granular glaze, the golden yellow crystallization dry granular glaze that (1), will make and water, ball milling, wherein ball milling is the diameter of the ball of zirconium white or aluminum oxide material, the fineness of the corresponding meeting of the diameter value of different ball milling ectocrine abrasive lapping, integral body is 1:(0.9~1 in proportion): (0.6~0.8) is through ball milling slurrying; (2) with the gained slurry, employing soaks glaze, be coated with glaze or glaze spraying mode to the base substrate glazing, glazing thickness is 1~1.5mm, behind the body drying after the glazing, under 1200 ℃~1350 ℃, fired 5~7 hours, slowly obtain the base substrate of golden yellow brilliant flower face after the cooling with stove, cost is low, suitability is high and very attractive in appearance.
Above-described, only be preferred embodiment of the present invention, can not limit scope of the invention process, every equalization of doing according to the present patent application claim changes and decorates, and all should still belong in the scope that the present invention contains.
Claims (3)
1. golden yellow crystallization dry granular glaze is characterized in that: may further comprise the steps:
(1), by weight percentage with 15%~22% feldspar, 20%~40% quartz, 6%~15% calcium carbonate, 6%~15% barium carbonate, 22%~50% zinc oxide, 0.7%~2.2%
With 0.7%~2.2%
, take by weighing that mixed grinding evenly behind each material, sieving obtains the crystallization glaze;
(2), by weight percentage with 20%~78% activated silica and 22%~80% zinc oxide, take by weighing mix dry mixing evenly behind each material after, after 5~10 hours, after shrend, obtain crystal seed through 1100 ℃ of calcinings again;
(3), the crystal seed that makes of crystallization glaze that step (1) is made and step (2), both mixed grindings evenly can make golden yellow crystallization dry granular glaze.
2. a kind of golden yellow crystallization dry granular glaze according to claim 1 is characterized in that: the fineness of described crystallization glaze for through the 10000-hole sieve excess less than 2%.
3. the using method of a kind of golden yellow crystallization dry granular glaze according to claim 1 and 2, it is characterized in that: (1), the golden yellow crystallization dry granular glaze that will make and water, ball milling, 1:(0.9~1 in proportion): (0.6~0.8) is through ball milling slurrying; (2), with the gained slurry, employing soaks glaze, be coated with glaze or glaze spraying mode to the base substrate glazing, and glazing thickness is 1~1.5mm, behind the body drying after the glazing, under 1200 ℃~1350 ℃, fired 5~7 hours, slowly obtain the golden yellow brilliant base substrate of spending face after the cooling with stove.