CN104478482B - A kind of Southern Song Guan kiln cream colour glaze - Google Patents
A kind of Southern Song Guan kiln cream colour glaze Download PDFInfo
- Publication number
- CN104478482B CN104478482B CN201410584727.9A CN201410584727A CN104478482B CN 104478482 B CN104478482 B CN 104478482B CN 201410584727 A CN201410584727 A CN 201410584727A CN 104478482 B CN104478482 B CN 104478482B
- Authority
- CN
- China
- Prior art keywords
- glaze
- kiln
- basic material
- glazing
- cream
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses a kind of Southern Song Guan kiln cream colour glaze, be made up of the raw material of following mass ratio: the cured stone 6-8% of porcelain stone 38-46%, rhombspar 10-14%, calcite 8-10%, Zijin soil 12-16%, feldspar 12-18% and dragon's fountain.Beneficial effect of the present invention is: the ceramic component that the cream-coloured glaze be fired into through present method makes has stronger opacifying property, and the beautiful texture of the glaze paint after burning till is strong, and bright-colored orthodox school, effectively adds the artistic effect of device; And manufacture craft is easy, easily realize, constant product quality, be conducive to the propagation and employment in market.
Description
Technical field
The present invention relates to a kind of Southern Song Guan kiln cream colour glaze.
Background technology
Southern Song Guan kiln is that first of Song dynasty " official, brother, you, fixed, an ancient unit of weight " five your name's kilns, its distinguished service is mainly manifested in the aspects such as technique, technology, type system, art.It inherits the technique tradition of more kiln, absorbs the device shape design art of all the kiln in the north, merges southern skill north skill; Due to the preparation of its glaze, the updating of glazing and firing technology; the glaze layer of product is thickeied; glaze colours is soft; sparkling and crystal-clear moist, blue or green green as beautiful, wherein; especially the most beautiful with the glaze colours of " pale blue ", " bluish white ", " cream-coloured glaze "; wherein pale blue, the moon white glaze be all produce to burn till in normal reduction atmosphere, only cream-coloured glaze be same pale blue, bluish white glaze within the same kiln same time, the result of kiln position, the local product generation transmutation produced because local atmosphere is different.
This kind of transmutation cream colour glaze is different from other beramic color yellow glazes completely, be celadon glaze in sintering process because insufficient the produced oxidation of furnace atmosphere is yellow, also known as transmutation cream colour glaze, therefore have its randomness, uncontrollability, the wooden earth kiln for fuel of imperial kiln bavin is fired especially in ancient times, is difficult to grasp its rule especially, thus ancient times, Southern Song Guan kiln cream colour glaze was accomplished something difficult and so deserve praise especially, complete vessel are very rare, and yellow is the true qualities of imperial family in ancient times, and thus cream-coloured glaze is extremely precious.
For the problem in existing correlation technique, at present effective solution is not yet proposed.
Summary of the invention
The object of this invention is to provide a kind of Southern Song Guan kiln cream colour glaze, to overcome currently available technology above shortcomings.
The object of the invention is to be achieved through the following technical solutions:
A kind of Southern Song Guan kiln cream colour glaze, is made up of the raw material of following mass ratio: the cured stone 6-8% of porcelain stone 38-46%, rhombspar 10-14%, calcite 8-10%, Zijin soil 12-16%, feldspar 12-18% and dragon's fountain.
A manufacture craft for Southern Song Guan kiln cream colour glaze, for the making of described cream-coloured glaze, and the manufacture craft of described cream-coloured glaze, comprises the following steps:
Step 1: ore dressing, chooses the basic material making cream-coloured glaze, comprises porcelain stone, rhombspar, calcite, Zijin soil, feldspar and the cured stone of dragon's fountain;
Step 2: the basic material chosen in step 1 is carried out first pulverization process respectively;
Step 3: the basic material after pulverizing in step 2 is carried out biscuiting process, and biscuiting temperature is about 1000 degree;
Step 4: the basic material after biscuiting process is carried out combination treatment according to above-mentioned mass ratio;
Step 5: the basic material after proportionally combination treatment is carried out water mill process again;
Step 6: utilize the device that sieves to carry out process of sieving, fineness requirement 180 order through the basic material of water mill process by after step 5;
Step 7: by after the basic material of step 6 fully mixes with moisture, to be used, wherein, the blending ratio of moisture and basic material is 50-52%;
Step 8: original work in-process vessel glaze method after biscuiting is carried out first time glazing treatment, glazing is wanted evenly, and ensures that the thickness of glaze is at 1-1.5mm, and wherein said glaze is through the mixed glaze of step 7;
Step 9: the work in-process vessel through glazing treatment are dried, the time is 24 hours, to ensure the degree of drying of vessel;
Step 10: the vessel after step 9 are carried out second time glazing treatment, carries out glazing by spray glazing, and glazing is wanted evenly, and makes the thickness of glaze at 1.9-2.1mm;
Step 11: again dried by the vessel of step 10, after vessel complete drying, carries out loading of kiln and formally burns till.
Further, the method for cooking of loading of kiln in described step 11 is oxidation sintering method, sintering procedure: first used time 6-8 hour, burns 500 degree with slow fire, after removing idiosome, glaze layer impurity and moisture completely, used time 4-5 hour again, is warmed up to 950 degree, insulation 1-2 hour, start the oxygenation that heats up, temperature is elevated to 1150 degree of oxygenations and terminates, then is warming up to about 1260 degree and burns till end, the now complete melting of glaze paint.
Further, the device that sieves in described step 6 comprises dotting punch sieve, wire gauze sieve, hand sieve, oscillating sieving machine, suspension type lay particular stress on powder shifter, hummer screen powder shifter.
Preferably, sieve described in the aperture of device is 180 orders.
Beneficial effect of the present invention is: the ceramic component that the cream-coloured glaze be fired into through present method makes has stronger opacifying property, and the beautiful texture of the glaze paint after burning till is strong, and bright-colored orthodox school, effectively adds the artistic effect of device; And manufacture craft is easy, constant product quality, easily realizes, and is conducive to the propagation and employment in market.
Embodiment
Be clearly and completely described the technical scheme in the embodiment of the present invention below, obviously, described embodiment is only the present invention's part embodiment, instead of whole embodiments.Based on the embodiment in the present invention, the every other embodiment that those of ordinary skill in the art obtain, all belongs to the scope of protection of the invention.
According to embodiments of the invention, provide a kind of Southern Song Guan kiln cream colour glaze formula and manufacture craft.
According to a kind of Southern Song Guan kiln cream colour glaze of the embodiment of the present invention, be made up of the raw material of following mass ratio: the cured stone 6-8% of porcelain stone 38-46%, rhombspar 10-14%, calcite 8-10%, Zijin soil 12-16%, feldspar 12-18% and dragon's fountain, wherein, described porcelain stone dragon's fountain old ore deposit in ancient times porcelain stone, described Zijin soil is dragon's fountain old ore deposit in ancient times Zijin soil.
Embodiment 1
A kind of Southern Song Guan kiln cream colour glaze, is made up of the raw material of following mass ratio: the cured stone 6% of porcelain stone 38%, rhombspar 10%, calcite 8%, Zijin soil 12%, feldspar 12% and dragon's fountain.
Embodiment 2
A kind of Southern Song Guan kiln cream colour glaze, is made up of the raw material of following mass ratio: the cured stone 7% of porcelain stone 42%, rhombspar 12%, calcite 9%, Zijin soil 14%, feldspar 16% and dragon's fountain.
Embodiment 3
A kind of Southern Song Guan kiln cream colour glaze, is made up of the raw material of following mass ratio: the cured stone 8% of porcelain stone 46%, rhombspar 14%, calcite 10%, Zijin soil 16%, feldspar 18% and dragon's fountain.
A manufacture craft for Southern Song Guan kiln cream colour glaze, comprises the following steps:
Step 1: ore dressing, chooses the basic material making cream-coloured glaze, comprises porcelain stone, rhombspar, calcite, Zijin soil, feldspar and the cured stone of dragon's fountain;
Step 2: the basic material chosen in step 1 is carried out first pulverization process respectively;
Step 3: the basic material after pulverizing in step 2 is carried out biscuiting process, and biscuiting temperature is about 1000 degree;
Step 4: the basic material after biscuiting process is carried out combination treatment according to above-mentioned mass ratio;
Step 5: the basic material after proportionally combination treatment is carried out water mill process again;
Step 6: utilize the device that sieves to carry out process of sieving by after step 5 through the basic material of water mill process, the aperture of the wherein said device that sieves is 180 orders;
Step 7: by after the basic material of step 6 fully mixes with moisture, to be used, wherein, the blending ratio of moisture and basic material is 50-52%;
Step 8: original work in-process vessel glaze method after biscuiting is carried out first time glazing treatment, glazing is wanted evenly, and ensures that the thickness of glaze is at 1-1.5mm, and wherein said glaze is through the mixed glaze of step 7;
Step 9: the work in-process vessel through glazing treatment are dried, the time is 24 hours, to ensure the degree of drying of vessel;
Step 10: the vessel after step 9 are carried out second time glazing treatment, carries out glazing by spray glazing, and glazing is wanted evenly, and makes the thickness of glaze at 1.9-2.1mm;
Step 11: again dried by the vessel of step 10, after vessel complete drying, carries out loading of kiln and formally burns till.
The method for cooking of loading of kiln in described step 11 is oxidation sintering method, sintering procedure: first used time 6-8 hour, 500 degree are burnt, after removing idiosome, glaze layer impurity and moisture completely, with 4-5 hour with slow fire, be warmed up to 950 degree, insulation 1-2 hour, start the oxygenation that heats up, temperature is elevated to 1150 degree of oxygenations and terminates, be warming up to about 1260 degree again and burn till end, the now complete melting of glaze paint; The device that sieves in described step 6 comprises dotting punch sieve, wire gauze sieve, hand sieve, oscillating sieving machine, suspension type lay particular stress on powder shifter or hummer screen powder shifter.
The ceramic component that the cream-coloured glaze be fired into through present method makes has stronger opacifying property, and the beautiful texture of the glaze paint after burning till is strong, and bright-colored orthodox school, effectively adds the artistic effect of device; And manufacture craft is simple, easily realizes, is conducive to the propagation and employment in market.
The foregoing is only preferred embodiment of the present invention, not in order to limit the present invention, within the spirit and principles in the present invention all, any amendment done, equivalent replacement, improvement etc., all should be included within protection scope of the present invention.
Claims (4)
1. a Southern Song Guan kiln cream colour glaze, is characterized in that, Southern Song Guan kiln cream colour glaze formula is made up of the raw material of following mass ratio: the cured stone 6-8% of porcelain stone 38-46%, rhombspar 10-14%, calcite 8-10%, Zijin soil 12-16%, feldspar 12-18% and dragon's fountain;
Southern Song Guan kiln cream colour glaze manufacture craft, comprises the following steps:
Step 1: ore dressing, chooses the basic material making cream-coloured glaze, comprises porcelain stone, rhombspar, calcite, Zijin soil, feldspar and the cured stone of dragon's fountain;
Step 2: the basic material chosen in step 1 is carried out first pulverization process respectively;
Step 3: the basic material after pulverizing in step 2 is carried out biscuiting process, and biscuiting temperature is 1000 degree;
Step 4: the basic material after biscuiting process is carried out combination treatment according to above-mentioned mass ratio;
Step 5: the basic material after proportionally combination treatment is carried out water mill process again;
Step 6: utilize the device that sieves to carry out process of sieving by after step 5 through the basic material of water mill process, fineness is 180 orders;
Step 7: by after the basic material of step 6 fully mixes with moisture, to be used, wherein, the blending ratio of moisture and basic material is 50-52%;
Step 8: carry out first time glazing treatment by for original work in-process vessel glaze method after biscuiting, glazing is wanted evenly, and ensures that the thickness of glaze is at 1-1.5mm, and wherein said glaze is through the mixed glaze of step 7;
Step 9: the work in-process vessel through glazing treatment are dried, the time is 24 hours, to ensure the degree of drying of vessel;
Step 10: the vessel after step 9 are carried out second time glazing treatment, carries out glazing by spray glazing, and glazing is wanted evenly, and makes the thickness of glaze at 1.9-2.1mm;
Step 11: again dried by the vessel of step 10, after vessel complete drying, carries out loading of kiln and formally burns till.
2. Southern Song Guan kiln cream colour glaze according to claim 1, is characterized in that, the method for cooking of loading of kiln in described step 11 is oxidation sintering method, sintering procedure: first used time 6-8 hour, 500 degree are burnt with slow fire, after removing idiosome, glaze layer impurity and moisture completely, then used time 4-5 hour, be warmed up to 950 degree, insulation 1-2 hour, start the oxygenation that heats up, temperature is elevated to 1150 degree of oxygenations and terminates, be warming up to 1260 degree again and burn till end, the now complete melting of glaze paint.
3. Southern Song Guan kiln according to claim 1 cream colour glaze, is characterized in that, the device that sieves in described step 6 comprises dotting punch sieve, wire gauze sieve, hand sieve, oscillating sieving machine, suspension type lay particular stress on powder shifter or hummer screen powder shifter.
4. Southern Song Guan kiln according to claim 3 cream colour glaze, is characterized in that, described in the sieve aperture of device be 180 orders.