CN104448707A - 一种易脱模的环氧树脂复合材料及其制作方法 - Google Patents
一种易脱模的环氧树脂复合材料及其制作方法 Download PDFInfo
- Publication number
- CN104448707A CN104448707A CN201410671673.XA CN201410671673A CN104448707A CN 104448707 A CN104448707 A CN 104448707A CN 201410671673 A CN201410671673 A CN 201410671673A CN 104448707 A CN104448707 A CN 104448707A
- Authority
- CN
- China
- Prior art keywords
- parts
- minute
- epoxy resin
- add
- hour
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种易脱模的环氧树脂复合材料，其特征在于，由下列重量份的原料制成：环氧树脂53-57、聚酰胺树脂10-12、纳米萤石粉1-3、地沥青5-7、蔗渣纤维3-4、二硫化钼1.2-2.3、防老剂ODA0.7-1.3、4,4’-二苯基甲烷二异氰酸酯7-9、硬酯酸单甘油酯6-8、马来酸12-14、聚酯多元醇9-11、十二烷基缩水甘油醚15-18、安息香双甲醚4-7、沉淀硫酸钡2.1-3.4、助剂3-6；本发明添加二硫化钼是一种很好的润滑剂，同时还添加纳米萤石粉、地沥青等，制得的环氧树脂易脱模，具有粘度高、耐高温、防腐防辐射等优点。
Description
技术领域
本发明涉及高分子复合材料领域，具体涉及一种易脱模的环氧树脂复合材料及其制作方法。
背景技术
环氧树脂是泛指分子中含有两个或两个以上活泼环氧基团的有机化合物，它们可与多种类型的固化剂发生交联反应而形成不溶、不熔的具有三向网状结构的高聚物。具有优良的电绝缘、机械、粘接、耐化学腐蚀性能及良好的物理、化学性能，广泛用做层压料、粘结剂、涂料等，在轮船、汽车、航空航天等领域越来越受到重视。
目前，环氧树脂被作为复合材料的基体，表现出很多问题，如硬度低、绝缘性差、受热软化、易分层、传质传热困难、气味大等缺点，需要改进环氧树脂的制备工艺。
发明内容
本发明的目的就是提供一种易脱模的环氧树脂复合材料及其制作方法，以克服现有技术的不足。
本发明的目的是这样实现的：
一种易脱模的环氧树脂复合材料，其特征在于，由下列重量份的原料制成：环氧树脂53-57、聚酰胺树脂10-12、纳米萤石粉1-3、地沥青5-7、蔗渣纤维3-4、二硫化钼1.2-2.3、防老剂ODA 0.7-1.3、4,4’-二苯基甲烷二异氰酸酯7-9、硬酯酸单甘油酯6-8、马来酸12-14、聚酯多元醇9-11、十二烷基缩水甘油醚15-18、安息香双甲醚4-7、沉淀硫酸钡2.1-3.4、助剂3-6。
所述的助剂由下列重量份原料制成：甲基丙烯酸酯3-4、四丁基溴化铵1-2、滑石粉1-3、纳米氧化锌2-4、硬脂酸钡1.1-2.5、三聚磷酸铝0.6-0.8、甲基异噻唑啉酮0.4-0.9、聚氧化乙烯2.1-3.5、聚乙二醇4-7、二苯甲酮0.7-1.7、丙烯酸乳液16-19、丙二醇苯醚8-10、适量水，其制备方法为：将四丁基溴化铵、聚氧化乙烯、聚乙二醇溶于热水搅拌10-15分钟，加入经煅烧处理后的滑石粉和纳米氧化锌研磨30-40分钟，喷雾干燥后加入硬脂酸钡、三聚磷酸铝研磨20-30分钟后超声波分散于丙烯酸乳液中，再加入丙二醇苯醚、二苯甲酮、甲基异噻唑啉酮一起搅拌30-40分钟，升温至175-195℃，保温3-5小时，将反应产物降温至85-95℃，加入甲基丙烯酸酯搅拌1-2小时即得。
所述的一种易脱模的环氧树脂复合材料的制备方法，其特征在于包括以下步骤：
（1）将纳米萤石粉于450-560℃下煅烧处理1-2小时，取出冷却加入地沥青、蔗渣纤维、二硫化钼研磨30-40分钟，然后加入环氧树脂，超声研磨处理20-40分钟；
（2）将聚酯多元醇、十二烷基缩水甘油醚放入反应釜中混匀，加入马来酸、防老剂ODA搅拌10-15分钟，升温至145-160℃，保温搅拌4-6小时；
（3）将步骤（2）反应产物降温至75-90℃，加入步骤（1）反应物料、4,4’-二苯基甲烷二异氰酸酯、硬酯酸单甘油酯搅拌30-40分钟，加入安息香双甲醚唑及其他剩余成分搅拌10-15分钟，在100-110℃下进行固化4-5小时即得。
本发明有以下有益效果：本发明添加二硫化钼是一种很好的润滑剂，同时还添加纳米萤石粉、地沥青等，制得的环氧树脂易脱模，具有粘度高、耐高温、防腐防辐射等优点。
具体实施方式
所述的一种易脱模的环氧树脂复合材料，其特征在于，由下列重量份的原料制成：环氧树脂56、聚酰胺树脂11、纳米萤石粉1、地沥青7、蔗渣纤维3、二硫化钼1.6、防老剂ODA 1.3、4,4’-二苯基甲烷二异氰酸酯8、硬酯酸单甘油酯6、马来酸13、聚酯多元醇9、十二烷基缩水甘油醚15、安息香双甲醚5、沉淀硫酸钡2.1、助剂5。
所述的助剂由下列重量份原料制成：甲基丙烯酸酯4、四丁基溴化铵1、滑石粉2、纳米氧化锌4、硬脂酸钡1.9、三聚磷酸铝0.7、甲基异噻唑啉酮0.6、聚氧化乙烯2.7、聚乙二醇7、二苯甲酮1.7、丙烯酸乳液18、丙二醇苯醚8、适量水，其制备方法为：将四丁基溴化铵、聚氧化乙烯、聚乙二醇溶于热水搅拌10-15分钟，加入经煅烧处理后的滑石粉和纳米氧化锌研磨30-40分钟，喷雾干燥后加入硬脂酸钡、三聚磷酸铝研磨20-30分钟后超声波分散于丙烯酸乳液中，再加入丙二醇苯醚、二苯甲酮、甲基异噻唑啉酮一起搅拌30-40分钟，升温至175-195℃，保温3-5小时，将反应产物降温至85-95℃，加入甲基丙烯酸酯搅拌1-2小时即得。
制作方法包括以下步骤：
（1）将纳米萤石粉于450-560℃下煅烧处理1-2小时，取出冷却加入地沥青、蔗渣纤维、二硫化钼研磨30-40分钟，然后加入环氧树脂，超声研磨处理20-40分钟；
（2）将聚酯多元醇、十二烷基缩水甘油醚放入反应釜中混匀，加入马来酸、防老剂ODA搅拌10-15分钟，升温至145-160℃，保温搅拌4-6小时；
（3）将步骤（2）反应产物降温至75-90℃，加入步骤（1）反应物料、4,4’-二苯基甲烷二异氰酸酯、硬酯酸单甘油酯搅拌30-40分钟，加入安息香双甲醚唑及其他剩余成分搅拌10-15分钟，在100-110℃下进行固化4-5小时即得。
使用本发明生产的环氧树脂复合材料的技术参数指标如下：
（1）导热率（Wm-1K-1）：3.179；
（2）抗重强度：112Mpa。
Claims (2)
1.一种易脱模的环氧树脂复合材料，其特征在于，由下列重量份的原料制成：环氧树脂53-57、聚酰胺树脂10-12、纳米萤石粉1-3、地沥青5-7、蔗渣纤维3-4、二硫化钼1.2-2.3、防老剂ODA 0.7-1.3、4,4’-二苯基甲烷二异氰酸酯7-9、硬酯酸单甘油酯6-8、马来酸12-14、聚酯多元醇9-11、十二烷基缩水甘油醚15-18、安息香双甲醚4-7、沉淀硫酸钡2.1-3.4、助剂3-6；所述的助剂由下列重量份原料制成：甲基丙烯酸酯3-4、四丁基溴化铵1-2、滑石粉1-3、纳米氧化锌2-4、硬脂酸钡1.1-2.5、三聚磷酸铝0.6-0.8、甲基异噻唑啉酮0.4-0.9、聚氧化乙烯2.1-3.5、聚乙二醇4-7、二苯甲酮0.7-1.7、丙烯酸乳液16-19、丙二醇苯醚8-10、适量水，其制备方法为：将四丁基溴化铵、聚氧化乙烯、聚乙二醇溶于热水搅拌10-15分钟，加入经煅烧处理后的滑石粉和纳米氧化锌研磨30-40分钟，喷雾干燥后加入硬脂酸钡、三聚磷酸铝研磨20-30分钟后超声波分散于丙烯酸乳液中，再加入丙二醇苯醚、二苯甲酮、甲基异噻唑啉酮一起搅拌30-40分钟，升温至175-195℃，保温3-5小时，将反应产物降温至85-95℃，加入甲基丙烯酸酯搅拌1-2小时即得。
2.根据权利要求1所述的一种易脱模的环氧树脂复合材料的制作方法，其特征在于包括以下步骤：
（1）将纳米萤石粉于450-560℃下煅烧处理1-2小时，取出冷却加入地沥青、蔗渣纤维、二硫化钼研磨30-40分钟，然后加入环氧树脂，超声研磨处理20-40分钟；
（2）将聚酯多元醇、十二烷基缩水甘油醚放入反应釜中混匀，加入马来酸、防老剂ODA搅拌10-15分钟，升温至145-160℃，保温搅拌4-6小时；
（3）将步骤（2）反应产物降温至75-90℃，加入步骤（1）反应物料、4,4’-二苯基甲烷二异氰酸酯、硬酯酸单甘油酯搅拌30-40分钟，加入安息香双甲醚唑及其他剩余成分搅拌10-15分钟，在100-110℃下进行固化4-5小时即得。