CN104446263A - 一种保温复合发泡水泥板及其制备方法 - Google Patents

一种保温复合发泡水泥板及其制备方法 Download PDF

Info

Publication number
CN104446263A
CN104446263A CN201410765672.1A CN201410765672A CN104446263A CN 104446263 A CN104446263 A CN 104446263A CN 201410765672 A CN201410765672 A CN 201410765672A CN 104446263 A CN104446263 A CN 104446263A
Authority
CN
China
Prior art keywords
parts
foam concrete
composite foam
concrete plate
insulation composite
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410765672.1A
Other languages
English (en)
Inventor
朱万旭
马倩
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Guangxi University of Science and Technology
Original Assignee
Guangxi University of Science and Technology
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Guangxi University of Science and Technology filed Critical Guangxi University of Science and Technology
Priority to CN201410765672.1A priority Critical patent/CN104446263A/zh
Publication of CN104446263A publication Critical patent/CN104446263A/zh
Pending legal-status Critical Current

Abstract

本发明提供一种保温复合发泡水泥板，所述水泥板由以下质量份数的各组分组成：硅酸盐水泥140-160份、粉煤灰20-30份、石膏3-5份、聚乙烯纤维0.2-0.4份、pp纤维0.1-0.3份、偏硅酸钠0.4-0.6份、硬脂酸钠0.2-0.4份、硫酸铝2-3份、氯化钙0.4-0.6份、发泡剂1-1.5份、稳泡剂0.3-0.5份、憎水剂3-6份、水130-150份。本发明还提供其制备方法。本发明的保温复合发泡水泥板抗拉强度和抗压强度高，外墙保温施工时不易开裂，发泡板内部孔径大小一致，具有很好的保温效果和抗燃效果。

Description

一种保温复合发泡水泥板及其制备方法
技术领域
本发明属于外墙外保温系统技术领域，具体涉及一种保温复合发泡水泥板。
背景技术
复合发泡水泥板是一种经发泡、养护、切割等工艺制成的闭孔轻质无机发泡保温板，可用于房屋建筑的外墙外保温系统施工工程，替代原先普遍使用的聚苯板或挤塑板为代表的有机可燃性保温材料。
现有的复合发泡水泥板的缺陷有以下几点：大部分产品用硫铝酸盐水泥为主材，抗拉强度、抗压强度低，遇水粉化严重，脆性大，外墙保温施工时易开裂，发泡板的内部孔泡较大且孔径不一，保温性能难以达标。
发明内容
为了解决现有技术中存在的问题，本发明提供了一种保温复合发泡水泥板；为此，本发明还提供其制备方法。
本发明提供一种保温复合发泡水泥板，所述水泥板由以下质量份数的各组分组成：硅酸盐水泥140-160份、粉煤灰20-30份、石膏3-5份、聚乙烯纤维0.2-0.4份、pp纤维0.1-0.3份、偏硅酸钠0.4-0.6份、硬脂酸钠0.2-0.4份、硫酸铝2-3份、氯化钙0.4-0.6份、发泡剂1-1.5份、稳泡剂0.3-0.5份、憎水剂3-6份、水130-150份。
优选地，所述憎水剂为有机硅憎水剂。
优选地，所述发泡剂为浓度为35%的H2O2发泡剂。
优选地，所述稳泡剂为十二烷基甜菜碱。
优选地，所述pp纤维为5-6mm的pp纤维。
本发明还提供上述保温复合发泡水泥板的制备方法，是按上述各组分的重量比备料，在粉料搅拌机中先加入硅酸盐水泥、粉煤灰、石膏、聚乙烯纤维、pp纤维、偏硅酸钠、硬脂酸钠和水充分搅拌制浆，再加入硫酸铝、氯化钙、发泡剂、稳泡剂和憎水剂充分搅拌混合，注入模具，不加以任何压力，静停发泡，在常温下，24小时后，脱模，再自然养护30小时，即可。
本发明的保温复合发泡水泥板抗拉强度和抗压强度高，外墙保温施工时不易开裂，发泡板内部孔径大小一致，具有很好的保温效果和抗燃效果。
具体实施方式
以下的实施例便于更好地理解本发明，但并不限定本发明。下述实施例中的实验方法，如无特殊说明，均为常规方法。
实施例1
本发明的保温复合发泡水泥板的配方如下：
硅酸盐水泥150kg、粉煤灰25kg、石膏4kg、聚乙烯纤维0.3kg、pp纤维0.2kg、偏硅酸钠0.5kg、硬脂酸钠0.3kg、硫酸铝2.5kg、氯化钙0.5kg、发泡剂1.2kg、稳泡剂0.4kg、憎水剂5kg、水140kg。
本发明的保温复合发泡水泥板的制备方法为：
按上述各组分的重量比备料，在粉料搅拌机中先加入硅酸盐水泥、粉煤灰、石膏、聚乙烯纤维、pp纤维、偏硅酸钠、硬脂酸钠和水充分搅拌制浆，再加入硫酸铝、氯化钙、发泡剂、稳泡剂和憎水剂充分搅拌混合，注入模具，不加以任何压力，静停发泡，在常温下，24小时后，脱模，再自然养护30小时，即可。
实施例2
本发明的保温复合发泡水泥板的配方如下：
硅酸盐水泥140kg、粉煤灰20kg、石膏3kg、聚乙烯纤维0.4kg、pp纤维0.3kg、偏硅酸钠0.4kg、硬脂酸钠0.4kg、硫酸铝2kg、氯化钙0.4kg、发泡剂1.5kg、稳泡剂0.5kg、憎水剂6kg、水130kg。
本实施例的保温复合发泡水泥板的制备方法与实施例1相同。
实施例3
本发明的保温复合发泡水泥板的配方如下：
硅酸盐水泥160kg、粉煤灰30kg、石膏5kg、聚乙烯纤维0.2kg、pp纤维0.1kg、偏硅酸钠0.6kg、硬脂酸钠0.2kg、硫酸铝3kg、氯化钙0.6kg、发泡剂1kg、稳泡剂0.3kg、憎水剂3kg、水150kg。
本实施例的保温复合发泡水泥板的制备方法与实施例1相同。
最后应说明的是：以上所述仅为本发明的优选实施例而已，并不用于限制本发明，尽管参照前述实施例对本发明进行了详细的说明，对于本领域的技术人员来说，其依然可以对前述各实施例所记载的技术方案进行修改，或者对其中部分技术特征进行等同替换。凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。

Claims (6)

1.一种保温复合发泡水泥板，其特征在于：所述水泥板由以下质量份数的各组分组成：硅酸盐水泥140-160份、粉煤灰20-30份、石膏3-5份、聚乙烯纤维0.2-0.4份、pp纤维0.1-0.3份、偏硅酸钠0.4-0.6份、硬脂酸钠0.2-0.4份、硫酸铝2-3份、氯化钙0.4-0.6份、发泡剂1-1.5份、稳泡剂0.3-0.5份、憎水剂3-6份、水130-150份。
2.根据权利要求1所述的保温复合发泡水泥板，其特征在于：所述憎水剂为有机硅憎水剂。
3.根据权利要求1所述的保温复合发泡水泥板，其特征在于：所述发泡剂为浓度为35%的H2O2发泡剂。
4.根据权利要求1所述的保温复合发泡水泥板，其特征在于：所述稳泡剂为十二烷基甜菜碱。
5.根据权利要求1所述的保温复合发泡水泥板，其特征在于：所述pp纤维为5-6mm的pp纤维。
6.权利要求1-5任一所述的保温复合发泡水泥板的制备方法，其特征在于：是按上述各组分的重量比备料，在粉料搅拌机中先加入硅酸盐水泥、粉煤灰、石膏、聚乙烯纤维、pp纤维、偏硅酸钠、硬脂酸钠和水充分搅拌制浆，再加入硫酸铝、氯化钙、发泡剂、稳泡剂和憎水剂充分搅拌混合，注入模具，不加以任何压力，静停发泡，在常温下，24小时后，脱模，再自然养护30小时，即可。
CN201410765672.1A 2014-12-15 2014-12-15 一种保温复合发泡水泥板及其制备方法 Pending CN104446263A (zh)