CN104496531B - 一种抗冻发泡水泥保温板及其制备方法 - Google Patents

一种抗冻发泡水泥保温板及其制备方法 Download PDF

Info

Publication number
CN104496531B
CN104496531B CN201410767248.0A CN201410767248A CN104496531B CN 104496531 B CN104496531 B CN 104496531B CN 201410767248 A CN201410767248 A CN 201410767248A CN 104496531 B CN104496531 B CN 104496531B
Authority
CN
China
Prior art keywords
insulation board
freeze proof
cement insulation
foaming agent
proof cement
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201410767248.0A
Other languages
English (en)
Other versions
CN104496531A (zh
Inventor
朱万旭
马倩
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Guangxi University of Science and Technology
Original Assignee
Guangxi University of Science and Technology
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Guangxi University of Science and Technology filed Critical Guangxi University of Science and Technology
Priority to CN201410767248.0A priority Critical patent/CN104496531B/zh
Publication of CN104496531A publication Critical patent/CN104496531A/zh
Application granted granted Critical
Publication of CN104496531B publication Critical patent/CN104496531B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明提供一种抗冻发泡水泥保温板，所述保温板由以下质量份数的各组分组成：硅酸盐水泥140-160份、粉煤灰15-20份、氯化钠0.5-0.8份、硝酸钾0.4-0.8份、石英砂0.1-0.3份、十二烷基磺酸钠2-3份、聚丙烯纤维1-2份、硼酸钠0.2-0.4份、硬脂酸钙0.1-0.3份、发泡剂1-1.5份、稳泡剂0.3-0.5份、憎水剂3-6份、水110-120份。本发明还提供其制备方法。本发明的抗冻发泡水泥保温板具有良好的保温效果，同时，具有良好的抗冻效果，在低温下不开裂，遇水不粉化，能够应用于北方寒冷的天气。

Description

一种抗冻发泡水泥保温板及其制备方法
技术领域
本发明涉及一种抗冻发泡水泥保温板。
背景技术
发泡水泥保温板是一种经发泡、养护、切割等工艺制成的闭孔轻质无机发泡保温板，可用于房屋建筑的外墙外保温系统施工工程，替代原先普遍使用的聚苯板或挤塑板为代表的有机可燃性保温材料。现有的发泡水泥保温板抗冻效果不佳。
发明内容
本发明提供了一种抗冻发泡水泥保温板，具备良好的抗冻效果；为此，本发明还提供其制备方法。
本发明提供一种抗冻发泡水泥保温板，所述保温板由以下质量份数的各组分组成：硅酸盐水泥140-160份、粉煤灰15-20份、氯化钠0.5-0.8份、硝酸钾0.4-0.8份、石英砂0.1-0.3份、十二烷基磺酸钠2-3份、聚丙烯纤维1-2份、硼酸钠0.2-0.4份、硬脂酸钙0.1-0.3份、发泡剂1-1.5份、稳泡剂0.3-0.5份、憎水剂3-6份、水110-120份。
优选地，所述保温板由以下质量份数的各组分组成：硅酸盐水泥150份、粉煤灰18份、氯化钠0.4份、硝酸钾0.5份、石英砂0.2份、十二烷基磺酸钠2.5份、聚丙烯纤维1.5份、硼酸钠0.3份、硬脂酸钙0.2份、发泡剂1.2份、稳泡剂0.4份、憎水剂5份、水115份。
优选地，所述憎水剂为有机硅憎水剂。
优选地，所述发泡剂为浓度为27.5%的H2O2发泡剂。
优选地，所述稳泡剂为十二烷基甜菜碱。
本发明还提供上述抗冻发泡水泥保温板的制备方法，步骤如下：是按上述各组分的重量比备料，在粉料搅拌机中先加入硅酸盐水泥、粉煤灰、氯化钠、硝酸钾、石英砂、十二烷基磺酸钠、聚丙烯纤维1-2份、硼酸钠0.2-0.4份、硬脂酸钙和水充分搅拌制浆，再加入发泡剂、稳泡剂和憎水剂充分搅拌混合，注入模具，不加以任何压力，静停发泡，在常温下，24小时后，脱模，再自然养护30小时，即可。
本发明的抗冻发泡水泥保温板具有良好的保温效果，同时，具有良好的抗冻效果，在低温下不开裂，遇水不粉化，能够应用于北方寒冷的天气。
具体实施方式
以下的实施例便于更好地理解本发明，但并不限定本发明。下述实施例中的实验方法，如无特殊说明，均为常规方法。
实施例1
本发明的抗冻发泡水泥保温板的配方如下：
硅酸盐水泥150kg、粉煤灰18kg、氯化钠0.4kg、硝酸钾0.5kg、石英砂0.2kg、十二烷基磺酸钠2.5kg、聚丙烯纤维1.5kg、硼酸钠0.3kg、硬脂酸钙0.2kg、发泡剂1.2kg、稳泡剂0.4kg、憎水剂5kg、水115kg。
本发明的抗冻发泡水泥保温板的制备方法如下：
按上述各组分的重量比备料，在粉料搅拌机中先加入硅酸盐水泥、粉煤灰、氯化钠、硝酸钾、石英砂、十二烷基磺酸钠、聚丙烯纤维、硼酸钠、硬脂酸钙和水充分搅拌制浆，再加入发泡剂、稳泡剂和憎水剂充分搅拌混合，注入模具，不加以任何压力，静停发泡，在常温下，24小时后，脱模，再自然养护30小时，即可。
实施例2
本发明的抗冻发泡水泥保温板的配方如下：
硅酸盐水泥140kg、粉煤灰15kg、氯化钠0.5kg、硝酸钾0.8kg、石英砂0.3kg、十二烷基磺酸钠2kg、聚丙烯纤维1kg、硼酸钠0.4kg、硬脂酸钙0.3kg、发泡剂1kg、稳泡剂0.5kg、憎水剂6kg、水120kg。
本实施例的发泡水泥保温板的制备方法与实施例1相同。
实施例3
本发明的抗冻发泡水泥保温板的配方如下：
硅酸盐水泥160kg、粉煤灰20kg、氯化钠0.8kg、硝酸钾0.4kg、石英砂0.1kg、十二烷基磺酸钠3kg、聚丙烯纤维2kg、硼酸钠0.2kg、硬脂酸钙0.1kg、发泡剂1.5kg、稳泡剂0.3kg、憎水剂3kg、水110kg。
本实施例的发泡水泥保温板的制备方法与实施例1相同。
最后应说明的是：以上所述仅为本发明的优选实施例而已，并不用于限制本发明，尽管参照前述实施例对本发明进行了详细的说明，对于本领域的技术人员来说，其依然可以对前述各实施例所记载的技术方案进行修改，或者对其中部分技术特征进行等同替换。凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。

Claims (5)

1.一种抗冻发泡水泥保温板，其特征在于：所述保温板由以下质量份数的各组分组成：硅酸盐水泥140-160份、粉煤灰15-20份、氯化钠0.5-0.8份、硝酸钾0.4-0.8份、石英砂0.1-0.3份、十二烷基磺酸钠2-3份、聚丙烯纤维1-2份、硼酸钠0.2-0.4份、硬脂酸钙0.1-0.3份、发泡剂1-1.5份、稳泡剂0.3-0.5份、憎水剂3-6份、水110-120份；所述抗冻发泡水泥保温板的制备方法为：按上述各组分的重量比备料，在粉料搅拌机中先加入硅酸盐水泥、粉煤灰、氯化钠、硝酸钾、石英砂、十二烷基磺酸钠、聚丙烯纤维1-2份、硼酸钠0.2-0.4份、硬脂酸钙和水充分搅拌制浆，再加入发泡剂、稳泡剂和憎水剂充分搅拌混合，注入模具，不加以任何压力，静停发泡，在常温下，24小时后，脱模，再自然养护30小时，即可。
2.根据权利要求1所述的抗冻发泡水泥保温板，其特征在于：所述憎水剂为有机硅憎水剂。
3.根据权利要求1所述的抗冻发泡水泥保温板，其特征在于：所述发泡剂为浓度为27.5%的H2O2发泡剂。
4.根据权利要求1所述的抗冻发泡水泥保温板，其特征在于：所述稳泡剂为十二烷基甜菜碱。
5.权利要求1-4任一所述的抗冻发泡水泥保温板的制备方法，其特征在于：步骤如下：是按上述各组分的重量比备料，在粉料搅拌机中先加入硅酸盐水泥、粉煤灰、氯化钠、硝酸钾、石英砂、十二烷基磺酸钠、聚丙烯纤维1-2份、硼酸钠0.2-0.4份、硬脂酸钙和水充分搅拌制浆，再加入发泡剂、稳泡剂和憎水剂充分搅拌混合，注入模具，不加以任何压力，静停发泡，在常温下，24小时后，脱模，再自然养护30小时，即可。
CN201410767248.0A 2014-12-15 2014-12-15 一种抗冻发泡水泥保温板及其制备方法 Expired - Fee Related CN104496531B (zh)