CN104420215A - 亚麻织物的柔软化整理方法 - Google Patents

亚麻织物的柔软化整理方法 Download PDF

Info

Publication number
CN104420215A
CN104420215A CN201310401798.6A CN201310401798A CN104420215A CN 104420215 A CN104420215 A CN 104420215A CN 201310401798 A CN201310401798 A CN 201310401798A CN 104420215 A CN104420215 A CN 104420215A
Authority
CN
China
Prior art keywords
treatment
sodolin
carry out
acetic acid
temperature conditions
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310401798.6A
Other languages
English (en)
Inventor
王玉英
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Qingdao Singao High New Coated and Laminated Fabric Co Ltd
Original Assignee
Qingdao Singao High New Coated and Laminated Fabric Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Qingdao Singao High New Coated and Laminated Fabric Co Ltd filed Critical Qingdao Singao High New Coated and Laminated Fabric Co Ltd
Priority to CN201310401798.6A priority Critical patent/CN104420215A/zh
Publication of CN104420215A publication Critical patent/CN104420215A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种亚麻织物的柔软化整理方法，采用醋酸处理液进行处理，醋酸处理液的浓度为2g/L，在室温下处理5min—10min，之后进行酶处理，酶剂用量为0.5g/L-1.5g/L，浴比1：30，在50℃-60℃温度条件下处理40min-60min，并在处理过程中用醋酸调节pH为4.0-5.0；之后采用柔软剂处理液进行亚麻织物柔软处理，柔软剂的浓度为10g/L-20g/L，浴比1：15，在60℃温度条件下处理15min-20min，之后取出，在130℃-150℃温度条件下烘干；最后采用预缩机进行预缩处理即可。

Description

亚麻织物的柔软化整理方法
 
技术领域
本发明属于亚麻织物功能性处理技术领域，具体涉及一种亚麻织物的柔软化整理方法。
 
背景技术
几年来随着亚麻产品国际、国内市场需求的增长，受市场规律的调节作用，亚麻纺织业出现了蓬勃发展的大好局面。亚麻纺纱、织造工艺从摸索、完善，逐渐走向成熟，工艺技术水平有了长足的发展，特别是与亚麻工艺、技术相配套的新型、高档次设备的引进，亚麻纱、亚麻布的产品质量和档次有了飞跃性的提高。但是麻类织物纤维较粗、杨氏模易较大，因而刚硬度较强。并且由于纤维间抱合力弱、可纺性低，在加工过程中容易生成毛羽，因而染色后手感粗硬。
 
发明内容
为了克服现有技术领域存在的上述技术问题，本发明的目的在于，提供一种亚麻织物的柔软化整理方法，解决亚麻织物手感粗硬的问题。
本发明提供的亚麻织物的柔软化整理方法包括以下步骤：（一）烧毛，彻底的去除织物表面的毛羽；（二）纤维素酶预处理：采用醋酸处理液进行处理，醋酸处理液的浓度为2g/L，在室温下处理5min—10min,之后进行酶处理，酶剂用量为0.5 g/L -1.5 g/L，浴比1：30，在50℃-60℃温度条件下处理40min -60min，并在处理过程中用醋酸调节pH为4.0-5.0；（三）柔软处理：采用柔软剂处理液进行亚麻织物柔软处理，柔软剂的浓度为10 g/L -20 g/L，浴比1：15，在60℃温度条件下处理15min -20min，之后取出，在130℃-150℃温度条件下烘干；（四）采用预缩机进行预缩处理即可。
本发明提供的亚麻织物的柔软化整理方法，其有益效果在于，在烧毛工序中，彻底去除织物表面的毛羽，有效避免粗硬的毛羽根部，影响织物手感；纤维素酶能催化纤维素的B-1.4葡萄苷健的水解，有效改善亚麻织物手感；经过柔软化处理的亚麻织物手感也会柔软而且富有弹性，解决亚麻织物手感粗硬的问题。
 
具体实施方式
下面结合一个实施例，对本发明提供的亚麻织物的柔软化整理方法进行详细的说明。
 
实施例
本实施例的亚麻织物的柔软化整理方法包括以下步骤：（一）烧毛，彻底的去除织物表面的毛羽；（二）纤维素酶预处理：采用醋酸处理液进行处理，醋酸处理液的浓度为2g/L，在室温下处理5min,之后进行酶处理，酶剂用量为1 g/L，浴比1：30，在60℃温度条件下处理50min，并在处理过程中用醋酸调节pH为5.0；（三）柔软处理：采用柔软剂处理液进行亚麻织物柔软处理，柔软剂的浓度为20 g/L，浴比1：15，在60℃温度条件下处理15min，之后取出，在150℃温度条件下烘干；（四）采用预缩机进行预缩处理即可。

Claims (1)

1.一种亚麻织物的柔软化整理方法，其特征在于：包括以下步骤：（一）烧毛，彻底的去除织物表面的毛羽；（二）纤维素酶预处理：采用醋酸处理液进行处理，醋酸处理液的浓度为2g/L，在室温下处理5min—10min,之后进行酶处理，酶剂用量为0.5 g/L -1.5 g/L，浴比1：30，在50℃-60℃温度条件下处理40min -60min，并在处理过程中用醋酸调节pH为4.0-5.0；（三）柔软处理：采用柔软剂处理液进行亚麻织物柔软处理，柔软剂的浓度为10 g/L -20 g/L，浴比1：15，在60℃温度条件下处理15min -20min，之后取出，在130℃-150℃温度条件下烘干；（四）采用预缩机进行预缩处理即可。
CN201310401798.6A 2013-09-06 2013-09-06 亚麻织物的柔软化整理方法 Pending CN104420215A (zh)