CN104403153A - 一种减振橡胶 - Google Patents

一种减振橡胶 Download PDF

Info

Publication number
CN104403153A
CN104403153A CN201410651353.8A CN201410651353A CN104403153A CN 104403153 A CN104403153 A CN 104403153A CN 201410651353 A CN201410651353 A CN 201410651353A CN 104403153 A CN104403153 A CN 104403153A
Authority
CN
China
Prior art keywords
parts
rubber
vibration isolation
vibration damping
damping rubber
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410651353.8A
Other languages
English (en)
Inventor
马深同
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
LIUZHOU TONGJIN AUTO PART MANUFACTURING Co Ltd
Original Assignee
LIUZHOU TONGJIN AUTO PART MANUFACTURING Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by LIUZHOU TONGJIN AUTO PART MANUFACTURING Co Ltd filed Critical LIUZHOU TONGJIN AUTO PART MANUFACTURING Co Ltd
Priority to CN201410651353.8A priority Critical patent/CN104403153A/zh
Publication of CN104403153A publication Critical patent/CN104403153A/zh
Pending legal-status Critical Current

Abstract

本发明公开一种减振橡胶，按重量份数计，该减振橡胶包括如下成分：丁苯橡胶100份，天然橡胶20-30份，二氧化硅20-60份，辛二酸二乙酯2-20份，防老剂1-4份，硫化剂1-5份、促进剂1-5份，交联剂3-8份。与现有减振橡胶相比，本发明的减振橡胶的蠕变特性能得到明显改善。

Description

一种减振橡胶
技术领域
本发明涉及一种减振橡胶。
背景技术
为降低机动车的振动及噪音，一般情况下是采用减振橡胶来达到该目的，对于这类减振橡胶具有良好的蠕变特性，否则将直接影响产品的寿命及机辆安全，然而现有减振橡胶的压缩蠕变指数一般达到15-30%。
发明内容
本发明要解决的技术问题是克服现有的缺陷，提供了一种减振橡胶。
为了解决上述技术问题，本发明提供了如下的技术方案：
一种减振橡胶，按重量份数计，包括如下成分：
丁苯橡胶100份，天然橡胶20-30份，二氧化硅20-60份，辛二酸二乙酯2-20份，防老剂1-4份，硫化剂1-5份、促进剂1-5份，交联剂3-8份。
进一步，所述减振橡胶还含有防护蜡1-3份和硬脂酸1-3份。
与现有减振橡胶相比，本发明的减振橡胶的蠕变特性能得到明显改善。
具体实施方式
以下对本发明的优选实施例进行说明，应当理解，此处所描述的优选实施例仅用于说明和解释本发明，并不用于限定本发明。
实施例1
按重量计，将丁苯橡胶100份和天然橡胶20份，在炼胶机上塑炼10分钟后，再加入二氧化硅（比表面积为160-180m2/g）20份、辛二酸二乙酯2份、防老剂4010NA 1份、硫磺1份、促进剂TMTD 1份、交联剂氧化锌 3份、防护蜡石蜡1份和硬脂酸1份，在50℃下混炼50分钟后，挤出成型，在130℃下硫化50分钟，得到减振橡胶，压缩蠕变指数：7.5%。
实施例2
按重量计，将丁苯橡胶100份和天然橡胶25份在炼胶机上塑炼15分钟后，再加入二氧化硅（比表面积为160-180m2/g）60份、辛二酸二乙酯10份、防老剂4010NA 3份、硫磺3份、促进剂TMTD 4份、交联剂氧化锌 5份、防护蜡石蜡2份和硬脂酸2份，在55℃下混炼50分钟后，挤出成型，在140℃下硫化50分钟，得到减振橡胶，压缩蠕变指数：6%。
实施例3
按重量计，将丁苯橡胶100份和天然橡胶30份在炼胶机上塑炼10分钟后，再加入二氧化硅（比表面积为160-180m2/g）40份、辛二酸二乙酯20份、防老剂4010NA 4份、硫磺5份、促进剂TMTD 5份、交联剂氧化锌 8份、防护蜡石蜡1份和硬脂酸1份，在60℃下混炼50分钟后，挤出成型，在130℃下硫化60分钟，得到减振橡胶，压缩蠕变指数：7%。
压缩蠕变指数依GB/T 19242-2003标准检测。
最后应说明的是：以上所述仅为本发明的优选实施例而已，并不用于限制本发明，尽管参照前述实施例对本发明进行了详细的说明，对于本领域的技术人员来说，其依然可以对前述各实施例所记载的技术方案进行修改，或者对其中部分技术特征进行等同替换。凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。

Claims (2)

1.一种减振橡胶，按重量份数计，包括如下成分：
丁苯橡胶100份，天然橡胶20-30份，二氧化硅20-60份，辛二酸二乙酯2-20份，防老剂1-4份，硫化剂1-5份、促进剂1-5份，交联剂3-8份。
2.根据权利要求1所述的减振橡胶，其特征在于，所述减振橡胶还含有防护蜡1-3份和硬脂酸1-3份。
CN201410651353.8A 2014-11-17 2014-11-17 一种减振橡胶 Pending CN104403153A (zh)