CN104402364A - 快凝型(ⅰ型)聚合物水泥防水浆料及其制备方法 - Google Patents

快凝型(ⅰ型)聚合物水泥防水浆料及其制备方法 Download PDF

Info

Publication number
CN104402364A
CN104402364A CN201410584189.3A CN201410584189A CN104402364A CN 104402364 A CN104402364 A CN 104402364A CN 201410584189 A CN201410584189 A CN 201410584189A CN 104402364 A CN104402364 A CN 104402364A
Authority
CN
China
Prior art keywords
type
polymer cement
waterproof slurry
cement waterproof
powder
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201410584189.3A
Other languages
English (en)
Other versions
CN104402364B (zh
Inventor
陈晓龙
李聚刚
赵长才
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SUZHOU GUSU NOVEL BUILDING MATERIALS CO Ltd
Original Assignee
SUZHOU GUSU NOVEL BUILDING MATERIALS CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SUZHOU GUSU NOVEL BUILDING MATERIALS CO Ltd filed Critical SUZHOU GUSU NOVEL BUILDING MATERIALS CO Ltd
Priority to CN201410584189.3A priority Critical patent/CN104402364B/zh
Publication of CN104402364A publication Critical patent/CN104402364A/zh
Application granted granted Critical
Publication of CN104402364B publication Critical patent/CN104402364B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种快凝型(Ⅰ型)聚合物水泥防水浆料及其制备方法，该快凝型(Ⅰ型)聚合物水泥防水浆料采用普通硅酸盐水泥、快凝快硬硫铝酸盐水泥、低碱度硫铝酸盐水泥等为无机粘结料，以高分子乳液为有机粘结料，加入早强剂、缓凝剂、减水剂等助剂，并且使用电解锰矿渣和矿渣微粉为功能性填料，经分散而成。本发明所述快凝型(Ⅰ型)聚合物水泥防水浆料，施工简单快捷、强度发展迅速、柔韧性好、可以用于干燥、潮湿、渗漏界面施工。

Description

快凝型(Ⅰ型)聚合物水泥防水浆料及其制备方法
技术领域
本发明涉及一种建筑材料，具体涉及一种快凝型(Ⅰ型)聚合物水泥防水浆料及其制备方法。
背景技术
目前，我国的主流防水抗渗材料已形成了沥青及改性沥青防水卷材、合成高分子防水卷材、防水涂料、密封材料和刚性止水堵漏材料五大类。各类防水材料在各种建筑的防水、抗渗、密封、堵漏发挥了巨大的作用。但是在目前的实践中，对一些背水面的渗漏和诸如电梯井、基体等带水界面的防水抗渗的快速治理上，并没有一款非常合适有效的材料和方法。现在通常在此类场合使用的材料一般来讲有两类：(1)渗透结晶型防水涂料。渗透结晶型防水涂料具有渗透结晶、耐腐蚀、增加混凝土密实度和提高混凝土强度的优点，但是在此类有明水甚至渗漏的情况下施工强度发展缓慢，而且养护期长，不能起到快速防水抗渗的要求。(2)水不漏。速凝型水不漏凝结时间快，往往来不及批刮施工已经凝结；缓凝型水不漏虽然初凝时间在10分钟以上，但是对于大面积的批抹施工仍然显得非常仓促，而且缓凝型的抗渗压力较低，只有0.4MPa.还有现场常常采用水不漏与聚合物乳液复配成浆料使用，以期达到快速止水、防水抗渗的作用。但是此种作业从原材料、现场配比、工艺等完全凭现场操作者的经验感觉进行，没有任何的规范；标准、规程遵循，其防水效果也根本难以保证。
鉴于目前状况，并结合绿色、可持续发展思路，本发明公开了一种快凝型(Ⅰ型)聚合物水泥防水浆料，施工简单快捷、强度发展迅速、柔韧性好、可以用于干燥、潮湿、渗漏界面施工的优点。本产品的开发不但符合中央和行业的政策导向，也填补了防水材料领域的一大空白。
发明内容
本发明的目的是提供一种具有快凝快干、强度发展迅速、柔韧性好、施工方便、可以用于干燥、潮湿、渗漏界面施工的优点的快凝型(Ⅰ型)聚合物水泥防水浆料。
本发明的另一目的提供一种快凝型(Ⅰ型)聚合物水泥防水浆料的制备方法
为实现上述发明目的，本发明采用了如下技术方案：
一种快凝型(Ⅰ型)聚合物水泥防水浆料，其特征在于，所述浆料有粉料和液料组成，所述粉料和液料按质量百分比计由如下组分组成：
粉料：
液料：
优选的，所述普通硅酸盐水泥为市售的42.5#普通硅酸盐水泥。
优选的，所述早强剂为无机电解质，如氯盐、硫酸盐、碳酸盐、硝酸盐、亚硝酸盐、硅酸盐、铝酸盐中的一种或几种；所述缓凝剂为羟基羧酸及其盐、多元醇及其衍生物、糖类及碳水化合物中的一种或几种。
优选的，所述减水剂为木质素减水剂、萘磺酸盐减水剂、密胺减水剂、聚羧酸减水剂中的一种。
优选的，所述填料为重质碳酸钙、方解石粉、重晶石粉、滑石粉中的一种或几种。
优选的，所述乳液为乙烯-醋酸乙烯酯乳液，如塞拉尼斯公司生产的1320乳液或瓦克公司生产的547ED乳液；所述消泡剂为有机硅消泡剂，如spa202或SN345；所述防腐剂为异噻唑酮类化合物，如华科981。
如上所述的快凝型(Ⅰ型)聚合物水泥防水浆料的制备方法，其特征在于，包括如下步骤：将粉料中早强剂、缓凝剂、减水剂预先混合均匀，然后与其余各组分按配比依次投入干粉双螺旋锥形混合机中，分散30-60分钟分散均匀出料即得粉料；将液料中各个组分按配比依次投入配有分散机的分散缸中，分散15-30分钟分散均匀出料即得液料。
发明原理：
本发明以普通硅酸盐水泥、快凝快硬硫铝酸盐水泥、低碱度硫铝酸盐水泥复配成无机粘结材料，使产品具有快干快凝、早期强度高的特点；以高分子乳液为有机粘结材料，在水泥水化固化过程中，高分子聚合物在浆料体系中逐渐成膜，形成了由“无机水化矿物-化合物”向“无机水化矿物-化合物-大分子胶黏剂”构成的复合框架体系，即水硬性材料构成的脆硬性骨架，以及大分子聚合物在间隙与固体表面成膜构成的柔韧性连接，这种连接可以想象成由很多细小的弹簧连接在刚性的骨架上，产品较好的柔性和弹性性能。
本发明采用早强剂、缓凝剂来调节产品的凝结时间，使产品在不损失强度、柔性的基础上具有充裕的可施工时间。
电解锰矿渣的主要化学成分为SiO2、AL2O3、Fe2O3、CaO、MgO、SO3、MnO2等，当水泥熟料的主要物质之一铝酸三钙在石膏、石灰分的环境中生产溶解度极低的硫铝酸钙，这些棱柱状的小晶体生长在水泥颗粒的表面上，成为一层薄膜，封闭了水泥组织的生长，阻滞了水分子及离子的扩散，减缓了水泥颗粒特别是铝酸三钙与硅酸三钙的水化作用，从而延缓了水泥凝结过程，起到了调节水泥凝结时间的作用。而电解锰矿渣中的SO3能与铝酸三钙、铁铝酸四钙生产针状的硫铝酸钙，这种水化产物强度较高，并且含有较多的结晶水，能在同样水灰比的条件下，降低水泥石的孔隙率，从而提高了水泥石的强度、耐蚀性和抗冻性等性能。所以电解锰矿渣的加入，不但可以调节可操作时间，而且对增加产品的强度、耐蚀性和抗冻性有很大帮助。
矿渣微粉是比表面积大于350m2/kg高炉矿渣的磨细料，其主要成分是由CaO、MgO、Al2O3、MgO、SiO2、MnO、Fe2O3等组成的硅酸盐和铝酸盐。矿渣微粉在本产品中发生微集料效应和二次水化反应，可提高产品致密度，从而大幅提高抗渗性能。
发明优点：
本发明相对现有技术具有如下有益效果：
1.本发明公开了通硅酸盐水泥、快凝快硬硫铝酸盐水泥、低碱度硫铝酸盐水泥复配使用保证了产品的快凝快硬、早期强度的特点；并且将早强剂和缓凝剂结合使用，使产品具有充足的可施工时间。
2.通过水泥体系与高分子乳液配合使用，产品体系的抗渗性大大增强；由于聚合物的柔性，形变能力远高于单独水泥体系的刚性结构，因而赋予了产品较好的柔性和弹性性能。
3.本发明公开的快凝型(Ⅰ型)聚合物水泥防水浆料首次采用了电解锰矿渣和矿渣微粉作为功能性填料，不但可以调节可操作时间、增加产品的强度、耐蚀性和抗冻性和抗渗性能，而且变废为宝，有很好的社会效益。
具体实施方式
为使本发明的目的、技术方案和优点更加清楚，下面将结合实施案例对本发明作进一步地技术参数描述。
实施例一：
一种快凝型(Ⅰ型)聚合物水泥防水浆料，其制备方法如下：
粉料：预先将0.2kg碳酸锂、0.1kg柠檬酸、0.1kg聚羧酸减水剂混合均匀，然后依次将20kg42.5普通硅酸盐水泥、15kg快凝快硬硫铝酸盐水泥、30kg方解石粉、2kg电解锰矿渣、5kg矿渣微粉依次投入干粉双螺旋锥形混合机中，分散35分钟分散均匀出料即得粉料。
液料：将40kg塞拉尼斯1320乳液、0.1kgspa202消泡剂、0.05kg华科981防腐剂、10kg水依次投入配有分散机的分散缸中，分散15分钟分散均匀出料即得液料。
实施例二：
一种快凝型(Ⅰ型)聚合物水泥防水浆料，其制备方法如下：
粉料：预先将0.4kg甲酸钙早强剂、0.2kg酒石酸缓凝剂、0.3kg聚羧酸减水剂混合均匀，然后将28kg42.5普通硅酸盐水泥、20kg快凝快硬硫铝酸盐水泥、22kg重钙、3kg电解锰矿渣、3kg矿渣微粉依次投入干粉双螺旋锥形混合机中，分散45分钟分散均匀出料即得粉料。
液料：将45kg瓦克547ED乳液、0.2kgspa202消泡剂、0.08kg华科981防腐剂、18kg水依次投入配有分散机的分散缸中，分散20分钟分散均匀出料即得液料。
实施例三：
一种快凝型(Ⅰ型)聚合物水泥防水浆料，其制备方法如下：
粉料：预先将0.6kg甲酸钙早强剂、0.3kg酒石酸缓凝剂、0.4kg聚羧酸减水剂混合均匀，然后将35kg42.5普通硅酸盐水泥、18kg快凝快硬硫铝酸盐水泥、25kg重钙、4kg电解锰矿渣、2kg矿渣微粉依次投入干粉双螺旋锥形混合机中，分散45分钟分散均匀出料即得粉料。
性能测试
本发明参照了GB/T23445-2009《聚合物水泥防水涂料》、JC/T2090-2011《聚合物水泥防水浆料》制定了相关指标；并对上述快凝型(Ⅰ型)聚合物水泥防水浆料进行测试，结果如表1所示。
表1快凝型(Ⅰ型)聚合物水泥防水浆料的性能表征
需要指出的是，以上所述者仅为用以解释本发明之实施例，并非企图据以对本发明作任何形式上之限制，在不脱离本发明原理的前提下，还可以做出若干变更和润饰，是以，凡有在相同之发明精神下所作有关本发明之任何变更或润饰，这些变更或润饰也视为本发明的保护范围。

Claims (7)

1.一种快凝型(Ⅰ型)聚合物水泥防水浆料，其特征在于，所述浆料有粉料和液料组成，所述粉料和液料按质量百分比计由如下组分组成：
2.根据权利要求1所述的快凝型(Ⅰ型)聚合物水泥防水浆料，其特征在于，所述普通硅酸盐水泥为市售的42.5#普通硅酸盐水泥。
3.根据权利要求1所述的快凝型(Ⅰ型)聚合物水泥防水浆料，其特征在于，所述早强剂为无机电解质，如氯盐、硫酸盐、碳酸盐、硝酸盐、亚硝酸盐、硅酸盐、铝酸盐中的一种或几种；所述缓凝剂为羟基羧酸及其盐、多元醇及其衍生物、糖类及碳水化合物中的一种或几种。
4.根据权利要求1所述的快凝型(Ⅰ型)聚合物水泥防水浆料，其特征在于，所述减水剂为木质素减水剂、萘磺酸盐减水剂、密胺减水剂、聚羧酸减水剂中的一种。
5.根据权利要求1所述的快凝型(Ⅰ型)聚合物水泥防水浆料，其特征在于，所述填料为重质碳酸钙、方解石粉、重晶石粉、滑石粉中的一种或几种。
6.根据权利要求1所述的快凝型(Ⅰ型)聚合物水泥防水浆料，其特征在于，所述乳液为乙烯-醋酸乙烯酯乳液，如塞拉尼斯公司生产的1320乳液或瓦克公司生产的547ED乳液；所述消泡剂为有机硅消泡剂，如spa202或SN345；所述防腐剂为异噻唑酮类化合物，如华科981。
7.如权利要求1～6任一项所述的快凝型(Ⅰ型)聚合物水泥防水浆料的制备方法，其特征在于，包括如下步骤：将粉料中早强剂、缓凝剂、减水剂预先混合均匀，然后与其余各组分按配比依次投入干粉双螺旋锥形混合机中，分散30-60分钟分散均匀出料即得粉料；将液料中各个组分按配比依次投入配有分散机的分散缸中，分散15-30分钟分散均匀出料即得液料。
CN201410584189.3A 2014-10-27 2014-10-27 快凝型(ⅰ型)聚合物水泥防水浆料及其制备方法 Active CN104402364B (zh)