CN105130349A - 一种基于工业废渣的基坑工程止水帷幕材料 - Google Patents
一种基于工业废渣的基坑工程止水帷幕材料 Download PDFInfo
- Publication number
- CN105130349A CN105130349A CN201510417484.4A CN201510417484A CN105130349A CN 105130349 A CN105130349 A CN 105130349A CN 201510417484 A CN201510417484 A CN 201510417484A CN 105130349 A CN105130349 A CN 105130349A
- Authority
- CN
- China
- Prior art keywords
- cement
- mass
- industrial waste
- waste residue
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种本发明涉及一种以黏土/砂土和水泥为原材料,通过掺加工业废渣-粉煤灰或者矿渣代替部分水泥,配制达到基坑工程止水帷幕-等厚度水泥土搅拌连续墙(TRD)要求的新型水泥土材料。包括以下质量分数的组分:包括以下质量分数的组分:水:15%~25%,剩余为固体和水玻璃;其中水玻璃的质量为固体质量的3%;其中,固体由基料和固化剂组成,其中基料为黏土或砂土,固化剂由水泥与工业废渣、生石灰组成,并且固化剂占总质量的25%;所述工业废渣为粉煤灰或矿渣;所述固化剂中,水泥的质量分数为10%~40%;所述生石灰与工业废渣的质量分数之比为1:10~1:5。
Description
技术领域
本发明涉及土木工程领域,特别是一种用于基坑工程止水帷幕-等厚度水泥土搅拌连续墙的材料。
背景技术
目前等厚度水泥土搅拌连续墙(TRD)工法作为新技术,己被广泛应用于深大基坑的止水帷幕和截渗墙中,并取得了良好效果。并且随着基坑建设向着更大和更深的方向发展,这种工法由于其自身的优点将会有很大的应用市场。但由于其较高的造价,在推广中存在着很大的阻力。
等厚度水泥土搅拌连续墙(TRD)工法是一种日本开发的较为新型地下支护形式,凭借其墙体均匀、止水性好、厚度一致、表面平整、H型钢设置灵活等优点,在深基坑工程中越来越得到重视和应用。国内的研究大多集中在工法介绍、工法特点、工效及材料消耗数量等方面。陈晨通过现场钻墙取芯及室内三轴渗透试验的方法对TRD工法水泥土墙的渗透性进行了系统的研究表明,TRD工法优于传统的SMW工法。根据上海国际金融中心项目,李星、吴国明和王卫东等人采用国产化的TRD-E型工法主机及配套设备做了非原位试成墙试验,为上海地区乃至全国超深TRD工法设计与施工提供了参考。压汞实验在材料的孔隙分布方面有着很好的应用,是分析研究土体内孔隙定量分布的一种非常有效的方法。
在工程中,普遍采用刚性防水材料(如防渗混凝土)或者柔性防水材料(如高分子防水材料)进行防渗工程的施工,由于这两种防水材料本身都有其内在的缺陷,如刚性防水材料的变形性能较差或者说是存在脆性的缺陷,部分柔性防水材料存在刚度太小的缺陷。另外,无论哪一种防水材料,其成本都比较高,而且效果也不是很好。而水泥土属于半刚性材料,其本身具有刚性材料强度较高的优点,同时又具有柔性材料可以发生较大变形的优点,另外水泥土的施工成本较防渗混凝土和高分子防水材料低得很多,在掺加大量工业废渣后,成本还将显著下降,这就使得水泥土在防水工程中得到越来越广泛的应用。
发明内容
发明目的:为了克服现有技术中存在的不足,本发明提供一种用于基坑工程止水帷幕-等厚度水泥土搅拌连续墙的新型水泥土材料,不仅能够达到抗压强度高的目的,还拥有优异的经济性,更能变废为宝,节约资源减少污染,从而为TRD的进一步发展甚至对基坑支护的发展提供一定的参考。
技术方案:为实现上述目的,本发明采用的技术方案为:
一种基于工业废渣的基坑工程止水帷幕材料,包括以下质量分数的组分:水:15%~25%,剩余为固体和水玻璃;其中水玻璃的质量为固体质量的3%;其中,固体由基料和固化剂组成,其中基料为黏土或砂土,固化剂由水泥与工业废渣、生石灰组成,并且固化剂占总质量的25%;所述工业废渣为粉煤灰或矿渣;所述固化剂中,水泥的质量分数为10%~40%;所述生石灰与工业废渣的质量分数之比为1:10~1:5。
进一步的,在本发明中,所述生石灰与工业废渣的质量分数之比为15:100。
利用上述组分配制达到基坑工程止水帷幕-等厚度水泥土搅拌连续墙(TRD)要求的的新型水泥土材料,以便应用于工程实际。
粉煤灰和高炉矿渣均属于火山灰物质,其活性需要碱性物质激发,考虑工程实际选用生石灰(CaO),参考如下文献:林振荣,张程博,杨友全.掺加矿渣的土聚水泥的研究.[J].21世纪建筑材料,2009,5(1):17-18,优选设置生石灰的添加量为粉煤灰或矿渣的质量的15%。
水玻璃作为早强剂使用,参考如下文献:庞文台.掺合粉煤灰的复合水泥土力学性能及耐久性试验研究.内蒙古农业大学博士学位论文,水玻璃的掺量设定为为土样质量的3%。
有益效果:
本发明可选用的工业废渣有粉煤灰和矿渣两类;其中在传统的水泥和生石灰组成的固化土中加入粉煤灰,粉煤灰不仅起到密实土体、增加土体强度的作用;在一定条件下,粉煤灰自身也可以参与化学反应来增强土体强度,研究表明当土体PH值达到13.2时,粉煤灰被激发,并与土体内的氢氧化钙发生火山灰作用,俗称“二次反应”,生成与水泥水化作用生成物类似的生成物,将大大提高固化土强度;
而矿渣中具有较多的玻璃体,其含量越高,矿渣活性也越高。如矿渣结构中玻璃体的聚合度较低,易被碱激发,水化速度快,所以矿渣多用做水泥混凝土材料的掺加成分,以提高水泥混凝土的早期强度。
基于上面的结论,考虑到经济性原则,并综合考虑养护龄期、水固比(水与固化剂的质量之比)、掺入比(水泥占固化剂的质量分数)、拌合土料和固化剂,经过多角度理论研究与试验测试,最终获得既能满足强度和渗透性的要求、也能降低工程造价的配比;与现有技术相比,本发明在达到相同强度的前提下,能够降低工程费用,同时减少粉煤灰/矿渣对环境的污染。
附图说明
图128d黏土试样渗透系数与水泥掺入比的关系;
图228d砂土试样渗透系数与水泥掺入比的关系;
图328d黏土试样无侧限抗压强度与水泥掺入比的关系;
图428d砂土试样无侧限抗压强度与水泥掺入比的关系;
图528d添加粉煤灰的砂土试样渗透系数与水固比的关系;
图628d添加粉煤灰的黏土试样渗透系数与水固比的关系;
图728d添加粉煤灰的黏土试样无侧限抗压强度与水固比的关系;
图828d添加粉煤灰的砂土试样无侧限抗压强度与水固比的关系。
具体实施方式
下面结合附图对本发明作更进一步的说明。
本发明所述的新型水泥土材料是以黏土/砂土和水泥为原材料,通过掺加工业废渣-粉煤灰或者矿渣代替部分水泥,配制具有低渗透性的新型水泥土材料,包括以下质量分数的组分:水:15%~25%,剩余为固体和水玻璃;其中水玻璃的质量为固体质量的3%;其中,固体由基料和固化剂组成,其中基料为黏土或砂土,固化剂由水泥与工业废渣、生石灰组成,并且固化剂占总质量的25%;所述工业废渣为粉煤灰或矿渣;所述固化剂中,水泥的质量分数为10%~40%;所述生石灰与工业废渣的质量分数之比为15:100。
具体的配比可以在本发明提供的范围内,根据综合考虑的经济性和强度要求,进行几组不同的室内配合比试验,确定最优配比。
实施例中的原材料:
黏土:东南大学九龙湖校区土木交通大楼施工场地;
砂土:厦门艾思欧公司标准砂有限公司生产的ISO标准砂,满足GB178-1997,其规格为1350±5g袋装;
水泥:徐州矿务局水泥厂生产的普通硅酸盐水泥(425#);
粉煤灰:徐州电厂所生产的F类、Ⅰ级粉煤灰;
矿渣:南京钢铁厂生产的高炉矿渣;
生石灰:南京化学试剂有限公司生产的生石灰;
水玻璃:成都市科龙化工试剂厂生产的硅酸钠。
在该实施例中,对于设计的指标要求是:对于黏土,抗压强度不低于0.8MPa,28天的渗透系数不低于10-7cm/s;对于砂土,抗压强度不低于0.2MPa,28天的渗透系数不低于10-4cm/s,流动性良好,水稳定性良好、且经济性高的水泥土材料。
该实施例中,分为两组试验,第一组为黏土,第二组为砂土;两组试验分别采用对比分析,龄期分别是7d、14d、28d,d表示天。试验过程中,根据现有文献,固定固化剂、水玻璃的质量分数、以及生石灰与工业废渣的质量分数之比,在各自的质量分数范围内调整水与固化剂之间的比例、水泥占固化剂的质量分数,并辅以相应质量分数的不同基料,具体如下:水与固化剂的质量之比即水固比分别是0.6、0.8、1,水泥占固化剂的质量分数为10%、20%、30%、40%,工业废渣为粉煤灰或矿渣。经多次调整,最后的试验结果如说明书附图1~附图8所示。
最终从图中可以看出,对于本实施例,综合考虑渗透性能和强度特性,对于黏土,最佳水泥掺入比即水泥占固化剂的质量分数为30%,最佳水固比0.6,工业废渣选用粉煤灰最佳;对于砂土,最佳水泥掺入比40%,最佳水固比0.6,工业废渣选用粉煤灰最佳。该配比既能满足该实施例中的抗压强度和渗透性能的要求,还能够降低工程造价。
Claims (2)
1.一种基于工业废渣的基坑工程止水帷幕材料,其特征在于:包括以下质量分数的组分:水:15%~25%,剩余为固体和水玻璃;其中水玻璃的质量为固体质量的3%;其中,固体由基料和固化剂组成,其中基料为黏土或砂土,固化剂由水泥与工业废渣、生石灰组成,并且固化剂占总质量的25%;所述工业废渣为粉煤灰或矿渣;所述固化剂中,水泥的质量分数为10%~40%;所述生石灰与工业废渣的质量分数之比为1:10~1:5。
2.根据权利要求1所述的基于工业废渣的基坑工程止水帷幕材料,其特征在于:所述生石灰与工业废渣的质量分数之比为15:100。