CN1043923A - 釉面水泥制品 - Google Patents

釉面水泥制品 Download PDF

Info

Publication number
CN1043923A
CN1043923A CN 88109165 CN88109165A CN1043923A CN 1043923 A CN1043923 A CN 1043923A CN 88109165 CN88109165 CN 88109165 CN 88109165 A CN88109165 A CN 88109165A CN 1043923 A CN1043923 A CN 1043923A
Authority
CN
China
Prior art keywords
cement
enamel
forming blocks
glazed
cement product
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 88109165
Other languages
English (en)
Inventor
李明时
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN 88109165 priority Critical patent/CN1043923A/zh
Publication of CN1043923A publication Critical patent/CN1043923A/zh
Pending legal-status Critical Current

Abstract

一种用作墙体装饰材料的釉面水泥制品，它是在水泥成型制品上涂覆一层特制的无机硅酸盐并经焙烧与养护而成，具有表面光洁、无裂纹、渗水率低、化学稳定性好的特点，用作地砖、墙体面砖、瓦或管道，其生产成本较一般瓷制品大为降低。

Description

本发明釉面水泥制品属于一种墙体装饰材料。
现有的墙体面砖、地砖、瓦及非金属管道一般采用陶瓷材料，也有利用着色白水泥制品或有机物涂层装饰材料以及直接用水泥成型制品的，其中陶瓷材料需要较高的烧成温度，甚至有需要二次入窑焙烧的，因此，生产成本偏高，而其他非陶瓷制品除售价昂贵的天然花岗岩和大理石板材外，一般存在表面光洁度不高，抗压强度与耐久性不好的缺点。日本专利昭62-12198、昭62-61553、昭59-50623、昭58-38391、昭63-1277近年介绍了一种新型墙体装饰材料即釉面水泥制品，如釉面水泥瓦和采用金属材料混凝提高强度的釉面水泥板材，而涂于水泥制品表面的瓷釉含有较高的Al2O3，这样就需要过高的烧成温度和过长的焙烧时间。不仅提高了制作成本，还影响了产品的表面强度。
本发明的目的在于提供一种釉面水泥制品，它不仅具有良好的表面强度和耐久性、且降低生产成本。
本发明是这样实现的，在按一定比例的普通硅酸盐水泥和河沙制成的水泥成型制品中涂复一层无机硅酸盐瓷釉，该瓷釉的组份（摩尔比）如下：
SiO20.4993～0.7490
PbO    0.0448～0.1120
B2O30.1436～0.4309
BaO    0～0.0978
Al2O30.0196～0.0588
CaO    0.0713～0.1783
Na2O    0.0807～0.2420
K2O 0.0106～0.1062
Li2O 0～0.0669
ZrO20～0.0406
将含有上述成分的原料混合在1250～1350℃下焙制2～3小时，然后按通常的方法制成釉浆。在制备釉浆时，按如下比例（重量份）添加磨加物：
釉块    100
悬浮剂    1
电解质    0.5～1
颜料    3～5
水    65
将上述方法制备的釉浆用浸渍、喷涂、浇淋或其他方法涂复在成型水泥制品上，待干燥后在600～950℃窑温下烧成，冷却，再按通常的方法养护3～7天即成。
在本发明中，配方中引入SiO2、Al2O3、ZrO2以提高瓷釉的化学稳定性、硬度和耐磨强度，引入PbO、R2O、B2O3降低烧成温度和表面张力，引入BaO和CaO改善瓷釉光泽与工艺性能，因而该瓷釉具有较好的表面强度和耐久性能，其生产成本也随着烧成温度的降低和PbO含量的减少而降低。
实施例：
瓷釉的成分（摩尔比）如下：
其中R2O＝（K2O+Na2O+Li2O）
将上述瓷釉配方所配原料混和经1300℃焙制2.5小时后按通常方法制成釉浆，制浆时添加磨加物，该磨加物组份（重量份）为：
釉块    100
悬浮剂    1
电解质    0.75
颜料    3
水    65
将上述方法制备的釉浆喷涂于规格为150×150×12（mm3）的水泥成型块上，成型块按如下比例（重量份）混合制成：
500＃普通硅酸盐水泥 100
河沙    250
水    60
涂复釉浆的成型块干燥后在750～850℃下烧至釉面呈现光泽，冷却后按通常方法养护3～7天即成。制得的釉面水泥块表面光洁、无裂纹、渗水率低、化学稳定性好，具有较高的表面强度和耐久性。可广泛用作墙体面砖、地砖、瓦及管道，而成本较一般瓷制品大为降低。

Claims (1)

1、一种用作墙体装饰材料的釉面水泥制品，它包括水泥成型块和涂复在水泥成型块上并经烧制而成的无机硅酸盐瓷釉。其中水泥成型块的主成分为普通硅酸盐水泥与河沙，不含或含有少量无机纤维、其特征在于所述无机硅酸盐瓷釉的组份(摩尔比)如下：
SiO20.4993～0.7490
PbO    0.0448～0.1120
B2O30.1436～0.4309
BaO    0～0.0978
Al2C30.0196～0.0588
CaO    0.0713～0.1783
Ra2O 0.0807～0.2420
K2O 0.0106～0.1062
Li2O 0～0.0669
ZnO20～0.0406
上述瓷釉在烧制过程中添加的磨加物的组份(重量份)如下：
釉块    100
悬浮剂  1
电解质  0.5～1
颜料    3～5
水      65
CN 88109165 1988-12-30 1988-12-30 釉面水泥制品 Pending CN1043923A (zh)