CN104389099B - A kind of uvioresistant Anti-static textile fabric and preparation method thereof - Google Patents
A kind of uvioresistant Anti-static textile fabric and preparation method thereof Download PDFInfo
- Publication number
- CN104389099B CN104389099B CN201410659362.1A CN201410659362A CN104389099B CN 104389099 B CN104389099 B CN 104389099B CN 201410659362 A CN201410659362 A CN 201410659362A CN 104389099 B CN104389099 B CN 104389099B
- Authority
- CN
- China
- Prior art keywords
- parts
- fibre
- textile fabric
- solution
- spinning
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of uvioresistant Anti-static textile fabric and preparation method thereof.This uvioresistant Anti-static textile fabric, in parts by mass, including bamboo fibre 60～80 parts, flax fiber 10～30 parts, aloe fibre 10～20 parts, polyester fiber 5～10 parts, polyacrylonitrile 5～10 parts, conductive silver paste 1～3 parts, dispersant 0.5～2 parts.The uvioresistant Anti-static textile fabric of the present invention is to human body skin nonirritant, and has good air permeable waterproof, uvioresistant antistatic, health-care effect.
Description
Technical field
The present invention relates to knitted fabric and textile technical field, particularly relate to a kind of uvioresistant Anti-static textile fabric and
Preparation method.
Background technology
Knitting fabric, is divided by method for weaving, has Weft knitted fabric and warp knitted fabric two class.Weft knitting pin
Knitted fabric, often with low-elasticity terylene fibre or special-shaped dacron thread, Polyamide Yarns, cotton yarn, wool yarn etc. as raw material, uses flat
Pin tissue, changes plain stitch, rib-loop plain stitch, double rib plain stitch, figured texture weave, looped pile group
Knit, various weft machines weave and forms.
The ultraviolet outside line injury to human body, is paid attention to by increasing consumer.In solar spectrum
Ultraviolet not only makes textile fade and brittle, it is possible to makes human body skin sunburn aging, produces melanin and color
Speckle, more serious also can induce canceration, endanger human health.
Along with the enhancing of health of people consciousness, prevent the ultraviolet injury to human body, by more and more
Consumer is paid attention to.Requirement to clothing fabric is more and more higher, to human body skin nonirritant, has
Effect of uvioresistant antistatic.
Summary of the invention
It is an object of the invention on the one hand propose a kind of uvioresistant Anti-static textile fabric, this uvioresistant
Anti-static textile fabric to human body skin nonirritant, has good air permeable waterproof, uvioresistant antistatic
Effect.
For reaching this purpose, the present invention by the following technical solutions:
A kind of uvioresistant Anti-static textile fabric, in parts by mass, including following components:
Preferably, this uvioresistant Anti-static textile fabric, in parts by mass, including following components:
Preferably, one during dispersant is glycerol monostearate, sodium lauryl sulphate, polyacrylamide
Or the mixture of at least two.
Bamboo fibre is exactly a kind of cellulose fibre extracted from the bamboo of growth naturally, and bamboo fibre has good
The characteristics such as good breathability, stronger wearability and good dyeability, have again natural antibacterial simultaneously, press down
Bacterium and anti-ultraviolet function.
Flax fiber is a kind of rare natural fiber, has homoiothermic, antiallergic, antistatic, antibacterial function,
Due to the good hygroscopicity of Caulis et Folium Lini, the moisture being equivalent to own wt 20 times can be absorbed, so sodolin feel
Dry and comfortable；Meanwhile, flax fiber has moisture absorption heat radiation, health care, antifouling, ultraviolet resistance, and fire-retardant
Excellent.
Aloe fibre is that the another novel of exploitation after milk protein fiber, pearl fiber and alginate fibre is protected
Skin fiber；Containing abundant Aloe polysaccharide in aloe fibre, human body skin is had good nourishing, brightens work
With, other ingredient such as organized enzyme, aminoacid, aloe-emodin etc., not only human body skin is had well
Moist effect, moreover it is possible to accelerate skin metabolism, strengthen skin elasticity so that skin seems smooth soft
Soft；Aloe gel in aloe fibre the most still sunlight screen, and it can stop ultraviolet to siberian crabapple
System produces harm, and can recover the immunologic function being damaged, and makes sunburn obtain recovery from illness, thus prevents skin carcinoma
Formation, aminoacid contained in aloe fibre can stop long wave ultraviolet in sunlight to the injury of epidermis and oxygen
Change.
Another aspect of the present invention provides a kind of method preparing above-mentioned uvioresistant Anti-static textile fabric, the party
The uvioresistant Anti-static textile fabric that method obtains to human body skin nonirritant, and have good ventilative,
Uvioresistant antistatic performance.
A kind of method preparing above-mentioned uvioresistant Anti-static textile fabric, comprises the following steps:
(1) in parts by mass, by bamboo fibre 30～50 parts, flax fiber 15～25 parts, aloe fibre 10～20
Part is ground respectively, joins in 30～50 parts of water, is thoroughly mixed, obtains fiber mixed liquor；
(2) conductive silver paste 0.2～1 part and dispersant 1～3 parts are joined in fiber mixed liquor it is stirred mixing
Close, prepare spinning solution；
(3) polyacrylonitrile 5～10 parts, polyvinyl alcohol 2～10 parts of water of 8 parts of respective additions are made into polyacrylonitrile
Solution, poly-vinyl alcohol solution；
(4) will be blended in spinning solution, polyacrylonitrile solution and poly-vinyl alcohol solution input double screw extruder,
Carry out melt spinning, obtain spinning fibre；
(5) spinning fibre is entered with polyester fiber 20～40 parts after washing, plasticization drawing, cut-out are dried
Row weaving, prepared sterilization weaving face fabric.
Preferably, the detailed process of step (1) is: in parts by mass, by bamboo fibre 30～50 parts, Caulis et Folium Lini
Fiber 15～25 parts, aloe fibre 10～20 parts are ground into 400～500 mesh fiber dusts respectively, add
In 30～50 parts of water, it is heated to 80～90 DEG C of stirrings 5～6min, obtains fiber mixed liquor.
Preferably, the detailed process of step (2) is: conductive silver paste 0.2～1 part are added with dispersant 1～3 parts
Enter in fiber mixed liquor, be heated to 60～70 DEG C of stirrings 2～3min, prepare spinning solution.
Preferably, the detailed process of step (4) is: by spinning solution, polyacrylonitrile solution, polyvinyl alcohol
Solution puts into and is blended 4～6min in double screw extruder, carries out melt spinning, spun at 160～180 DEG C
Silk fiber.
Beneficial effects of the present invention: a kind of uvioresistant Anti-static textile fabric, in parts by mass, including
Bamboo fibre 30～50 parts, flax fiber 15～25 parts, aloe fibre 10～20 parts, polyester fiber 20～40 parts,
Polyacrylonitrile 5～10 parts, polyvinyl alcohol 2～8 parts, conductive silver paste 0.2～1 part, dispersant 1～3 parts.This
Bright uvioresistant Anti-static textile fabric is added with bamboo fibre, flax fiber, aloe fibre and conductive silver
Its content is also optimized by slurry so that the uvioresistant Anti-static textile fabric of the present invention to human body skin without
Zest, has good good air permeable waterproof, uvioresistant antistatic performance.
Detailed description of the invention
Technical scheme is further illustrated below by detailed description of the invention.
Embodiment 1: the uvioresistant Anti-static textile fabric of the present embodiment, in parts by mass, including following
Component:
The uvioresistant Anti-static textile fabric of the present embodiment uses following methods to prepare:
In parts by mass, bamboo fibre 30 parts, flax fiber 15 parts, aloe fibre 10 parts are ground respectively
Wear into 400 mesh fiber dusts, join in 30 parts of water, be heated to 80 DEG C of stirring 5min, obtain fiber and mix
Close liquid；Conductive silver paste 0.2 part and dispersant 1 part are joined in fiber mixed liquor, is heated to 60 DEG C of stirrings
2min, prepares spinning solution；Polyacrylonitrile 5 parts, polyvinyl alcohol 2 parts 10 parts of water of respective addition are made into poly-
Acrylonitrile solution, poly-vinyl alcohol solution；
Spinning solution, polyacrylonitrile solution, poly-vinyl alcohol solution are put into and 4min are blended in double screw extruder,
At 160 DEG C, carry out melt spinning, obtain spinning fibre, by spinning fibre through washing, plasticization drawing,
Cut off and carry out with 20 parts of polyester fiber after drying weaving, preparing sterilization weaving face fabric.
Embodiment 2: the uvioresistant Anti-static textile fabric of the present embodiment, in parts by mass, including following
Component:
The uvioresistant Anti-static textile fabric of the present embodiment uses following methods to prepare:
In parts by mass, bamboo fibre 40 parts, flax fiber 20 parts, aloe fibre 15 parts are ground respectively
Wear into 400 mesh fiber dusts, join in 40 parts of water, be heated to 90 DEG C of stirring 5min, obtain fiber and mix
Close liquid；Conductive silver paste 0.8 part and dispersant 1 part are joined in fiber mixed liquor, is heated to 70 DEG C of stirrings
3min, prepares spinning solution；Polyacrylonitrile 8 parts, polyvinyl alcohol 5 parts 10 parts of water of respective addition will be made into
Polyacrylonitrile solution, poly-vinyl alcohol solution；
Spinning solution, polyacrylonitrile solution, poly-vinyl alcohol solution are put into and 5min are blended in double screw extruder,
At 170 DEG C, carry out melt spinning, obtain spinning fibre, by spinning fibre through washing, plasticization drawing,
Cut off and carry out with 30 parts of polyester fiber after drying weaving, preparing sterilization weaving face fabric.
Embodiment 3: the uvioresistant Anti-static textile fabric of the present embodiment, in parts by mass, including following
Component:
The uvioresistant Anti-static textile fabric of the present embodiment uses following methods to prepare:
In parts by mass, bamboo fibre 50 parts, flax fiber 25 parts, aloe fibre 20 parts are ground respectively
Wear into 500 mesh fiber dusts, join in 50 parts of water, be heated to 90 DEG C of stirring 6min, obtain fiber and mix
Close liquid；Conductive silver paste 1 part and dispersant 3 parts are joined in fiber mixed liquor, is heated to 70 DEG C of stirrings
3min, prepares spinning solution；Polyacrylonitrile 10 parts, polyvinyl alcohol 8 parts 10 parts of water of respective addition will be joined
Become polyacrylonitrile solution, poly-vinyl alcohol solution；
Spinning solution, polyacrylonitrile solution, poly-vinyl alcohol solution are put into and 6min are blended in double screw extruder,
At 180 DEG C, carry out melt spinning, obtain spinning fibre, by spinning fibre through washing, plasticization drawing,
Cut off and carry out with 40 parts of polyester fiber after drying weaving, preparing sterilization weaving face fabric.
Performance by the uvioresistant Anti-static textile fabric of the following experiment test present invention.
Uvioresistant antistatic fabric embodiment 1～3 obtained and existing weaving face fabric are according to ASTM
Breathability (with vapor transfer rate as index) is tested by D737 standard；Mark according to AS/NZS4399:1996
Ultraviolet resistance (with UPF as index) is tested by standard；With carry out static impedance test.Result
Such as following table:
As can be seen from the above table, the uvioresistant Anti-static textile fabric that prepared by the present invention and existing weaving face fabric
Compare, there is good ventilative, uvioresistant antistatic performance.
Containing bamboo fibre, flax fiber, aloe fibre etc. in the uvioresistant Anti-static textile fabric of the present invention
Natural fiber is to human body skin nonirritant, and there is good good air permeable waterproof, uvioresistant is prevented quiet
Electrical property.
It should be noted that and understand, in the spirit without departing from appended claims the present invention for required protection
In the case of scope, it is possible to the present invention of foregoing detailed description is made various modifications and improvements.Therefore,
The scope of claimed technical scheme is not limited by given any specific exemplary teachings.
Applicant states, the present invention illustrates detailed process equipment and the technique of the present invention by above-described embodiment
Flow process, but the invention is not limited in above-mentioned detailed process equipment and technological process, i.e. do not mean that the present invention
Have to rely on above-mentioned detailed process equipment and technological process could be implemented.Person of ordinary skill in the field should
This understands, any improvement in the present invention, and the equivalence of raw material each to product of the present invention is replaced and auxiliary element
Interpolation, concrete way choice etc., within the scope of all falling within protection scope of the present invention and disclosure.
Claims (4)
1. the method preparing uvioresistant Anti-static textile fabric, it is characterised in that bag
Include following steps:
(1) in parts by mass, by bamboo fibre 30～50 parts, flax fiber 15～25 parts,
Aloe fibre 10～20 parts are ground respectively, join in 30～50 parts of water, are sufficiently stirred for
Mixing, obtains fiber mixed liquor；
(2) conductive silver paste 0.2～1 part are joined fiber mixed liquor with dispersant 1～3 parts
In be stirred mixing, prepare spinning solution；
(3) by polyacrylonitrile 5～10 parts, polyvinyl alcohol 2～10 parts of water of 8 parts of respective additions
It is made into polyacrylonitrile solution, poly-vinyl alcohol solution；
(4) spinning solution, polyacrylonitrile solution and poly-vinyl alcohol solution input twin screw is squeezed
Go out in machine and be blended, carry out melt spinning, obtain spinning fibre；
(5) by spinning fibre through washing, plasticization drawing, cut-out dry after with polyester fiber
20～40 parts carry out weaving, preparing weaving face fabric.
The side of preparation uvioresistant Anti-static textile fabric the most according to claim 1
Method, it is characterised in that the detailed process of step (1) is: in parts by mass, by bamboo fibre
30～50 parts, flax fiber 15～25 parts, aloe fibre 10～20 parts are ground respectively
Become 400～500 mesh fiber dusts, join in 30～50 parts of water, be heated to 80～90 DEG C
Stirring 5～6min, obtains fiber mixed liquor.
The side of preparation uvioresistant Anti-static textile fabric the most according to claim 1
Method, it is characterised in that the detailed process of step (2) is: by conductive silver paste 0.2～1 part and
Dispersant 1～3 parts join in fiber mixed liquor, be heated to 60～70 DEG C of stirrings 2～
3min, prepares spinning solution.
The side of preparation uvioresistant Anti-static textile fabric the most according to claim 1
Method, it is characterised in that the detailed process of step (4) is: by spinning solution, polyacrylonitrile
Solution, poly-vinyl alcohol solution put into and are blended 4～6min in double screw extruder, 160～
Carry out melt spinning at 180 DEG C, obtain spinning fibre.