CN104387001A - 一种免烧砖的制备方法 - Google Patents

一种免烧砖的制备方法 Download PDF

Info

Publication number
CN104387001A
CN104387001A CN201410569438.1A CN201410569438A CN104387001A CN 104387001 A CN104387001 A CN 104387001A CN 201410569438 A CN201410569438 A CN 201410569438A CN 104387001 A CN104387001 A CN 104387001A
Authority
CN
China
Prior art keywords
parts
brick
raw materials
free
stalk
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410569438.1A
Other languages
English (en)
Inventor
梁坐红
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
QIQIHAR YUEFENG TECHNOLOGY Co Ltd
Original Assignee
QIQIHAR YUEFENG TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by QIQIHAR YUEFENG TECHNOLOGY Co Ltd filed Critical QIQIHAR YUEFENG TECHNOLOGY Co Ltd
Priority to CN201410569438.1A priority Critical patent/CN104387001A/zh
Publication of CN104387001A publication Critical patent/CN104387001A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种免烧砖制作方法,其工艺简单,对固体废弃物利用率高,所述免烧砖重量轻、强度较好、耐久性好,对能源消耗较小对环境无污染,原料采用水泥、粉煤灰等,经混合搅拌均匀,再在模具内经振动、挤压成型制成砖坯,蒸汽养护48小时后,将其在常温下室外放置10-15天得成品。

Description

一种免烧砖的制备方法
技术领域
本发明涉及免烧砖的制备方法,具体涉及利用废弃粉煤灰来制备免烧砖的方法。
背景技术
我国每年有大量的废弃粉煤灰,主要来源于电厂、矿区,近年粉煤灰只少量地用于肥料,更多的粉煤灰被废弃对环境造成了极大的破坏。但粉煤灰由于具有一定的活性人们尝试将其作为建材原料,但性能欠佳。而将粉煤灰制备成免烧砖不但能够减轻环境的负担,同时也变废为宝、节约自然资源,同时由其制成的免烧砖性能优良保温、隔热。
发明内容
本发明的目的是提供了一种免烧砖制作方法,工艺简单,对固体废弃物利用率高,所述免烧砖重量轻、强度较好、耐久性好,对能源消耗较小对环境无污染。 
本发明技术方案为:原料采用水泥、粉煤灰、石膏、砂、秸秆、纤维素醚和水,上述原料按重量比计为15-20份、40-65份、5-10份、20-35份、5-10份、3-5份、2-6份,所述秸秆的长度为2-5mm,经混合搅拌均匀,再在模具内经振动、挤压成型制成砖坯,蒸汽养护48小时后,将其在常温下室外放置10- 15 天得成品。。
本发明的有益技术效果: 
本发明工艺简单,对固体废弃物利用率高,所述免烧砖重量轻、强度较好、耐久性好,对能源消耗较小对环境无污染,重量轻、且无污染。
具体实施方式
实施例1
一种免烧砖的制备方法,原料采用水泥、粉煤灰、石膏、砂、秸秆、纤维素醚和水,上述原料按重量比计为15份、65份、10份、35份、10份、5份、6份,所述秸秆的长度为2-5mm,经混合搅拌均匀,再在模具内经振动、挤压成型制成砖坯,蒸汽养护48小时后,将其在常温下室外放置12天得成品。
实施例2
一种免烧砖的制备方法,其特征在于:原料采用水泥、粉煤灰、石膏、砂、秸秆、纤维素醚和水,上述原料按重量比计为16份、40份、5份、20份、5份、3份、2份,所述秸秆的长度为2-5mm,经混合搅拌均匀,再在模具内经振动、挤压成型制成砖坯,蒸汽养护48小时后,将其在常温下室外放置10天得成品。
实施例3
一种免烧砖的制备方法,其特征在于:原料采用水泥、粉煤灰、石膏、砂、秸秆、纤维素醚和水,上述原料按重量比计为18份、50份、8份、25份、8份、3份、2份,所述秸秆的长度为2-5mm,经混合搅拌均匀,再在模具内经振动、挤压成型制成砖坯,蒸汽养护48小时后,将其在常温下室外放置15 天得成品。
实施例4
一种免烧砖的制备方法,其特征在于:原料采用水泥、粉煤灰、石膏、砂、秸秆、纤维素醚和水,上述原料按重量比计为19份、42份、5份、20份、10份、5份、5份,所述秸秆的长度为2-5mm,经混合搅拌均匀,再在模具内经振动、挤压成型制成砖坯,蒸汽养护48小时后,将其在常温下室外放置13 天得成品。
实施例5
一种免烧砖的制备方法,其特征在于:原料采用水泥、粉煤灰、石膏、砂、秸秆、纤维素醚和水,上述原料按重量比计为15份、60份、8份、23份、8份、5份、6份,所述秸秆的长度为2-5mm,经混合搅拌均匀,再在模具内经振动、挤压成型制成砖坯,蒸汽养护48小时后,将其在常温下室外放置12 天得成品。

Claims (1)

1.一种免烧砖的制备方法,其特征在于:原料采用水泥、粉煤灰、石膏、砂、秸秆、纤维素醚和水,上述原料按重量比计为15-20份、40-65份、5-10份、20-35份、5-10份、3-5份、2-6份,所述秸秆的长度为2-5mm,经混合搅拌均匀,再在模具内经振动、挤压成型制成砖坯,蒸汽养护48小时后,将其在常温下室外放置10- 15 天得成品。
CN201410569438.1A 2014-10-23 2014-10-23 一种免烧砖的制备方法 Pending CN104387001A (zh)