CN104609810A - 一种利用再生骨料和改性植物纤维制备多孔免烧制品的方法 - Google Patents
一种利用再生骨料和改性植物纤维制备多孔免烧制品的方法 Download PDFInfo
- Publication number
- CN104609810A CN104609810A CN201410784843.5A CN201410784843A CN104609810A CN 104609810 A CN104609810 A CN 104609810A CN 201410784843 A CN201410784843 A CN 201410784843A CN 104609810 A CN104609810 A CN 104609810A
- Authority
- CN
- China
- Prior art keywords
- regeneration aggregate
- vegetable fibre
- mentioned
- modified plant
- raw material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种利用再生骨料和改性植物纤维制备多孔免烧制品的方法,其工艺简单,对固体废弃物利用率高,所述免烧制品重量轻、强度较好、耐久性好、韧性抗裂性好,对能源消耗较小对环境无污染,原料采用水泥、再生骨料、改性植物纤维等,经混合搅拌均匀,再在模具内经振动、挤压成型制成砖坯,经蒸汽养护后,将其在常温下室外放置一段时间得成品。
Description
技术领域
本发明涉及一种免烧制品的方法,具体涉及利用一种利用再生骨料和改性植物纤维制备多孔免烧制品的方法。
背景技术
我国每年有大量的废弃再生骨料,主要来源于工业建筑和日常生活等,而再生骨料大量堆积废弃对环境造成了极大的破坏。但再生骨料由于具有一定的强度人们尝试将其作为建材原料,只是性能欠佳。而将再生骨料制备成免烧制品不但能够减轻环境的负担,同时也变废为宝、节约自然资源,同时由其制成的免烧制品性能优良保温、隔热。
发明内容
本发明的目的是提供了一种免烧制品制作方法,工艺简单,对固体废弃物利用率高,所述免烧制品重量轻、强度较好、耐久性好,对能源消耗较小对环境无污染,同时又利用改性的天然植物纤维使其韧性和抗裂性得到明显的加强。
本发明技术方案为:原料(按重量比计)采用水泥9-18份、再生骨料35-68份、硅灰9-15份、可再分散乳胶粉10-20份、石膏3-8份、植物纤维10-15份、羟甲基纤维素3-5份、水5-10份、发泡剂0.1-0.5份、减水剂0.05-0.2份,上述原料经混合搅拌均匀,再在模具内经振动、挤压成型制成砖坯,蒸汽养护24-48小时后,将其在常温下室外放置12-15天得成品;所述植物纤维为秸秆、木质纤维或稻草,上述植物纤维经改性处理,利用如下步骤对其进行改性处理,首先将植物纤维粉碎成直径为3-6mm,然后将其置于由(按重量百分比计)5-10%纳米二氧化硅、5-10%纳米碳酸钙、20-30%苯丙乳液、10-15%柠檬酸和35-50%水配制成的溶液中浸渍处理,其中(按重量比计)植物纤维:上述溶液为1:5-10;所述再生骨料通过下述方式获得,其采用废弃混凝土、废弃砖或废弃陶瓷作为再生骨料原料,将上述再生骨料原料破碎为小于25mm。
本发明的有益技术效果:
本发明工艺简单,对固体废弃物利用率高,所述免烧制品重量轻、强度较好、耐久性好,对能源消耗较小对环境无污染,重量轻、且无污染,产品抗裂性、韧性较好。
具体实施方式
实施例1
一种利用再生骨料和改性植物纤维制备多孔免烧制品的方法,其特征在于:原料(按重量比计)采用水泥10份、再生骨料40份、硅灰15份、可再分散乳胶粉10份、石膏6份、植物纤维10份、羟甲基纤维素5份、水10份、发泡剂0.1份、减水剂0.05份,上述原料经混合搅拌均匀,再在模具内经振动、挤压成型制成砖坯,蒸汽养护24小时后,将其在常温下室外放置12天得成品;所述再生骨料通过下述方式获得,其采用废弃混凝土、废弃砖或废弃陶瓷作为再生骨料原料,将上述再生骨料原料破碎为小于25mm;所述植物纤维为秸秆、木质纤维或稻草,上述植物纤维经改性处理,优选利用如下步骤对其进行改性处理,首先将植物纤维粉碎成直径为3-6mm,然后将其置于由(按重量百分比计)5-10%纳米二氧化硅、5-10%纳米碳酸钙、20-30%苯丙乳液、10-15%柠檬酸和35-50%水配制成的溶液中浸渍处理,其中(按重量比计)植物纤维:上述溶液为1:5-10。
实施例2
一种利用再生骨料和改性植物纤维制备多孔免烧制品的方法,其特征在于:原料(按重量比计)采用水泥15份、再生骨料70份、硅灰15份、可再分散乳胶粉20份、石膏8份、植物纤维12份、羟甲基纤维素3份、水10份、发泡剂0.1份、减水剂0.05份,上述原料经混合搅拌均匀,再在模具内经振动、挤压成型制成砖坯,蒸汽养护48小时后,将其在常温下室外放置15天得成品;所述再生骨料通过下述方式获得,其采用废弃混凝土、废弃砖或废弃陶瓷作为再生骨料原料,将上述再生骨料原料破碎为小于25mm;所述植物纤维为秸秆、木质纤维或稻草,上述植物纤维经改性处理,优选利用如下步骤对其进行改性处理,首先将植物纤维粉碎成直径为3-6mm,然后将其置于由(按重量百分比计)5-10%纳米二氧化硅、5-10%纳米碳酸钙、20-30%苯丙乳液、10-15%柠檬酸和35-50%水配制成的溶液中浸渍处理,其中(按重量比计)植物纤维:上述溶液为1:5-10。
Claims (1)
1.一种利用再生骨料和改性植物纤维制备多孔免烧制品的方法,其特征在于:原料(按重量比计)采用水泥9-18份、再生骨料35-68份、硅灰9-15份、可再分散乳胶粉10-20份、石膏3-8份、植物纤维10-15份、羟甲基纤维素3-5份、水5-10份、发泡剂0.1-0.5份、减水剂0.05-0.2份,上述原料经混合搅拌均匀,再在模具内经振动、挤压成型制成砖坯,蒸汽养护24-48小时后,将其在常温下室外放置12-15天得成品;所述再生骨料通过下述方式获得,其采用废弃混凝土、废弃砖或废弃陶瓷作为再生骨料原料,将上述再生骨料原料破碎为小于25mm;所述植物纤维为秸秆、木质纤维或稻草,上述植物纤维经改性处理,优选利用如下步骤对其进行改性处理,首先将植物纤维粉碎成直径为3-6mm,然后将其置于由(按重量百分比计)5-10%纳米二氧化硅、5-10%纳米碳酸钙、20-30%苯丙乳液、10-15%柠檬酸和35-50%水配制成的溶液中浸渍处理,其中(按重量比计)植物纤维:上述溶液为1:5-10。