CN104356711A - 一种木地板用耐火环氧树脂油漆及其制备方法 - Google Patents

一种木地板用耐火环氧树脂油漆及其制备方法 Download PDF

Info

Publication number
CN104356711A
CN104356711A CN201410582013.4A CN201410582013A CN104356711A CN 104356711 A CN104356711 A CN 104356711A CN 201410582013 A CN201410582013 A CN 201410582013A CN 104356711 A CN104356711 A CN 104356711A
Authority
CN
China
Prior art keywords
parts
paint
preparation
epoxy resin
propylene glycol
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410582013.4A
Other languages
English (en)
Inventor
周全
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI YIXIN WOOD INDUSTRY Co Ltd
Original Assignee
ANHUI YIXIN WOOD INDUSTRY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI YIXIN WOOD INDUSTRY Co Ltd filed Critical ANHUI YIXIN WOOD INDUSTRY Co Ltd
Priority to CN201410582013.4A priority Critical patent/CN104356711A/zh
Publication of CN104356711A publication Critical patent/CN104356711A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种油漆，具体涉及一种木地板用耐火环氧树脂油漆及其制备方法，本发明油漆由以下重量份的原料制成：E-12环氧树脂32-35、羟基丙烯酸树脂10-12、醋酸纤维4-5、环烷油2-3、硼酸铵1-2、氧化锆1-2、二氧化钛1-2、聚丙烯酸丁酯12-14、脂肪酸聚乙二醇酯1-2、二缩三丙二醇二丙烯酸酯10-12、三乙胺1-2、二甘醇4-5、单丁基氧化锡1-2、交联剂TAC1-2、二氨基二苯基甲烷4-6、助剂5-6、二甲苯10-12、乙酸丁酯10-12；本发明油漆漆膜干燥快、光泽度高，柔韧性好、耐冲击，附着力强，防水防腐蚀，耐火性好，安全可靠，工艺相对简单，可以广泛用于防护各类木质的木地板材料。

Description

一种木地板用耐火环氧树脂油漆及其制备方法
技术领域
本发明涉及一种油漆，具体涉及一种木地板用耐火环氧树脂油漆及其制备方法。
背景技术
木地板是一类应用广泛的装修材料，由于木材天然具有多孔有机结构，在使用过程中受环境的影响很大，比如灰尘、油脂等物质会影响产品外观，光照、高热等会导致地板变形、使用寿命缩短，而水份则会直接导致地板变形、翘曲、开裂等，而这些影响因素在日常生活中十分常见，因此，为了提高木地板的使用寿命和装饰效果，常规的手段是在木地板表面喷涂防护油漆，以最大限度的保护木材地板免受外界环境的侵蚀，提高地板的使用寿命。
发明内容
本发明的目的在于，提供一种木地板用耐火环氧树脂油漆及其制备方法，为了实现上述目的，本发明采用的技术方案如下：
一种木地板用耐火环氧树脂油漆及其制备方法，其特征在于，本发明材料由以下重量份的原料制成：E-12环氧树脂32-35、羟基丙烯酸树脂10-12、醋酸纤维4-5、环烷油2-3、硼酸铵1-2、氧化锆1-2、二氧化钛1-2、聚丙烯酸丁酯12-14、脂肪酸聚乙二醇酯1-2、二缩三丙二醇二丙烯酸酯10-12、三乙胺1-2、二甘醇4-5、单丁基氧化锡1-2、交联剂TAC 1-2、二氨基二苯基甲烷4-6、助剂5-6、二甲苯10-12、乙酸丁酯10-12。
所述的助剂由以下重量份的原料制成：锂皂石4-5、苯胺甲基三乙氧基硅烷2-3、碱式碳酸镁4-5、聚异丁烯4-6、N-乙烯基吡咯烷酮1-2、没食子酸丙酯1-2、丙二醇甲醚丙酸酯12-15；其制备方法为：先将锂皂石与苯胺甲基三乙氧基硅烷混合研磨分散20-30min，得改性锂皂石备用，再将聚异丁烯、N-乙烯基吡咯烷酮、没食子酸丙酯一起投入丙二醇甲醚丙酸酯中，搅拌使物料完全溶解分散后，再加入先前制备的改性锂皂石粉体和其它剩余成分，继续研磨分散40-50min，制得稳定均匀的浆料，即为助剂。
所述的一种木地板用耐火环氧树脂油漆及其制备方法，其制备方法为：
（1）将二缩三丙二醇二丙烯酸酯、二甘醇、助剂混合，加入到二甲苯、乙酸丁酯溶剂中，加热至120-130℃，反应3-4小时；
（2）将步骤（1）的物料冷却至70-85℃，加入脂肪酸聚乙二醇酯、单丁基氧化锡，搅拌反应3-4小时；
（3）将步骤（2）的物料降温至50-65℃，加入其它剩余物料，搅拌反应40-60分钟后，冷却至室温，研磨成20-60μm浆料，即得。
与现有技术相比，本发明提供的油漆具备以下优点：漆膜干燥快、光泽度高，柔韧性好、耐冲击，附着力强，防水防腐蚀，耐火性好，安全可靠，工艺相对简单，能有效防护木地板材料。
具体实施方式
实施例
本实施例油漆由以下重量份原料制成：E-12环氧树脂35、羟基丙烯酸树脂12、醋酸纤维5、环烷油3、硼酸铵2、氧化锆2、二氧化钛2、聚丙烯酸丁酯14、脂肪酸聚乙二醇酯2、二缩三丙二醇二丙烯酸酯12、三乙胺2、二甘醇5、单丁基氧化锡2、交联剂TAC 2、二氨基二苯基甲烷6、助剂6、二甲苯12、乙酸丁酯12。
所述的助剂由以下重量份的原料制成：锂皂石5、苯胺甲基三乙氧基硅烷3、碱式碳酸镁4、聚异丁烯5、N-乙烯基吡咯烷酮2、没食子酸丙酯2、丙二醇甲醚丙酸酯15；其制备方法为：先将锂皂石与苯胺甲基三乙氧基硅烷混合研磨分散30min，得改性锂皂石备用，再将聚异丁烯、N-乙烯基吡咯烷酮、没食子酸丙酯一起投入丙二醇甲醚丙酸酯中，搅拌使物料完全溶解分散后，再加入先前制备的改性锂皂石粉体和其它剩余成分，继续研磨分散50min，制得稳定均匀的浆料，即为助剂。
所述的一种木地板用耐火环氧树脂油漆及其制备方法，其制备方法为：
（1）将二缩三丙二醇二丙烯酸酯、二甘醇、助剂混合，加入到二甲苯、乙酸丁酯溶剂中，加热至120-130℃，反应4小时；
（2）将步骤（1）的物料冷却至70-85℃，加入脂肪酸聚乙二醇酯、单丁基氧化锡，搅拌反应4小时；
（3）将步骤（2）的物料降温至50-65℃，加入其它剩余物料，搅拌反应60分钟后，冷却至室温，研磨成60μm浆料，即得。
本发明油漆的性能测试结果为：
测试项目 技术指标
外观 漆膜平整、光亮丰满
表干时间/h ≤2
实干时间/h ≤24
柔韧性/mm ≤1
冲击强度kg/cm ≥50
附着力等级 ≤2
耐盐水性（25℃×120h） 不起泡、不起皱、不脱落
耐水性（25℃×48h） 不起泡、不起皱、不脱落
耐碱性（68h） 不起泡、不起皱、不脱落
耐酸性（68h） 不起泡、不起皱、不脱落
耐火时间/min 120min内涂层不起泡、不起皱
上述测试均遵循相关标准进行。

Claims (2)

1.一种木地板用耐火环氧树脂油漆及其制备方法，其特征在于，该油漆由以下重量份的原料制成：E-12环氧树脂32-35、羟基丙烯酸树脂10-12、醋酸纤维4-5、环烷油2-3、硼酸铵1-2、氧化锆1-2、二氧化钛1-2、聚丙烯酸丁酯12-14、脂肪酸聚乙二醇酯1-2、二缩三丙二醇二丙烯酸酯10-12、三乙胺1-2、二甘醇4-5、单丁基氧化锡1-2、交联剂TAC 1-2、二氨基二苯基甲烷4-6、助剂5-6、二甲苯10-12、乙酸丁酯10-12；
所述的助剂由以下重量份的原料制成：锂皂石4-5、苯胺甲基三乙氧基硅烷2-3、碱式碳酸镁4-5、聚异丁烯4-6、N-乙烯基吡咯烷酮1-2、没食子酸丙酯1-2、丙二醇甲醚丙酸酯12-15；其制备方法为：先将锂皂石与苯胺甲基三乙氧基硅烷混合研磨分散20-30min，得改性锂皂石备用，再将聚异丁烯、N-乙烯基吡咯烷酮、没食子酸丙酯一起投入丙二醇甲醚丙酸酯中，搅拌使物料完全溶解分散后，再加入先前制备的改性锂皂石粉体和其它剩余成分，继续研磨分散40-50min，制得稳定均匀的浆料，即为助剂。
2.如权利要求1所述的一种木地板用耐火环氧树脂油漆及其制备方法，其制备方法为：
（1）将二缩三丙二醇二丙烯酸酯、二甘醇、助剂混合，加入到二甲苯、乙酸丁酯溶剂中，加热至120-130℃，反应3-4小时；
（2）将步骤（1）的物料冷却至70-85℃，加入脂肪酸聚乙二醇酯、单丁基氧化锡，搅拌反应3-4小时；
（3）将步骤（2）的物料降温至50-65℃，加入其它剩余物料，搅拌反应40-60分钟后，冷却至室温，研磨成20-60μm浆料，即得。
CN201410582013.4A 2014-10-27 2014-10-27 一种木地板用耐火环氧树脂油漆及其制备方法 Pending CN104356711A (zh)