CN104774485A - 一种木质桌椅用防水耐候环氧树脂油漆及其制备方法 - Google Patents
一种木质桌椅用防水耐候环氧树脂油漆及其制备方法 Download PDFInfo
- Publication number
- CN104774485A CN104774485A CN201510164258.XA CN201510164258A CN104774485A CN 104774485 A CN104774485 A CN 104774485A CN 201510164258 A CN201510164258 A CN 201510164258A CN 104774485 A CN104774485 A CN 104774485A
- Authority
- CN
- China
- Prior art keywords
- parts
- epoxy resin
- preparation
- oil paint
- chairs
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种油漆,具体涉及一种木质桌椅用防水耐候环氧树脂油漆及其制备方法,本发明油漆由以下重量份的原料制成:E-12环氧树脂24-28、氨基树脂10-12、醇酸树脂5-8、气相二氧化硅3-4、氮化铝1-2、硫酸锰2-3、硼酸1-2、邻二甲苯硫脲1-2、甲基丙烯酸酯20-25、巯基聚硅氧烷3-4、丙烯酸甲酯20-23、季戊四醇12-14、环氧大豆油5-6、N220炭黑3-4、促进剂CZ 1-2、过氧化二异丙苯1-2、助剂5-6、二甲苯10-12、乙酸丁酯10-12;本发明油漆附着力好,漆膜光泽度高,防水性能优良,耐冲击,耐候老化,耐环境氧化腐蚀,生产工艺相对简单,适合防护室外各类木质桌椅材料。
Description
技术领域
本发明涉及一种油漆,具体涉及一种木质桌椅用防水耐候环氧树脂油漆及其制备方法。
背景技术
木质桌椅是一类应用广泛的装修材料,由于木材天然具有多孔有机结构,在使用过程中受环境的影响很大,比如灰尘、油脂等物质会影响产品外观,光照、高热等会导致木质桌椅变形、使用寿命缩短,而水份则会直接导致木质桌椅变形、翘曲、开裂等,而这些影响因素在日常生活中十分常见,因此,为了提高木质桌椅的使用寿命和装饰效果,常规的手段是在木质桌椅表面喷涂防护油漆,以最大限度的保护木材免受外界环境的侵蚀,提高木质桌椅的使用寿命。
发明内容
本发明的目的在于,提供一种木质桌椅用防水耐候环氧树脂油漆及其制备方法,为了实现上述目的,本发明采用的技术方案如下:
一种木质桌椅用防水耐候环氧树脂油漆及其制备方法,其特征在于,本发明材料由以下重量份的原料制成:E-12环氧树脂24-28、氨基树脂10-12、醇酸树脂5-8、气相二氧化硅3-4、氮化铝1-2、硫酸锰2-3、硼酸1-2、邻二甲苯硫脲1-2、甲基丙烯酸酯20-25、巯基聚硅氧烷3-4、丙烯酸甲酯20-23、季戊四醇12-14、环氧大豆油5-6、N220炭黑3-4、促进剂CZ 1-2、过氧化二异丙苯1-2、助剂5-6、二甲苯10-12、乙酸丁酯10-12。
所述的助剂由以下重量份的原料制成:锂皂石4-5、苯胺甲基三乙氧基硅烷2-3、碱式碳酸镁4-5、聚异丁烯4-6、N-乙烯基吡咯烷酮1-2、没食子酸丙酯1-2、丙二醇甲醚丙酸酯12-15;其制备方法为:先将锂皂石与苯胺甲基三乙氧基硅烷混合研磨分散20-30min,得改性锂皂石备用,再将聚异丁烯、N-乙烯基吡咯烷酮、没食子酸丙酯一起投入丙二醇甲醚丙酸酯中,搅拌使物料完全溶解分散后,再加入先前制备的改性锂皂石粉体和其它剩余成分,继续研磨分散40-50min,制得稳定均匀的浆料,即为助剂。
所述的一种木质桌椅用防水耐候环氧树脂油漆及其制备方法,其制备方法为:
(1)将气相二氧化硅、硼酸、季戊四醇、N220炭黑、助剂混合,加入到二甲苯、乙酸丁酯溶剂中,加热至120-130℃,反应3-4小时;
(2)将步骤(1)的物料冷却至70-85℃,加入邻二甲苯硫脲、过氧化二异丙苯,搅拌反应3-4小时;
(3)将步骤(2)的物料降温至50-65℃,加入其它剩余物料,搅拌反应40-60分钟后,冷却至室温,研磨成20-60μm浆料,即得。
与现有技术相比,本发明提供的油漆具备以下优点:附着力好,漆膜光泽度高,防水性能优良,耐冲击,耐候老化,耐环境氧化腐蚀,生产工艺相对简单,适合防护室外各类木质桌椅材料。
具体实施方式
实施例
本实施例油漆由以下重量份原料制成:E-12环氧树脂28、氨基树脂12、醇酸树脂8、气相二氧化硅4、氮化铝2、硫酸锰3、硼酸2、邻二甲苯硫脲2、甲基丙烯酸酯25、巯基聚硅氧烷4、丙烯酸甲酯23、季戊四醇14、环氧大豆油6、N220炭黑4、促进剂CZ 2、过氧化二异丙苯2、助剂6、二甲苯12、乙酸丁酯12。
所述的助剂由以下重量份的原料制成:锂皂石5、苯胺甲基三乙氧基硅烷3、碱式碳酸镁4、聚异丁烯5、N-乙烯基吡咯烷酮2、没食子酸丙酯2、丙二醇甲醚丙酸酯15;其制备方法为:先将锂皂石与苯胺甲基三乙氧基硅烷混合研磨分散30min,得改性锂皂石备用,再将聚异丁烯、N-乙烯基吡咯烷酮、没食子酸丙酯一起投入丙二醇甲醚丙酸酯中,搅拌使物料完全溶解分散后,再加入先前制备的改性锂皂石粉体和其它剩余成分,继续研磨分散50min,制得稳定均匀的浆料,即为助剂。
所述的一种木质桌椅用防水耐候环氧树脂油漆及其制备方法,其制备方法为:
(1)将气相二氧化硅、硼酸、季戊四醇、N220炭黑、助剂混合,加入到二甲苯、乙酸丁酯溶剂中,加热至120-130℃,反应4小时;
(2)将步骤(1)的物料冷却至70-85℃,加入邻二甲苯硫脲、过氧化二异丙苯,搅拌反应4小时;
(3)将步骤(2)的物料降温至50-65℃,加入其它剩余物料,搅拌反应60分钟后,冷却至室温,研磨成60μm浆料,即得。
本发明油漆的性能测试结果为:
上述测试均遵循相关标准进行。
Claims (2)
1.一种木质桌椅用防水耐候环氧树脂油漆及其制备方法,其特征在于,该油漆由以下重量份的原料制成:E-12环氧树脂24-28、氨基树脂10-12、醇酸树脂5-8、气相二氧化硅3-4、氮化铝1-2、硫酸锰2-3、硼酸1-2、邻二甲苯硫脲1-2、甲基丙烯酸酯20-25、巯基聚硅氧烷3-4、丙烯酸甲酯20-23、季戊四醇12-14、环氧大豆油5-6、N220炭黑3-4、促进剂CZ 1-2、过氧化二异丙苯1-2、助剂5-6、二甲苯10-12、乙酸丁酯10-12;
所述的助剂由以下重量份的原料制成:锂皂石4-5、苯胺甲基三乙氧基硅烷2-3、碱式碳酸镁4-5、聚异丁烯4-6、N-乙烯基吡咯烷酮1-2、没食子酸丙酯1-2、丙二醇甲醚丙酸酯12-15;其制备方法为:先将锂皂石与苯胺甲基三乙氧基硅烷混合研磨分散20-30min,得改性锂皂石备用,再将聚异丁烯、N-乙烯基吡咯烷酮、没食子酸丙酯一起投入丙二醇甲醚丙酸酯中,搅拌使物料完全溶解分散后,再加入先前制备的改性锂皂石粉体和其它剩余成分,继续研磨分散40-50min,制得稳定均匀的浆料,即为助剂。
2.如权利要求1所述的一种木质桌椅用防水耐候环氧树脂油漆及其制备方法,其制备方法为:
(1)将气相二氧化硅、硼酸、季戊四醇、N220炭黑、助剂混合,加入到二甲苯、乙酸丁酯溶剂中,加热至120-130℃,反应3-4小时;
(2)将步骤(1)的物料冷却至70-85℃,加入邻二甲苯硫脲、过氧化二异丙苯,搅拌反应3-4小时;
(3)将步骤(2)的物料降温至50-65℃,加入其它剩余物料,搅拌反应40-60分钟后,冷却至室温,研磨成20-60μm浆料,即得。