CN104313596A - 一种船舶甲板防腐蚀剂及其制备方法 - Google Patents

一种船舶甲板防腐蚀剂及其制备方法 Download PDF

Info

Publication number
CN104313596A
CN104313596A CN201410621161.2A CN201410621161A CN104313596A CN 104313596 A CN104313596 A CN 104313596A CN 201410621161 A CN201410621161 A CN 201410621161A CN 104313596 A CN104313596 A CN 104313596A
Authority
CN
China
Prior art keywords
parts
anticorrosive agent
ship deck
anticorrosive
mbt
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410621161.2A
Other languages
English (en)
Inventor
姚红花
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
NANJING LISHUI ZHENXING SHIP ACCESSORIES Co Ltd
Original Assignee
NANJING LISHUI ZHENXING SHIP ACCESSORIES Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by NANJING LISHUI ZHENXING SHIP ACCESSORIES Co Ltd filed Critical NANJING LISHUI ZHENXING SHIP ACCESSORIES Co Ltd
Priority to CN201410621161.2A priority Critical patent/CN104313596A/zh
Publication of CN104313596A publication Critical patent/CN104313596A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种船舶甲板防腐蚀剂，其特征在于；其组分按重量百分比由以下成分组成：MBT0.9~3.2份，硫脲1.2~1.5份，松香胺聚氧乙烯醚10~12份，矿物油16~18份，白凡士林21~28份，丙醇18~25份，卤代烷基吡啶12~15份，溴代酸5~9份。本发明中制备的产品通过MBT、硫脲和松香胺聚氧乙烯醚与卤代烷基吡啶和矿物油作用能够牢牢与碳钢结合，不仅能够提高了防腐蚀剂在甲板的吸附能力，能够大大增加甲板的抗腐蚀性能。

Description

一种船舶甲板防腐蚀剂及其制备方法
技术领域
本发明涉及一种金属防护剂，具体涉及一种船舶甲板防腐蚀剂及其制备方法。
背景技术
防腐蚀剂是一种超级高效的合成渗透剂，它能强力渗入铁锈、腐蚀物、油污内从而轻松地清除掉螺丝、螺拴上的锈迹和腐蚀物，具有渗透除锈、松动润滑、抵制腐蚀、保护金属等性能，并可在部件表面上形成并贮存一层润滑膜，可以抑制湿气及许多其它化学成份造成的腐蚀。尤其是在船舶甲板，常年接触各种恶劣天气和海水的腐蚀，这就需要对船舶甲板需要性能更加强劲的防腐蚀剂。
发明内容
发明目的：为了克服现有技术中存在的不足，本发明提供一种船舶甲板防腐蚀剂。
本发明还提供了上述腐蚀剂的制备方法。
技术方案：为实现上述目的，本发明提供一种船舶甲板防腐蚀剂，其组分按重量百分比由以下成分组成：MBT（2-巯基苯并噻唑） 0.9~3.2份，硫脲1.2~1.5份，松香胺聚氧乙烯醚10~12份，矿物油16~18份，白凡士林21~28份，丙醇18~25份，卤代烷基吡啶12~15份，溴代酸5~9份。
优选地，其组分按重量百分比由以下成分组成：MBT 0.9~1.5份，硫脲1.2~1.5份，松香胺聚氧乙烯醚10份，矿物油17份，白凡士林21~25份，丙醇18~20份，卤代烷基吡啶12~15份，溴代酸5~9份。
优选地，所述卤代烷基吡啶包括溴代十四烷基吡啶、溴代十六烷基吡啶、氯代十二烷基吡啶中的一种或者两种。
上述的船舶甲板防腐蚀剂的制备方法，所述制备方法包括如下步骤：
（1）按照权利要求1所述的组分重量份称取原料组分；
（2）将上述原料放在反应釜中加热混配均匀，加热至128℃高速搅拌40~60min即可。
有益效果：本发明相对于传统技术而言，具有以下优势：
本发明中制备的产品通过MBT、硫脲和松香胺聚氧乙烯醚与卤代烷基吡啶和矿物油作用能够牢牢与碳钢结合，不仅能够提高了防腐蚀剂在甲板的吸附能力，能够大大增加甲板的抗腐蚀性能。
具体实施方式
下面结合实施例对本发明作更进一步的说明。
实施例1：
一种船舶甲板防腐蚀剂，其组分按重量百分比由以下成分组成：MBT（2-巯基苯并噻唑） 3.2份，硫脲1.2份，松香胺聚氧乙烯醚10份，矿物油16份，白凡士林21份，丙醇18份，卤代烷基吡啶12份，溴代酸5份。
上述的船舶甲板防腐蚀剂的制备方法，所述制备方法包括如下步骤：
（1）按照权利要求1所述的组分重量份称取原料组分；
（2）将上述原料放在反应釜中加热混配均匀，加热至128℃高速搅拌40~60min即可。
实施例2：
一种船舶甲板防腐蚀剂，其组分按重量百分比由以下成分组成：MBT（2-巯基苯并噻唑） 0.9份，硫脲1.5份，松香胺聚氧乙烯醚12份，矿物油18份，白凡士林28份，丙醇25份，卤代烷基吡啶15份，溴代酸9份。
上述的船舶甲板防腐蚀剂的制备方法，所述制备方法包括如下步骤：
（1）按照权利要求1所述的组分重量份称取原料组分；
（2）将上述原料放在反应釜中加热混配均匀，加热至128℃高速搅拌40~60min即可。
实施例3：
一种船舶甲板防腐蚀剂，其组分按重量百分比由以下成分组成：MBT（2-巯基苯并噻唑）1.5份，硫脲1.3份，松香胺聚氧乙烯醚11份，矿物油17份，白凡士林25份，丙醇19份，卤代烷基吡啶14份，溴代酸8份。
上述的船舶甲板防腐蚀剂的制备方法，所述制备方法包括如下步骤：
（1）按照权利要求1所述的组分重量份称取原料组分；
（2）将上述原料放在反应釜中加热混配均匀，加热至128℃高速搅拌40~60min即可。
实施例4：
一种船舶甲板防腐蚀剂，其组分按重量百分比由以下成分组成：MBT（2-巯基苯并噻唑） 2.5份，硫脲1.4份，松香胺聚氧乙烯醚12份，矿物油16份，白凡士林22份，丙醇24份，卤代烷基吡啶14份，溴代酸7份。
上述的船舶甲板防腐蚀剂的制备方法，所述制备方法包括如下步骤：
（1）按照权利要求1所述的组分重量份称取原料组分；
（2）将上述原料放在反应釜中加热混配均匀，加热至128℃高速搅拌40~60min即可。
实施例1~4所制备的产品性能见下表：
以上所述仅是本发明的优选实施方式，应当指出：对于本技术领域的技术人员来说，在不脱离本发明原理的前提下，还可以做出若干改进和润饰，这些改进和润饰也应视为本发明的保护范围。

Claims (4)

1.一种船舶甲板防腐蚀剂，其特征在于；其组分按重量百分比由以下成分组成：MBT 0.9~3.2份，硫脲1.2~1.5份，松香胺聚氧乙烯醚10~12份，矿物油16~18份，白凡士林21~28份，丙醇18~25份，卤代烷基吡啶12~15份，溴代酸5~9份。
2.根据权利要求1所述的一种船舶甲板防腐蚀剂，其特征在于：其组分按重量百分比由以下成分组成：MBT 0.9~1.5份，硫脲1.2~1.5份，松香胺聚氧乙烯醚10份，矿物油17份，白凡士林21~25份，丙醇18~20份，卤代烷基吡啶12~15份，溴代酸5~9份。
3.根据权利要求1所述的一种船舶甲板防腐蚀剂，其特征在于：所述卤代烷基吡啶包括溴代十四烷基吡啶、溴代十六烷基吡啶、氯代十二烷基吡啶中的一种或者两种。
4.一种权利要求1~4所述的船舶甲板防腐蚀剂的制备方法，其特征在于：所述制备方法包括如下步骤：
（1）按照权利要求1所述的组分重量份称取原料组分；
（2）将上述原料放在反应釜中加热混配均匀，加热至128℃高速搅拌40~60min即可。
CN201410621161.2A 2014-11-07 2014-11-07 一种船舶甲板防腐蚀剂及其制备方法 Pending CN104313596A (zh)