CN104312318A - Thermally-insulating waterproof coating used for automobiles - Google Patents
Thermally-insulating waterproof coating used for automobiles Download PDFInfo
- Publication number
- CN104312318A CN104312318A CN201410502452.XA CN201410502452A CN104312318A CN 104312318 A CN104312318 A CN 104312318A CN 201410502452 A CN201410502452 A CN 201410502452A CN 104312318 A CN104312318 A CN 104312318A
- Authority
- CN
- China
- Prior art keywords
- parts
- stirring
- minute
- rev
- raw material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Thermally-insulating waterproof coating used for automobiles is disclosed. The coating comprises following raw materials by weight: 71-80 parts of vinyl-acrylic emulsion, 1-2 parts of sodium thiocyanate, 1-2 parts of coconut oil, 2-4 parts of polyvinylidene chloride, 1-2 parts of diazolidinyl urea, 6-10 parts of fumed silica, 3-4 parts of cresyl diphenyl phosphate, 10-12 parts of nanometer carbon powder, 3-5 parts of hollow glass microbeads, 2-3 parts of aluminium nitride, 1-2 parts of antimonous oxide, 1-2 parts of dimethyl aminopropyl amine, 0.5-1 part of dibutyltin dilaurate, 14-20 parts of deionized water and 4-7 parts of an adhesion auxiliary agent. The hollow glass microbeads added into the coating can reflect a large quantity of solar infrared ray radiant heat, and reduce the surface temperature of coatings. The coating effectively insulates transmission of external heat and is good in waterproofness and high in resistance.
Description
?
Technical field
The present invention relates generally to a kind of coating, particularly relates to a kind of automobile heat-insulating waterproof coating.
Background technology
So-called coating refers to that coating body surface can form film under certain conditions and play protection, the class I liquid I of decoration or other specific functions (insulation, antirust, mildew-resistant, heat-resisting etc.) or solid material.Be main raw material mainly with vegetables oil greatly because of early stage coating, therefore also known as painting.Present synthetic resins is most of or all instead of vegetables oil, therefore is called coating.Application of paints is all respects in life, and coating not only requires that cohesiveness is strong, good weatherability, and resistance is high, also wants nontoxic pollution-free, therefore improves constantly the overall quality of coating for improving people's living standard, and accelerating urban development has very great meaning.
Summary of the invention
The object of the invention is just to provide a kind of automobile heat-insulating waterproof coating.
The present invention is achieved by the following technical solutions:
A kind of automobile heat-insulating waterproof coating, it is made up of the raw material of following weight parts:
Acrylate and vinyl acetate emulsion 71-80, Sodium Thiocyanate 99 1-2, cocounut oil 1-2, poly(vinylidene fluoride) 2-4, two Imidurea 1-2, gas-phase silica 6-10, phosphate toluene diphenyl ester 3-4, nano-carbon powder 10-12, hollow glass microballoon 3-5, aluminium nitride 2-3, antimonous oxide 1-2, dimethylaminopropylamine 1-2, dibutyl tin laurate 0.5-1, deionized water 14-20, adhesive aid 4-7;
Described adhesive aid is made up of the raw material of following weight parts:
Eva emulsion 40-46, lauryl glucosyl 1-2, methyl methacrylate 2-4, ammonium persulphate 1-2, allyl polyglycol 3-4, potassium zirconium carbonate 1-2, nano-carbon powder 2-3, tetrafluoroethylene wax 2-3, nano titanium oxide 0.1-1, deionized water 6-8;
By potassium zirconium carbonate, nano-carbon powder mixing, add tetrafluoroethylene wax after stirring, at 60-70 DEG C, be uniformly mixed 10-16 minute, add allyl polyglycol, be stirred to normal temperature, join in Eva emulsion, 200-300 rev/min of dispersed with stirring 10-12 minute;
Lauryl glucosyl is joined in deionized water, after stirring, add ammonium persulphate, methyl methacrylate, 60-80 rev/min of dispersed with stirring 3-5 minute;
Mixed with each raw material of residue by each raw material after above-mentioned process, 800-1000 rev/min of dispersed with stirring 2-4 minute, obtains described adhesive aid.
A preparation method for automobile heat-insulating waterproof coating, is characterized in that comprising the following steps:
By gas-phase silica, nano-carbon powder, hollow glass microballoon mixing, dibutyl tin laurate is added after stirring, 100-200 rev/min is uniformly mixed 10-16 minute, join in acrylate and vinyl acetate emulsion, add dimethylaminopropylamine, 300-400 rev/min is stirred a point 5-10 minute, mixes with each raw material of residue, 600-800 rev/min of dispersed with stirring 20-30 minute, obtains described automobile heat-insulating waterproof coating.
Advantage of the present invention is:
The hollow glass microballoon that waterproof paint of the present invention adds can reflect a lot of solar infrared radiant heat, and reduce Coated Surface Temperature, effectively can intercept the transmission of outside heat, good waterproof performance, resistance is high.
Embodiment
Embodiment 1
A kind of automobile heat-insulating waterproof coating, it is made up of the raw material of following weight parts (kilogram):
Acrylate and vinyl acetate emulsion 80, Sodium Thiocyanate 99 1, cocounut oil 1, poly(vinylidene fluoride) 4, two Imidurea 1, gas-phase silica 10, phosphate toluene diphenyl ester 4, nano-carbon powder 12, hollow glass microballoon 3, aluminium nitride 2, antimonous oxide 2, dimethylaminopropylamine 2, dibutyl tin laurate 0.5, deionized water 20, adhesive aid 7;
Described adhesive aid is made up of the raw material of following weight parts:
Eva emulsion 46, lauryl glucosyl 2, methyl methacrylate 4, ammonium persulphate 2, allyl polyglycol 4, potassium zirconium carbonate 1, nano-carbon powder 3, tetrafluoroethylene wax 2, nano titanium oxide 0.1, deionized water 6;
By potassium zirconium carbonate, nano-carbon powder mixing, add tetrafluoroethylene wax after stirring, at 70 DEG C, be uniformly mixed 16 minutes, add allyl polyglycol, be stirred to normal temperature, join in Eva emulsion, 300 revs/min of dispersed with stirring 12 minutes;
Lauryl glucosyl is joined in deionized water, after stirring, add ammonium persulphate, methyl methacrylate, 80 revs/min of dispersed with stirring 5 minutes;
Mixed with each raw material of residue by each raw material after above-mentioned process, 1000 revs/min of dispersed with stirring 4 minutes, obtain described adhesive aid.
A preparation method for automobile heat-insulating waterproof coating, is characterized in that comprising the following steps:
By gas-phase silica, nano-carbon powder, hollow glass microballoon mixing, dibutyl tin laurate is added after stirring, 200 revs/min are uniformly mixed 16 minutes, join in acrylate and vinyl acetate emulsion, add dimethylaminopropylamine, 400 revs/min of stirrings divide 10 minutes, mix with each raw material of residue, 800 revs/min of dispersed with stirring 30 minutes, obtain described automobile heat-insulating waterproof coating.
Performance test:
Unit elongation: >=300%;
Watertightness: 0.3MPa (one hour waterproof).
Claims (2)
1. an automobile heat-insulating waterproof coating, is characterized in that what it was made up of the raw material of following weight parts:
Acrylate and vinyl acetate emulsion 71-80, Sodium Thiocyanate 99 1-2, cocounut oil 1-2, poly(vinylidene fluoride) 2-4, two Imidurea 1-2, gas-phase silica 6-10, phosphate toluene diphenyl ester 3-4, nano-carbon powder 10-12, hollow glass microballoon 3-5, aluminium nitride 2-3, antimonous oxide 1-2, dimethylaminopropylamine 1-2, dibutyl tin laurate 0.5-1, deionized water 14-20, adhesive aid 4-7;
Described adhesive aid is made up of the raw material of following weight parts:
Eva emulsion 40-46, lauryl glucosyl 1-2, methyl methacrylate 2-4, ammonium persulphate 1-2, allyl polyglycol 3-4, potassium zirconium carbonate 1-2, nano-carbon powder 2-3, tetrafluoroethylene wax 2-3, nano titanium oxide 0.1-1, deionized water 6-8;
By potassium zirconium carbonate, nano-carbon powder mixing, add tetrafluoroethylene wax after stirring, at 60-70 DEG C, be uniformly mixed 10-16 minute, add allyl polyglycol, be stirred to normal temperature, join in Eva emulsion, 200-300 rev/min of dispersed with stirring 10-12 minute;
Lauryl glucosyl is joined in deionized water, after stirring, add ammonium persulphate, methyl methacrylate, 60-80 rev/min of dispersed with stirring 3-5 minute;
Mixed with each raw material of residue by each raw material after above-mentioned process, 800-1000 rev/min of dispersed with stirring 2-4 minute, obtains described adhesive aid.
2. a preparation method for automobile heat-insulating waterproof coating as claimed in claim 1, is characterized in that comprising the following steps:
By gas-phase silica, nano-carbon powder, hollow glass microballoon mixing, dibutyl tin laurate is added after stirring, 100-200 rev/min is uniformly mixed 10-16 minute, join in acrylate and vinyl acetate emulsion, add dimethylaminopropylamine, 300-400 rev/min is stirred a point 5-10 minute, mixes with each raw material of residue, 600-800 rev/min of dispersed with stirring 20-30 minute, obtains described automobile heat-insulating waterproof coating.