CN104119711B - A kind of asphalt waterproofing paint - Google Patents
A kind of asphalt waterproofing paint Download PDFInfo
- Publication number
- CN104119711B CN104119711B CN201410293034.4A CN201410293034A CN104119711B CN 104119711 B CN104119711 B CN 104119711B CN 201410293034 A CN201410293034 A CN 201410293034A CN 104119711 B CN104119711 B CN 104119711B
- Authority
- CN
- China
- Prior art keywords
- raw material
- water
- stirring
- minutes
- deionized water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
nullThe invention discloses a kind of asphalt waterproofing paint，It is made up of the raw material of following weight parts: silicone acrylic emulsion 63 70、Colophonium 35、Cera Flava 23、Sodium aluminate 0.5 1、Captan 12、Hexafluoroacetylacetone 0.2 0.3、Four water eight borate two sodium 0.7 2、Fluor-apatite 57、Butyl polyacrylate 45、Antioxidant 1010 0.5 1、Konjac glucomannan 23、Octylisothiazolinone 0.4 1、Fluorspar Powder 6 10、Dihydrate gypsum powder 35、N n-methylolacrylamide 0.2 0.4、Coalescents 67、Deionized water 10 15，The Colophonium that the water-repellent paint of the present invention adds、Cera Flava、Konjac glucomannan etc. can effectively improve the adhesion strength of coating，Strengthen the bond effect with base material，Improve stability and the peel strength of film，Film is water-fast、Resistance to acids and bases is good，Ageing resistance is strong.
Description
Technical field
The invention mainly relates to a kind of coating, particularly relate to a kind of asphalt waterproofing paint.
Background technology
Traditional waterproof material mainly has the flexible waterproof materials such as waterproof roll, water-repellent paint, sealing cement, and based on cement matrix, adds liquid medicine agent and the rigidity water-proofing material of other auxiliary agent.China's major part waterproofing work shortcoming such as loss of properties on aging, hot strength be low, temperature sensitive that all uses conventional waterproof material, conventional waterproof material to also exist.Conventional waterproof coating is used for roof waterproof, easily cause aging, dry and cracked, deform, fracture, the phenomenon such as layering, waterproof for indoor, for complex-shaped place, constructional difficulties, and to Seepage, quality is more difficult to ensure, people's every few years will spend substantial amounts of fund and labour force to reprocess, and not only confuse the orthobiosis of people, work and the production order, and affect the service life of whole building Colophonium thing.In order to meet the every profession and trade requirement to water-repellent paint, producing high-performance, widely used water-repellent paint is necessary.
Summary of the invention
The object of the invention is just to provide a kind of asphalt waterproofing paint.
The present invention is achieved by the following technical solutions:
A kind of asphalt waterproofing paint, it is made up of the raw material of following weight parts:
Silicone acrylic emulsion 63-70, Colophonium 3-5, Cera Flava 2-3, sodium aluminate 0.5-1, captan 1-2, hexafluoroacetylacetone 0.2-0.3, four water eight borate two sodium 0.7-2, fluor-apatite 5-7, butyl polyacrylate 4-5, antioxidant 1010 0.5-1, Konjac glucomannan 2-3, octylisothiazolinone 0.4-1, Fluorspar Powder 6-10, dihydrate gypsum powder 3-5, N hydroxymethyl acrylamide 0.2-0.4, coalescents 6-7, deionized water 10-15；
Described coalescents is made up of the raw material of following weight parts:
Silicone acrylic emulsion 30-35, Aloe extraction solution 0.3-2, ethyl hydroxybenzoate 1-2, prodan 0.8-1, tetramethylolmethane 2-3, dibutyl tin laurate 0.1-0.2, micropowder silica gel 2-4, trimethyl benzyl ammonia chloride 0.8-2, deionized water 70-75；
Micropowder silica gel being mixed with tetramethylolmethane, at 65-70 DEG C, stirring mixing 2-4 minute, adds the 30-40% of above-mentioned deionized water weight, trimethyl benzyl ammonia chloride, 100-200 rev/min of dispersed with stirring 6-12 minute, obtains dispersion liquid；
Ethyl hydroxybenzoate is mixed with Aloe extraction solution, it is stirring evenly and then adding in silicone acrylic emulsion, insulated and stirred 10-15 minute at 35-40 DEG C, add above-mentioned dispersion liquid, dibutyl tin laurate, stirring is to room temperature, add and remain each raw material, 300-400 rev/min of dispersed with stirring 7-10 minute, obtain described coalescents.
The preparation method of a kind of asphalt waterproofing paint, comprises the following steps:
Add dihydrate gypsum powder, sodium aluminate after Colophonium is added heat fusing, stir；
By fluor-apatite pulverizing, mix with butyl polyacrylate, Cera Flava, be stirring evenly and then adding in deionized water, stir, rise high-temperature and be 60-70 DEG C, add four water eight borate two sodium, stir；
Each raw material after above-mentioned process is mixed with remaining each raw material, 500-600 rev/min of dispersed with stirring 20-30 minute, obtain described asphalt waterproofing paint.
The invention have the advantage that
The Colophonium of water-repellent paint addition of the present invention, Cera Flava, Konjac glucomannan etc. can effectively improve the adhesion strength of coating, strengthen the bond effect with base material, improve stability and the peel strength of film, and film is water-fast, resistance to acids and bases good, and ageing resistance is strong.
Detailed description of the invention
Embodiment 1
A kind of asphalt waterproofing paint, it is made up of the raw material of following weight parts (kilogram):
Silicone acrylic emulsion 70, Colophonium 5, Cera Flava 2, sodium aluminate 0.5, captan 2, hexafluoroacetylacetone 0.3, four water eight borate two sodium 0.7, fluor-apatite 7, butyl polyacrylate 5, antioxidant 1010 0.5, Konjac glucomannan 2, octylisothiazolinone 0.4, Fluorspar Powder 10, dihydrate gypsum powder 5, N hydroxymethyl acrylamide 0.4, coalescents 7, deionized water 15；
Described coalescents is made up of the raw material of following weight parts:
Silicone acrylic emulsion 35, Aloe extraction solution 0.3, ethyl hydroxybenzoate 2, prodan 0.8, tetramethylolmethane 3, dibutyl tin laurate 0.2, micropowder silica gel 4, trimethyl benzyl ammonia chloride 0.8, deionized water 75；
Micropowder silica gel is mixed with tetramethylolmethane, stirring mixing 2 minutes at 70 DEG C, add the 40% of above-mentioned deionized water weight, trimethyl benzyl ammonia chloride, 200 revs/min of dispersed with stirring 12 minutes, obtain dispersion liquid；
Ethyl hydroxybenzoate is mixed with Aloe extraction solution, is stirring evenly and then adding in silicone acrylic emulsion, insulated and stirred 15 minutes at 40 DEG C, add above-mentioned dispersion liquid, dibutyl tin laurate, stir to room temperature, add and remain each raw material, 400 revs/min of dispersed with stirring 10 minutes, obtain described coalescents.
The preparation method of a kind of asphalt waterproofing paint, it is characterised in that comprise the following steps:
Add dihydrate gypsum powder, sodium aluminate after Colophonium is added heat fusing, stir；
By fluor-apatite pulverizing, mixing with butyl polyacrylate, Cera Flava, be stirring evenly and then adding in deionized water, stir, rising high-temperature is 70 DEG C, adds four water eight borate two sodium, stirs；
Each raw material after above-mentioned process is mixed with remaining each raw material, 600 revs/min of dispersed with stirring 30 minutes, obtain described asphalt waterproofing paint.
Performance test:
Elongation percentage: >=300%；
Impermeability: 0.3MPa (one hour waterproof).
Claims (2)
1. an asphalt waterproofing paint, it is characterised in that it is made up of the raw material of following weight parts: silicone acrylic emulsion 70, Colophonium 5, Cera Flava 2, sodium aluminate 0.5, captan 2, hexafluoroacetylacetone 0.3, four water eight borate two sodium 0.7, fluor-apatite 7, butyl polyacrylate 5, antioxidant 1010 0.5, Konjac glucomannan 2, octylisothiazolinone 0.4, Fluorspar Powder 10, dihydrate gypsum powder 5, N hydroxymethyl acrylamide 0.4, coalescents 7, deionized water 15；
Described coalescents is made up of the raw material of following weight parts:
Silicone acrylic emulsion 35, Aloe extraction solution 0.3, ethyl hydroxybenzoate 2, prodan 0.8, tetramethylolmethane 3, dibutyl tin laurate 0.2, micropowder silica gel 4, trimethyl benzyl ammonia chloride 0.8, deionized water 75；
Micropowder silica gel is mixed with tetramethylolmethane, stirring mixing 2 minutes at 70 DEG C, add the 40% of above-mentioned deionized water weight, trimethyl benzyl ammonia chloride, 200 revs/min of dispersed with stirring 12 minutes, obtain dispersion liquid；
Ethyl hydroxybenzoate is mixed with Aloe extraction solution, is stirring evenly and then adding in silicone acrylic emulsion, insulated and stirred 15 minutes at 40 DEG C, add above-mentioned dispersion liquid, dibutyl tin laurate, stir to room temperature, add and remain each raw material, 400 revs/min of dispersed with stirring 10 minutes, obtain described coalescents.
2. the preparation method of an asphalt waterproofing paint as claimed in claim 1, it is characterised in that comprise the following steps: add dihydrate gypsum powder, sodium aluminate after Colophonium is added heat fusing, stir；
By fluor-apatite pulverizing, mixing with butyl polyacrylate, Cera Flava, be stirring evenly and then adding in deionized water, stir, rising high-temperature is 70 DEG C, adds four water eight borate two sodium, stirs；
Each raw material after above-mentioned process is mixed with remaining each raw material, 600 revs/min of dispersed with stirring 30 minutes, obtain described asphalt waterproofing paint.