CN103614017B - A kind of waterproof paint containing rosin - Google Patents
A kind of waterproof paint containing rosin Download PDFInfo
- Publication number
- CN103614017B CN103614017B CN201310516355.1A CN201310516355A CN103614017B CN 103614017 B CN103614017 B CN 103614017B CN 201310516355 A CN201310516355 A CN 201310516355A CN 103614017 B CN103614017 B CN 103614017B
- Authority
- CN
- China
- Prior art keywords
- waterproof paint
- raw material
- rosin
- add
- adhesive aid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of waterproof paint containing rosin, it is made up of the raw material of following weight parts: water-base fluorocarbon emulsion resin 70-75, rosin 2-3, metal particle 3-5, Virahol 2-3, diacetone-acryloamide(DAA) 1-2, organopolysiloxane 1-2, Sodium Persulfate 1-2, guar gum 2-3, aluminum silicate fiber 5-10, gas-phase silica 10-13, polypropylene glycol diglycidyl ether 0.4-1, adhesive aid 7-10, deionized water 5-20; Waterproof paint cohesiveness of the present invention is strong, good weatherability, and suitability is extensive, is specially adapted to mosaic, ceramic tile, glass curtain wall, exterior wall and the maintenance of concrete wall crack-leakage, color steel roofing, door and window dividing plate periphery filleting and overall brushing.
Description
Technical field
The present invention relates generally to a kind of coating, particularly relates to a kind of waterproof paint containing rosin.
Background technology
Along with development and the refinement of domestic coating industry, market is also more and more outstanding to the requirement with special functional coating, wherein more increase for containing rosin, water-fast, acid-alkali-corrosive-resisting, the performance requriements such as fire-retardant, in order to meet the requirement of every profession and trade to waterproof paint, production high-performance, widely used waterproof paint is necessary.
Summary of the invention
The object of the invention is just to provide a kind of waterproof paint containing rosin.
The present invention is achieved by the following technical solutions:
A waterproof paint containing rosin, it is made up of the raw material of following weight parts:
Water-base fluorocarbon emulsion resin 70-75, rosin 2-3, metal particle 3-5, Virahol 2-3, diacetone-acryloamide(DAA) 1-2, organopolysiloxane 1-2, Sodium Persulfate 1-2, guar gum 2-3, aluminum silicate fiber 5-10, gas-phase silica 10-13, polypropylene glycol diglycidyl ether 0.4-1, adhesive aid 7-10, deionized water 5-20;
Described adhesive aid is made up of the raw material of following weight parts:
White glue with vinyl 32-40, silane resin acceptor kh-550 4-6, polyvinylpyrrolidone 1-2, sodium silicate 2-3, poly(lactic acid) 3-5, Starso 1-2, nano-sized carbon 1-2;
Above-mentioned poly(lactic acid) is heated to 180-185 DEG C, adds silane resin acceptor kh-550, be uniformly mixed 3-5 minute, reduction temperature is 55-60 DEG C, adds nano-sized carbon, 300-500 rev/min of dispersed with stirring 6-10 minute, be reduced to normal temperature, add Starso, polyvinylpyrrolidone, sodium silicate, ball milling 1-2 hour, add each raw material of residue, at 70-90 DEG C, insulation leaves standstill 1-2 hour, cooling, abundant ball milling, obtains described adhesive aid.
A preparation method for waterproof paint containing rosin, comprises the following steps:
Mixed with gas-phase silica by above-mentioned aluminum silicate fiber, add Virahol, add adhesive aid after stirring, ball milling mixing fully, then adds each raw material of residue, and high-speed stirring, to mixing, obtains the described waterproof paint containing rosin.
Advantage of the present invention is:
Waterproof paint cohesiveness of the present invention is strong, good weatherability, and suitability is extensive, is specially adapted to mosaic, ceramic tile, glass curtain wall, exterior wall and the maintenance of concrete wall crack-leakage, color steel roofing, door and window dividing plate periphery filleting and overall brushing.
Embodiment
Embodiment 1
A waterproof paint containing rosin, it is made up of the raw material of following weight parts (kilogram):
Water-base fluorocarbon emulsion resin 75, rosin 2, metal particle 3, Virahol 3, diacetone-acryloamide(DAA) 1, organopolysiloxane 1, Sodium Persulfate 2, guar gum 2, aluminum silicate fiber 10, gas-phase silica 13, polypropylene glycol diglycidyl ether 0.4, adhesive aid 10, deionized water 20;
Described adhesive aid is made up of the raw material of following weight parts:
White glue with vinyl 40, silane resin acceptor kh-550 4, polyvinylpyrrolidone 1, sodium silicate 2, poly(lactic acid) 5, Starso 2, nano-sized carbon 2;
Above-mentioned poly(lactic acid) is heated to 185 DEG C, adds silane resin acceptor kh-550, be uniformly mixed 5 minutes, reducing temperature is 60 DEG C, adds nano-sized carbon, 500 revs/min of dispersed with stirring 10 minutes, be reduced to normal temperature, add Starso, polyvinylpyrrolidone, sodium silicate, ball milling 2 hours, add each raw material of residue, at 90 DEG C, insulation leaves standstill 2 hours, cooling, abundant ball milling, obtains described adhesive aid.
A preparation method for waterproof paint containing rosin, comprises the following steps:
Mixed with gas-phase silica by above-mentioned aluminum silicate fiber, add Virahol, add adhesive aid after stirring, ball milling mixing fully, then adds each raw material of residue, and high-speed stirring, to mixing, obtains the described waterproof paint containing rosin.
Performance test:
Unit elongation: >=300%;
Watertightness: 0.3MPa (one hour waterproof).
Claims (2)
1. the waterproof paint containing rosin, is characterized in that what it was made up of the raw material of following weight parts: water-base fluorocarbon emulsion resin 70-75, rosin 2-3, metal particle 3-5, Virahol 2-3, diacetone-acryloamide(DAA) 1-2, organopolysiloxane 1-2, Sodium Persulfate 1-2, guar gum 2-3, aluminum silicate fiber 5-10, gas-phase silica 10-13, polypropylene glycol diglycidyl ether 0.4-1, adhesive aid 7-10, deionized water 5-20;
Described adhesive aid is made up of the raw material of following weight parts: white glue with vinyl 32-40, silane resin acceptor kh-550 4-6, polyvinylpyrrolidone 1-2, sodium silicate 2-3, poly(lactic acid) 3-5, Starso 1-2, nano-sized carbon 1-2;
Above-mentioned poly(lactic acid) is heated to 180-185 DEG C, adds silane resin acceptor kh-550, be uniformly mixed 3-5 minute, reduction temperature is 55-60 DEG C, adds nano-sized carbon, 300-500 rev/min of dispersed with stirring 6-10 minute, be reduced to normal temperature, add Starso, polyvinylpyrrolidone, sodium silicate, ball milling 1-2 hour, add each raw material of residue, at 70-90 DEG C, insulation leaves standstill 1-2 hour, cooling, abundant ball milling, obtains described adhesive aid.
2. the preparation method of the waterproof paint as claimed in claim 1 containing rosin, it is characterized in that comprising the following steps: above-mentioned aluminum silicate fiber is mixed with gas-phase silica, add Virahol, adhesive aid is added after stirring, ball milling mixing fully, add each raw material of residue again, high-speed stirring, to mixing, obtains the described waterproof paint containing rosin.