CN103614077A - Waterproof asphalt coating - Google Patents
Waterproof asphalt coating Download PDFInfo
- Publication number
- CN103614077A CN103614077A CN201310517155.8A CN201310517155A CN103614077A CN 103614077 A CN103614077 A CN 103614077A CN 201310517155 A CN201310517155 A CN 201310517155A CN 103614077 A CN103614077 A CN 103614077A
- Authority
- CN
- China
- Prior art keywords
- parts
- raw material
- add
- waterproof
- adds
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a waterproof asphalt coating. The waterproof asphalt coating comprises, 50-60 parts of asphalt, 10-14 parts of an aqueous acrylic emulsion, 4-6 parts of a thermoplastic elastomer TPEG130D, 4-6 parts of light calcium carbonate, 1-2 parts of caprylic capric triglyceride, 2-4 parts of polyethylene glycol 1000, 1-2 parts of polyvinylpyrrolidone, 2-3 parts of aluminum dihydrogen phosphate, 8-10 parts of precipitated barium sulfate, 3-5 parts of ash calcium powder, 7-10 parts of a bonding aid and a proper amount of water. The coat of the waterproof coating is stable and tough, has a strong adhesion, can be firmly cohered on a base surface, and has an effective waterproof protection effect for a long term.
Description
Technical field
The present invention relates generally to a kind of coating, relates in particular to a kind of asphalt waterproofing paint.
Background technology
Development and refinement along with domestic coating industry, market is also more and more outstanding to having the requirement of special functional coating, wherein for anti-aging, water-fast, acid-alkali-corrosive-resisting, the performance requriements such as fire-retardant, more increase, in order to meet the requirement of every profession and trade to waterproof paint, production high-performance, widely used waterproof paint is necessary.
Summary of the invention
The object of the invention is just to provide a kind of asphalt waterproofing paint.
The present invention is achieved by the following technical solutions:
An asphalt waterproofing paint, it is comprised of the raw material of following weight parts:
Pitch 50-60, aqueous acrylic emulsion 10-14, thermoplastic elastomer TPE G130D4-6, light calcium carbonate 4-6, Glycerin, mixed triester with caprylic acid capric acid 1-2, cetomacrogol 1000 2-4, Polyvinylpyrolidone (PVP) 1-2, aluminium dihydrogen phosphate 2-3, process white 8-10, grey calcium powder 3-5, adhesive aid 7-10, water are appropriate;
Described adhesive aid is comprised of the raw material of following weight parts:
White glue with vinyl 32-40, silane resin acceptor kh-550 4-6, polyvinylpyrrolidone 1-2, flower bulb alkali 2-3, poly(lactic acid) 3-5, Starso 1-2, nano-sized carbon 1-2;
Above-mentioned poly(lactic acid) is heated to 180-185 ℃, adds silane resin acceptor kh-550, be uniformly mixed 3-5 minute, reduction temperature is 55-60 ℃, adds nano-sized carbon, 300-500 rev/min of dispersed with stirring 6-10 minute, be reduced to normal temperature, add Starso, polyvinylpyrrolidone, flower bulb alkali, ball milling 1-2 hour, adds each raw material of residue, at 70-90 ℃, be incubated standing 1-2 hour, cooling, fully ball milling, obtains described adhesive aid.
A preparation method for asphalt waterproofing paint, comprises the following steps:
In above-mentioned pitch, add thermoplastic elastomer TPE G130D, heating rising temperature is to 150-160 ℃, with colloidal mill, grind, reach completely dispersed till, add Glycerin, mixed triester with caprylic acid capric acid, process white, grey calcium powder, be fully uniformly mixed, add each raw material of residue, high-speed stirring, to mixing, obtains described asphalt waterproofing paint.
Advantage of the present invention is:
Waterproof paint coating of the present invention is stable, and tough and tensile, strong adhesion, can firmly cohere on basal plane, produces permanent effectively waterproofing protection effect.
Embodiment
Embodiment 1
An asphalt waterproofing paint, it by following weight parts (kilogram) raw material form:
Pitch 60, aqueous acrylic emulsion 14, thermoplastic elastomer TPE G130D6, light calcium carbonate 6, Glycerin, mixed triester with caprylic acid capric acid 1, cetomacrogol 1000 2, Polyvinylpyrolidone (PVP) 2, aluminium dihydrogen phosphate 3, process white 10, grey calcium powder 5, adhesive aid 7-10, water are appropriate;
Described adhesive aid is comprised of the raw material of following weight parts:
White glue with vinyl 40, silane resin acceptor kh-550 4, polyvinylpyrrolidone 1, flower bulb alkali 3, poly(lactic acid) 3-5, Starso 1, nano-sized carbon 1;
Above-mentioned poly(lactic acid) is heated to 180-185 ℃, adds silane resin acceptor kh-550, be uniformly mixed 5 minutes, reduction temperature is 55-60 ℃, adds nano-sized carbon, 500 revs/min of dispersed with stirring 10 minutes, be reduced to normal temperature, add Starso, polyvinylpyrrolidone, flower bulb alkali, ball milling 1 hour, adds each raw material of residue, at 70-90 ℃, be incubated standing 1 hour, cooling, fully ball milling, obtains described adhesive aid.
A preparation method for asphalt waterproofing paint, comprises the following steps:
In above-mentioned pitch, add thermoplastic elastomer TPE G130D, heating rising temperature to 160 ℃, with colloidal mill, grind, reach completely dispersed till, add Glycerin, mixed triester with caprylic acid capric acid, process white, grey calcium powder, be fully uniformly mixed, add each raw material of residue, high-speed stirring, to mixing, obtains described asphalt waterproofing paint.
Performance test:
Cohesive strength: 2.63MPa;
Watertightness (0.3MPa, 40min): waterproof.
Claims (2)
1. an asphalt waterproofing paint, is characterized in that what it was comprised of the raw material of following weight parts:
Pitch 50-60, aqueous acrylic emulsion 10-14, thermoplastic elastomer TPE G130D4-6, light calcium carbonate 4-6, Glycerin, mixed triester with caprylic acid capric acid 1-2, cetomacrogol 1000 2-4, Polyvinylpyrolidone (PVP) 1-2, aluminium dihydrogen phosphate 2-3, process white 8-10, grey calcium powder 3-5, adhesive aid 7-10, water are appropriate;
Described adhesive aid is comprised of the raw material of following weight parts:
White glue with vinyl 32-40, silane resin acceptor kh-550 4-6, polyvinylpyrrolidone 1-2, flower bulb alkali 2-3, poly(lactic acid) 3-5, Starso 1-2, nano-sized carbon 1-2;
Above-mentioned poly(lactic acid) is heated to 180-185 ℃, adds silane resin acceptor kh-550, be uniformly mixed 3-5 minute, reduction temperature is 55-60 ℃, adds nano-sized carbon, 300-500 rev/min of dispersed with stirring 6-10 minute, be reduced to normal temperature, add Starso, polyvinylpyrrolidone, flower bulb alkali, ball milling 1-2 hour, adds each raw material of residue, at 70-90 ℃, be incubated standing 1-2 hour, cooling, fully ball milling, obtains described adhesive aid.
2. a preparation method for asphalt waterproofing paint as claimed in claim 1, is characterized in that comprising the following steps:
In above-mentioned pitch, add thermoplastic elastomer TPE G130D, heating rising temperature is to 150-160 ℃, with colloidal mill, grind, reach completely dispersed till, add Glycerin, mixed triester with caprylic acid capric acid, process white, grey calcium powder, be fully uniformly mixed, add each raw material of residue, high-speed stirring, to mixing, obtains described asphalt waterproofing paint.