CN103614017A - Waterproof coating containing rosin water - Google Patents
Waterproof coating containing rosin water Download PDFInfo
- Publication number
- CN103614017A CN103614017A CN201310516355.1A CN201310516355A CN103614017A CN 103614017 A CN103614017 A CN 103614017A CN 201310516355 A CN201310516355 A CN 201310516355A CN 103614017 A CN103614017 A CN 103614017A
- Authority
- CN
- China
- Prior art keywords
- parts
- rosin
- raw material
- adds
- waterproof coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a waterproof coating containing rosin water. The waterproof coating comprises, by weight, 70-75 parts of an aqueous fluorocarbon emulsion resin, 2-3 parts of rosin water, 3-5 parts of a metal particle, 2-3 parts of isopropanol, 1-2 parts of diacetone-acryloamide, 1-2 parts of polysiloxane, 1-2 parts of sodium persulfate, 2-3 parts of a guar gum, 5-10 parts of an alumina silicate fiber, 10-13 parts of fumed silica, 0.4-1 part of polypropylene glycol diglycidyl ether, 7-10 parts of a bonding assistant, and 5-20 parts of deionized water. The waterproof coating has the advantages of strong adhesion, good weatherability and wide applicability, is especially suitable for the crack seepage maintenance of mosaics, ceramic tiles, glass curtain walls, exterior walls and concrete walls, and the circumferential sealing and the overall coating of color steel tile roofs and door and window separators.
Description
Technical field
The present invention relates generally to a kind of coating, relates in particular to a kind of waterproof paint that contains rosin.
Background technology
Development and refinement along with domestic coating industry, market is also more and more outstanding to having the requirement of special functional coating, wherein for contain rosin, water-fast, acid-alkali-corrosive-resisting, the performance requriements such as fire-retardant more increase, in order to meet the requirement of every profession and trade to waterproof paint, production high-performance, widely used waterproof paint is necessary.
Summary of the invention
The object of the invention is just to provide a kind of waterproof paint that contains rosin.
The present invention is achieved by the following technical solutions:
A waterproof paint that contains rosin, it is comprised of the raw material of following weight parts:
Water-base fluorocarbon emulsion resin 70-75, rosin 2-3, metal particle 3-5, Virahol 2-3, diacetone-acryloamide(DAA) 1-2, organopolysiloxane 1-2, Sodium Persulfate 1-2, guar gum 2-3, aluminum silicate fiber 5-10, gas-phase silica 10-13, polypropylene glycol diglycidyl ether 0.4-1, adhesive aid 7-10, deionized water 5-20;
Described adhesive aid is comprised of the raw material of following weight parts:
White glue with vinyl 32-40, silane resin acceptor kh-550 4-6, polyvinylpyrrolidone 1-2, flower bulb alkali 2-3, poly(lactic acid) 3-5, Starso 1-2, nano-sized carbon 1-2;
Above-mentioned poly(lactic acid) is heated to 180-185 ℃, adds silane resin acceptor kh-550, be uniformly mixed 3-5 minute, reduction temperature is 55-60 ℃, adds nano-sized carbon, 300-500 rev/min of dispersed with stirring 6-10 minute, be reduced to normal temperature, add Starso, polyvinylpyrrolidone, flower bulb alkali, ball milling 1-2 hour, adds each raw material of residue, at 70-90 ℃, be incubated standing 1-2 hour, cooling, fully ball milling, obtains described adhesive aid.
A preparation method for the waterproof paint that contains rosin, comprises the following steps:
Above-mentioned aluminum silicate fiber is mixed with gas-phase silica, add Virahol, after stirring, add adhesive aid, ball milling mixes fully, then adds each raw material of residue, and high-speed stirring, to mixing, contains the waterproof paint of rosin described in obtaining.
Advantage of the present invention is:
Waterproof paint cohesiveness of the present invention is strong, good weatherability, and suitability is extensive, is specially adapted to mosaic, ceramic tile, glass curtain wall, exterior wall and the maintenance of concrete wall crack-leakage, color steel roofing, door and window dividing plate periphery filleting and whole brushing.
Embodiment
Embodiment 1
The waterproof paint that contains rosin, it by following weight parts (kilogram) raw material form:
Water-base fluorocarbon emulsion resin 75, rosin 2, metal particle 3, Virahol 3, diacetone-acryloamide(DAA) 1, organopolysiloxane 1, Sodium Persulfate 2, guar gum 2, aluminum silicate fiber 10, gas-phase silica 13, polypropylene glycol diglycidyl ether 0.4, adhesive aid 10, deionized water 20;
Described adhesive aid is comprised of the raw material of following weight parts:
White glue with vinyl 40, silane resin acceptor kh-550 4, polyvinylpyrrolidone 1, flower bulb alkali 2, poly(lactic acid) 5, Starso 2, nano-sized carbon 2;
Above-mentioned poly(lactic acid) is heated to 185 ℃, adds silane resin acceptor kh-550, be uniformly mixed 5 minutes, reducing temperature is 60 ℃, adds nano-sized carbon, 500 revs/min of dispersed with stirring 10 minutes, be reduced to normal temperature, add Starso, polyvinylpyrrolidone, flower bulb alkali, ball milling 2 hours, adds each raw material of residue, at 90 ℃, be incubated standing 2 hours, cooling, fully ball milling, obtains described adhesive aid.
A preparation method for the waterproof paint that contains rosin, comprises the following steps:
Above-mentioned aluminum silicate fiber is mixed with gas-phase silica, add Virahol, after stirring, add adhesive aid, ball milling mixes fully, then adds each raw material of residue, and high-speed stirring, to mixing, contains the waterproof paint of rosin described in obtaining.
Performance test:
Unit elongation: >=300%;
Watertightness: 0.3MPa (one hour waterproof).
Claims (2)
1. a waterproof paint that contains rosin, is characterized in that what it was comprised of the raw material of following weight parts:
Water-base fluorocarbon emulsion resin 70-75, rosin 2-3, metal particle 3-5, Virahol 2-3, diacetone-acryloamide(DAA) 1-2, organopolysiloxane 1-2, Sodium Persulfate 1-2, guar gum 2-3, aluminum silicate fiber 5-10, gas-phase silica 10-13, polypropylene glycol diglycidyl ether 0.4-1, adhesive aid 7-10, deionized water 5-20;
Described adhesive aid is comprised of the raw material of following weight parts:
White glue with vinyl 32-40, silane resin acceptor kh-550 4-6, polyvinylpyrrolidone 1-2, flower bulb alkali 2-3, poly(lactic acid) 3-5, Starso 1-2, nano-sized carbon 1-2;
Above-mentioned poly(lactic acid) is heated to 180-185 ℃, adds silane resin acceptor kh-550, be uniformly mixed 3-5 minute, reduction temperature is 55-60 ℃, adds nano-sized carbon, 300-500 rev/min of dispersed with stirring 6-10 minute, be reduced to normal temperature, add Starso, polyvinylpyrrolidone, flower bulb alkali, ball milling 1-2 hour, adds each raw material of residue, at 70-90 ℃, be incubated standing 1-2 hour, cooling, fully ball milling, obtains described adhesive aid.
2. a preparation method for the waterproof paint that contains rosin as claimed in claim 1, is characterized in that comprising the following steps:
Above-mentioned aluminum silicate fiber is mixed with gas-phase silica, add Virahol, after stirring, add adhesive aid, ball milling mixes fully, then adds each raw material of residue, and high-speed stirring, to mixing, contains the waterproof paint of rosin described in obtaining.