CN103614037B - A kind of Green environmental-protection building waterproof paint - Google Patents
A kind of Green environmental-protection building waterproof paint Download PDFInfo
- Publication number
- CN103614037B CN103614037B CN201310516341.XA CN201310516341A CN103614037B CN 103614037 B CN103614037 B CN 103614037B CN 201310516341 A CN201310516341 A CN 201310516341A CN 103614037 B CN103614037 B CN 103614037B
- Authority
- CN
- China
- Prior art keywords
- waterproof paint
- raw material
- green environmental
- protection building
- building waterproof
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of Green environmental-protection building waterproof paint, it is made up of the raw material of following weight parts: silica powder 10-16, trimethylolpropane allyl ether 1-2, 2, 2-dimethylol propionic acid 1-2, water glass 1-2, borax 1-2, 1-hydroxycyclohexyl phenyl ketone 0.5-1, polybenzimidazole fibre 2-3, organosilicon crylic acid latex 60-70, zirconium carbonate ammonium 1-2, ceramic fiber 3-4, epoxy soybean oil 2-3, tripoly phosphate sodium STPP 0.4-1, adhesive aid 5-10, deionized water 8-20, waterproof paint of the present invention not only good water-proof effect, and ageing-resistant performance is excellent, bonding force is strong, material ductility is good, application property is good, material safety and environmental protection, have no side effect.
Description
Technical field
The present invention relates generally to a kind of coating, particularly relates to a kind of Green environmental-protection building waterproof paint.
Background technology
Along with development and the refinement of domestic coating industry, market is also more and more outstanding to the requirement with special functional coating, wherein anti-aging, water-fast, acid-alkali-corrosive-resisting, the performance requriements such as fire-retardant are more increased, in order to meet the requirement of every profession and trade to waterproof paint, production high-performance, widely used waterproof paint is necessary.
Summary of the invention
The object of the invention is just to provide a kind of Green environmental-protection building waterproof paint.
The present invention is achieved by the following technical solutions:
A kind of Green environmental-protection building waterproof paint, it is made up of the raw material of following weight parts:
Silica powder 10-16, trimethylolpropane allyl ether 1-2,2,2-dimethylol propionic acid 1-2, water glass 1-2, borax 1-2,1-hydroxycyclohexyl phenyl ketone 0.5-1, polybenzimidazole fibre 2-3, organosilicon crylic acid latex 60-70, zirconium carbonate ammonium 1-2, ceramic fiber 3-4, epoxy soybean oil 2-3, tripoly phosphate sodium STPP 0.4-1, adhesive aid 5-10, deionized water 8-20;
Described adhesive aid is made up of the raw material of following weight parts:
White glue with vinyl 32-40, silane resin acceptor kh-550 4-6, polyvinylpyrrolidone 1-2, sodium silicate 2-3, poly(lactic acid) 3-5, Starso 1-2, nano-sized carbon 1-2;
Above-mentioned poly(lactic acid) is heated to 180-185 DEG C, adds silane resin acceptor kh-550, be uniformly mixed 3-5 minute, reduction temperature is 55-60 DEG C, adds nano-sized carbon, 300-500 rev/min of dispersed with stirring 6-10 minute, be reduced to normal temperature, add Starso, polyvinylpyrrolidone, sodium silicate, ball milling 1-2 hour, add each raw material of residue, at 70-90 DEG C, insulation leaves standstill 1-2 hour, cooling, abundant ball milling, obtains described adhesive aid.
A preparation method for Green environmental-protection building waterproof paint, comprises the following steps:
By above-mentioned silica powder, ceramic fiber, borax mixing, add epoxy soybean oil, tripoly phosphate sodium STPP, the deionized water of above-mentioned weight 50-60% is added after abundant mixing, stirring reaction 10-20 minute at 50-60 DEG C, be cooled to normal temperature, add each raw material of residue, high-speed stirring, to mixing, obtains described Green environmental-protection building waterproof paint.
Advantage of the present invention is:
Waterproof paint of the present invention not only good water-proof effect, and ageing-resistant performance is excellent, bonding force is strong, material ductility is good, application property is good, material safety and environmental protection, has no side effect.
Embodiment
Embodiment 1
A kind of Green environmental-protection building waterproof paint, it is made up of the raw material of following weight parts (kilogram):
Silica powder 16, trimethylolpropane allyl ether 1,2,2-dimethylol propionic acid 1, water glass 2, borax 1,1-hydroxycyclohexyl phenyl ketone 0.5, polybenzimidazole fibre 3, organosilicon crylic acid latex 70, zirconium carbonate ammonium 1, ceramic fiber 4, epoxy soybean oil 3, tripoly phosphate sodium STPP 0.4, adhesive aid 10, deionized water 20;
Described adhesive aid is made up of the raw material of following weight parts:
White glue with vinyl 40, silane resin acceptor kh-550 6, polyvinylpyrrolidone 1, sodium silicate 3, poly(lactic acid) 5, Starso 1, nano-sized carbon 1;
Above-mentioned poly(lactic acid) is heated to 185 DEG C, adds silane resin acceptor kh-550, be uniformly mixed 5 minutes, reducing temperature is 60 DEG C, adds nano-sized carbon, 500 revs/min of dispersed with stirring 10 minutes, be reduced to normal temperature, add Starso, polyvinylpyrrolidone, sodium silicate, ball milling 2 hours, add each raw material of residue, at 90 DEG C, insulation leaves standstill 1 hour, cooling, abundant ball milling, obtains described adhesive aid.
A preparation method for Green environmental-protection building waterproof paint, comprises the following steps:
By above-mentioned silica powder, ceramic fiber, borax mixing, add epoxy soybean oil, tripoly phosphate sodium STPP, the deionized water of above-mentioned weight 60% is added after abundant mixing, stirring reaction 20 minutes at 60 DEG C, be cooled to normal temperature, add each raw material of residue, high-speed stirring, to mixing, obtains described Green environmental-protection building waterproof paint.
Performance test:
Unit elongation: >=300%;
Watertightness: 0.3MPa (one hour waterproof).
Claims (2)
1. a Green environmental-protection building waterproof paint, it is characterized in that what it was made up of the raw material of following weight parts: silica powder 10-16, trimethylolpropane allyl ether 1-2,2,2-dimethylol propionic acid 1-2, water glass 1-2, borax 1-2,1-hydroxycyclohexyl phenyl ketone 0.5-1, polybenzimidazole fibre 2-3, organosilicon crylic acid latex 60-70, zirconium carbonate ammonium 1-2, ceramic fiber 3-4, epoxy soybean oil 2-3, tripoly phosphate sodium STPP 0.4-1, adhesive aid 5-10, deionized water 8-20; Described adhesive aid is made up of the raw material of following weight parts: white glue with vinyl 32-40, silane resin acceptor kh-550 4-6, polyvinylpyrrolidone 1-2, sodium silicate 2-3, poly(lactic acid) 3-5, Starso 1-2, nano-sized carbon 1-2; Above-mentioned poly(lactic acid) is heated to 180-185 DEG C, adds silane resin acceptor kh-550, be uniformly mixed 3-5 minute, reduction temperature is 55-60 DEG C, adds nano-sized carbon, 300-500 rev/min of dispersed with stirring 6-10 minute, be reduced to normal temperature, add Starso, polyvinylpyrrolidone, sodium silicate, ball milling 1-2 hour, add each raw material of residue, at 70-90 DEG C, insulation leaves standstill 1-2 hour, cooling, abundant ball milling, obtains described adhesive aid.
2. the preparation method of a Green environmental-protection building waterproof paint as claimed in claim 1, it is characterized in that comprising the following steps: by above-mentioned silica powder, ceramic fiber, borax mixing, add epoxy soybean oil, tripoly phosphate sodium STPP, the deionized water of above-mentioned weight 50-60% is added after abundant mixing, at 50-60 DEG C, stirring reaction 10-20 minute, is cooled to normal temperature, adds each raw material of residue, high-speed stirring, to mixing, obtains described Green environmental-protection building waterproof paint.