CN105348970A - Process for preparing waterproof material - Google Patents
Process for preparing waterproof material Download PDFInfo
- Publication number
- CN105348970A CN105348970A CN201510948936.1A CN201510948936A CN105348970A CN 105348970 A CN105348970 A CN 105348970A CN 201510948936 A CN201510948936 A CN 201510948936A CN 105348970 A CN105348970 A CN 105348970A
- Authority
- CN
- China
- Prior art keywords
- weight part
- weight
- component
- parts
- mixed
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a process for preparing a waterproof material. The process comprises the following steps: 1) uniformly mixing 1-2 parts by weight of sodium silicate, 1.1 parts by weight of polytetrafluoroethylene micro powder, 1.3 parts by weight of imidazoline, 7.9 parts by weight of silicone acrylic emulsion and 15.5 parts by weight of water to prepare a component A; 2) uniformly mixing 1.2 parts by weight of cis-isoprene rubber, 0.7 part by weight of calcium lactate, 1.3 parts by weight of fluorine-containing acrylic acid resin, 1.9 parts by weight of vinyl trimethoxy silane and 9.2 parts by weight of quartz sand to prepare a component B; and 3) mixing 1.5 parts by weight of the component A with 2.3 parts by weight of the component B, heating to 59 DEG C, stirring uniformly, and cooling naturally to prepare the waterproof material. The waterproof material prepared by the process for preparing the waterproof material, disclosed by the invention, is good in flexibility, water resistance and crack resistance, and is suitable for preparing kitchen and toilet products.
Description
Technical field
The present invention relates to the technique preparing water-proof material.
Background technology
Existing kitchen products, its snappiness, water-repellancy, crack resistence performance have much room for improvement.
Summary of the invention
The object of the present invention is to provide a kind of technique preparing water-proof material, the water-proof material of preparation has good snappiness, water-repellancy, crack resistence, is applicable to preparing kitchen products.
For achieving the above object, technical scheme of the present invention is a kind of technique preparing water-proof material of design, comprises the steps:
1) 1 ~ 2 weight part sodium silicate, 1.1 weight part ptfe micropowders, 1.3 weight part tetrahydroglyoxalines, 7.9 weight part organosilicon crylic acid latexs, 15.5 weight parts waters are mixed, obtained component A;
2) 1.2 weight part cis polyisoprene rubbers, 0.7 weight part calcium lactate, 1.3 weight part fluoroacrylic resins, 1.9 parts by weight of ethylene base Trimethoxy silanes, 9.2 weight part quartz sands are mixed, obtained B component;
3) 1.5 weight part component A are mixed with 2.3 weight part B component, be heated to 59 DEG C, then stir, naturally cooling, obtained water-proof material.
Preferably, prepare the technique of water-proof material, comprise the steps:
1) 1 weight part sodium silicate, 1.1 weight part ptfe micropowders, 1.3 weight part tetrahydroglyoxalines, 7.9 weight part organosilicon crylic acid latexs, 15.5 weight parts waters are mixed, obtained component A;
2) 1.2 weight part cis polyisoprene rubbers, 0.7 weight part calcium lactate, 1.3 weight part fluoroacrylic resins, 1.9 parts by weight of ethylene base Trimethoxy silanes, 9.2 weight part quartz sands are mixed, obtained B component;
3) 1.5 weight part component A are mixed with 2.3 weight part B component, be heated to 59 DEG C, then stir, naturally cooling, obtained water-proof material.
Preferably, prepare the technique of water-proof material, comprise the steps:
1) 2 weight part sodium silicate, 1.1 weight part ptfe micropowders, 1.3 weight part tetrahydroglyoxalines, 7.9 weight part organosilicon crylic acid latexs, 15.5 weight parts waters are mixed, obtained component A;
2) 1.2 weight part cis polyisoprene rubbers, 0.7 weight part calcium lactate, 1.3 weight part fluoroacrylic resins, 1.9 parts by weight of ethylene base Trimethoxy silanes, 9.2 weight part quartz sands are mixed, obtained B component;
3) 1.5 weight part component A are mixed with 2.3 weight part B component, be heated to 59 DEG C, then stir, naturally cooling, obtained water-proof material.
Advantage of the present invention and beneficial effect are: provide a kind of technique preparing water-proof material, and the water-proof material of preparation has good snappiness, water-repellancy, crack resistence, is applicable to preparing kitchen products.
Embodiment
Below in conjunction with embodiment, the specific embodiment of the present invention is further described.Following examples only for technical scheme of the present invention is clearly described, and can not limit the scope of the invention with this.
The technical scheme that the present invention specifically implements is:
Embodiment 1
Prepare a technique for water-proof material, comprise the steps:
1) 1 ~ 2 weight part sodium silicate, 1.1 weight part ptfe micropowders, 1.3 weight part tetrahydroglyoxalines, 7.9 weight part organosilicon crylic acid latexs, 15.5 weight parts waters are mixed, obtained component A;
2) 1.2 weight part cis polyisoprene rubbers, 0.7 weight part calcium lactate, 1.3 weight part fluoroacrylic resins, 1.9 parts by weight of ethylene base Trimethoxy silanes, 9.2 weight part quartz sands are mixed, obtained B component;
3) 1.5 weight part component A are mixed with 2.3 weight part B component, be heated to 59 DEG C, then stir, naturally cooling, obtained water-proof material.
Embodiment 2
Prepare the technique of water-proof material, comprise the steps:
1) 1 weight part sodium silicate, 1.1 weight part ptfe micropowders, 1.3 weight part tetrahydroglyoxalines, 7.9 weight part organosilicon crylic acid latexs, 15.5 weight parts waters are mixed, obtained component A;
2) 1.2 weight part cis polyisoprene rubbers, 0.7 weight part calcium lactate, 1.3 weight part fluoroacrylic resins, 1.9 parts by weight of ethylene base Trimethoxy silanes, 9.2 weight part quartz sands are mixed, obtained B component;
3) 1.5 weight part component A are mixed with 2.3 weight part B component, be heated to 59 DEG C, then stir, naturally cooling, obtained water-proof material.
Embodiment 3
Prepare the technique of water-proof material, comprise the steps:
1) 2 weight part sodium silicate, 1.1 weight part ptfe micropowders, 1.3 weight part tetrahydroglyoxalines, 7.9 weight part organosilicon crylic acid latexs, 15.5 weight parts waters are mixed, obtained component A;
2) 1.2 weight part cis polyisoprene rubbers, 0.7 weight part calcium lactate, 1.3 weight part fluoroacrylic resins, 1.9 parts by weight of ethylene base Trimethoxy silanes, 9.2 weight part quartz sands are mixed, obtained B component;
3) 1.5 weight part component A are mixed with 2.3 weight part B component, be heated to 59 DEG C, then stir, naturally cooling, obtained water-proof material.
The above is only the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, under the prerequisite not departing from the technology of the present invention principle; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.
Claims (3)
1. prepare the technique of water-proof material, it is characterized in that, comprise the steps:
1) 1 ~ 2 weight part sodium silicate, 1.1 weight part ptfe micropowders, 1.3 weight part tetrahydroglyoxalines, 7.9 weight part organosilicon crylic acid latexs, 15.5 weight parts waters are mixed, obtained component A;
2) 1.2 weight part cis polyisoprene rubbers, 0.7 weight part calcium lactate, 1.3 weight part fluoroacrylic resins, 1.9 parts by weight of ethylene base Trimethoxy silanes, 9.2 weight part quartz sands are mixed, obtained B component;
3) 1.5 weight part component A are mixed with 2.3 weight part B component, be heated to 59 DEG C, then stir, naturally cooling, obtained water-proof material.
2. the technique preparing water-proof material according to claim 1, is characterized in that, comprise the steps:
1) 1 weight part sodium silicate, 1.1 weight part ptfe micropowders, 1.3 weight part tetrahydroglyoxalines, 7.9 weight part organosilicon crylic acid latexs, 15.5 weight parts waters are mixed, obtained component A;
2) 1.2 weight part cis polyisoprene rubbers, 0.7 weight part calcium lactate, 1.3 weight part fluoroacrylic resins, 1.9 parts by weight of ethylene base Trimethoxy silanes, 9.2 weight part quartz sands are mixed, obtained B component;
3) 1.5 weight part component A are mixed with 2.3 weight part B component, be heated to 59 DEG C, then stir, naturally cooling, obtained water-proof material.
3. the technique preparing water-proof material according to claim 1, is characterized in that, comprise the steps:
1) 2 weight part sodium silicate, 1.1 weight part ptfe micropowders, 1.3 weight part tetrahydroglyoxalines, 7.9 weight part organosilicon crylic acid latexs, 15.5 weight parts waters are mixed, obtained component A;
2) 1.2 weight part cis polyisoprene rubbers, 0.7 weight part calcium lactate, 1.3 weight part fluoroacrylic resins, 1.9 parts by weight of ethylene base Trimethoxy silanes, 9.2 weight part quartz sands are mixed, obtained B component;
3) 1.5 weight part component A are mixed with 2.3 weight part B component, be heated to 59 DEG C, then stir, naturally cooling, obtained water-proof material.