CN105503073A - Waterproof material production method - Google Patents
Waterproof material production method Download PDFInfo
- Publication number
- CN105503073A CN105503073A CN201510948931.9A CN201510948931A CN105503073A CN 105503073 A CN105503073 A CN 105503073A CN 201510948931 A CN201510948931 A CN 201510948931A CN 105503073 A CN105503073 A CN 105503073A
- Authority
- CN
- China
- Prior art keywords
- weight part
- weight
- parts
- component
- mixed
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a waterproof material production method. The method comprises the steps of 1, evenly mixing 1-2 parts by weight of hexyldecanol, 3.5 parts by weight of chlorinated paraffin, 1.8 parts by weight of lauryl sodium sulfate, 8.5 parts by weight of silicone acrylic emulsion and 15 parts by weight of water, so that a component A is obtained; 2, evenly mixing 2.6 parts by weight of amorphous state alpha-olefin copolymer, 2.3 parts by weight of portland cement, 1.7 parts by weight of polyethylene glycol octylphenol ether, 2.4 parts by weight of hydroxy propyl methylcellulose and 8.1 parts by weight of quartz sand, so that a component B is obtained; 3, mixing 6.7 parts by weight of component A and 3.5 parts by weight of component B, increasing temperature to 50 DEG C, and conducting even stirring and natural cooling, so that a waterproof material is obtained. The waterproof material prepared with the method has high flexibility, water resistance and cracking resistance and is suitable for manufacturing kitchen and toilet products.
Description
Technical field
The present invention relates to the production method of water-proof material.
Background technology
Existing kitchen products, its snappiness, water-repellancy, crack resistence performance have much room for improvement.
Summary of the invention
The object of the present invention is to provide a kind of production method of water-proof material, the water-proof material of preparation has good snappiness, water-repellancy, crack resistence, is applicable to preparing kitchen products.
For achieving the above object, technical scheme of the present invention designs a kind of production method of water-proof material, comprises the steps:
1) 1 ~ 2 weight part hexyl decyl alcohol, 3.5 weight part clorafins, 1.8 weight part sodium lauryl sulphate, 8.5 weight part organosilicon crylic acid latexs, 15 weight parts waters are mixed, obtained component A;
2) 2.6 weight part non-crystalline state a-olefin copolymers, 2.3 parts by weight silicate cement, 1.7 weight part Triton X-100s, 2.4 weight part HYDROXY PROPYL METHYLCELLULOSE, 8.1 weight part quartz sands are mixed, obtained B component;
3) 6.7 weight part component A are mixed with 3.5 weight part B component, be heated to 50 DEG C, then stir, naturally cooling, obtained water-proof material.
Preferably, the production method of water-proof material, comprises the steps:
1) 1 weight part hexyl decyl alcohol, 3.5 weight part clorafins, 1.8 weight part sodium lauryl sulphate, 8.5 weight part organosilicon crylic acid latexs, 15 weight parts waters are mixed, obtained component A;
2) 2.6 weight part non-crystalline state a-olefin copolymers, 2.3 parts by weight silicate cement, 1.7 weight part Triton X-100s, 2.4 weight part HYDROXY PROPYL METHYLCELLULOSE, 8.1 weight part quartz sands are mixed, obtained B component;
3) 6.7 weight part component A are mixed with 3.5 weight part B component, be heated to 50 DEG C, then stir, naturally cooling, obtained water-proof material.
Preferably, the production method of water-proof material, comprises the steps:
1) 2 weight part hexyl decyl alcohol, 3.5 weight part clorafins, 1.8 weight part sodium lauryl sulphate, 8.5 weight part organosilicon crylic acid latexs, 15 weight parts waters are mixed, obtained component A;
2) 2.6 weight part non-crystalline state a-olefin copolymers, 2.3 parts by weight silicate cement, 1.7 weight part Triton X-100s, 2.4 weight part HYDROXY PROPYL METHYLCELLULOSE, 8.1 weight part quartz sands are mixed, obtained B component;
3) 6.7 weight part component A are mixed with 3.5 weight part B component, be heated to 50 DEG C, then stir, naturally cooling, obtained water-proof material.
Advantage of the present invention and beneficial effect are: the production method providing a kind of water-proof material, and the water-proof material of preparation has good snappiness, water-repellancy, crack resistence, is applicable to preparing kitchen products.
Embodiment
Below in conjunction with embodiment, the specific embodiment of the present invention is further described.Following examples only for technical scheme of the present invention is clearly described, and can not limit the scope of the invention with this.
The technical scheme that the present invention specifically implements is:
Embodiment 1
A production method for water-proof material, comprises the steps:
1) 1 ~ 2 weight part hexyl decyl alcohol, 3.5 weight part clorafins, 1.8 weight part sodium lauryl sulphate, 8.5 weight part organosilicon crylic acid latexs, 15 weight parts waters are mixed, obtained component A;
2) 2.6 weight part non-crystalline state a-olefin copolymers, 2.3 parts by weight silicate cement, 1.7 weight part Triton X-100s, 2.4 weight part HYDROXY PROPYL METHYLCELLULOSE, 8.1 weight part quartz sands are mixed, obtained B component;
3) 6.7 weight part component A are mixed with 3.5 weight part B component, be heated to 50 DEG C, then stir, naturally cooling, obtained water-proof material.
Embodiment 2
The production method of water-proof material, comprises the steps:
1) 1 weight part hexyl decyl alcohol, 3.5 weight part clorafins, 1.8 weight part sodium lauryl sulphate, 8.5 weight part organosilicon crylic acid latexs, 15 weight parts waters are mixed, obtained component A;
2) 2.6 weight part non-crystalline state a-olefin copolymers, 2.3 parts by weight silicate cement, 1.7 weight part Triton X-100s, 2.4 weight part HYDROXY PROPYL METHYLCELLULOSE, 8.1 weight part quartz sands are mixed, obtained B component;
3) 6.7 weight part component A are mixed with 3.5 weight part B component, be heated to 50 DEG C, then stir, naturally cooling, obtained water-proof material.
Embodiment 3
The production method of water-proof material, comprises the steps:
1) 2 weight part hexyl decyl alcohol, 3.5 weight part clorafins, 1.8 weight part sodium lauryl sulphate, 8.5 weight part organosilicon crylic acid latexs, 15 weight parts waters are mixed, obtained component A;
2) 2.6 weight part non-crystalline state a-olefin copolymers, 2.3 parts by weight silicate cement, 1.7 weight part Triton X-100s, 2.4 weight part HYDROXY PROPYL METHYLCELLULOSE, 8.1 weight part quartz sands are mixed, obtained B component;
3) 6.7 weight part component A are mixed with 3.5 weight part B component, be heated to 50 DEG C, then stir, naturally cooling, obtained water-proof material.
The above is only the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, under the prerequisite not departing from the technology of the present invention principle; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.
Claims (3)
1. the production method of water-proof material, is characterized in that, comprises the steps:
1) 1 ~ 2 weight part hexyl decyl alcohol, 3.5 weight part clorafins, 1.8 weight part sodium lauryl sulphate, 8.5 weight part organosilicon crylic acid latexs, 15 weight parts waters are mixed, obtained component A;
2) 2.6 weight part non-crystalline state a-olefin copolymers, 2.3 parts by weight silicate cement, 1.7 weight part Triton X-100s, 2.4 weight part HYDROXY PROPYL METHYLCELLULOSE, 8.1 weight part quartz sands are mixed, obtained B component;
3) 6.7 weight part component A are mixed with 3.5 weight part B component, be heated to 50 DEG C, then stir, naturally cooling, obtained water-proof material.
2. the production method of water-proof material according to claim 1, is characterized in that, comprises the steps:
1) 1 weight part hexyl decyl alcohol, 3.5 weight part clorafins, 1.8 weight part sodium lauryl sulphate, 8.5 weight part organosilicon crylic acid latexs, 15 weight parts waters are mixed, obtained component A;
2) 2.6 weight part non-crystalline state a-olefin copolymers, 2.3 parts by weight silicate cement, 1.7 weight part Triton X-100s, 2.4 weight part HYDROXY PROPYL METHYLCELLULOSE, 8.1 weight part quartz sands are mixed, obtained B component;
3) 6.7 weight part component A are mixed with 3.5 weight part B component, be heated to 50 DEG C, then stir, naturally cooling, obtained water-proof material.
3. the production method of water-proof material according to claim 1, is characterized in that, comprises the steps:
1) 2 weight part hexyl decyl alcohol, 3.5 weight part clorafins, 1.8 weight part sodium lauryl sulphate, 8.5 weight part organosilicon crylic acid latexs, 15 weight parts waters are mixed, obtained component A;
2) 2.6 weight part non-crystalline state a-olefin copolymers, 2.3 parts by weight silicate cement, 1.7 weight part Triton X-100s, 2.4 weight part HYDROXY PROPYL METHYLCELLULOSE, 8.1 weight part quartz sands are mixed, obtained B component;
3) 6.7 weight part component A are mixed with 3.5 weight part B component, be heated to 50 DEG C, then stir, naturally cooling, obtained water-proof material.