CN104446273A - Production process of waterproof material - Google Patents
Production process of waterproof material Download PDFInfo
- Publication number
- CN104446273A CN104446273A CN201410730570.6A CN201410730570A CN104446273A CN 104446273 A CN104446273 A CN 104446273A CN 201410730570 A CN201410730570 A CN 201410730570A CN 104446273 A CN104446273 A CN 104446273A
- Authority
- CN
- China
- Prior art keywords
- parts
- weight
- weight part
- component
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a production process of a waterproof material. The production process comprises the following steps of (1) uniformly mixing the following components in parts by weight: 5 parts of diatomite, 3.7 parts of epichlorohydrin, 4 parts of a silicone-acrylate emulsion, 3 parts of oleic acid and 9 parts of water to prepare a component A; (2) uniformly mixing the following components in parts by weight: 4.6 parts of ordinary portland cement, 2.1 parts of calcium lignosulfonate, 2.1 parts of high-alumina cement, 1.8 parts of quartz sand and 1.7 parts of cellulose ether to prepare a component B; and (3) mixing 3 parts by weight of the component A and 2 parts by weight of the component B, heating to 54 DEG C, then, uniformly stirring, and naturally cooling to prepare the waterproof material. The waterproof material prepared by using the production process is favorable in flexibility, water resistance and cracking resistance and is suitable for preparing kitchen and toilet products.
Description
Technical field
The present invention relates to the technique for the production of water-proof material.
Background technology
Existing kitchen products, its snappiness, water-repellancy, crack resistence performance have much room for improvement.
Summary of the invention
The object of the present invention is to provide a kind of technique for the production of water-proof material, its water-proof material prepared has good snappiness, water-repellancy, crack resistence, is applicable to preparing kitchen products.
For achieving the above object, technical scheme of the present invention is a kind of technique for the production of water-proof material of design, comprises the steps:
1) 5 weight part diatomite, 3.7 parts by weight epoxy chloropropanes, 4 weight part organosilicon crylic acid latexs, 3 weight part oleic acid, 9 weight parts waters are mixed, obtained component A;
2) 4.6 weight part ordinary Portland cements, 2.1 weight part calcium lignosulfonates, 2.1 weight part high-alumina cements, 1.8 weight part quartz sands, 1.7 part by weight of cellulose ethers are mixed, obtained B component;
3) 3 weight part component A are mixed with 2 weight part B component, be heated to 54 DEG C, then stir, naturally cooling, obtained water-proof material.
Advantage of the present invention and beneficial effect are: provide a kind of technique for the production of water-proof material, and its water-proof material prepared has good snappiness, water-repellancy, crack resistence, is applicable to preparing kitchen products.
Embodiment
Below in conjunction with embodiment, the specific embodiment of the present invention is further described.Following examples only for technical scheme of the present invention is clearly described, and can not limit the scope of the invention with this.
The technical scheme that the present invention specifically implements is:
For the production of a technique for water-proof material, comprise the steps:
1) 5 weight part diatomite, 3.7 parts by weight epoxy chloropropanes, 4 weight part organosilicon crylic acid latexs, 3 weight part oleic acid, 9 weight parts waters are mixed, obtained component A;
2) 4.6 weight part ordinary Portland cements, 2.1 weight part calcium lignosulfonates, 2.1 weight part high-alumina cements, 1.8 weight part quartz sands, 1.7 part by weight of cellulose ethers are mixed, obtained B component;
3) 3 weight part component A are mixed with 2 weight part B component, be heated to 54 DEG C, then stir, naturally cooling, obtained water-proof material.
The above is only the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, under the prerequisite not departing from the technology of the present invention principle; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.
Claims (1)
1. for the production of the technique of water-proof material, it is characterized in that, comprise the steps:
1) 5 weight part diatomite, 3.7 parts by weight epoxy chloropropanes, 4 weight part organosilicon crylic acid latexs, 3 weight part oleic acid, 9 weight parts waters are mixed, obtained component A;
2) 4.6 weight part ordinary Portland cements, 2.1 weight part calcium lignosulfonates, 2.1 weight part high-alumina cements, 1.8 weight part quartz sands, 1.7 part by weight of cellulose ethers are mixed, obtained B component;
3) 3 weight part component A are mixed with 2 weight part B component, be heated to 54 DEG C, then stir, naturally cooling, obtained water-proof material.