CN104496366A - Production method of waterproof material - Google Patents
Production method of waterproof material Download PDFInfo
- Publication number
- CN104496366A CN104496366A CN201410730619.8A CN201410730619A CN104496366A CN 104496366 A CN104496366 A CN 104496366A CN 201410730619 A CN201410730619 A CN 201410730619A CN 104496366 A CN104496366 A CN 104496366A
- Authority
- CN
- China
- Prior art keywords
- parts
- weight
- component
- weight part
- production method
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a production method of a waterproof material. The production method comprises the following steps of (1) uniformly mixing the following components in parts by weight: 1 part of acetic acid, 4.2 parts of calcium chloride, 7 parts of a silicone-acrylate emulsion, 1.1 parts of salicylic acid and 6.8 parts of water to obtain a component A; (2) uniformly mixing the following components in parts by weight: 3 parts of cellulose ether, 4.8 parts of high alumina cement, 3.4 parts of ordinary portland cement, 2.5 parts of quartz sand and 1.6 parts of sodium sulfite to obtain a component B; and (3) mixing 4 parts of the component A and 6 parts of the component B, heating to 52 DEG C, then, uniformly stirring, and naturally cooling to obtain the waterproof material. The waterproof material prepared by using the production method is favorable in flexibility, waterproofness and crack resistance and suitable for preparing kitchen and toilet products.
Description
Technical field
The present invention relates to the method for the production of water-proof material.
Background technology
Existing kitchen products, its snappiness, water-repellancy, crack resistence performance have much room for improvement.
Summary of the invention
The object of the present invention is to provide a kind of method for the production of water-proof material, its water-proof material prepared has good snappiness, water-repellancy, crack resistence, is applicable to preparing kitchen products.
For achieving the above object, technical scheme of the present invention is a kind of method for the production of water-proof material of design, comprises the steps:
1) 1 parts by weight acetic acid, 4.2 weight part calcium chloride, 7 weight part organosilicon crylic acid latexs, 1.1 weight part Whitfield's ointments, 6.8 weight parts waters are mixed, obtained component A;
2) 3 part by weight of cellulose ethers, 4.8 weight part high-alumina cements, 3.4 weight part ordinary Portland cements, 2.5 weight part quartz sands, 1.6 parts by weight sodium sulfite are mixed, obtained B component;
3) 4 weight part component A are mixed with 6 weight part B component, be heated to 52 DEG C, then stir, naturally cooling, obtained water-proof material.
Advantage of the present invention and beneficial effect are: provide a kind of method for the production of water-proof material, and its water-proof material prepared has good snappiness, water-repellancy, crack resistence, is applicable to preparing kitchen products.
Embodiment
Below in conjunction with embodiment, the specific embodiment of the present invention is further described.Following examples only for technical scheme of the present invention is clearly described, and can not limit the scope of the invention with this.
The technical scheme that the present invention specifically implements is:
For the production of a method for water-proof material, comprise the steps:
1) 1 parts by weight acetic acid, 4.2 weight part calcium chloride, 7 weight part organosilicon crylic acid latexs, 1.1 weight part Whitfield's ointments, 6.8 weight parts waters are mixed, obtained component A;
2) 3 part by weight of cellulose ethers, 4.8 weight part high-alumina cements, 3.4 weight part ordinary Portland cements, 2.5 weight part quartz sands, 1.6 parts by weight sodium sulfite are mixed, obtained B component;
3) 4 weight part component A are mixed with 6 weight part B component, be heated to 52 DEG C, then stir, naturally cooling, obtained water-proof material.
The above is only the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, under the prerequisite not departing from the technology of the present invention principle; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.
Claims (1)
1. for the production of the method for water-proof material, it is characterized in that, comprise the steps:
1) 1 parts by weight acetic acid, 4.2 weight part calcium chloride, 7 weight part organosilicon crylic acid latexs, 1.1 weight part Whitfield's ointments, 6.8 weight parts waters are mixed, obtained component A;
2) 3 part by weight of cellulose ethers, 4.8 weight part high-alumina cements, 3.4 weight part ordinary Portland cements, 2.5 weight part quartz sands, 1.6 parts by weight sodium sulfite are mixed, obtained B component;
3) 4 weight part component A are mixed with 6 weight part B component, be heated to 52 DEG C, then stir, naturally cooling, obtained water-proof material.